• Proceedings of the KOSOMBE Conference
• /
• v.1998 no.11
• /
• pp.229-230
• /
• 1998

Triblock copolymers from poly(ethylene glycol) (PEG) and D,L-lactide or $\varepsilon$-carprolactone were synthesized to prepare semi-interpenetrating polymer network (semi-IPN) with chitosan by U.V. irradiation method. Then, solute permeation through these semi-IPNs hydrogels were investigated. The structures of semi-IPNs were confirmed by FT-IR spectroscopy and wide angle X-ray diffractometer (WAXD). Equilibrium water content (EWC) of these hydrogels was in the range of 67-75%. The crystallinity, thermal properties and mechanical properties of semi-IPNs hydrogels were studied. All the hydrogels revealed a remarkable decrease in crystallinity as compared with PEG macromer itself. The tensile strengths of semi-IPNs hydrogels in dry state were rather high, but those of hydrogels in wet state decreased drastically. The permeabilities of solutes of hydrogels followed the swelling behaviors and were regulated by solute size.

• Journal of the Korean Society for Precision Engineering
• /
• v.24 no.5
• /
• pp.97-103
• /
• 2007

A novel selective metallization process to fabricate the fine conductive line based on inkjet printing has been investigated. Recently, Inkjet printing has been widely used in flat panel display, electronic circuits, biochips and bioMEMS because direct inkjet printing is an alternative and cost-effective technology for patterning and fabricating objects directly from design without masks. The photosensitive etching resist used in this process is an organic polymer which becomes solidified when exposed to ultraviolet lights and has high viscosity at ambient temperature. A piezoelectric-driven inkjet printhead is used to dispense 20-30 ${\mu}m$ diameter droplets onto the copper substrate to prevent subsequent etching. Repeatability of circuitry fabrication is closely related to the formation of steady droplets, adhesion between etching resist and copper substrate. Therefore, the ability to form small and stable droplets and surface topography of the copper surface and chemical attack must be taken into consideration for fine and precise patterns. In this study, factors affecting the pattern formation such as adhesion strength, etching mechanism, UV curing have been investigated. As a result, microscale copper patterns with tens of urn high have been fabricated.

• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.43 no.3
• /
• pp.98-105
• /
• 2011

Patterns and levels of aging vary between the book volume and sheets, even though both are made from the same paper materials. In case of book format, the outside is more easily affected than inner side by environmental factors such as temperature, humidity and air. In this study, the change in optical properties after dry heating accelerated aging was comparatively analyzed to understand the difference of the optical aging characteristics between outside and inner side of the duplicated beeswax-treated volume. It is found that the cover pages of the beeswax-treated volumes were more optically deteriorated than their middle pages. This indicates that outer sides of aging book volume directly exposed to the air is more vulnerable to serious deterioration than inner sides. Also, aromatic compounds such as benzoic acid and cinnamic acid were observed in the investigation of UV/VIS absorbance of the beeswax in each aged sample.

• Journal of the Korean Society for Precision Engineering
• /
• v.25 no.1
• /
• pp.138-144
• /
• 2008

Micro-machining of a brittle material such as glass, silicon, etc., is important in micro fabrication. Particularly, micro-abrasive jet machining (${\mu}-AJM$) has become a useful technique for micro-machining of such materials. The ${\mu}-AJM$ process is mainly based on the erosion of a mask which protects brittle substrate against high velocity of micro-particle. Therefore, fabrication of an adequate mask is very important. Generally, for the fabrication of a mask in the ${\mu}-AJM$ process, a photomask based on the semi-conductor fabrication process was used. In this research a rapid mask fabrication technology has been developed for the ${\mu}-AJM$. By scanning the focused UV laser beam, a micro-mask pattern was fabricated directly without photolithography process and photomask. Two kinds of mask patterns were fabricated using SU-8 and photopolymer (Watershed 11110). Using fabricated mask patterns, abrasive-jet machining of Si wafer were conducted successfully.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.07a
• /
• pp.502-503
• /
• 2005

본 연구에서는 TFT-LCD(Thin Film Transistor-Liquid Crystal Display)의 배경광원인 BLU(Back Light Unit)의 고효율화, 고품질화를 통한 원가 절감을 달성하기 위해 BLU의 대표적 핵심부품중에 하나인 프리즘 시트를 사용하지 않는 구조의 MNT용 BLU를 개발하는데 목적을 두었다. 고효율의 BLU를 만들기위하여 17인치 BLU의 도광판의 상, 하면에 Prism 형상을 구현하였으며, 광학적 시뮬레이션을 통하여 먼저 가능성을 검토하였고, UV에 반응하는 Resin을 경화시키는 방법을 이용하여 일반 도광판에 프리즘형상을 각인(Imprint)시키는 방법으로 실물을 재현하였다. 실험 결과 프리즘 시트를 사용하지 않는 구조의 MNT용 17인치 BLU에서 중심휘도 4,984nit, 균일도 70% 달성하였다.

