• The Journal of Korean Academy of Prosthodontics
• /
• v.47 no.1
• /
• pp.46-52
• /
• 2009

Statement of problem: Recently, titanium has become popular as superstructure material in implant dentistry because titanium superstructure can be easily milled by means of computer-aided design and manufacture (CAD/CAM) technique. But retention form such as nail head or bead cannot be cut as a result of technical limitation of CAD/CAM milling and bond strength between titanium and porcelain is not as strong as that of conventional gold or metal alloy. Purpose: The objective of this study was to evaluate the shear bond strength of three different materials: heat curing resin, composite resin, porcelain which were bonded to grade II commercially pure Titanium (CP-Ti). Material and methods: Thirty seven CP-Ti discs with 9 mm diameter, 10 mm height were divided into three groups and were bonded with heat curing resin (Lucitone 199), indirect composite resin (Sinfony), and porcelain (Triceram) which were mounted in a former with 7 mm diameter and 1 mm height. Samples were thermocycled for 1000 cycles at between $5-55^{\circ}C$. Shear bond strength (MPa) was measured with Instron Universal Testing Machine with cross head speed of 1 mm/min. The failure pattern was observed at the fractured surface and divided into adhesive, cohesive, and combination failure. The data were analyzed by one-way ANOVA and Scheffe's multiple range test (${\alpha}=0.05$). Results: Lucitone 199 ($17.82{\pm}5.13\;MPa$) showed the highest shear bond strength, followed by Triceram ($12.97{\pm}2.11\;MPa$), and Sinfony ($6.00{\pm}1.31\;MPa$). Most of the failure patterns in Lucitone 199 and Sinfony group were adhesive failure, whereas those in Triceram group were combination failure. Conclusion: Heat curing resin formed the strongest bond to titanium which is used as a CAD/CAM milling block. But the bond strength is still low compared with the bond utilizing mechanical interlocking and there are many adhesive failures which suggest that more studies to enhance bond strength are needed.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2017.05a
• /
• pp.157-157
• /
• 2017

Titanium and its alloys that have a good biocompatibility, corrosion resistance, and mechanical properties such as hardness and wear resistance are widely used in dental and orthopedic implant applications. They can directly connect to bone. However, they do not form a chemical bond with bone tissue. Plasma electrolytic oxidation (PEO) that combines the high voltage spark and electrochemical oxidation is a novel method to form ceramic coatings on light metals such as titanium and its alloys. This is an excellent reproducibility and economical, because the size and shape control of the nano-structure is relatively easy. Silicon (Si), manganese (Mn), and magnesium (Mg) has a useful to bone. Particularly, Si has been found to be essential for normal bone, cartilage growth and development. Manganese influences regulation of bone remodeling because its low content in body is connected with the rise of the concentration of calcium, phosphates and phosphatase out of cells. Insufficience of Mn in human body is probably contributing cause of osteoporosis. Pre-studies have shown that Mg plays very important roles in essential for normal growth and metabolism of skeletal tissue in vertebrates and can be detected as minor constituents in teeth and bone. The objective of this work was to study nucleation and growth of bone-like apatite formation on Ti-6Al-4V in solution containing Mn, Mg, and Si ions after plasma electrolytic oxidation. Anodized alloys was prepared at 270V~300V voltages. And bone-like apatite formation was carried out in SBF solution for 1, 3, 5, and 7 days. The morphologies of PEO-treated Ti-6Al-4V alloy in containing Mn, Mg, and Si ions were examined by FE-SEM, EDS, and XRD.

• Applied Chemistry for Engineering
• /
• v.5 no.2
• /
• pp.255-262
• /
• 1994

Arc melted Ti-5Bi alloy was oxidized by thermal oxidation method. In the present study free energy efficiency(${\eta}_e$) of titanium oxide electrode(TOE) was measured as a function of light intensity and light energy. Flat-band potential of TOE was measured as a function of the light intensity and the solution pH. The ${\eta}_e$ of TOE increased with the increase of light intensity and tight energy to maximum value of 3.2% and 13%, respectively, at $0.2W/cm^2$ and 4.0eV. The ${\eta}_e$ was strongly dependent on the magnitude of the bias voltage. Maximum value was found at 0.5V bias. Photocurrent of TOE was controlled by electron-hole pair generation in depletion layer. The flat-band potential of the illuminated TOE shifted to -0.065V/decade with increasing light intensity. With the decrease of pH of electrolyte, flat-band potential shifted to anodic direction. The experimental slope was in good agreement with the Nernstian value of 0.059V/pH decade.

