• 한국전기전자재료학회논문지
• /
• 제14권8호
• /
• pp.640-646
• /
• 2001

The electrical stability for DC stress of Pr$_{6}$O$_{11}$-based ZnO varistos consisting of ZnO-Pr$_{6}$O$_{11}$-CoO-Cr$_2$O$_3$-Er$_2$O$_3$-based ceramics were investigated with sintering temperature in the range of 1325~1345$^{\circ}C$. A the sintering temperature is raised, the nonlinear exponent of varistors was decreased, whereas the stability was markedly improved. The density of ceramics was found to greatly affect the electrical stability for DC stress. The varistors sintered at 13$25^{\circ}C$ were completely degraded because of thermal runaway attributing to low density. The varistors sintered at 1335$^{\circ}C$ exhibited the highest nonlinearity, with a nonlinear exponent of 70.53 and a leakage current of 1.92$\mu$A, whereas they did not exhibit relatively high stability. On the contrary, the varistors sintered at >134$0^{\circ}C$ exhibited not only a high nonlinearity marking the nonlinear exponent above 50 and the leakage current below 3$\mu$A, but also a high stability marking the variation rate of the varistor voltage below 2%, even under DC stress such as (0.80V$_{1mA}$/9$0^{\circ}C$/12h)+(0.85V$_{1mA}$/115$^{\circ}C$/12h)+(0.90V$_{1mA}$/12$0^{\circ}C$/12h)+(0.95V$_{1mA}$/1$25^{\circ}C$/12h)+(0.95V$_{1mA}$/15$0^{\circ}C$/12h). In particular, ti was found that the varistors sintered at 134$0^{\circ}C$ were more nonlinear and more stable, compared with that of 1345$^{\circ}C$.EX>.}C$.EX>.

• 한국재료학회지
• /
• 제13권11호
• /
• pp.761-768
• /
• 2003

The corrosion resistance and cytotoxicity behavior of Ti alloys were studied as a function of Nb contents(3wt.%Nb, 20wt.%Nb, 40wt.%Nb). Ti-Nb alloys were melted by vacuum arc furnace and then rolled to 50% reduction ratio after homogenized at 105$0^{\circ}C$ for 24hrs. The corrosion resistance of Ti-Nb alloys were investigated by potentiodynamic polarization test in the 0.9% NaCl and 5% HCI solution. Biocompatibility of Ti-Nb alloys was evaluated by cytotoxicity test. The results can be summarized as follows 1) The microstructure change from equiaxial to acicular and the increased $\beta$ phase in Ti-Nb alloys were obtained as the Nb content increased. 2) For the corrosion test in the solution of 0.9% NaCl and 5% HCI, the corrosion behavior of Ti-Nb alloys was similar to ASTM grade 2 CP Ti. 3) For the cytotoxicity test, Ti-Nb alloys showed excellent biocompatibility compared to ASTM grade 2 CP Ti, 316L STS and Co-Cr alloys.

• 한국재료학회지
• /
• 제20권5호
• /
• pp.257-261
• /
• 2010

A non-volatile resistive random access memory (RRAM) device with a Cr-doped $SrZrO_3/SrRuO_3$ bottom electrode heterostructure was fabricated on $SrTiO_3$ substrates using pulsed laser deposition. During the deposition process, the substrate temperature was $650^{\circ}C$ and the variable ambient oxygen pressure had a range of 50-250 mTorr. The sensitive dependences of the film structure on the processing oxygen pressure are important in controlling the bistable resistive switching of the Cr-doped $SrZrO_3$ film. Therefore, oxygen pressure plays a crucial role in determining electrical properties and film growth characteristics such as various microstructural defects and crystallization. Inside, the microstructure and crystallinity of the Cr-doped $SrZrO_3$ film by oxygen pressure were strong effects on the set, reset switching voltage of the Cr-doped $SrZrO_3$. The bistable switching is related to the defects and controls their number and structure. Therefore, the relation of defects generated and resistive switching behavior by oxygen pressure change will be discussed. We found that deposition conditions and ambient oxygen pressure highly affect the switching behavior. It is suggested that the interface between the top electrode and Cr-doped $SrZrO_3$ perovskite plays an important role in the resistive switching behavior. From I-V characteristics, a typical ON state resistance of $100-200\;{\Omega}$ and a typical OFF state resistance of $1-2\;k{\Omega}$, were observed. These transition metal-doped perovskite thin films can be used for memory device applications due to their high ON/OFF ratio, simple device structure, and non-volatility.

