• 한국초전도ㆍ저온공학회논문지
• /
• 제25권4호
• /
• pp.19-23
• /
• 2023

The Second-generation high-temperature superconducting (HTS) Rare-Earth Barium Copper Oxide (REBCO) wire is a composite laminate having a multi-layer structure (8 or more layers). HTS wires will undergo multiple loads including the bending-tension loads during winding, high current density, and high magnetic fields. In particular, the wires are subjected to bending stress and magnetic field stress because HTS wires are wound around a circular bobbin when making a high-field magnetic. Each of the different laminated wires inevitably exhibits damage and fracture behavior of wire due to stress deformation, mismatches in thermal, physical, electrical, and magnetic properties. Therefore, when manufacturing high-field magnets and other applications, it is necessary to calculate the stress-strain experienced by high-temperature superconducting wire to present stable operating conditions in the product's use environment. In this study, the finite element model (FEM) was used to simulate the strain-stress characteristics of the HTS wire under high current density and magnetic field, and bending loads. In addition, the result of obtaining the neutral axis of the wire and the simulation result was compared with the theoretical calculation value and reviewed. As a result of the simulation using COMSOL Multiphysics, when a current of 100 A was applied to the wire, the current value showed the difference of 10^-9. The stress received by the wire was 501.9 MPa, which showed a theoretically calculated value of 500 MPa and difference of 0.38% between simulation and theoretical method. In addition, the displacement resulted is 30.0012 ㎛, which is very similar to the theoretically calculated value of 30 ㎛. Later, the amount of bending stress by the circular mandrel was received for each layer and the difference with the theoretically obtained the neutral axis result was compared and reviewed. This result will be used as basic data for manufacturing high-field magnets because it can be expanded and analyzed even in the case of wire with magnetic flux pinning.

• 한국주조공학회지
• /
• 제38권5호
• /
• pp.103-110
• /
• 2018

코발트기 주조용 초내열합금 X45를 이용하여 다양한 형태의 열처리에 따른 미세조직과 기계적 특성의 변화에 대하여 고찰한 결과를 요약하면 다음과 같다. 1) 합금의 응고 시 결정립계와 수지상간 경계를 따라 Cr이 다량 함유된 조대한 $M_{23}C_6$ 탄화물과 W과 Co의 함량이 높은 $M_6C$ 탄화물이 형성되어 있었고, $1274^{\circ}C$에서 용체화 처리하면 대부분의 탄화물이 용해되었다. $1150^{\circ}C$에서의 용체화 처리 동안 일부 결정립계 탄화물이 용해되지만 공정탄화물 근처에서 새로운 탄화물의 석출이 일어났다. $927^{\circ}C$와 $982^{\circ}C$에서 시효처리만 했을 때 용체화 처리 후 시효처리 한 시편 보다 공정 탄화물 근처에서 석출되는 탄화물의 양이 많았고, 크기가 작았다. 2) $1150^{\circ}C$에서 용체화 처리한 후 시효처리 하면 경도의 증가가 뚜렷하지 않으며, $927^{\circ}C$와 $982^{\circ}C$에서 시효처리만 했을 때 다량의 매우 미세한 탄화물의 석출에 의하여 경도의 증가 폭이 더 컸다. 상온 항복강도는 $927^{\circ}C$에서 시효처리 했을 때 가장 컸지만 인장강도와 연신율은 $982^{\circ}C$에서 12시간 시효처리 했을 때 가장 컸다. 고온 크리프 특성은 $982^{\circ}C$에서 12시간 시효처리 했을 때 가장 우수하였다. 3) 장시간 고온 노출 되는 동안 탄화물의 석출과 성장이 일어났고, 8000시간 고온에서 노출시킨 시편에서는 수지상 중심부에도 탄화물이 석출되어 크리프 파단 수명이 증가하였다.