• Korean Journal of Optics and Photonics
• /
• v.14 no.3
• /
• pp.331-337
• /
• 2003

This paper represents 50 ㎓ narrow band pass filters for fiber optical communication fabricated by dual ion beam sputtering method. We have analyzed the characteristics of the TA$_2$ $O_{5}$ and $SiO_2$ single layers in order to optimize the process conditions for the 50 ㎓ narrow band pass filters, and controlled the film thickness uniformity to less than 0.1 nm deviation by dual peak spike filter pre-deposition. We designed and fabricated 50 ㎓ narrow band pass filters that consist of 216 layers including 4 cavities based on quarter wave optical thickness. Class substrates with high thermal expansion coefficients were used to reduce the film stress. Anti-reflection coating at the rear side of the substrate was also needed to reduce the optical thickness errors of the Optical Monitoring System caused by multiple beam interference between the front side and the rear side of substrate. The optical characteristics of this 50 ㎓ narrow band pass filters are insertion loss of 0.40 ㏈, pass band ripple of 0.20 ㏈, and pass bandwidth at -0.5 ㏈ of 0.20 nm. and isolation bandwidth at -25 ㏈ of 0.6 nm, which satisfy specifications of dense WDM system in fiber optical communications.tions.

• Journal of Korean Ophthalmic Optics Society
• /
• v.15 no.4
• /
• pp.361-366
• /
• 2010

Purpose: HCD ion plating apparatus by hollow cathod discharge method was fabricated and TiN films were deposited on stainless steel by this apparatus with increasing in $N_2$ gas flow and the fine color changes of TiN films were analyzed. Methods: The spectroradiometer and spectrophotometer were used to observe optically the fine color changes of TiN thin films, and XPS was used to analyze the compositions of TiN thin films with increasing in $N_2$ gas flow. Results: The color coordinate of TiN thin film with $N_2$ 120 sccm gas flow showed (0.382, 0.372) which had the mixed colors of gold and silver, and the color coordinate changed to the increasing value of (x,y) with increasing in $N_2$ gas flow which indicated the deep gold color. It was found that the slopes of the reflectances at 550nm were increased with increasing in $N_2$ gas flow. And from the Ti scans using XPS, it was found that the peak heights of 455 eV derived from TiN composition were increased with increasing in $N_2$ gas flow, while the peak heights of 459 eV from $TiO_2$ composition were decreased. Conclusions: The results obtained above were that the color of TiN film with 120 sccm $N_2$ gas flow had been observed from the mixed color of silver and gold due to TiC, $N_2$, TiN on the surface and TiN, $N_2$ inside film, and the color of TiN films changed a deep gold color with increasing in $N_2$ gas flow due to increasing TiN composition.

• Corrosion Science and Technology
• /
• v.4 no.4
• /
• pp.140-146
• /
• 2005

Fossil fired power plant produces the electric energy by using a thermal energy by the combustion of fossil fuels as like oil, gas and coal. The exhausted flue gas by the combustion of oil etc. contains usually many contaminated species, and especially sulfur-content has been controlled strictly and then FGD (Flue Gas Desulfurization) facility should be installed in every fossil fired power plant. To minimize the content of contaminations in final exhaust gas, high corrosive environment including sulfuric acid (it was formed during the process which $SO_2$ gas combined with $Mg(OH)_2$ solution) can be formed in cooling zone of FGD facility and severe corrosion damage is reported in this zone. These conditions are formed when duct materials are immersed in fluid that flows on the duct floors or when exhausted gas is condensed into thin layered medium and contacts with materials of the duct walls and roofs. These environments make troublesome corrosion and air pollution problems that are occurred from the leakage of those ducts. The frequent shut down and repairing works of the FGD systems also demand costs and low efficiencies of those facilities. In general, high corrosion resistant materials have been used to solve this problem. However, corrosion problems have severely occurred in a cooling zone even though high corrosion resistant materials were used. In this work, a new technology has been proposed to solve the corrosion problem in the cooling zone of FGD facility. This electrochemical protection system contains cathodic protection method and protection by coating film, and remote monitoring-control system.

• Journal of the Korean Institute of Telematics and Electronics D
• /
• v.35D no.11
• /
• pp.55-61
• /
• 1998

Organic light emitting devices from a single layer thin film with a hole transport polymer, poly(N-vinylcarbazole) (PVK) doped with 2-(4-bi phenyl)-5-(4-t-butyl-phenyl) -1,3,4-oxadiazole (Bu-PBD) as electron transporting molecules and Coumurine 6(C6), 1,1,4,4-tetraphenyl-1,3-butadiene (TPB), Rhodamine B as a emitter dye were fabricated. The sing1e layer structure and the use of soluble materials simplify the fabrication of devices by spin coating technique. The active layer consists of one polymer layer that is simply sandwiched between two electrodes, indium-tin oxide (ITO), and aluminum. In this structure, electron and hole inject from the electrodes to the PVK : Bu-PBD active layer. Respectively, Blue, green and orange colored emission spectrum by the use of TPB, C6, Rhodamine B dye emitted at 481nm, 500nm and 585nm were achieved during applied voltages. PVK materials can be useful as the host polymer to be molecularly doped with other organic dyes of the different luminescence colors. And EL color can be tuned to the full visible wavelength.

