Sensitized STS 304 stainless steel crack growth rate(CGR) in high temperature water was investigated under trapezoidal wave loading test using fracture mechanics techniques. The CGR, due to stress corrosion cracking(SCC), were systematically measured as a function of the stress intensity factor and stress. holding time under trapezoidal wave loading. In high temperature water, CGR was enhanced by a synergistic effects in combination with an aggressive environment and mechanical damage. The CGR, $(da/dN)_{env}$ was basically described as a summation of the environmentally assisted crack growth rate $(da/dN)_{SCC}$, $(da/dN)_{CF}$ and fatigue crack growth rate in air $(da/dN)air,. The CGR, $(da/dN)_{env}$, increased linearly with increasing stress holding time. The CGR, $(da/dN)_{SCC}$ decreased linearly with increasing stress holding time. Fracture surface mode varied from trans-granular cracking to inter-granular cracking with increasing stress holding time.

• 대한기계학회논문집A
• /
• 제39권10호
• /
• pp.1039-1044
• /
• 2015

차량의 개발단계에서 내구성 평가는 많은 시간과 비용이 소요된다. 최근 완성차 업체들은 자사만의 내구성 평가방법을 개발하고 수정 보완하는데 많은 노력을 기울이고 있다. 본 연구는 토션빔 액슬의 내구성 평가를 위한 통합 CAE 기법을 개발함에 있어 세계적인 자동차 업체의 정형화된 CAE 기법과의 비교를 통해 경제성을 평가하고 실험적 방법을 통해 얻은 데이터와의 비교를 통해 신뢰성을 확보하는 것을 목표로 하였다. 이를 위해 현재까지 널리 사용되어 온 준정적 내구해석의 과정 및 결과에서 보완점과 문제점을 분석하였고, 업계의 요구사항을 면밀히 검토하여 정규모드해석을 통해 다물체 동역학 모델을 구성하고 이를 이용한 동역학 해석을 진행한 후 그 결과를 이용하여 내구해석인 공진 내구해석 기법을 제안하였다.