• 한국염색가공학회지
• /
• 제29권1호
• /
• pp.37-44
• /
• 2017

An issue of major concern in the utilization of laminated composites based epoxy resin is associated with the occurrence of delaminations or interlaminar cracks, which may be related to manufacturing defects or are induced in service by low-velocity impacts. A strong interfacial filament/brittle epoxy resin bonding can, however, be combined with the high fracture toughness of weak interfacial bonding, when the filaments are arranged to have alternate sections of shear stress. To improve this drawback of the epoxy resin, UV-thermal dual curable resin were developed. This paper presents UV-thermal dual curable resin which were prepared using epoxy acrylate oligomer, photoinitiators, a thermal-curing agent and thermoset epoxy resin. The UV curing behaviors and characteristics of UV-thermal dual curable epoxy resin were investigated using Photo-DSC, DMA and FTIR-ATR spectroscopy. The mechanical properties of UV-thermal dual curable epoxy resin impregnated CF prepreg by UV curable resin content were measured with Tensile, Flextural, ILSS and Sharpy impact test. The obtained results showed that UV curable resin content improves the epoxy toughness.

• 한국환경과학회지
• /
• 제17권11호
• /
• pp.1227-1233
• /
• 2008

The effect of freeze drying and fixatives in post-treating freeze drying on the morphological properties of the rose (Rosa hybrida L.) petal were investigated for the production of high quality of freeze dried rose. The morphology including form and color of the dried flowers of cut rose were depended on the drying methods. The drying time was extended due to their density and water content, and was shorter in the freeze drying than that in the natural and hot air drying. Freeze dried process for dried flowers took 2 days in a freeze dryer and did not cause shrinkage or toughening of rose petal being dried, preserving its natural shape and color. The diameter of freeze dried flowers showed little reduction compared to fresh flowers. In Hunter color values of petals of freeze dried flowers, L and a values were high and showed little variations in comparison to fresh petals. Freeze drying led to a noticeable increase in anthocyanin contents in petals, suggesting that anthocyanin contents play an important role in the acquisition of freezing tolerance. Exposure of flowers to freeze drying was accompanied by an increase in the carotenoid content. In the post-treating freeze drying, epoxy resin, a fixative, applied alone or in combination to petals of freeze dried flowers showed efficient coating for the protection from humidity and sunlight. Combined application of epoxy and acetone to freeze dried petals permitted maintenance of natural color and excellent tissue morphology, showing color stability and shiny texture in surface of petals. These findings suggest that application of fixatives to freeze dried rose petals improves the floral preservation and epoxy coating provides good quality in the freeze dried flower product.

• 공업화학
• /
• 제9권2호
• /
• pp.172-176
• /
• 1998

에폭시 adduct carboxyl terminated butadiene acrylonitrile(CTBN)은 CTBN과 에폭시수지를 블렌딩하여 제조하였다. CTBN과 폴리우레탄(PU) 및 에폭시수지로 CTBN/PU/epoxy를 제조하였다. CTBN이 5 wt%에서 CTBN/PU/Epoxy는 PU의 함량이 증가할 수록 damping 피크가 이동하였다. PU의 함량이 증가할수록 상용성이 증가함을 의미한다. 그러나 CTBN의 함량이 증가함에 따라 상용성은 감소하였다. CTBN/PU/epoxy에서는 PU의 함량이 10wt%에서 최대 굴곡값을 나타냈으나, PU 함량이 증가할수록 감소하였다. CTBN/epoxy에서 PU를 첨가함에 따라 파괴인성은 증가하였다. 파괴단면에서 전단변형과 공동화에 의한 응력백화현상을 보였다. CTBN의 공동화와 PU를 도입한 에폭시 매트릭스의 전단변형이 CTBN/PU/epoxy의 강인화기구이다.

