Particulate composites of Al2O3/SiC, Al2O3/ZrO2 and Al2O3/ZrO2/SiC have been fabricated to investigate their R-curve behaviors and toughening mechanisms. Al2O3 containing 30 vol% SiC particles of 3${\mu}{\textrm}{m}$ showed rising R-curve behavior owing to the strong crack bridging by SiC particles. The fracture toughness reached 9.1 MPa {{{{ SQRT {m} }} at the crack length of 1000${\mu}{\textrm}{m}$. On the other hand, ZrO2-toughened Al2O3 had a high flat R-curve since it rose steeply in the short crack region due to the well known transformation toughening. For Al2O3/ZrO2/SiC composites, the R-curve behavior was similar to that of Al2O3/SiC but with slightly higher toughness. The SiC particles in this composite decreased the amount of transformable tetragonal phase to reduce the effect of transformation toughening by 50%. It was also found that the fracture toughness of this composite with two different toughening mechanisms was markedly lower than that estimated by the simple addition of two contributions.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1997.10a
• /
• pp.20-20
• /
• 1997

• Proceedings of the Korea Association of Crystal Growth Conference
• /
• 2000.06a
• /
• pp.233-242
• /
• 2000

Cordierite/ZrO$_2$ composites with 5 to 25wt% ZrO$_2$ were fabricated by prssureless sintering, and their densification behavior, fracture strength, fracture toughness, microstructure and thermal expansion behavior were studied. The ZrO$_2$ addition into cordierite matrix affects the densification behavior and mechanical properties of the composites. By dispersing 25wt% ZrO$_2$, densified cordierite/ZrO$_2$ composite with a relative density of 98.5% was obtained at optimum sintering condition of 144$0^{\circ}C$/2H. Both fracture strength and toughness were increased from 140 to 290MPa and from 1.6 to 3.5 MPam$\frac{1}{2}$, respectively, by dispersing 25wt% ZrO$_2$ into the cordierite matrix. ZrO$_2$ particles were homogenously dispersed into cordierite matrix, which intragranular particles were fine(<100nm) and intergranular particles were coarse. The toughening mechanisms in the present composites were mainly attributed to martensitic transformation toughening. Then, the addition of ZrO$_2$ is likely to have little deleterious effect upon thermal expansion coefficient of cordierite.

• The Korean Journal of Ceramics
• /
• v.5 no.3
• /
• pp.224-229
• /
• 1999

The preparation and toughening of SiC-AIN solid solution from powder mixtures of $\beta$-SiC, AIN and $\alpha$-SiC by hot-pressing were studied in the 1870 to $2030^{\circ}C$ temperature range. The reaction of AIN and $\beta$-SiC(3C) powders causing transformation to the 2H(wurtzite) structure appeared to depend on hot-pressing temperatures and an additive of $\alpha$-SiC. For the composition of 49wt% SiC with 2 wt% $\alpha$-SiC and 47.5 wt% AIN47.5wt% SiC with 5 wt % $\alpha$-SiC at 203$0^{\circ}C$ for 1 h, th complete solid solutions with a single phase of 2H could be obtained. The appreciable amount of $\alpha$-SiC could develop the columnar inter-grains of 4H phase and the stable 2H phase with the relatively uniform composition and grain size distributions. The effect of $\alpha$-SiC on the phases present and compositional microstructures with columnar inter-grains was invetigated using X-ray diffraction, scanning electron microscopy and transmission electron microscopy. The fracture toughness and Vickers hardness of the hot-pressed solid solutions wre examined by the indentation-fracture-test method.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1999.11a
• /
• pp.335-338
• /
• 1999

The effect of monoclinic $ZrO_2$(pure) and tetragonal $ZrO_2$ containing 5.35wt% $Y_2$$O_3$(Y-TZP) addition on the mechanical properties and thermal shock resistance of $Al_2$$O_3$ ceramic were investigated. The addition of $ZrO_2$(m) and Y-TZP increased sintering density of $Al_2$$O_3$. The vickers hardness increased with increasing the volume fraction of Y-TZP going through a maximum at 20wt%. The hardness of the specimens was found to be depend on the sintering density. With increasing the volume fraction of $ZrO_2$(m) and Y-TZP, the fracture toughness of the composite is increased. This result may be taken as evidence that toughening of ${Al_2}{O_3}$ can also be achieved by the transformation toughening and microcrack toughening of $ZrO_2$. The property of the& shock for ${Al_2}{O_3}$-$ZrO_2$ composites was improved by increasing the volume fraction of monoclinic $ZrO_2$(pure).Grain size increased with increasing the volume fraction of $ZrO_2$.