• 한국자기학회지
• /
• 제15권1호
• /
• pp.1-6
• /
• 2005

높은 큐리온도를 가질 수 것으로 예측된 전이금속이 도핑된 ZnO의 전자구조와 자성을 제일원리계산방법을 이용하여 연구하였다. 본 연구에서 전이금속은 Ti, Cr, Mn, Fe, Co, Ni, Ru, Pd, Ag 이고 도핑 수준은 25%로 두고 계산하였다. 자성연구에서 가장 적합한 방법으로 알려져 있는 Full-potential Linearized Augmented Plane Wave(FLAPW)방법을 사용하였으며 교환-상관 전위는 general gradient approximation(GGA)를 사용하였다. 도핑된 전이금속 (Ti, Cr, Mn, Fe, Co, Ni, Ru, Pd, Ag)은 각각 0.83, 3.03, 4.03, 3.48, 2.47, 1.56, 0.43, 0.75, 0.01 ${\mu}_B$의 자기모멘트를 가지며, 전이금속에 이웃한 O 원자도 가안 띠혼성으로 측정 가능한 자기모멘트를 가질 수도 있는 것으로 계산되었다. 3d 전이금속이 도핑된 ZnO는 (CoZnO를 제외하고) 절반금속 특성을 가지는 것으로 계산되었다. 또한 4d 전이금속이 도핑된 경우는 강자성 상태가 상자성 상태에 비해 에너지차이가 크지 않을 뿐 아니라 페르미 준위에 다수 스핀과 소수 스핀 상태 모두가 페르미 준위에 위치해 있어 스핀분극 정도가 낮았다.

• 보존과학연구
• /
• 통권22호
• /
• pp.93-114
• /
• 2001

The composition analysis of Danchung pigments at Geunjeongjeon Hall in Gyeongbokgung Palace were carried out by FXRF and MXRD. The analytical result of the inside pigments at Geunjeongjeon showed that these painted in use the mineral pigments. Gold pigment was pure gold(Au).The main composition identified in green pigments were chalcanthite($CuSO_4$.$5H_2O$) and celadonite($K(Mg, Fe, Al)_2$.$(Si, Al)_4O_10(OH)_2$ ). Red pigments werecinnnabar(HgS).The analytical result of the outside pigments at Geunjeongjeon revealed that these applied to the artificial synthetic pigment. Yellow pigment was chromeyellow($PbCrO_4$). The main composition identified in red pigments were red lead($Pb_3O_4$)and hematite($Fe_2O_3$). Green pigments were emeral green($C_2H_3A_s3Cu_2O_8$) and chromegreen($Cr_2O_3$). Blue pigment was lazurite($Na_6Ca2Al_6Si_6O_24(SO_4)_2$), titanium dioxide($TiO_2$) of white pigment.

• Nuclear Engineering and Technology
• /
• 제42권6호
• /
• pp.662-669
• /
• 2010

To develop the manufacturing methods for the blanket first wall (FW) of the International Thermonuclear Experimental Reactor (ITER) and to verify the integrity of the joint, Be/Cu mockups were fabricated and tested at the KoHLT-1 (Korea Heat Load Test facility), a graphite heater facility located at the Korea Atomic Energy Research Institute (KAERI). Since Be and Cu joining is the focus of the present study, the fabricated mockups had a CuCrZr heat sink joined with three Be tiles as an armor material, unlike the original ITER blanket FW, which has a stainless steel structure and coolant tubes. Hot isostatic pressing (HIP) was carried out at $580^{\circ}C$ and 100 MPa for 2 hours as the method for Be/Cu joining. Three interlayers, namely, $1{\mu}mCr/10{\mu}mCu$, $1{\mu}mTi/0.5{\mu}mCr/10{\mu}mCu$, and $5{\mu}mTi/10{\mu}mCu$ were applied as a coating to the Be tiles by a physical vapor deposition (PVD) method. A shear test was performed with the specimens, which were fabricated by the same methods as those used to fabricate the mockups. The average values were 125 MPa to 180 MPa, and the samples with the $1{\mu}mCr/10{\mu}mCu$ interlayer showed the lowest value. No defect or delamination was found in the joints of the mockups by the developed ultrasonic test using a flat-type probe with a 10 MHz frequency and a 0.25 inch diameter. High heat flux (HHF) tests were performed at $1.0\;MW/m^2$ heat flux for each mockup using the given conditions, and the results were analyzed by ANSYS-CFX code. For the test criteria, an expected fatigue lifetime about 1,000 cycles was obtained by analysis with ANSYS-mechanical code. Mockups using the interlayers of $1{\mu}mTi/0.5{\mu}mCr/10{\mu}mCu$ and $5{\mu}mTi/10{\mu}mCu$ survived up to 1,100 cycles over the required number of cycles. However, one of the Be tiles in the other two mockups using the $1{\mu}mCr/10{\mu}mCu$ interlayer was detached during the screening test, and others were detached by discharge after 862 cycles. The integrity of the joints using the proposed interlayers was proven by the HHF test, but the other interlayer requires more study before it can be used for the joining of Be to Cu. Moreover, it was confirmed that the measured temperatures agreed well with the analysis temperatures, which were used to estimate the lifetime and that the developed facility showed its capability of the long time operation.