• 대한의용생체공학회:의공학회지
• /
• 제19권5호
• /
• pp.433-441
• /
• 1998

본 연구에서는 전부도재관용 도재의 균열전파 양상과 구강환경이 파절강도에 미치는 영향을 평가하기 위해 시행되었다. 도재의 굽힘강도 늘 In-Ceram, IPS-Empress 및 VMK68의 순으로 나타났으며, 수중에서 좌다 기름중에서 더 놀은 강도를 보였다. 비커스 압자 압입부와 압입부를 중심으로 한 파면의 관찰 결과, VMK68 도재의 경우에는 9.8N의 압인하중하에서, IPS-Empress의 경우에는 47.0N의 압입하중하에서 교면에 median crack이 형성되는 양상을 보였으며, 균열이 압자의 압입시에 형성된 벽개면을 따라서 빠르게 성장하여 파괴에 도달한 양상을 보였다. In-Ceram의 경우에는 49.0h의 압임하중하에서 Palmqvlst clack이 형성되는 양상을 보였으며, 알루미나 입자에 의한 균열의 굴곡과 creak bridging으로 인한 강화기전이 관찰되었다.

• 폴리머
• /
• 제24권2호
• /
• pp.245-251
• /
• 2000

에폭시 (EP) 수지와 폴리우레탄(PU) 으로 제조된 블렌드 시스템의 접촉각과 기계적 특성을 연구하였다. EP의 경화제로 20 phr의 DDM (4,4'-diamino diphenyl methane)이 사용되었으며 EP/PU의 함량은 100/0~100/60까지 변화시켰다. 접촉각은 Rame-Hart goniometer를 사용 하였으며 젖음액으로는 증류수와 diiodomethane을 사용하였다. 본 연구에서는 geometric 방법을 사용한 Owens-Wendt와 Wu's model이 블렌드 시스템의 표면 자유에너지를 알아보는데 사용되었다. 시편의 기계적 성질과 강인성은 임계 응력 세기 인자(critical stress intensity factor, $K_{IC}$)와 충격 강도 시험을 통하여 알아보았다. 그리고 특히 충격 강도는 상온과 극저온에서 알아보았다. 그 결과로서, 블렌드 시스템에 있어서 표면 자유에너지의 극성 요소는 저온에서 충격 강도를 증가시키는 PU의 함량에 크게 영향을 주었음을 알 수 있었다.

• Macromolecular Research
• /
• 제15권4호
• /
• pp.308-314
• /
• 2007

The effects of a compatibilizer on polypropylene (PP)/poly(acrylonitrile-butadiene-styrene) (ABS) blends were studied. Blends of the PP/ABS, with PP-g-SAN copolymer as a compatibilizer, were prepared using a twin screw extruder. The flexural and impact strength of the PP/ABS blends with the PP-g-SAN copolymer increased significantly with PP-rich compositions on the addition of the PP-g-SAN copolymer at 3 phr. The increase in the mechanical properties of the PP/ABS/PP-g-SAN blend may have been due to the toughening effects of the ABS in the PP-rich compositions. In the morphology study of the PP/ABS/PP-g-SAN (80/20) blend with the PP-g-SAN copolymer, the minimum droplet size, $5.1{\mu}m$, was observed with the addition on phr of the PP-g-SAN copolymer. The complex viscosity of the PP/ABS/PP-g-SAN (80/20) blends increased with the addition of3 phr of the PP-g-SAN copolymer. From the above mechanical properties, morphology and complex viscosity results for the PP/ABS blends, it is suggested that the compatibility is more increased with the PP-rich composition (PP:ABS=80/20 wt%) of the PP/ABS blend on the addition of 3 phr of the PP-g-SAN copolymer.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2002년도 Proceedings of the International Welding/Joining Conference-Korea
• /
• pp.53-58
• /
• 2002

Electrical insulation and mechanical properties of the plasma sprayed oxide ceramic coatings were studied before and after the sealing treatment of the ceramic coatings. Plasma sprayed A1$_2$O$_3$-TiO$_2$ coating as the reference coating was sealed using three commercial sealants based on polymer. Penetration depth of the sealants to the ceramic coating was evaluated directly from the optical microscope using a fluorescent dye. It is estimated that the penetration depth of the sealants to the ceramic coating is from 0.2 to 0.5 mm depending on the sealants used. The preliminary test results with a DC puncture tester imply that the dielectric breakdown voltage mechanism of plasma sprayed ceramic coatings has been determined to be a corona mechanism. Dielectric breakdown voltage of the as-sprayed and as-ground samples have shown a linear trend with regard to the thickness showing an average dielectric strength of 20 kV/mm for the thickness scale studied. It is also shown that grinding the coating before sealing and adding fluorescent dye do not agent the penetration depth of sealants. All of the microhardness, two-body abrasive wear resistance, bond strength, and surface roughness of the ceramic coating after the sealing treatment are improved. The extent of improvement is different from the sealants used. However, three-point bending stress of the ceramic coating after the sealing treatment is decreased. This is attributed to the reduced micro-crack toughening effect since the cracks propagate easily through the lamellar of the coating without crack deflection and/or branching after the sealing treatment.