• Transactions of the Korean hydrogen and new energy society
• /
• v.21 no.4
• /
• pp.271-277
• /
• 2010

$(Ba(Zr_{0.85}Y_{0.15})O_{3-\delta})$ oxide, showing high protonic conductivity at high temperatures and good chemical stability with $CO_2$ are referred to as hydrogen separation membrane. For high efficiency of hydrogen separation ($H_2$ flux and selectivity) and low fabrication cost, ultimate thin and dense BZY-Ni layer has to be coated on a porous substrate such as $ZrO_2$. Aerosol depostion (AD) process is a novel technique to grow ceramic film with high density and nano-crystal structure at room-temperature, and may be applicable to the fabrication process of AD integration ceramic layer effectively. XRD, SEM, X-ray mapping measurements were conducted in order to analyze the characteristics of BZY-Ni membrane fabricated by AD process. it is observed that it is homogeneous distribution for BZY-Ni. The result of $H_2$ permeation rate suggests that BZY-Ni composite is higher than BZY.

• Carbon letters
• /
• v.12 no.4
• /
• pp.207-217
• /
• 2011

We discuss the influence of few-walled carbon nanotubes (FWCNTs) treated with nitric acid and/or sulfuric acid on field emission characteristics. FWCNTs/tetraethyl orthosilicate (TEOS) thin film field emitters were fabricated by a spray method using FWCNTs/TEOS sol one-component solution onto indium tin oxide (ITO) glass. After thermal curing, they were found tightly adhered to the ITO glass, and after an activation process by a taping method, numerous FWCNTs were aligned preferentially in the vertical direction. Pristine FWCNT/TEOS-based field emitters revealed higher current density, lower turn-on field, and a higher field enhancement factor than the oxidized FWCNTs-based field emitters. However, the unstable dispersion of pristine FWCNT in TEOS/N,N-dimethylformamide solution was not applicable to the field emitter fabrication using a spray method. Although the field emitter of nitric acid-treated FWCNT showed slightly lower field emission characteristics, this could be improved by the introduction of metal nanoparticles or resistive layer coating. Thus, we can conclude that our spray method using nitric acid-treated FWCNT could be useful for fabricating a field emitter and offers several advantages compared to previously reported techniques such as chemical vapor deposition and screen printing.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2014.02a
• /
• pp.347.1-347.1
• /
• 2014

최근, 박막 트랜지스터는 빠른 동작 속도, 낮은 공정비용 그리고 저온공정 등의 특성을 필요로 하고 있다. 그 중 indium-zinc oxide (InZnO)는 높은 전기적 특성, 높은 광 투과도 그리고 우수한 안정성 때문에 기존의 반도체를 대체할 수 있을 것으로 기대된다. InZnO의 경우 indium과 zinc의 조성비에 따라 특성 변화의 차이가 크기 때문에 다양한 조성비에 대한 연구가 보고되고 있는데, 기존의 InZnO 박막을 증착하는 방법의 경우에 조성비의 변화 과정에 많은 공정상의 어려움이 있다. 이 같은 문제점 때문에 조성비의 변화를 용이하게 할 수 있는 용액공정을 이용한 연구가 진행되고 있다. 또한 용액공정은 높은 균일성, 공정 시간 및 비용 감소 그리고 대면적화가 가능한 장점을 가지고 있다. 한편, 용액공정을 기반으로 한 InZnO의 경우에 용액 상태에서 고체 상태의 순수한 금속 산화물 상태로 바꾸기 위해 post-treatment 가 필요하다. 일반적으로 furnace 열처리 방법을 사용하는데, 이 경우 낮은 열효율 및 고비용 등의 문제점을 가지고 있다. 특히 glass 또는 flexible 기판의 경우 열처리 온도에 대한 제약이 있다. 이러한 문제를 해결하기 위한 방법으로 최근에 microwave irradiation를 이용한 저온 post-treatment 방법이 보고되고 있다. Microwave irradiation는 짧은 공정시간 및 열 균일성 등의 장점이 있다. 따라서 본 연구에서는 다양한 indium과 zinc의 조성비를 갖는 용액을 제작한 후 spin coating을 이용하여 증착한 InZnO 기반의 박막 트랜지스터를 제작하였다. Furnace와 microwave 방식으로 post-treatment 하여 비교 평가한 결과 microwave irradiation 한 경우 furnace 열처리 한 경우 보다 더 안정된 동작 전압을 가지는 것으로 나타났다. 따라서 저온공정이 가능한 microwave irradiation 방법으로 post-treatment 한다면 차세대 산화물 반도체로서의 적용이 가능할 것으로 기대된다.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2014.02a
• /
• pp.291.2-291.2
• /
• 2014

