• 한국표면공학회지
• /
• 제51권6호
• /
• pp.344-353
• /
• 2018

Plasma electrolytic oxidation of Ti-25Ta-xHf alloy in electrolyte containing Ca and P for dental implants was investigated using various experimental techniques. Ti-25Ta-xHf (x=0 and 15 wt.%) alloys were manufactured in an arc-melting vacuum furnace. Micropores were formed in PEO films on Ti-25Ta-xHf alloys in 0.15 M calcium acetate monohydrate + 0.02 M calcium glycerophosphate at 240 V, 270 V and 300 V for 3 min, respectively. The microstructure of Ti-25Ta-xHf alloys changed from (${\alpha}^{\prime}+{\alpha}^{{\prime}{\prime}}$) phase to (${\alpha}^{{\prime}{\prime}}+{\beta}$) phase by addition of Hf. As the applied potential increased, the number of pore and the area ratio of occupied by micro-pore decreased, whereas the pore size increased. The anatase phase increase as the applied potential increased. Also, the crystallite size of anatase-$TiO_2$ can be controlled by applied voltage.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2015년도 춘계학술대회 논문집
• /
• pp.106-106
• /
• 2015

In this study, we investigated electrochemically formed nanotube shape on ternary Ti-25Ta-xHf alloys with Hf contents. Ti-25Ta-xHf (x=0~15 wt.%) alloys were manufactured by vacuum arc-melting furnace. The obtained ingots were homogenized in an argon atmosphere at $1050^{\circ}C$ for 2h and then water quenching. The specimens were cut from ingots to 4 mm thickness and first ground and polished using SiC paper (grades from #100 to #2000). The anodization treatments on Ti-25Nb-xHf alloys were carried out at room temperature for experiments. The formation of nanotubular film was conducted by electrochemical method in mixed electrolytes with 1 M $H_3PO_4$ + 0.8 wt. % NaF at 30 V for 2 h. The morphologies of nanotube depended on the Hf content in Ti-25Ta-xHf ternary system.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2014년도 추계학술대회 논문집
• /
• pp.187-187
• /
• 2014

In this study, we investigated mechanical properties and surface characteristics of Ti-25Ta-xHf alloys. The samples were manufactured for composition of Ti-25Ta-xHf(x=0 to 15 wt. %) alloys. Each alloy was melted twenty times in an arc-melting vacuum furnace. The microstructural phases and phase transformation of Ti-25Ta-xHf alloys were identified with the aid of an XRF, XRD and DSC. And mechanical properties were investigated using Vickers hardness, nanoindentation, and tensile test.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2015년도 추계학술대회 논문집
• /
• pp.138-138
• /
• 2015

In this study, highly ordered nanotubular surface of Ti-25Ta-xHf alloys for dental applications was researched. Ti-25Ta-xHf alloys were contained from 0% to 15% Hf content. Formation of nanotubular structure was achieved by an electrochemical method in 1M $H_3PO_4$ electrolytes containing 0.8%wt. % NaF.