• Restorative Dentistry and Endodontics
• /
• v.41 no.1
• /
• pp.6-11
• /
• 2016

Objectives: The purpose of this in vitro study was to evaluate the accuracy of working length (WL) determination of four electronic apex locators (EALs), namely, Root ZX (RZX), Elements diagnostic unit and apex locator (ELE), SybronEndo Mini Apex locator (MINI) and Propex pixi (PIXI) using Stainless steel (SS) and nickel-titanium (NiTi) hand files. The null hypothesis was that there was no difference between canal length determination by SS and NiTi files of 4 EALs. Materials and Methods: Sixty extracted, single rooted human teeth were decoronated and the canal orifice flared. The actual length (AL) was assessed visually, and the teeth were embedded in an alginate model. The electronic length (EL) measurements were recorded with all four EALs using SS and NiTi files at '0.5' reading on display. The differences between the AL and EL were compared. Results: The results obtained with each EAL with SS and NiTi files were compared with AL. A paired sample t test showed that there was a statistical significant difference between EAL readings with SS and NiTi files for RZX and MINI (p < 0.05). The accuracy of RZX, ELE, MINI and PIXI within ${\pm}0.5 mm$ of AL with SS/NiTi files were 93.3%/70%, 90%/91.7%, 95%/68.3%, and 83.3%/83.3%, respectively. Conclusions: The results of this study indicate that Root ZX was statistically more accurate with NiTi files compared to SS files, while MINI was statistically more accurate with SS files compared to NiTi files. ELE and PIXI were not affected by the alloy type of the file used to determine WL.

• Journal of Korean Academy of Oral and Maxillofacial Radiology
• /
• v.29 no.1
• /
• pp.119-147
• /
• 1999

The purpose of this study was to investigate the effects of the Co-60 γ irradiation on the osseointegration. 2.0 mm titanium alloy screw implants(Sankin Industry Co. Ltd., Japan) were placed in the tibial metaphysis of the rabbits, bilaterally. The mean length of the implants was 6.0 mm. The right tibia was irradiated with a single dose of 15Gy from 60Co teletherapic machine at 5th postoperative day. The experimental group was irradiated tibia. The control group was non­irradiated tibia. To observe the phase of bone formation, the bone labeling by intramuscular injection of 20mg/Kg of Tetracycline, Calcein, Alizarin red S, was performed. The rabbits were sacrificed on the 1st, 2nd, 4th, 6th, 8th week and the tibia including implants were taken, and then the specimens were examined by the microradiography, light microscopy, and fluorescent microscopy. The obtained results were as follows: 1. There were connective tissue between bone and titanium at 1st week, in both group. Especially, the many empty lacunae without nucleus and obscure cytoplasm in experimental group, were observed. 2. The osteons were observed at 4th week in control group, and at 6th week in experimental group. The bone formation in experimental group was retarded as compared to the control group. 3. In fluorescent microscopy, bone labelling band was observed as linear, arc or concentric shape. Occasionary interrupted labelling band was observed, which is demonstrated bone remodeling. 4. In microradiographic examination, the radiolucent image was found between bone and implant with widening of bone marrow spaces as compared to the control group.

• The Journal of Advanced Prosthodontics
• /
• v.4 no.3
• /
• pp.162-169
• /
• 2012

PURPOSE. Fracture of the veneering material of zirconia restorations frequently occurs in clinical situations. The purpose of this in vitro study was to compare the fracture strengths of zirconia crowns veneered with various ceramic materials by various techniques. MATERIALS AND METHODS. A 1.2 mm, $360^{\circ}$ chamfer preparation and occlusal reduction of 2 mm were performed on a first mandibular molar, and 45 model dies were fabricated in a titanium alloy by CAD/CAM system. Forty-five zirconia copings were fabricated and divided into three groups. In the first group (LT) zirconia copings were veneered with feldspathic porcelain by the layering technique. In the second group (HT) the glass ceramic was heat-pressed on the zirconia coping, and for the third group (ST) a CAD/CAM-fabricated high-strength anatomically shaped veneering cap was sintered onto the zirconia coping. All crowns were cemented onto their titanium dies with Rely $X^{TM}$ Unicem (3M ESPE) and loaded with a universal testing machine (Instron 5583) until failure. The mean fracture values were compared by an one-way ANOVA and a multiple comparison post-hoc test (${\alpha}$= 0.05). Scanning electron microscope was used to investigate the fractured interface. RESULTS. Mean fracture load and standard deviation was $4263.8{\pm}1110.8$ N for Group LT, $5070.8{\pm}1016.4$ for Group HT and $6242.0{\pm}1759.5$ N for Group ST. The values of Group ST were significantly higher than those of the other groups. CONCLUSION. Zirconia crowns veneered with CAD/CAM generated glass ceramics by the sintering technique are superior to those veneered with feldspathic porcelain by the layering technique or veneered with glass ceramics by the heat-pressing technique in terms of fracture strength.