ZnO 박막(thin film)은 씨앗층(seed layer)의 종류, 두께, 증착 조건 등에 따라 그 특성이 달라지는 것으로 알려져 있다. 이에 본 연구에서는 씨앗층의 종류에 따른 박막의 특성변화를 알아 보기 위해, 졸겔 스핀코팅(sol-gel spin-coating) 방법으로 4가지 종류의 씨앗층(Al-ZnO, Co-ZnO, Cu-ZnO, In-ZnO) 위에 ZnO 박막을 성장 한 후 성장된 ZnO 박막의 구조적, 광학적 특성을 field emission scanning electron microscope, X-ray diffractometer, UV-visible spectrometer를 통해 조사하였다. ZnO 박막의 표면구조는 씨앗층의 종류에 따라 변하였으며, 씨앗층 위에 성장된 ZnO 박막들의 c축 배향성과 결정성이 씨앗층 없이 성장된 ZnO 박막보다 더 우수하게 나타났다. 투과도(transmittance) 측정값을 통해 계산된 광학적 밴드갭(optical bandgap)과 Urbach 에너지는 씨앗층에 따라 다른 값을 나타내었다. 광학적 밴드갭은 Al-ZnO 씨앗층 위에 성장된 ZnO 박막에서 가장 크게 나타났으며, Urbach 에너지는 Co-ZnO 씨앗층 위에 성장된 ZnO 박막에서 가장 낮았다. 따라서 ZnO박막 성장 시 용도에 맞게 적절한 씨앗층을 사용하는 것은 소자의 성능을 향상시키는데 매우 중요한 역할을 할 수 있다.

• Korean Journal of Materials Research
• /
• v.17 no.3
• /
• pp.147-151
• /
• 2007

Cu-free multi-component sol, of which final oxide composition becomes $Bi_{1.9}Pb{0.35}SrCaO,\;Bi_{1.8}Pb_{0.2}SrCaO\;and\;Bi_{1.5}SrCaO$, respectively, was prepared through sol-gel route and coated on a bare Cu substrate. Starting materials were metal-alkoxides as follows.; [$Bi(OC_{2}H_{5})_{3}\;Pb(O^{1}C_{3}H_{7})_{2},\;Sr(O^{i}C_{3}H_{7})_{2},\;Ca(OC_{2}H_{5})_{2}$] as a reagent grade. Transparent light yellowish sol was obtained in the case of $Bi_{1.9}Pb_{0.35}SrCaO\;and\;Bi_{1.8}Pb_{0.2}SrCaO$ composition and $Bi_{1.5}SrCaO$ composition's sol was light greenish. Each sol was repeatedly dip-coated on Cu substrate four times and pre-heated at $400^{\circ}C$ and finally heat-treated in the range of $740{\sim}900^{\circ}C$. In the results, crystalline phases confirmed by XRD were (2201) orthorhombic and monoclinic phases. However, only $Bi_{1.9}Pb_{0.35}SrCaO_{x}$ composition showed pseudo-superconductive behavior after heat-treatment at $900^{\circ}C$ for 12 seconds and then onset temperature was 77 K, even though it did not exhibit zero resistance below Tc.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.08a
• /
• pp.281-281
• /
• 2010

Very low refractive index (<1.4) materials have been proved to be the key factor improving the performance of various optical components, such as reflectors, filters, photonic crystals, LEDs, and solar cell. Highly porous SiO2 are logically designed for ultralow refractive index materials because of the direct relation between porosity and index of refraction. Among them, ordered macroporous SiO2 is of potential material since their theoretically low refractive index ~1.10. However, in the conventional synthesis of ordered macroporous SiO2, the time required for the crystallization of organic nanoparticles, such as polystyrene (PS), from colloidal solution into well ordered template is typical long (several days for 1 cm substrate) due to the low interaction between particles and particle - substrate. In this study, polystyrene - polyacrylic acid (PS-AA) nanoparticles synthesized by miniemulsion polymerization method have hydrophilic polyacrylic acid tails on the surface of particles which increase the interaction between particle and with substrate giving rise to the formation of PS-AA film by simply spin - coating method. Less ordered with controlled thickness films of PS-AA on silicon wafer were successfully fabricated by changing the spinning speed or concentration of colloidal solution, as confirmed by FE-SEM. Based on these template films, a series of macroporous SiO2 films whose thicknesses varied from 300nm to ~1000nm were fabricated either by conventional sol - gel infiltration or gas phase deposition followed by thermal removal of organic template. Formations of SiO2 films consist of interconnected air balls with size ~100 nm were confirmed by FE-SEM and TEM. These highly porous SiO2 show very low refractive indices (<1.18) over a wide range of wavelength (from 200 to 1000nm) as shown by SE measurement. Refraction indices of SiO2 films at 633nm reported here are of ~1.10 which, to our best knowledge, are among the lowest values having been announced.