• Journal of the Korean Ceramic Society
• /
• v.42 no.6 s.277
• /
• pp.411-416
• /
• 2005

Y-TZP(Yttria-stabilized Tetragonal Zirconia Polycrystal) ceramics are of great interest as engineering and structural materials due to their excellent mechanical properties arising from transformation toughening, it is also reported that the 3Y-TZP($3 mol\%$ Yttria-stabilized Tetragonal Zirconia Polycrystal) has the best mechanical properties in Y-TZP ceramics. But to use widely for engineering and structural materials, it remains an important challenge to be able to improve its fracture toughness. In order to produce the 3Y- TZP ceramics showing much better mechanical properties, milling method adding monoclinic zirconia to 3Y-TZP was adopted and the resultant mechanical properties containing apparent density and fracture toughness were measured by using proper techniques. Experimental results showed that the 3Y-TZP specimen containing $33 wt\%$ of monoclinic zirconia, which was sintered at $1450^{\circ}C$, has the highest fracture toughness value of $11.38 MPa{\cdot}m^{1/2}$ which is three times higher than that of normal 3Y-TZP ceramics.

• Journal of the Korean Ceramic Society
• /
• v.42 no.2 s.273
• /
• pp.140-144
• /
• 2005

The microstructures and mechanical properties of Tetragonal Zirconia Polycrystals (TZP) sintered bodies, which made by pressureless and spark plasma sintering techniques, were investigated using XRD, SEM, and TEM techniques. In the spark plasma sintered samples, the TZP grains were equiaxed type including many sub-grain boundaries regardless of sintering conditions. The biaxial strength of TZP having an average of 80 nm grains in diameter was high in value with 1025 MPa, but fracture toughness showed a low value due to the absence of a fracture toughening mechanism such as transformation toughening. In the Pressureless Sintered (PLSed) samples, the grain size of TZP was strongly dependent on the sintering temperature; i.e., it gradually increased as the sintering temperature increased. The value of fracture toughness increased as the grain size increased by the stress-induced phase transformation and Borne crack deflection.

• Journal of the Korean Ceramic Society
• /
• v.37 no.4
• /
• pp.368-375
• /
• 2000

Fracture toughness of particulate composites of Al2O3/SiC, Al2O3/ZrO2 and Al2O3/ZrO2/SiC was analysed theoretically. According to the suggested particle bridging model for obtaining the R-curve height, the crack extension resistance for the long crack was linearly proportional to the residual calmping stress at the interface between the second phase and the matrix. It was also a function of the particle size and the content. It was confirmed that the rising R-curve behavior of Al2O3 containing 30 vol% SiC particles of 3${\mu}{\textrm}{m}$ was owing to the strong crack bridging by SiC particles. For Al2O3/ZrO2/SiC composites, the tensional stress from the 3${\mu}{\textrm}{m}$ SiC particles was large enough to activate the spontaneous transformation of the ZrO2. The crack extension resistance due to the particle bridging mechanism did not seem to be affected much by the coupled toughening, but its resultant toughness increase could be significantly smaller due to the dependency on the matrix toughness.

• Journal of Korea Foundry Society
• /
• v.8 no.3
• /
• pp.310-321
• /
• 1988

This study is aimed to investigate the effects of the multi-phase(ferrite-bainite-martensite) on the strengthening and toughening in ductile cast iron. All the specimen were austenitized at eutectoid transformation temperature range(${\alpha}+{\gamma}$) for 1hr and austempered at $300^{\circ}C$ and $400^{\circ}C$ for various holding time, and then quenched in iced water for multi - phase (${\alpha}-B-M$). When the volume fraction of martensite is below 15%, excellent maximum fracture load can be obtained due to strengthening by the fine martensite, but, with increasing of volume fraction over 15%, it was decreased drastically. The martensite size became finer and the shape of it changed from bar to spherical type with increasing of austempering holding time. The higher the austenitizing temperature is, the more preferential is the formation of austenite phase around the graphite nodules improving strength and toughness of austempered ductile cast iron.

• 전자공학회논문지 IE
• /
• v.49 no.2
• /
• pp.1-8
• /
• 2012

The effects of the addition of either monoclinic $ZrO_2(pure)$ or tetragonal $ZrO_2$ containing 5.35wt% $Y_2O_3(Y-TZP)$ on the mechanical properties and thermal shock resistance of $Al_2O_3$ ceramics were investigated. The addition of $ZrO_2$(m) and Y-TZP increased sintered density of $Al_2O_3$. The Vickers hardness also increased as the volume fraction of Y-TZP increased going through a maximum at 20wt%. The hardness of the specimens was found to be dependent on the sintered density. The higher volume fraction of either $ZrO_2(m)$ or Y-TZP resulted in the higher fracture toughness of the composite was. This result may be taken as evidence that toughening of $Al_2O_3$ can be achieved by not only the transformation toughening but microcrack toughening of $ZrO_2$. The thermal shock property for $Al_2O_3-ZrO_2$ composites was improved by increasing the volume fraction of monoclinic $ZrO_2(pure)$. The grain size increased as the volume fraction of $ZrO_2$ did.