• 한국재료학회지
• /
• 제30권4호
• /
• pp.169-175
• /
• 2020

Silicon nitride thin films are deposited by RF (13.57 MHz) magnetron sputtering process using a Si (99.999 %) target and with different ratios of Ar/N₂ sputtering gas mixture. Corning G type glass is used as substrate. The vacuum atmosphere, RF source power, deposit time and temperature of substrate of the sputtering process are maintained consistently at 2 ~ 3 × 10^-3 torr, 30 sccm, 100 watt, 20 min. and room temperature, respectively. Cross sectional views and surface morphology of the deposited thin films are observed by field emission scanning electron microscope, atomic force microscope and X-ray photoelectron spectroscopy. The hardness values are determined by nano-indentation measurement. The thickness of the deposited films is approximately within the range of 88 nm ~ 200 nm. As the amount of N₂ gas in the Ar:N₂ gas mixture increases, the thickness of the films decreases. AFM observation reveals that film deposited at high Ar:N₂ gas ratio and large amount of N₂ gas has a very irregular surface morphology, even though it has a low RMS value. The hardness value of the deposited films made with ratio of Ar:N₂=9:1 display the highest value. The XPS spectrum indicates that the deposited film is assigned to non-stoichiometric silicon nitride and the transmittance of the glass with deposited SiO₂-Si_xN_y thin film is satisfactory at 97 %.

• 한국전기전자재료학회논문지
• /
• 제21권1호
• /
• pp.1-4
• /
• 2008

The electrical characteristics of polycrystalline silicon (poly-Si) thin film transistor (TFT) crystallized by excimer laser annealing (ELA) method were evaluated, The polycrystalline silicon thin-film transistor (poly-Si TFT) has higher electric field-effect-mobility and larger drivability than the amorphous silicon TFT. However, to poly-Si TFT's using conventional processes, the temperature must be very high. For this reason, an amorphous silicon film on a buried oxide was crystallized by annealing with a KrF excimer laser (248 nm)to fabricate a poly-Si film at low temperature. Then, High permittivity $HfO_2$ of 20 nm as the gate-insulator was deposited by atomic layer deposition (ALD) to low temperature process. In addition, the solid phase crystallization (SPC) was compared to the ELA method as a crystallization technique of amorphous-silicon film. As a result, the crystallinity and surface roughness of poly-Si crystallized by ELA method was superior to the SPC method. Also, we obtained excellent device characteristics from the Poly-Si TFT fabricated by the ELA crystallization method.

• 한국전기전자재료학회논문지
• /
• 제24권7호
• /
• pp.525-531
• /
• 2011

In this paper, experimental analyses have been performed to compare the electrical characteristics of n channel LT(low temperature) and HT(high temperature) poly-Si TFTs(polycrystalline silicon thin film transistors) on quartz substrate according to activated step annealing. The size of the particles step annealed at low temperature are bigger than high temperature poly-Si TFTs and measurements show that the electric characteristics those are transconductance, threshold voltage, electric effective mobility, on and off current of step annealed at LT poly-Si TFTs are high more than HT poly-Si TFT's. Especially we can estimated the defect in the activated grade poly crystalline silicon and the grain boundary of LT poly-Si TFT have more high than HT poly-Si TFT's due to high off electric current. Even though the size of particles of step annealed at low temperature, the electrical characteristics of LT poly-Si TFTs were investigated deterioration phenomena that is decrease on/off current ratio depend on high off current due to defects in active silicon layer.

• 대한전자공학회:학술대회논문집
• /
• 대한전자공학회 2003년도 하계종합학술대회 논문집 II
• /
• pp.727-730
• /
• 2003

Thin tin oxide film with nano-size particle was prepared on silicon substrate by hydrothermal synthetic method and successive sol-gel spin coating method. The fabrication method of tin oxide film with ultrafine nano-size crystalline structure was tried to be applied to fabrication of micro gas sensor array on silicon substrate. The tin oxide film on silicon substrate was well patterned by chemical etching upto 5${\mu}{\textrm}{m}$width and showed very uniform flatness. The tin oxide film preparation method and patterning method were successfully applied to newly proposed 2-dimensional micro sensor fabrication.

• 한국전기전자재료학회논문지
• /
• 제29권8호
• /
• pp.505-509
• /
• 2016

We have investigated the characteristics of amorphous silicon (a-Si) thin-film solar cell by inserting barrier layer. The conversion efficiency of a-Si thin-film solar cells on graphite substrate shows nearly zero because of the surface roughness of the graphite substrate. To enhance the performance of solar cells, the surface morphology of the back side were modified by changing the barrier layer on graphite. The surface roughness of graphite substrate with the barrier layer grown by plasma enhanced chemical vapor deposition (PECVD) reduced from ~2 um to ~75 nm. In this study, the combination of the barrier layer on graphite substrate is important to increase solar cell efficiency. We achieved ~ 7.8% cell efficiency for an a-Si thin-film solar cell on graphite substrate with SiNx/SiOx stack barrier layer.

