• Journal of Powder Materials
• /
• v.9 no.3
• /
• pp.174-181
• /
• 2002

Nanosized tungsten carbide powders were synthesized by the chemical vapor condensation(CVC) process using the pyrolysis of tungsten hexacarbonyl($W(CO)_6$). The effect of CVC parameters on the formation and the microstructural change of as-prepared powders were studied by XRD, BET and TEM. The loosely agglomerated nanosized tungsten-carbide($WC_{1-x}$) particles having the smooth rounded tetragonal shape could be obtained below $1000^{\circ}C$ in argon and air atmosphere respectively. The grain size of powders was decreased from 53 nm to 28 nm with increasing reaction temperature. The increase of particle size with reaction temperature represented that the condensation of precursor vapor dominated the powder formation in CVC reactor. The powder prepared at $1000^{\circ}C$ was consisted of the pure W and cubic tungsten-carbide ($WC_{1-x}$), and their surfaces had irregular shape because the pure W was formed on the $WC_{1-x}$ powders. The $WC_{1-x}$ and W powders having the average particles size of about 5 nm were produced in vacuum.

• Journal of Powder Materials
• /
• v.11 no.2
• /
• pp.124-129
• /
• 2004

Nanosized WC and WC-Co powders were synthesised by chemical vapor condensation(CVC) process using the pyrolysis of tungsten hexacarbonyl(W(CO)$_6$) and cobalt octacarbonyl(Co$_2$(CO)$_8$). The microstructural changes and phase evolution of the CVC powders during post heat-treatment were studied using the XRD, FE-SEM, TEM, and ICP-MS. CVC powders were consisted of the loosely agglomerated sub-stoichimetric WC$_{1-x}$ and the long-chain Co nanopowders. The sub-stochiometric CVC WC and WC-Co powders were carburized using the mixture gas of CH$_4$-H$_2$ in the temperature range of 730-85$0^{\circ}C$. Carbon content of CVC powder controlled by the gas phase carburization at 85$0^{\circ}C$ was well matched with the theoretical carbon sioichiometry of WC, 6.13 wt％. During the gas phase carburization, the particle size of WC increased from 20 nm to 40 nm and the long chain structure of Co powders disappeared.

• Korean Chemical Engineering Research
• /
• v.49 no.4
• /
• pp.405-410
• /
• 2011

A study on chemical vapor deposition(CVD) of $WO_3$ and the electrochromic properties of the CVD $WO_3$ films have been carried out. The crystalinity, purity, and growth rate of the films depending on substrate temperatures are investigated. The highest growth rate is $8{\mu}m/min$ at the substrate temperatures above $300^{\circ}C$ and the estimated activation energy for overall film growth is about 45.9 kJ/mol at the temperatures of $225{\sim}275^{\circ}C$, where the CVD process is controlled by a surface reaction kinetics. The films grown below $275^{\circ}C$ are amorphous, while those deposited above $300^{\circ}C$ are crystalline. The effects of thickness and deposition temperature of the $WO_3$ films on electrochromic activity are also investigated. The coloration efficiency of the films increases with increase in film thickness and decrease in deposition temperature.