• Corrosion Science and Technology
• /
• v.8 no.4
• /
• pp.143-147
• /
• 2009

In biomedical implants and dental fields, titanium has been widely utilized for excellent corrosion resistance and biocompatibility. However, Ti and its alloys are nonbioactive after being implanted in bone. In this study, for the purpose of improvement in biocompatibility the anodic $TiO_2$ layer on Ti-xNb alloys were fabricated by electrochemical method in phosphate solution, and the effect of Nb content on the pore size, the morphology and crystallinity of Ti oxide layer formed by the anodic oxidation method was investigated. The Ti containing Nb up to 3 wt%, 20 wt% and 40 wt% were melted by using a vacuum furnace. The sample were cut, polished, and homogenized for 24 hr at $1050^{\circ}C$ for surface roughness test and anodizing. Titanium anodic layer was formed on the specimen surface in an electrolytic solution of 1 M phosphoric acid at constant current densities ($30mA/cm^2$) by anodizing method. Microstructural morphology, crystallinity, composition, and surface roughness of oxide layer were observed by FE-SEM, XRD, EDS, and roughness tester, respectively. The structure of alloy was changed from $\alpha$-phase to $\beta$-phase with increase of Nb content. From XRD results, the structure of $TiO_2$ formed on the Ti-xNb surface was anatase, and no peaks of $Nb_2O_5$ or other Nb oxide were detected suggesting that Nb atoms are dispersed in $TiO_2$-based solid solution. Surface roughness test and SEM results, pore size formed on surface and surface roughness decreased as Nb content increased. From the line analysis results, intensity of Ti peak was high in the center of pore, whereas, intensity of O peak was high in the outside of pore center.

• Restorative Dentistry and Endodontics
• /
• v.47 no.2
• /
• pp.16.1-16.9
• /
• 2022

Objectives: This study compared the cyclic fatigue resistance of One Curve (C wire) and F6 Skytaper (conventional austenite nickel-titanium [NiTi]), and 2 instruments with thermos-mechanically treated NiTi: Protaper Next X2 (M wire) and Hyflex CM (CM wire). Materials and Methods: Ten new instruments of each group (size: 0.25 mm, 6% taper in the 3 mm tip region) were tested using a rotary bending machine with a 60° curvature angle and a 5 mm curvature radius, at room temperature. The number of cycles until fracture was recorded. The length of the fractured instruments was measured. The fracture surface of each fragment was examined with a scanning electron microscope (SEM). The data were analyzed using one-way analysis of variance and the post hoc Tukey test. The significance level was set at 0.05. Results: At 60°, One Curve, F6 Skytaper and Hyflex CM had significantly longer fatigue lives than Protaper Next X2 (p < 0.05). No statistically significant differences were found in the cyclic fatigue lives of One Curve, F6 Skytaper, and Hyflex CM (p > 0.05). SEM images of the fracture surfaces of the different instruments showed typical features of fatigue failure. Conclusions: Within the conditions of this study, at 60° and with a 5 mm curvature radius, the cyclic fatigue life of One Curve was not significantly different from those of F6 Skytaper and Hyflex CM. The cyclic fatigue lives of these 3 instruments were statistically significantly longer than that of Protaper Next.

• Korean Journal of Veterinary Research
• /
• v.43 no.2
• /
• pp.289-294
• /
• 2003

This study aimed to determine of osseointegration following dental implantation in the dog mandible using bone scintigraphy. Five mongrel dogs, weighing approximately 8.5 kg and averaging 1.8 years of age, without active periodontal disease were used. During the entire study period, all dogs were fed a soft commercial diet and water ad libitum to minimize functional loading of the implant. Titanium alloy implant systems 10 mm in length and 4 mm in diameter were chosen for insertion. Twelve weeks prior to implantation, the second and third left mandibular premolars in each dog were extracted for the dental implant insertion. Before the dental implantation procedures and 0, 4, 8, and 12 weeks after the insertions, clinical observation, radiography and bone scintigraphy were conducted. The scintigraphy was obtained using a large field of view gamma camera equipped with a paralled-hole, low-energy collimator about 3 hours after intravenous injection of Tc-99m-MDP (8 mCi/dog) to the dogs. There were not inflammation sign after insertion of dental implants on the mandible in dogs. Implants were slightly movable at the first and fourth weeks, and there was no mobility after 8 weeks. Twelve weeks after dental implantation, the bone uptake scintigraphy of peri-implant bone was similar to that of normal alveolar bone, indicating that peri-implant bone was completely regenerated by new bone. In conclusion, we recommend stable implant fixation with alveolar bone for the accurate and safe repair of teeth loot due to decacy, trauma or peridontal disease. Titanium alloy implants were optimal due to their biocompatibility.

• The Journal of the Korea Contents Association
• /
• v.10 no.9
• /
• pp.302-308
• /
• 2010

In MRI, the Ferromagnetic artifact is generated by the metalization within in which the before inspection removal is impossible and the distortion of an image is brought. The distortion measure according to the steel for each sequence of T1 image and magnetic field intensity are analyzed and minimized method is looked into. We used SIEMENS 1.5T and 3.0T MRI for experiment equipment. First, it places within the Phantom making a metalization(Ti+Al, Stainless, Nitinol) on 1.5T, 3.0T MRI and the T1 weighted image for each Sequence is acquired. The distortion of an image and about adjacent portion change of the metal material were compared through the obtained image, we analyzed. In all metalizations, a distortion was generated and a distortion was few in particularly, and Titanium-Aluminium alloy. And the extent of a distortion was worse image in the Turbo spin Echo. The use of the Titanium-Aluminium alloy the inserted in an internal material of the metalization is recommend. and, equipment of 1.5T the patient inserting a metal in an internal is used in an inspection than equipment of 3.0T. Also, the sequence is suitable when it obtains the optimum T1 weighted image of an impersonate to use the Turbo spin Echo.