• 한국세라믹학회지
• /
• 제25권2호
• /
• pp.168-172
• /
• 1988

In order to prevent the PbO vaporization during calcination and to produce the powder of good sinterability, a coprecipitation method for preparing homogeneous Lead-Zirconate-Titanate (PZT) powder from aqueous salt solution is described. In this method, the PZT-ceramics show low calcining and sintering temperature, and they have good sintering and electronic properties.

• 한국세라믹학회지
• /
• 제33권10호
• /
• pp.1138-1146
• /
• 1996

Al2TiO5 powder was prepared by the sol-gel processing from th metal alkoxides ; aluminium sec-butoxide (Al(OC4H9)3 and tetraethyl orthotitanate (Ti(OC2H5)4) The particles of Al2TiO5 produced from alkoxides were measured to be below $1.5mutextrm{m}$ and mre than 90% weere below 1 ${\mu}{\textrm}{m}$ however those from commercial alumina and titania were over 0.5-7${\mu}{\textrm}{m}$ and only 60% were below 1${\mu}{\textrm}{m}$ and 90% were below 2.5${\mu}{\textrm}{m}$ Therefore Al2TiO5 powder produced from alkoxides had the narrower distributionin size than that produced from the commercial alumina and titania powders. The addition of mullite or Al2O3 powder to the prepared aluminum titanate inhibited the grain growth and this resulted in decreased and increase in density.

• 한국분말재료학회지
• /
• 제17권2호
• /
• pp.101-106
• /
• 2010

In this study, we successfully synthesized a nano-sized lanthanum-modified lead-titanate (PLT) powder with a perovskite structure using a high-energy mechanochemical process (MCP). In addition, the sintering behavior of synthesized PLT nanopowder was investigated and the sintering temperature that can make the full dense PLT specimen decreased to below $1050^{\circ}C$ by using $Bi_2O_3$ powder as sintering agent. The pure PLT phase of perovskite structure was formed after MCP was conducted for 4 h and the average size of the particles was approximately 20 nm. After sintered at 1050 and $1150^{\circ}C$, the relative density of PLT was about 93.84 and 95.78%, respectively. The density of PLT increased with adding $Bi_2O_3$ and the specimen with the relative densitiy over 96% were fabricated below $1050^{\circ}C$ when 2 wt% of $Bi_2O_3$ was added.

• 한국세라믹학회지
• /
• 제39권4호
• /
• pp.336-340
• /
• 2002

Pure and nano-sized $TiO_2$ and $CaTiO_3$ powders were fabricated by a polymeric steric entrapment route and planetary milling process. An ethylene glycol was used as a polymeric carrier for the preparation of organic-inorganic precursors. Titanium isopropoxide and calcium nitrate were dissolved in liquid-type ethylene glycol without any precipitation. At the optimum amount of the polymer, the metal cations were dispersed in solution and a homogeneous polymeric network was formed. The dried precursor ceramic gels were turned to porous powders through calcination process. The porous powders were crystallized at low temperatures and the crystalline powders were planetary milled to nano size.

• 한국세라믹학회:학술대회논문집
• /
• 한국세라믹학회 2004년도 추계총회 및 연구발표회 초록집
• /
• pp.90.2-90.2
• /
• 2004

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2004년도 International Symposium on Powder Materials and Processing
• /
• pp.53-53
• /
• 2004

• 한국분말재료학회지
• /
• 제23권5호
• /
• pp.353-357
• /
• 2016

In this study, $TiO_2$ powders are synthesized from ammonium hexafluoride titanate (AHFT, $(NH_4)_2TiF_6$) as a precursor by heat treatment. First, we evaluate the physical properties of AHFT using X-ray diffraction (XRD), particle size analysis (PSA), thermogravimetric analysis (TGA), and field-emission scanning electron microscopy (FE-SEM). Then, to prepare the $TiO_2$ powders, is heat-treated at $300-1300^{\circ}C$ for 1 h. The ratio of anatase to rutile phase in $TiO_2$ is estimated by XRD. The anatase phase forms at $500^{\circ}C$ and phase transformation to the rutile phase occurs at $1200^{\circ}C$. Increase in the particle size is observed upon increasing the reaction temperature, and the phase ratio of the rutile phase is determined from a comparison with the calculated XRD data. Thus, we show that anatase and rutile $TiO_2$ powders could be synthesized using AHFT as a raw material, and the obtained data are utilized for developing a new process for producing high-quality $TiO_2$ powder.

• 한국세라믹학회지
• /
• 제48권1호
• /
• pp.99-105
• /
• 2011

Lead titanate ($PbTiO_3$) powder was prepared from lead nitrate ($Pb(NO_3)_2$) and titania ($TiO_2$) by hydrothermal route. Phase formation process was investigated by observing the phases formed in various experimental conditions like different KOH concentration, reaction temperature and time. $PbTiO_3$ powder was fabricated when the KOH concentration was 0.8M or higher. An intermediate compound, $PbTi_{0.8}O_{2.6}$, was formed at first by a reaction between PbO and $TiO_2$ and changed into $PbTiO_3$ powder with a perovskite crystal structure. A $PbTiO_3$ phase was formed in a shorter time when a KOH concentration was increased from 0.8M to 8M because a driving force for a $PbTiO_3$ formation was increased due to an increase in a degree of supersaturation. And $TiO_2$ (rutile) and $3PbO{\cdot}H_2O$ were observed at room temperature in a 0.8M KOH solution and $TiO_2$(rutile) and PbO (litharge) in a 8M KOH. A $PbTiO_3$phase was also formed in a shorter time at a higher reaction temperature as a reaction temperature influenced the rates for a dissolution and a precipitation.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part 1
• /
• pp.124-125
• /
• 2006

Multilayer ceramic capacitor (MLCC) miniaturization has increased the demand for superfine $BaTiO_3$ powder due to its thin dielectric layer. Hydrothermally synthesized $BaTiO_3$ powder a pseudo-cubic phase resulting in poor dielectric properties due to size effect and hydroxyl ion inclusion in the $BaTiO_3$ lattice. We attempted a superfine (lower than 100 nm) highly tetragonal $BaTiO_3$ powder via a solvothermal method without precipitating agent. The lattice parameters and the relative amounts of tetragonal and cubic phases were determined using Rietveld refinement.

• 한국세라믹학회지
• /
• 제25권1호
• /
• pp.54-58
• /
• 1988

In order to depress PbO vaporization during calcination and improve sinterability in low temperature, a method for preparing homogeous Lead-Zirconate-Titanate (PZT) powder from aqueous salt solution by precipitation is described. In this method, single phae PZT fine powders are formed at above 500$^{\circ}C$. PZT-ceramics using these powders have high sinterability, and good sintering characteristics relatively low temp. (-high apparent density, low porosity, low water adsorption etc.)