• Proceedings of the KWS Conference
• /
• 2001.10a
• /
• pp.81-84
• /
• 2001

This study introduces the new way for the evaluation criteria of the Mash-Seam Tailored Blank weldability, The materials used are low carbon automotive galvanized and high strength steels and the evaluation of weldability are examined with various thickness. Welding tests were conducted for both similar thickness and dissimilar thickness cases. The criteria developed for optimum welding conditions were based on the relationship among results of die press forming test, forming limit diagram, Erichsen test and microhardness measurements. The application of the developed criteria(fracture ratio, strength ratio, etc) in obtaining optimum welding condition revealed that a weld which satisfied ant of the criteria did not fracture during actual die press test and FLD dome test.

• Journal of Welding and Joining
• /
• v.34 no.6
• /
• pp.28-34
• /
• 2016

Galvannealed(GA) steels are now generally used in car body manufacturing for corrosion resistance. In this study, the weldability and joint mechanical behavior of a newly developed 1.2GPa grade GA ultra high strength TRIP(transformation induced plasticity) steel was investigated for three joining processes, such as adhesive bonding, resistance spot welding and weldbonding. Under both shear and peel stress conditions, the failure mode of the adhesive joints were the mixture of the adhesive cohesive failure, adhesive interface failure and coating layer failure. It means that the adhesion strength of GA coating onto the base metal was similar to that of adhesive bonding onto the GA coating. Under the shear stress condition, the weldbonding exerted to expand the optimal spot welding condition of 1.2GPa GA TRIP steel because the strength of adhesive bond overwhelmed that of the resistance spot weld. Under the peel stress condition, the weldbonding also exerted to expand the optimal spot welding condition of 1.2GPa GA TRIP steel by inducing the tear fracture mode rather than the partial plug fracture mode.

• Korean Journal of Materials Research
• /
• v.15 no.1
• /
• pp.19-24
• /
• 2005

For the good combination of high-temperature strength, toughness and creep property, $9-12\%$ chromium steels are often used for gas turbine compressors, steam turbine rotors, blade and casing. In this study, the correlation of microstructural evolution and mechanical properties was investigated fur the specimens heat-treated at 600, 650 and $700^{\circ}C$ for 1000, 3000 and 5000 hrs. The microstructure of as-received specimen was tempered martensite with a high dislocation density, small sub-grains and fine secondary phase such as $M_23C_6$. Aging for long-time at high temperature caused the growth of martensite lath and the decrease of dislocation density resulting in the decrease in strength. However, the evolution of secondary phases had influence on hardness, yield strength and impact property. In the group A specimen aged at $600^{\circ}C\;and\;650^{\circ}C$, Laves phase was observed. The Laves phase caused the increase of the hardness and the decrease of the impact property. In addition, the abrupt growth of secondary phases caused decrease of the impact property in both A and B group specimens.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 1999.08a
• /
• pp.356-365
• /
• 1999

The present study is aimed at developing the TRIP(transformation induced plasticity) aided high strength low carbon steel using reversion process. An excellent combination of elongation over 40% and tensile strength abut 100kgf/$\textrm{mm}^2$ achieved in processing of 0.15C-0.5 Si-6Mn steel by slow heating to intercritial temperature region and accelerated cooling into room temperature. This good combination is caused by TRIP phenomena of retained austenite in steels during deformation. The stability of retained austenite is very important for the good ductility and it depends on the diffusion of carbon and manganeses during heat treatment. The accelerated cooling after holding at annealing temperature retards the formation of pearlite and provides the carbon enrichment in retained austenite in steel, resulting in the increase in elongation of the cold-rolled TRIP steel. On the other hand, heat treating the steel at 600$^{\circ}C$ for 5 hour before cold rolling increases elongation but reduces the amount of retained austenite after reversion processing. It is accounted that the heat treating is effective for the increase in the stability of retained austenite.

• Journal of the Korean Society for Heat Treatment
• /
• v.30 no.3
• /
• pp.117-126
• /
• 2017

The variation in microstructure and mechanical properties during heat treatment was examined in a series of 0.27% C-1.5% Mn-1.0% Cr steels with silicon contents in the range of 0 to 1.0 wt%. It was found that addition of 0.5%~1.0% silicon increased both tensile strength and impact toughness through solid solution strengthening and microstructural refinement. 0.27% C-1.0% Si-1.5% Mn-1.0% Cr steel showed tensile strength of 1,700 MPa in the as-quenched condition and the steel revealed a full martensitic structure even after air cooling from $900^{\circ}C$ to room temperature, showing air hardening characteristics. Tempering at $150^{\circ}C$ which corresponds to the typical paint-baking temperature after painting of body in white, slightly decreased the tensile strength and increased elongation, but substantially increased the impact toughness compared to the as-quenched steel.

