Twin-roll process is a relatively new continuous casting process which can produce high-quality strip products directly, and solidification rate can reach $10^3$ to $10^4$ K/s, leading to fine and uniform microstructures with enhanced mechanical properties. The strip casting condition for producing fine Al-Sn alloy strip was obtained experimentally, and defects appearing on the strip was examined. Crack formation and surface quality of the strip was found to depend mainly on process parameters such as melt temperature, roller gap and rolling speed. Sn structure of network type was observed in Al-20Sn and Al-40Sn alloy strips, and cell spacing of Al-40Sn alloy was smaller than that of Al-20Sn. Banding strength of the heat treated specimens increased with increasing of soaking time and temperature, and bonding strength of Al-20Sn alloy was more superior than that of Al-40Sn alloy. However wear resistance of Al-40Sn alloy contained large amount of soft Sn which possess good anti-friction characteristics was superior than that of Al-20Sn alloy.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2009.10a
• /
• pp.463-463
• /
• 2009

• Journal of Korea Foundry Society
• /
• v.16 no.2
• /
• pp.149-157
• /
• 1996

Several aluminum based alloys were fabricated by a twin roll strip casting mill. As-cast microstructures and microsegregations of these aluminum alloys were investigated by means of optical microscope, scanning electron microscope and electron probe micro analysis. Clear distinction on microsegregation among the alloy systems was observed, that is, A1235 and A8011 alloys showed diffused segregation in the middle of the strip, while A3003 and A5086 alloys revealed a centerline segregation consisted of lamellar structure. Above center line segregation was resulted from enrichment of the alloying elements such as Mn, Fe, Cu, Si and eutictic reaction in central region of the alloy strip.

• Journal of Korea Foundry Society
• /
• v.15 no.5
• /
• pp.459-468
• /
• 1995

For high performance aerospace structures, the properties of highest priority are low density, high strength, and high stiffness(modulus of elasticity). Addition of beryllium decrease the density of the aluminum alloy and increase the strength and the stiffness of the alloy. However it is very difficult to produce the Al-Be alloy having useful engineering properties by conventional ingot casting, because of the extremely limited solid solubility of beryllium in aluminum. So, rapid solidification processing is necessary to obtain extended solid solubility. In this study, rapidly solidified Al-6 at% Be alloy were prepared by twin roll melt spinning process and single roll melt spinning process. Twin roll melt spun ribbons were extruded at $450^{\circ}C$ with reduction in area of 25 : 1 after vacuum hot pressing at $550^{\circ}C and 375^{\circ}C$. The microstructure of melt spun ribbon exhibited a refined cellular microstructure with dispersed Be particles. As advance velocity of liquid/solid interface increase, the morphology of Be particle vary from rod-like type to spherical type and the crystal structure of Be particle from HCP to BCC. These microstructural characteristics of rapidly solidified Al-6at.%Be alloy were described on the basis of metastable phase diagram proposed by Perepezko and Boettinger. The extruded ribbon consisted of recrystallized grains dispersed with Be particles and exhibited improved tensile property compared with that of extruded ingot.

• Elastomers and Composites
• /
• v.56 no.4
• /
• pp.217-222
• /
• 2021

In this study, random polypropylene (rPP) was compounded with two of monoglycerides, namely, glyceryl monolaurate (GML) and glyceryl monostearate (GMS), as antifogging agents to improve its antifogging performance. rPP film samples were prepared by a film-casting method using a three-roll casting machine after melt blending through a twin screw extruder. With an increase in the monoglyceride content, the melt flow index for rPP films with GML and GMS increased, and their yield strength decreased. The incorporation of GMS in rPP was proven to be more effective in improving its physical properties than was rPP with GML. When GML and GMS were separately added to the rPP film at contents of more than 1 phr and more than 5 phr, respectively, the film exhibited antifogging performance.

• Korean Journal of Metals and Materials
• /
• v.48 no.5
• /
• pp.387-393
• /
• 2010

High-strength aluminum alloy sheets with high magnesium contents were fabricated by a strip caster equipped with an asymmetric nozzle, which has been proven to be effective for reducing surface defects and internal segregation. 4 mm thick as-cast sheets consisting of fine dendrites and minor $Al_{8}Mg_{5}$ segregation were hot-rolled successfully to 1 mm sheets and subsequently annealed at various temperatures. The sheet revealed the tensile strength and elongation of 306 MPa and 34%, respectively, when it was rolled at 250${^{\circ}C}$ and subsequently annealed at 475${^{\circ}C}$, which exhibits the feasibility of the practical application for autobodies. The observed mechanical properties were explained on the basis of the microstructural characteristics of the alloy sheets.

