• Journal of Advanced Marine Engineering and Technology
• /
• v.23 no.3
• /
• pp.389-397
• /
• 1999

Recently the use of Pd catalyst have been continued to expand because of cost avaliabilityand performance advantages. Especially the Pd+Rh catalyst instead of the Pt+Rh catalyst had been used for most of three way catalysts because of the more stringent emission standards and its higher temperature effectiveness. The main purpose of this study is to investigate the design parameter impacts on the Pd+Rh cat-alyst for the automotive exhaust catalysts application. This study was investigated on the catalyst efficiency for the volume and the precious metal loading of the Pd+Rh ceramic monolithic cata-lyst. And experiments concerning the effects of volume and precious metal loading on Pd+Rh three way catalysts were conducted to examined the catalyst light-off temperature and conver-sion efficiency on higher volume demonstrated almost similar performance. But their effects on higher precious metal loading demonstrated considerably better performance.

• Journal of ILASS-Korea
• /
• v.21 no.3
• /
• pp.137-143
• /
• 2016

The LPG vehicles are being operated by commercial purposes generally such as taxis. Most of taxis have a long-mileage and a harsh driving pattern. These properties may accelerate aging of the three-way catalysts much faster than the passenger vehicles. Because of this background, it was analyzed the test result of fuel efficiency and emissions on the LPG-fueled light duty vehicle. It was selected for a LPG vehicle of ULEV level to measure the fuel efficiency and emissions of the aged three-way catalysts. And the aged three-way catalysts which was driven about 300,000km and 550,000km replaced on the test vehicle in consecutive order. As a result, The aged three-way catalysts generally had no effect on fuel efficiency result, and harmful exhaust emissions had been shown to increase in most of the test mode, even though it satisfied the regulation value on most test modes.

• Journal of Institute of Convergence Technology
• /
• v.1 no.1
• /
• pp.13-17
• /
• 2011

The car industry is one of the technological applications which more rare earth metals employes as three-way catalysts. Therefore, the recovery of rare earth metals from the used automotive three-way catalysts could be important source to obtain these metals. This work presents the analysis of market and demand for rare earth metal in automotive three-way catalyst and introduces the dry and the wet processes for the recovery of rare earth metals from used three-way catalyst. Finally, the alternative methods to conventional wet processes was simply suggested based on the economic and ecological point of view.

• Applied Chemistry for Engineering
• /
• v.20 no.4
• /
• pp.430-436
• /
• 2009

Deactivated three-way catalysts which had been exposed to gasoline engine exhaust for a long time were remanufactured by ultra sonic cleaning with distilled water, sulfuric acid solution and impregnation with precious metals (Pt, Pd, Rh). The catalytic properties as well as conversion reactivity of CO, THC and NOx about fresh, aged and remanufactured catalysts were examined. Most of the pollutants deposited on the aged three-way catalysts were removed in the remanufacturing process of those catalysts. At the same time a little amount of precious metals like Pt and Pd were removed in the remanufacturing process. Under the experimental condition used in this study, in the case of the remanufactured catalysts with impregnation of precious metals, the catalytic activities were recovered to almost the same level, or higher level of that of the fresh catalyst.

• Journal of Korean Society for Atmospheric Environment
• /
• v.15 no.5
• /
• pp.667-676
• /
• 1999

The roles of ceria on three-way catalyst is to improve the noble metal dispersion and thermal stability of support ${\gamma}$-$Al_2O_3$. And, ceria has a oxygen storage capacity(OSC) under fuel rich/lean conditions to improve the operating windows of NOx, THC and CO conversion. However, ceria has weak thermal stability under high temperature due to the crystallite growth. So that, the OSC of ceria is decreased, and then the conversions of NOx, THC and CO is decreased. One way of enhancing the thermal stability and NOx, THC and CO conversion Pd-only catalyst is to improve as well as its thermal stability and oxygen storage capacity of the ceria. Especially, the appropriate mixing ratios of bulk and stabilized ceria are very important for designing principles of Pd-only three-way catalysts. In this paper, we discussed the thermal properties of stabilizedand unstabilized (bulk) ceria, and the oxygen storage capacity (OSC) of catalysts, and found the correlation between activity and the OSC of Pd-only catalysts with various different mixing ratios of bulk and stabilized ceria. Finally, we propose the design principles to improve the thermal stability of washcoated Pd-only catalysts.

