• Journal of Welding and Joining
• /
• v.14 no.4
• /
• pp.99-108
• /
• 1996

The microstructure and bond strength are examined on the SiC/SiC and SiC/mild steel joints brazed by the Ag-Ti based alloys with different Ti contents. In the SiC/SiC brazed joints, the thickness of the reaction layers at the bond interface and the Ti particles in the brazing alloy matrices increase with Ti contents. When Ti is added up to 9 at% in the brazing alloy. $Ti_3SiC_2$ phase in addition to TiC and $Ti_5Si_3$ phase is newly created at the bond interface and TiAg phase is produced from peritectic reaction in the brazing alloy matrix. In the SiC/mild steel joints brazed with different Ti contents, the microstructure at the bond interface and in the brazing alloy matrix near SiC varies similarly to the case of SiC/SiC brazed joints. But, in the brazing alloy matrix near the mild steel, Fe-Ti intermetallic compounds are produced and increased with Ti contents. The bond strengths of the SiC/SiC and SiC/mild steel brazed joints are independent on Ti contents in the brazing alloy. There are no large differences of the bond strength between SiC/SiC and SiC/mild steel brazed joints. In the SiC/mild steel brazed joints, Fe dissolved from the mild steel does not affect on the bond strength of the joints. Thermal contraction of the mild steel has nearly no effects on the bond strength due to the wide brazing gap of specimens used in the four-point bend test. The brazed joints has the average bond strength of about 200 MPa independently on Ti contents, Fe dissolution and joint type. Fracture in four-point bend test initiates at the interface between SiC and TiC reaction layer and propagates through SiC bulk. The adhesive strength between SiC and TiC reaction layer seems to mainly control the bond strength of the brazed joints.

• The Transactions of the Korean Institute of Electrical Engineers
• /
• v.41 no.6
• /
• pp.633-639
• /
• 1992

The physical and electrical properties of TiN/TiSiS12T contact barrier were studied. The TiN/TiSiS12T system was formed by rapid thermal anneal in NS12T ambient after the Ti film was deposited on silicon substrate. The Ti film reacts with NS12T gas to make a TiN layer at the surface and reacts with silicon to make a TiSiS12T layer at the interface respectively. It was found that the formation of TiN/TiSiS12T system depends on RTA temperature. In this experiment, competitive reaction for TiN/TiSiS12T system occured above $600^{\circ}C$. Ti-rich TiNS1xT layer and Ti-rich TiSiS1xT layer were formed at $600^{\circ}C$. stable structure TiN layer and TiSiS1xT layer which has CS149T phase and CS154T phase were formed at $700^{\circ}C$. Both stable TiN layer and CS154T phase TiSiS12T layer were formed at 80$0^{\circ}C$. The thickness of TiN/TiSiS12T system was increased as the thickness of deposited Ti film increased.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.109-110
• /
• 2006

We have studied the effect of C/Ti atomic ratio of TiCx (x=0.5, 0.75 and 1.0) raw powder on the properties of the Ti-Mo-WTiC sintered hard alloy. The decrease of C/Ti atomic ratio accelerated the densification in the sintering process. The hardness was remarkably improved up to 1350HV with decreasing the C/Ti atomic ratio because of increase of TiCx phase volume content and its fine dispersion. From the results of electro-chemical tests in acid and 3% NaCl solutions, it was obvious that every alloy had excellent corrosion resistance, which meant about 200 times better than that of WC-Co cemented carbide.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2014.11a
• /
• pp.192-192
• /
• 2014

TiN, Ti(C,N), TiAlSiN, TiZrAlN, TiAlCrSiN 박막을 제조한 후, 이 들의 고온산화 특성을 SEM, EPMA, TGA, TEM, AES 등을 이용하여 조사하고, 산화기구를 제안하였다. 산화속도, 생성되는 산화물의 종류와 분포는 박막의 조성, 산화온도, 산화시간에 따라 변하였다.

• Journal of the Korean Ceramic Society
• /
• v.35 no.7
• /
• pp.749-756
• /
• 1998

TiC-Ni and TiC-Ni-Mo cermet powders were produced by Self-propagating High temperature Synthesis (SHS) process. The cooling rate of synthesized powders were controlled by using the V-shaped copper jig and the carbide size decreased with increasing the cooling rate I. e decreasing the width of copper jig Round shape carbide particles were produced after SHS reaction in TiC-Ni as well as TiC-Ni-Mo powders. Local segregation of Mo rich phases was observed in SHS powder of TiC-Ni-Mo and the uneven dis-triobution of Mo promoted the faster growth rate of carbide particles during sintering compared to the same composition specimen with commercial TiC powder. Howogeneous microstructure of TiC-Ni-Mo cermet was obtained when the elemental Mo powder was mixed with the SHS powder of TiC-Ni.