• Journal of Welding and Joining
• /
• 제18권2호
• /
• pp.49-56
• /
• 2000

Recently developed Austenite stainless steel, 309L was used to overlay on 3Cr-1Mo-V-Ti-B steels, using Electroslag welding process, which wide electrodes were adopted. Transition region in welding interlayer relating to disbonding crack was investigated. Also, the effect of welding condition on the width of transition region and coarsening grains of the austenite were studied. 1) With increasing welding speed the width of martensite at transient region was increased, but the amount of delta ferrite in weld metal was reduced, being fine grained. 2) The form of martensite at the transition region was occurred by reversible transformation during cooling since the interdiffusion of Cr and Ni from weld metal and Fe and C from base metals at the transition region, causes to lowering the concentration of Cr and Ni at the transition region, leading to increasing Ms point. 3) With increasing welding speed, the grain of austenite formed at the welding interface was finer. With increasing welding current under the same welding speed, the grain size of the austenite was finer. At high current, original grain size of the austenite is coarse, but the austenite has fine grains because the austenite was transformed to martensite during cooling. 4) In the case of high welding speed, the width of martensite at the welding interface was increased, but the grain size of austenite at the welding interface was finer. This indicates that the inhibition of disbonding crack may be achieved through dispersening fine carbides in the gain boundary.

• 대한의용생체공학회:의공학회지
• /
• 제6권1호
• /
• pp.37-46
• /
• 1985

Development of a dental Ni-Cr alloy system for porcelain veneering crown and bridge was studied in this research. The principles of alloy design were a) It should not contain toxic beryllium. b) It should have low melting Point. c) It should be easily ground and polished. d) It should possess an adequate strength to resist the deformational force In the mouth. e) It should be bondable Ivith porcelain by chemically. After investigating the effect of minor elements such as boron and rare earth metals on the mechanical properties of the Ni-Cr alloy system, the compromised ideal composition for dental use was determined. The composition was l9.6%, Cr, 5.6% Mo, 3.4% Si, 1, 0% Fe, 0.01% Ti, 0.5-1.0% B, 0.2-0.6% misch metal, balance Ni. To compare the performance of experimental alloy with commercially available alloys, the properties such as strength, melting point, and bond strength were measured. The results Ivere as follows: a) Boron increases the strength of the alloy but reduces the elongation. b) Misch metal increases the strength when the boron content is low, but does not increase the strength when boron content is high. And it reduces the elongation drastically, c) Mechanical strength of the experimental alloy was not superior to commercially available Be containing alloy, but handling performance such as castability, ease of granting and polishing, and cuttability were superior to the Be containing alloy.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2016년도 제50회 동계 정기학술대회 초록집
• /
• pp.247.1-247.1
• /
• 2016

Low-cost, high efficiency solar cells are tremendous interests for the realization of a renewable and clean energy source. ZnTe based solar cells have a possibility of high efficiency with formation of an intermediated energy band structure by impurity doping. In this work, ZnO/ZnTe:Cr and ZnO/i-ZnTe structures were fabricated by pulsed laser deposition (PLD) technique. A pulsed (10 Hz) Nd:YAG laser operating at a wavelength of 266 nm was used to produce a plasma plume from an ablated a ZnTe target, whose density of laser energy was 10 J/cm2. The base pressure of the chamber was kept at approximately $4{\times}10-7Torr$. ZnTe:Cr and i-ZnTe thin films with thickness of 210 nm were grown on p-Si substrate, respectively, and then ZnO thin films with thickness of 150 nm were grown on ZnTe:Cr layer under oxygen partial pressure of 3 mTorr. Growth temperature of all the films was set to $250^{\circ}C$. For fabricating ZnO/i-ZnTe and ZnO/ZnTe:Cr solar cells, indium metal and Ti/Au grid patterns were deposited on back and front side of the solar cells by using thermal evaporator, respectively. From the fabricated ZnO/ZnTe:Cr and ZnO/i-ZnTe solar cell, dark currents were measured by using Keithley 2600. Solar cell parameters were obtained under Air Mass 1.5 Global solar simulator with an irradiation intensity of 100 mW/cm2, and then the photoelectric conversion efficiency values of ZnO/ZnTe:Cr and ZnO/i-ZnTe solar cells were measured at 1.5 % and 0.3 %, respectively.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2005년도 추계학술대회 논문집
• /
• pp.118-121
• /
• 2005

The square cup drawing of magnesium alloy AZ31 $(aluminum\;3\%,\;Zinc\;1\%)$ sheets was studied by experimental approach in various temperatures (200, 250, 300, 350, $400^{\circ}C$) when blank holding force (BHF) was controlled in real-time. And so on, the drawability was measured with the different die and punch coating. The square cup drawing test was performed by three different coated punches (CrN, TiCN, Non-coated). BHF was set about 2.0 KN, forming speed was 50 mm/min, blank thickness were 0.5, 1.0mm and the cup size was 40 mm by 60 mm after forming. The experimental data of square cup drawing test show that the tools coating and temperature were effect on the drawbility.