• Clean Technology
• /
• v.15 no.3
• /
• pp.147-153
• /
• 2009

Waste three-way catalysts were remanufactured by ultrasonic wave treatment followed by active component re-impregnation and the catalytic activities and surface properties of remanufactured catalysts were measured at various remanufacturing conditions. In case of the catalyst prepared by ultrasonic wave cleaning, the optimal period for elimination of surface contaminants from the waste catalyst was found to be about 5 minutes. The proper re-impregnation amounts of the active components for the best catalytic performance were investigated and the catalytic performance tests were also carried out with various temperature for the total hydrocarbon (THC), carbon monoxide (CO) and nitrogen oxides (NOx) conversions. The experimental results showed that the catalytic performances of the remanufactured catalysts were recovered almost the same level as those of the fresh catalyst except those of the NOx conversion.

• Proceedings of the Korea Air Pollution Research Association Conference
• /
• 1999.04a
• /
• pp.231-232
• /
• 1999

• Proceedings of the Korean Vacuum Society Conference
• /
• 2000.02a
• /
• pp.145-145
• /
• 2000

M-CeO2 (M : noble metal) catalysts have been widely studied as three-way catalysts and methanol synthesis catalysts. Ceria is thought to play a number of roles in these catalysts. The Ce(IV)/Ce(III) redox pair may store/release gases under oxidizing/reducing conditions, extending the operational window. Additionally, metal-ceria interactions lead to several effects, including the dispersion of the active components and promoting the activation of molecules such as CO or NO. Pd is a promising component to current TWC formulations and behaves particularly well when compared with Pt and Rh-based catalysts for low-temperature oxidation of Co and hydrocarbon. However the effect of Pd-ceria interactions on the physicochemical properties of Pd and the redox properties of Ce is not elucidated yet. In order to know exactly about the metal-ceria interactions, the model study are expecting to give a better environment, resulting in the wide use of the surface science tools. The substrate was Si(100) wafer, on which Ta metal was sputtered as a thickness of 100nm. The CeO2 thin film of 30nm was deposited by using the magnetron sputtering. Spin coating and magnetron sputtering methods were used to make the Pd thin film layer. The prepared sample was investigated by in-situ XPS, AES, SEM and AFM analysis.

• Journal of Power System Engineering
• /
• v.7 no.3
• /
• pp.12-17
• /
• 2003

The purpose of this study is to observe the purification characteristics of NOx, CO and HC in various catalysts and excess air ratio conditions. For this purpose, we installed various catalysts on the back stream of the coaxial diffusion burner with swirler. As the result, in the case of NOx, Pt-Rh catalyst shows very high value that is more than 90%-conversion efficiency without the relation with the excess air ratio. After excess air ratio of ${\alpha}=1.14$, it shows that the conversion efficiencies were more than 80% in the every Pt catalyst in the view of conversion of every exhaust with changing of the excess air ratio.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.14 no.1
• /
• pp.8-16
• /
• 2006

The research was conducted to characterize of Rh-Pd-Pt TWC with a double-layer washcoat for gasoline vehicle. The physical characteristics on surface of catalyst were inspected by BET, SEM and TEM. The characteristics of catalytic reaction were examined by the TPD/TPR and CO-pulse chemisorption. The catalyst $6Hx(0.35\times11\times3)$ showed superior conversion performance after hydrothermal aging process, which was due to small difference of the surface area between. the fresh and the aged catalyst. The CO-chemisorption and surface area were superior in the 600 cpsi catalyst than other catalysts, this catalyst also shown the higher conversion efficiency of the exhaust emissions. From the TPR test, the conversion performance of the aged catalyst was decreased by the agglomeration and sintering of the PM and metal oxides. From the TPD result, it was found that the NO chemisorption was happed on the bottom-layer washcoat with Pd, and the NO chemisorption was re-happened on the upper-layer washcoat with Pt and Rh in the desorption process.