• Journal of the Korean Society for Heat Treatment
• /
• v.29 no.4
• /
• pp.181-189
• /
• 2016

The variation in microstructure and mechanical properties during heat treatment was examined in a series of 0.27% C-1.0% Si-1.5% Mn steels with chromium contents in the range of 0 to 1.0 wt%. It was found that chromium decreased the martensite packet size through the austenite grain refinement and increased tensile strength in the as-quenched steel, about 70 MPa per 1.0 wt%. The 0.27% C-1.0% Si-1.5% Mn-1.0% Cr steel showed tensile strength of 1700 MPa in the as-quenched steel. The 0.27% C-1.0% Si-1.5% Mn-1.0% Cr steel revealed a full martensitic structure after air cooling from $900^{\circ}C$ to room temperature, showing air hardening characteristics. Tempering at $150^{\circ}C$ slightly decreased the tensile strength and increased elongation, which is in a good agreement with impact toughness result.

• Journal of Welding and Joining
• /
• v.31 no.2
• /
• pp.30-36
• /
• 2013

Recently the use of ultra high strength steels(UHSS) in structural and safety component is rapidly increasing in the automotive industry. Furthermore, it commonly use in tailor welded blank laser welding process before hot stamping to reduce lightweight vehicle. However TWB process is to be a problem about welded strength after hot stamping because it's welded before heat treatment. Therefore, in this study, laser welds of TWB after heat treatment were analyzed for changes in the characteristics, especially the impact on the oxidation and decarburization in order to prevent pre-coated Al-Si layer welds on the properties for intensive investigation. As a result, the degradation of the TWB weldments changes in the heat treatment conditions alone, without any pre-treatment of the coating layer has confirmed that there is a limitation on the improvement. Furthermore Al-Si elements are overall distributed on the weldment and it specially concentrated along the fusion line. Hardness value of Al-Si segregation area is less than 350Hv and tensile strength showed just 78~83% compared with substrate. Accordingly, we proved that both side Al-Si coating should be removed in order to ensure the strength of the substrate.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2008.10a
• /
• pp.226-229
• /
• 2008

Hot press forming is an advanced forming technology fur manufacturing of complex and crash-resistant automotive parts using ultra high strength steels. The 3-dimensional FE analysis of hot press forming process, in which process the deformation, heat transfer and phase transformation behavior are fully coupled, is carried out. The vast amount of material properties for the FE analysis is obtained from material properties calculation software which is based on thermodynamic calculations. The overall methodology for the FE analysis of HPF process and the analysis results are discussed here.

• Proceedings of the KWS Conference
• /
• 2002.10a
• /
• pp.89-93
• /
• 2002

A study of noticeable improvement in welding speed in thin-plate Type 304 stainless steels gas tungsten arc (GTA) welding was investigated. The welding speeds were increased to more than 3m/min, up to 8m/min. During the welding, Direct Current Straight Polarity (DCSP) and pulsed current GTA welding processes were carried out, respectively. The appropriate high speed welding parameters were established while achieving a high quality weld. After this, Erichsen test and tensile test were performed. The results obtained wert summarized as following: ultra high speed welding for thin-plate Type 304 could be satisfactorily welded with high speed from 3m/min to 8m/min in both DCSP and pulsed GTA welding; Increasing welding speed was found to decrease the ductility, tensile strength md elongation of welded joint; The optimal frequency would be 200Hz-500Hz for high speed welding in pulsed current welding; DCSP welding could obtain the better results of Erichsen test and tensile test than those of pulsed current welding obtained.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.20 no.2
• /
• pp.98-102
• /
• 2012

Increasing the fuel economy has been an inevitable issue for the development of new cars, and one of the important measures to improve the fuel economy is to decrease the vehicle weight. In order to obtain this goal, the researches about lighter, stronger and the well impact absorbing bumper impact beam have been studied without sacrificing bumper safety. In this study, the overall weight reduction possibility of rear bumper impact beam could be examined based on the variation of frontal, offset and corner impact crash capability by substituting a ultra high strength steel material (boron steel ) having tensile strength of 1.5 GPa grade instead of conventional steels. In addition, the section variations (open section, closed section, open section with 5 stays) of the bumper impact beam structure were examined carefully. It could be reached that this analysis could be well established and be contributed for design guide and the optimum design conditions of the automotive rear bumper impact beam development.