• Journal of Korea Foundry Society
• /
• v.30 no.4
• /
• pp.147-150
• /
• 2010

An eco-friendly production technique of Al-8.6Ti-0.025C refiner was developed by melting a Al-Ti master alloy in a graphite crucible, in which the potential nucleation site, TiC effectively formed by the spontaneous in-situ reaction between excessive Ti and carbon from graphite crucible. The A3003 alloy refined by the Al-8.6Ti-0.025C showed effectively refined macrostructure and enhanced mechanical properties comparable to the commercial Al-Ti-B refiner. The effective refinement was achieved in a shorter compare to the melt-treating time commercial Al-Ti-B refiner.

• Journal of the Korean institute of surface engineering
• /
• v.25 no.5
• /
• pp.235-252
• /
• 1992

(Ti, Al)N films were deposited on 304 stainless steel sheet by D.C. magnetron sputtering using Al target and Ti plate. The high temperature oxidation of (T, Al)N films with the variation of composition has been investigated. The chemical composition of (Ti, Al)N films with the variation of composition has been investigated. The chemical composition of (Ti, Al)N films was similar to the sputter area ratio of titanium to aluminum target by means of EDS and AES survey. The high temperature oxidation test of (Ti, Al)N showed that (Ti, Al)N has better high temperature resistance than TiN and TiC films. TiC films were cracked at 40$0^{\circ}C$ in air TiN films quickly were oxidised at $600^{\circ}C$, were spalled more than $700^{\circ}C$. But (Ti, Al)N films are relatively stable to$ 900^{\circ}C$. The good resistance to high temperature oxida-tion of (Ti, Al)N films are due to the formation of dense Al2O3 and TiO2 oxide layer. Especially, Al2O3 oxide layer is more important. The results obtained from this study show, it is believe that the (Ti, Al)N film by D.C. magnetron sputtering is promising for the use of high temperature and wear resistance mate-rials.

• Journal of Powder Materials
• /
• v.15 no.6
• /
• pp.503-508
• /
• 2008

Ti(C,N) solid solutions in hot-pressed Ti($C_{x}N_{1-x}$) (x=0.0, 0.3, 0.5, 0.7, 1.0) and 40TiC-40TiN-20Ni (in wt.%) cermet were characterized in this study. For hot-pressed Ti(C,N)s, the lattice parameters and hardness values of Ti(C,N) were determined by using XRD (X-Ray Diffraction) and nanoindentation. The properties of hot-pressed Ti(C,N) samples changed linearly with their carbon or nitrogen contents. For the TiC-TiN-Ni cermet, the hardness of the hard phase and binder phase were determined by nanoindentation in conjunction with microstructural observation. The measured hardness values were ${\sim}8.7$ GPa for the binder phase and ${\sim}28.7$ GPa for the hard phase, which was close to the hardness of hot-pressed Ti($C_{0.7}N_{0.3}$).

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2008.11a
• /
• pp.83-85
• /
• 2008

4성분계 Ti-Si-C-N 코팅막은 $TiCl_4$, $SiH_4$, $CH_4$, Ar, 그리고 $N_2$ 가스 혼합체를 이용하여 RF-PECVD 기법에 의해 Si 와 AISI 304 기판위에 합성하였다. Ti-C-(0.6)-N(0.4) 조성의 코팅막에 Si를 첨가함으로 Ti(C,N) 결정질은 줄어들고, Si3N4 및 SiC 비정질상이 나타났다. Ti-Si(9.2 at.%)-C-N의 조성에서 나노 크기의 nc-Ti(C,N) 결정질을 비정질 a-Si3N4/SiC가 둘러싸고 있는 형태의 나노 복합체를 나타내었다. 경도 24 Gpa의 Ti-C-N 코팅막은 Si를 첨가함으로 Ti-Si(9.2 at.%)-C-N 조성에서 46 Gpa의 최고 경도를 나타내었으며, 마찰계수의 경우에도 Ti-C-N 코팅막에 Si를 첨가함으로 크게 낮아졌다.

• Journal of the Korean Vacuum Society
• /
• v.3 no.4
• /
• pp.405-413
• /
• 1994

초고진공에서 기판 Si(111)-7$\times$7 위에 Ti:Si 또는 1:2의 조성비로 Ti와 Si을 동시증착한 후 in situ 열처리하여 TiSi2 박막을 에피택셜 성장시켰다 XRD와 XPS 분석결과 동시증착된 혼합 층에서 C49-TiSi2 박막의 성장은 핵형성에 의함을 확인하였으며 양질의 C49-TiSi2 박막은 Ti를 증착한후 Ti와 Si를 동시 증착한 (Ti+2Si)/(Ti)/Si(111)-7$\times$7구조의 시료를 초고진공에서 50$0^{\circ}C$에서 열처리하여 얻을수 있었다. 형성된 C49-TiSi2/Si(111)의 계면은 깨끗하였고 HRTEM 분석 결과 C49-TiSi2\ulcornerSi(111)의 계면은 약 10。 의 편의를 가지면서 TiSi2[211]∥Si[110] TiSi2(031)/Si(111) 의 정합성을 가졌으며 시료의 전 영 역에 에피택셜 성장되었다.