• 대한전기학회논문지:전기물성ㆍ응용부문C
• /
• 제50권2호
• /
• pp.49-56
• /
• 2001

Diamond thin films have been deposited on the silicon substrate by inductively coupled radio frequency plasma enhanced chemical vapor deposition system. The morphological features of thin films depending on methane concentration and deposition time have been studied by scanning electron microscopy and Raman spectroscopy. The diamond particles deposited uniformly on silicon substrate($10{\times}10[mm^2]$) at the pressure of 1[torr], a methane concentration of 1[%], a hydrogen flow rate of 60[sccm], a substrate temperature of $840\{sim}870[^{\circ}C]$, an input power of 1[kw], and a deposition time of 1[hour]. With increasing deposition time, the diamond particles grew, and than about 3 hours have passed, the graphitic phase carbon thin film with "cauliflower-like" morphology deposited on the diamond thin films.

• JSTS:Journal of Semiconductor Technology and Science
• /
• 제5권3호
• /
• pp.182-186
• /
• 2005

In this work, thermal evaporation system was employed to deposit thin films of SiC on glass substrates in order to determine the parameters of them. Measurements included transmission, absorption, Seebak effect, resistivity and conductivity, absorption coefficient, type of energy band-gap, extinction coefficient as functions of photon energy and the effect of increasing film thickness on transmittance. Results explained that SiC thin film is an n-type semiconductor of indirect energy band-gap of ${\sim}3eV$, cut-off wavelength of 448nm, absorption coefficient of $3.4395{\times}10^{4}cm^{-1}$ and extinction coefficient of 0.154. The experimental measured values are in good agreement with the typical values of SiC thin films prepared by other advanced deposition techniques.

• 한국신재생에너지학회:학술대회논문집
• /
• 한국신재생에너지학회 2010년도 추계학술대회 초록집
• /
• pp.56.1-56.1
• /
• 2010

결정질 실리콘 태양전지의 표면 ARC(Anti-reflection Coating)layer는 반사도를 줄여 광 흡수율을 증가시키고, passivation 효과를 통하여 표면 재결합을 감소 시켜 태양전지의 효율을 높이는 중요한 역할을 한다. Silicon nitride 박막은 외부 stress 요인에 대해 안정성을 담보할 수 있어야한다. 따라서, 본 연구에서는 굴절률 가변에 따른 silicon nitride 박막을 PECVD를 이용하여 증착하고, 항온/항습 stability test를 통해 박막의 안정성을 확인하였다. Silicon nitride 증착을 위해 PECVD를 이용하였고, 공정압력 0.8Torr, 증착온도 $450^{\circ}C$, 증착파워 300W에서 실험을 진행하였다 박막의 굴절률은 1.9~2.3의 범위로 가변하였다. 항온/항습에 대한 신뢰성을 test 하기 위하여 5시간동안의 test를 1cycle로 하여 20회 동안 실험을 실시하였다. 증착된 silicon nitride 박막의 lifetime은 firing 이후 57.8us로 가장 높았으며, 항온/항습 test 이후에도 유사한 경향을 확인 할 수 있었다. 또한, 100h 동안의 항온/항습 test 결과 silicon nitride 박막의 lifetme 감소는 8.5%에 불과했다. 본 연구를 통하여 온도와 습도의 변화에 따른 결정질 실리콘 태양전지의 SiNx 박막의 증착 공정 조건에 대한 신뢰성을 확인 할 수 있었다.

• 한국신재생에너지학회:학술대회논문집
• /
• 한국신재생에너지학회 2010년도 추계학술대회 초록집
• /
• pp.46.1-46.1
• /
• 2010

Surface passivation of crystalline silicon(c-Si) surface with a-Si:H thin films has been investigated by using quasi-steady-state photo conductance(QSSPC) measurements. Analyzing the influence of a-Si:H film thickness, process gas ratio, deposition temperature and post annealing temperature on the passivation properties of c-Si, we optimized the passivation conditions at the substrate temperature of $200-250^{\circ}C$. Best surface passivation has been obtained by post-deposition annealing of a-Si:H film layer. Post annealing around the deposition temperature was sufficient to improve the surface passivation for silicon substrates. We obtained effective carrier lifetimes above 5.5 ms on average.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2009년도 추계학술대회 논문집
• /
• pp.111-111
• /
• 2009

In this work, we discuss simulation of surface acoustic wave device using Comsol Multiphysics. The structure SAW device based on piezoelectric thin film aluminum-nitride (AlN) on silicon was simulated. Some parameters of SAW device such as surface velocity, displacement of piezoelectric thin film were evaluated by software. Many modes and shapes of wave are also discussed in this paper. For evaluation physical parameters of AlN piezoelectric layer, the SAW resonator was modeled and simulation results were also compared with experiment results. we simulated arid evaluated the surface Rayleigh wave of AlN thin film on silicon substrate. Results simulation and experiment showed the surface velocity of AlN thin film was about 5200 m/s and shape of surface wave was also displayed. This paper has also proposed as method to study SAW characteristic of piezoelectric thin film and found out measurement values accurately of film such as stiffness matrix, piezoelectric matrix. These values are very important in calculation and design SAW device or MEMS device based on AlN piezoelectric layer.