• Journal of Korea Foundry Society
• /
• v.19 no.1
• /
• pp.77-83
• /
• 1999

Strip casting process, a new casting technology which makes thin strip of $0.5{\sim}5\;mm$ thickness directly from molten metal, has been dramatically developed for past 10 years and faced commercialization in the case of STS304 strip. In this study, ductile cast iron strip which is 1.1 mm thick and 100 mm wide is manufactured by the twin roll strip caster. Graphite and matrix structure of the strip can be controlled through heat treatments and the mechanical properties are examined. The microstructure of the as-cast strip consists of cementite and pearlite. Especially the equiaxed crystal zone of pearlite exists in the center region of the thickness due to the characteristics of the strip casting process. Matrix structure can be transformed into fully ferrite or ferrite/pearlite mixed structures by the different graphitization heat treatments. The heat-treated strip with ferrite/pearlite matrix structure showed higher hardness and tensile strength than that with full ferrite matrix structure.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2009.11a
• /
• pp.47.1-47.1
• /
• 2009

최근 환경과 에너지에 대한 관심이 증대됨에 따라 차체의 경량화를 위한 고합금계 알루미늄 합금의 연구가 활발히 진행되고 있다. 특히 5000계 알루미늄 합금은 비중이 낮을 뿐만 아니라 Mg의 첨가에 의해 높은 강도 및 성형성을 얻을 수 있기 때문에 자동차용 판재로 많은 주목을 받고 있다. 현재 사용되는 대부분의 알루미늄 합금판재는 DC주조법과 추가적인 압연공정으로 제조되기 때문에 경제성 문제와 낮은 냉각속도로 인한 금속학적인 문제를 갖는다. 그러나 DC주조법과는 달리 쌍롤 박판주조법은 용탕으로부터 직접 판재를 제조하기 때문에 경제적이며 효율적인 주조공정이다. 또한 냉각속도가 빠르기 때문에 비교적 주조편석이 적고 전반적인 미세조직이 균일하여 고합금계 알루미늄 합금 판재제조에 매우 유용하게 응용될 수 있다. 본 연구에서는 쌍롤 박판주조법으로 고합금계 알루미늄 합금 판재를제조하고, 제조된 합금의 열간압연 및 열처리 조건에 따른 기계적 특성을 비교 및 평가하였다. 또한 미세조직 및 집합조직을 분석함으로써 고합금계 알루미늄 합금 판재의 실용화 가능성을 평가하였다.

• Journal of Korea Foundry Society
• /
• v.20 no.2
• /
• pp.122-128
• /
• 2000

Strip casting process is a new technology that makes a near net shape thin strip directly from molten metal. With this process, a large amount of energy and casting cost could be decreased from the abbreviation of reheating and/or hot rolling process. Ductile cast iron which has spheroidal graphite in the matrix is the most commercial and industrial material, because of its supreme strength, toughness, and wear resistance etc. But it cannot be produced to the thin strip owing to difficulty in rolling of ductile cast iron. In this study, ductile cast iron strips are produced by the twin roll strip caster, with different chemical compositions of C, Si, and Mn contents. And then heat-treated, microstructures and mechanical properties are examined. The microstructures of as-cast strip are that of white cast iron which consists of the mixture of cementite and pearlite, but the equiaxed crystal zone of the pearlite or segregation zone of cementite exists in the center region of the strip thickness, which cannot be observed in the rapidly solidified metallic mold cast specimens. This structure is supposed to be formed from the thermal distribution of strip and the rolling force. Comparing with the structures of each strips after heat treatment, increasing Si content makes smaller spheroidal graphite and more compact in the matrix, furthermore the less of Mn content makes the ferrite matrix be obtained clearer and easier. As a result of the tensile test of graphitization heat-treated strips, the yield strengths are about 250 MPa, the tensile strengths are about $430{\sim}500$ MPa, and the elongations are about $10{\sim}13%$. In the case of the strip which has the smaller and more compact spheroidal graphite in the ferrite matrix, the higher tensile strength and better drawability could be obtained.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2009.11a
• /
• pp.43.2-43.2
• /
• 2009

Al-Mg 알루미늄 합금은 강도가 높고 성형성이 우수하여 수송기기 경량화용 소재로서 사용량이 증가하고 있다. 특히고강도 특성을 보이는 Al-Mg-Mn합금은 자동차, 선박및 철도차량등의 형재 및 판재로 그 사용량이 증가하고 있다. 또한 결정립을 미세화 시킨 Al-Mg-Mn합금판재의 경우에는 온간성형으로 복잡한 형상의 판재부품제조에 사용되고 있다. 연속주조공정인 Twin roll strip casting(TRC)은용탕으로부터 직접 판재를 생산할 수 있는 공정으로 주로 순알루미늄계열의 판재 생산에 사용되고 있으나 최근에는 고강도 판재의 저비용 생산을 위하여 고합금계 판재에 적용하는 연구가 수행되고 있다. 합금량이 높은 고강도Al-Mg계 합금의 TRC 주조시 고액공존구간이 커서 더욱 정밀한 공정제어가 필요하다. 또한 기존의 슬라브주조방식보다 높은 냉각속도로 주조가 가능하기 때문에 결정립 및 정출상의 미세화공정으로 응용되기도한다. 본 연구에서는 TRC공정을 기초로 주조시 열간 압연의효과를 동시에 부여하는 용탕직접압연공정을 개발하였으며 상용 고강도 알루미늄 합금인 5083합금 판재를제조하였다. 또한 기존 Al-Mg 합금에 Mn을 첨가하여 용탕직접압연함으로서 정출상의 크기 및 밀도를 제어하여 강도가 우수한 Al-Mg-Mn 합금판재를 제조하는 기술을 개발하였다. 용탕직접압연된 Al-Mg-Mn계 합금의 경우에 주조시 높은 냉각속도로 인하여 결정립이 미세하고 Al6Mn과 같은 미세한 정출상이 다량 형성되었으며, 최종압연 및 열처리에 의하여 높은 강도를 갖는 고강도 알루미늄 합금 판재의 제조가 가능하였다.