• 한국결정성장학회지
• /
• 제13권6호
• /
• pp.309-314
• /
• 2003

방전 플라즈마 소결법을 적용하여 $Al_2O_3$-SiC 나노 복합체를 150$0^{\circ}C$ 이하의 온도에서 완전치밀화를 이루었다. 제조된 $Al_2O_3$-SiC 복합체는 이상 결정립 성장 없이 매우 균질한 미세구조를 형성하고 있는데, 첨가된 SiC 입자는 주로 결정립 내 및 결정립계에 존재하면서 $Al_2O_3$기지상에서 결정립 성장을 억제하는데 매우 유호하였음을 확인 할 수 있다. 한편, SiC 입자의 첨가는 크랙 회절 및 브릿징 등에 의해서 유도된 재료 강도 및 인성 강화 기구에 의해서 $Al_2O_3$-SiC 복합체의 기계적 물성을 크게 향상시켰다.

• 한국전기전자재료학회논문지
• /
• 제28권3호
• /
• pp.170-174
• /
• 2015

Composite ceramics of alumina-TZP(3Y) have good mechanical and electrical properties. So, They have been used as high strength refractory materials and thick film substrates, etc. In this study, Composite ceramics of alumina-TZP(3Y) were fabricated by uniaxial pressing and sintering at 1,400, 1,500, and $1,600^{\circ}C$, and their microstructures and mechanical properties were investigated. As the TZP(3Y) content in composite ceramics increases from 20 wt.% to 80 wt.%, the fracture toughness increases monotonically, which seems to be related to the higher relative density and/or toughening mechanism by means of stabilized tetragonal zirconia phase at room temperature. In contrast to the fracture toughness, Vickers hardness of the composite ceramics shows maximum value (1,938 Hv) at a 40 wt.% of TZP(3Y). The result of Vickers hardness is likely to be due to more dense sintered microstructure of composite ceramics than pure alumina and reinforcement of composite ceramics with TZP(3Y), considering that Vickers hardness of pure $Al_2O_3$ is greater than that of TZP(3Y). It is also shown that the $ZrO_2$ particles are $l^{\circ}Cated$ between $Al_2O_3$ grains and suppress grain growth each other.

• KCI Concrete Journal
• /
• 제12권2호
• /
• pp.85-93
• /
• 2000

Potentially significant mechanical improvements in tension can be achieved by the incorporation of randomly distributed, short discrete fibers in concrete. The improvements due to the incorporation fibers significantly influence the composite stress - strain ($\sigma$-$\varepsilon$) characteristics. In general incorporating fibers in a plain concrete has relatively small effect on its precracking behavior. It, however, alters its post-cracking behavior quite significantly, resulting in greatly improved ductility, crack controls, and energy absorption capacity (or toughness). Therefore, a thorough understanding the complete tensile stress - strain ($\sigma$-$\varepsilon$) response of fiber reinforced concrete is necessary for proper analysis while using structural components made with fiber reinforced concrete. Direct tensile stress applied to a specimen is in principle the simplest configuration for determining the tensile response of concrete. However, problems associated with testing brittle materials in tension include (i) the problem related to gripping of the specimen and (ii) the problem of ensuring centric loading. Routinely, indirect tension tests for plain concrete, flexural and split-cylinder tests, have been used as simpler alternatives to direct uniaxial tension test. They are assumed to suitable for fiber reinforced concrete since typically such composites comprise 98% by volume of plain concrete. Clearly since the post-cracking characteristics are significantly influenced by the reinforcing parameters and interface characteristics, it would be fundamentally incorrect to use indirect tensile tests for determining the tensile properties of fiber reinforced concrete. The present investigation represents a systematic look at the failure and toughening mechanisms and macroscopic stress - strain ($\sigma$-$\varepsilon$) characteristics of fiber reinforced concrete in the uniaxial tension test. Results from an experimental parametric study involving used fiber quantity, type, and mechanical properties in the uniaxial tension test are presented and discussed.