The thin film that is electrically conductive and optically transparent is called conductive transparent thin film. ITO(Indium-Tin Oxide) which is a kind of conductive transparent thin film has been widely used in solar cell, transparent electrical heater, selective optical filter, FDP(Flat Display Panel) such as LCD(Liquid Crystal Display), PDP(Plasma Display Panel) and so on. Especially in PDP, ITO films is used as a transparent electrode in order to maintain discharge and decrease consumption power through the improvement of cell structure. In this study, we prepared ITO by reactive r.f. sputtering with indium-tin(Sn 10wt%) alloy target instead of indium-tin oxide target. The ITO films deposited at low temperature 15$0^{\circ}C$ and 8% $O_2$. Partial pressure showed about 3.6 Ω/$\square$. At the end of firing, the resistance of ITO was decreased, the optical transparence was improved above 90%.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1997년도 하계학술대회 논문집 C
• /
• pp.1411-1413
• /
• 1997

The thin film that is electrically conductive and optically transparent is called conductive transparent thin film. ITO(Indium-Tin Oxide) which is a kind of conductive transparent thin film has been widely used in solar cell, transparent electrical heater, selective optical filter, FDP(Flat Display Panel) such as LCD (Liquid Crystal Display), PDP(Plasma Display Panel) and so on. Especially in PDP, ITO films is used as a transparent electrode in order to maintain discharge and decrease consumption power through the improvement of cell structure. In this study, we prepared ITO by reactive r.f. sputtering with indium-tin(Sn wt 10%) alloy target instead of indium-tin oxide target. The ITO films deposited at low temperature $150^{\circ}C$ and 8% $O_2$ partial pressure showed about $3.6{\Omega}/{\square}$. At the end of firing, the resistance of ITO was decreased, the optical transparence was improved above 90%.

• 한국진공학회지
• /
• 제21권6호
• /
• pp.333-341
• /
• 2012

본 연구는 RF 마그네트론 스퍼터링법을 이용하여 산소유량 변화에 따라 증착된 ITO 박막 구조적, 전기적, 광학적 특성을 분석하였다. ITO (Indium Tin Oxide) 박막은 $1.0{\times}10^{-3}$ Torr의 공정 압력과 2 kW 및 13.56 MHz의 RF 전력, 1,000 sccm의 Ar 가스 조건하에 0~12 sccm의 $O_2$ 가스 유량을 변경하면서 증착하였다. 광투과율 측정은 적분구를 이용하였으며, 측정 파장 범위는 300~1,100 nm이다. 4-point probe를 이용하여 면저항을 측정하였으며, Hall Measurement System을 이용하여 비저항, 캐리어 농도 및 전자이동도를 측정하였다. Scanning electron microscope 장비를 이용하여 ITO 박막 표면을 분석하였고, 박막의 거칠기는 Atomic force microscope을 이용하여 측정하였다. ${\gamma}$-Focused ion beam system을 이용하여 ITO 박막의 이차전자방출계수를 측정하였으며, 이차전자방출계수 값으로 Auger neutralization mechanism 분석법을 이용해 ITO 박막의 일함수를 결정하였다. 3 sccm의 산소 유량에서 증착된 ITO 박막의 비저항은 약 $2.4{\times}10^{-4}{\Omega}{\cdot}cm$로 가장 좋았으며, 광학적 특성 또한 84.93% (Weighted average)로 가장 좋은 것을 확인할 수 있었다. 이 조건에서 이차전자방출 계수가 가장 높았고 일함수는 가장 낮은 경향의 일치함을 확인하였다.