• Journal of the Korean Applied Science and Technology
• /
• v.35 no.3
• /
• pp.595-605
• /
• 2018

In recent years, researches on organic-inorganic coating films have conducted a nanocomposite system composed of organic resin matrices having excellent flexibility and chemical stability and inorganic materials having excellent mechanical properties. The o-phenylphenoxyethyl acrylate (OPPEA) used as the acrylate monomer has a high refractive index of 1.58, and the bisphenol A ethoxylate diacrylate (BAEDA) has a low refractive index but improves the chemical stability of the organic resin. In addition, zirconia used as an inorganic material exhibits excellent durability and optical properties. In this study, the BAEDA contents in acrylate monomer were controlled to produce a film with suitable optical transparency. And optimum conditions were established by comparing the changes in surface properties of PET films detected with pencil hardness tester, Abbe's refractometer, and UV-vis spectrophotometer. The hydrophobicity and the dispersibility of zirconia in acrylate monomer were much improved after modification with ${\gamma}$-methacryloxypropyltrimethoxysilane (MPS), which is a silane coupling agent. And the existence of ester C=O bond peak at $1716cm^{-1}$ introduced by MPS through FT-IR ATR spectrophotometer confirmed the completion of surface modification of zirconia with MPS. In addition, the presence of silicon atom on the surface modified zirconia was also proved using X-ray fluorescence spectrometer. When the photocurable hybrid coating was prepared by introducing chemically modified zirconia into acrylate monomer, the refractive index of this coated PET film was improved by 1.2%, compared to the only acrylate coated PET film. The homogeneous distribution of zirconia in acrylate coating layer on PET film was also identified through SEM/EDS mapping analysis technique.

• Journal of Adhesion and Interface
• /
• v.15 no.3
• /
• pp.116-122
• /
• 2014

This work deals with the effects of different oligomers, monomers, photoinitiators, and steel plates on the variation of gloss for UV coated steel plates at $20^{\circ}$ and $60^{\circ}$ (ASTM D523). The gloss value was more significantly varied with $20^{\circ}$ angle as compared with $60^{\circ}$. No substantial change in gloss was observed for the type of single oligomer; however, the gloss varied with the mixing ratios of oligomers, type and mixing ratio of monomers, type and concentration of photoinitiator, and type of steel plate. The maximum gloss value was observed when the mixing ratio of polyurethane acrylate (UA) to epoxy acrylate (EA) was 70 : 30, the mixing ratio of trimethylolpropantriacrylate (TMPTA) to tetrahydrofurfurylacrylate (THFA) was 5 : 5, the content of the mixed oligomer (UA : EA = 70 : 30) was 90 wt%, respectively. Darocur MBF of liquid type showed better gloss property than the solid type of Irgacure 184, and the gloss was decreased as the concentration of Darocur MBF increased from 1 to 4 wt%. Regarding the type of steel plate, GI steel plate showed better gloss property as compared with EG and primer-coated steel plates. The maximum gloss values of 95 GU and 120 GU, respectively, at $20^{\circ}$ and $60^{\circ}$ angles throughout the parametric study in the absence of leveling agents enhancing the gloss.

• Applied Chemistry for Engineering
• /
• v.27 no.2
• /
• pp.221-226
• /
• 2016

Production of eco-friendly and biologically harmless materials is strongly required in all industries. In particular, reducing volatile organic compounds in coating processes is extremely important to secure worker's safety. During recent two decades, extensive research works on water-borne polyurethane dispersion (PUD) have been continuously developed as an alternative to solvent-borne polyurethane. However, PUD was shown inferior mechanical properties to the organic solvent-borne polyurethane due to a limit to the molecular weight increase, which resulted in the limit of applications. To overcome this drawback, several approaches have been examined such as polymer blends and thermal/radiation induced crosslinking. Among these methods, the radiation curing system was suitable for industrialization because of the high crosslinking density and fast curing speed. In this study, we overcame the drawback for PUD via introducing benzophenone radiation curable units to PUD. We synthesized PUD films which possessed good dispersion in water for 30 days, increased Tg and Td more than $5^{\circ}C$ after UV curing film as well as improved young's modulus more than double.

• Applied Chemistry for Engineering
• /
• v.26 no.4
• /
• pp.400-405
• /
• 2015

Traditional anti-reflective (AR) coating films prepared using tetraethylorthosilicate (TEOS) as a precursor absorbs water easily in addition to having a weak abrasion resistance. To improve the transmittance, hydrophobicity and abrasion resistance of AR coating film, various AR coating films were prepared using methyltrimethoxysilane (MTMS) as a precursor in addition to introducing a fluoroalkylsilane, acid catalyst, base catalyst and acid-base two step catalyst. The prepared AR coating films were then characterized by UV-Vis spectroscopy, contact angle analyzer, atomic force microscope (AFM), pencil scratch hardness test and cross-cut test. As a result, the transmittance of bare glass was 90.5%, while that of AR coating glass increased to 94.8% at curing temperature of $300^{\circ}C$. When the fluoroalkylsilane was added, the water contact angle of AR coating film increased from $96.3^{\circ}$ to $108^{\circ}$, indicating that the hydrophobicity of the film was greatly improved. The abrasion resistance of AR coating film was also improved by the acid catalyst, whereas the transmittance increased by the base catalyst. In the case of AR coating film prepared using an acid-base two step catalyzed reaction, both the transmittance and abrasion resistance of the film was synergistically enhanced as compared with those of AR coating films prepared without introduction of a catalyst.

• Journal of Technologic Dentistry
• /
• v.29 no.1
• /
• pp.121-131
• /
• 2007

A preparation process's conditions of aqueous sol which contains anatase-type nano titania particles with photocatalyic properties was established by using Yoldas process, so called, DCS(Destabilization of Colloidal Solution) process in this study. And crystal size change and phase transformation of titania particles in aqueous titania sol depending on reaction conditions was investigated by a light scattering method and XRD analysis of frozen dried powders, respectively. This sol with photo catalytic nano titania particles was used to the following hydrophilic hybrid coating film's fabrication and its properties was evaluated. Subsequently, for coating film using the above mentioned aqueous titania sol, non-aqueous titania sol was prepared without any chemical additives and its time stability according to aging time was investigate. By using the above mentioned aqueous titania sol and non-aqueous sol, a complex oxide coating sol for metal and ceramic substrate and a organic-inorganic hybrid coating sol for polymer substrate was prepared and it's hydrophilicity depending on UV irradiation conditions was evaluated. As a conclusions, the following results were obtained. (1)Aqueous titania sol The average particle size of titania in formed aqueous titania sol was distributed between 20$\sim$90nm range depending on reaction conditions. And the crystal phase of titania powders obtained by frozen drying method was changed from amorphous state to anatase and subsequently transformed to rutile crystal phase and it is attributed to concentration gradient in aqueous sol. (2)Non-aqueous titania sol Non-aqueous titania sol was prepared using methanol as a solvent and a little distilled water for hydrolysis and nitric acid as a catalyst were used. The obtained non-aqueous titania sol was stable at room temperature for 20 days. Additionally, non-aqueous titania sol with addition of chealating reagent such as acethylaceton and ethylene glycol prolonged the stability of sol by six months. (3)Complex sol and hybrid sol with super hydrophilicity The above mentioned aqueous titania sol as a main photocataylic component and non-aqueous titania sol as a binder for coating process was used to prepare a complex sol used for metal, ceramic and wood material substrate and also to prepare the organic-inorganic hybrid sol for polymer substrate such as polycarbonate and polyethylene, in which process APMS(3-Aminopropyltrimethoxysilane), GPTS(3-Glycidoxypropyl-trimethoxysilane) as a hydrophilic silane compound and HEMA(2-Hydroxyethyl methacrylate) as a forming network in hybrid coating film were used. The hybrid coating film such as prepared through this process showed a superhydrophilicity below 1$10^{\circ}$ depending on processing conditions and a pencil's hardness over 6 H.