• Composites Research
• /
• v.26 no.1
• /
• pp.60-65
• /
• 2013

A nanolaminate consisting of alternate layers of aluminium oxide ($Al_2O_3$) (5 nm) and zirconium oxide ($ZrO_2$) (20 nm) was deposited at an optimized oxygen partial pressure of $3{\times}10^{-2}$ mbar by pulsed laser deposition. The nanolaminate film was analysed using high temperature X-ray diffraction (HTXRD) to study phase transition and thermal expansion behaviour. The surface morphology was investigated using field emission scanning electron microscopy (FE-SEM). High temperature X-ray diffraction indicated the crystallization temperature of tetragonal zirconia in the $Al_2O_3/ZrO_2$ multilayer-film was 873 K. The mean linear thermal expansion coefficient of tetragonal $ZrO_2$ was $4.7{\times}10^{-6}\;K^{-1}$ along a axis, while it was $13.68{\times}10^{-6}\;K{-1}$ along c axis in the temperature range 873-1373 K. The alumina was in amorphous nature. The FESEM studies showed the formation of uniform crystallites of zirconia with dense surface.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 2001.06a
• /
• pp.346-353
• /
• 2001

Zirconia powder containing 3 mol% yttria(3Y-PSZ) with and with out Fe$_2$O$_3$ addition was coated on tile cast iron substrate by plasma spraying method. The erosion experiments were performed at temperatures from $25^{\circ}C$ to $600^{\circ}C$. A gas blast type erosion tester was used to examine erosion behavior of the specimens. The results of 3Y-PSZ coatings showed that tile erosion rate had maximum value at 40$0^{\circ}C$. It coincided with tile results of phase transformation tetragonal phase to monoclinic phase caused by low temperature thermal degradation. The tensile stress relaxation and the micro-hardness improvement significantly influenced on the erosion rate at $600^{\circ}C$. In the case of Fe$_2$O$_3$ added 3Y-PSZ coatings, the erosion rate of tested at $25^{\circ}C$ showed maximum value at 5.0 mol% Fe$_2$O$_3$ added coating. This tendency is caused by the improvement of mechanical properties and the tensile residual stress. The erosion rate at 200'c and 400'L showed significantly decrease by Fe203 addition. This decrease is believed to be the stabilization of the tetragonal phase and the increase of micro-hardness.

• Proceedings of the Korea Association of Crystal Growth Conference
• /
• 2000.06a
• /
• pp.143-150
• /
• 2000

Wet-chemical process using ammonia to precipitate aluminum ion dissolved in a zirconia sol solution is examined. Formation of crystalline bayerite is unfavorable for fine dispersion of zirconia nanoparticles in alumina matrix after heat treatment. To avoid the bayerite formation, it was preferred to make a precipitation with a diluted ammonia or with an ammonia gas flow at high temperature. By optimizing the precipitation process and the calcination temperature, we successfully prepared the uniform microstructure in which tetragonal zirconia particles of ∼30nm is finely dispersed within the alumina grains.

• Journal of Korean Dental Science
• /
• v.10 no.2
• /
• pp.74-81
• /
• 2017

This report describes two cases of complete arch implant-supported restorations. The first patient had seven dental implants in each arch with monolithic zirconia frameworks. At four weeks' follow-up, the one-piece maxillary framework was fractured, which was re-designed and re-fabricated using laser-sintered cobalt-chrome alloy. The second patient had four implants in the mandible only. A mandibular monolithic zirconia framework and a maxillary conventional complete denture were fabricated and delivered. At five years' follow-up, the patient reported no significant discomfort. Careful consideration and monitoring of the status of antagonistic arches and stress distribution on zirconia frameworks were suggested for complete arch implant-supported fixed restorations.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.37 no.4
• /
• pp.177-185
• /
• 2021

Clinical applications of translucent zirconia as well as traditional zirconia (3 mol% yttria stabilized tetragonal zirconia polycrystal, 3Y-TZP) are increasing. For this reason, studies on factors affecting the optical properties of dental zirconia have been continuously reported. The optical effect of dental zirconia may vary depending on the yttria content, the thickness of the prosthesis, the sintering process, polishing, glazing and cementation in laboratory and clinical procedures. Increasing the yttria concentration can reduce the masking effect. Translucency decreases as the thickness of the restoration increases, but the required thickness may vary depending on the properties of the zirconia block. The high-speed sintering method can shorten the manufacturing time, but in some cases, the translucency of the prosthesis may decrease. In addition, the optical properties can be affected by the surface roughness of zirconia and the polishing process. The use of an appropriate colored cement can help with the masking effect of zirconia and can be useful for color matching for more esthetic results.

• Journal of Powder Materials
• /
• v.14 no.5
• /
• pp.309-314
• /
• 2007

Zirconia powders with nano size pores and high specific surface areas were synthesized via aqueous precipitation and hydrothermal synthetic method using $ZrOCl_28H_2O$ and $NH_4OH$ under pH=11 and ambient condition. By this reaction. zirconia hydrate $(ZrO_x(OH)_{4-2x})$ was primarily synthesized and the obtained zirconia hydrate was heat treated hydrothermally using an autoclave at various temperatures under pH=11. X-ray diffraction, Scanning electron microscopy, Energy dispersive X-ray spectroscopy, FT-IR, Raman, Particle size analysis, DTA-TG, and BET techniques were used for the characterization of the powder. The synthesized zirconia showed an amorphous phase, however, the phase was transformed to the crystalline state during the hydrothermal process. The observed crystalline phase above $160^{\circ}C$ was a mixed phase of monoclinic and tetragonal zirconia. By the BET analysis, it was found that the specific surface area was ranged in $126{\sim}276m^2/g$ and the zirconia had the cylindrical shaped pores with average diameter of $2{\sim}7nm$.

• Korean Journal of Materials Research
• /
• v.24 no.12
• /
• pp.677-681
• /
• 2014

To increase the mechanical property of zirconia, we have investigated the phase change and the resulting hardness of zirconia ceramics by hydroxyapatite (HA) powder bed sintering. It was observed using X-ray diffraction that the cubic zirconia phase, which has a higher hardness value than that of the tetragonal phase, was obtained at the surface of 3 mol% $Y_2O_3$ doped tetragonal zirconia polycrystal (3Y-TZP) ceramics during the sintering process; in our experimental conditions, the phase change at the surface increased as the sintering time increased. We believe that the observed crystalline phase change originated from the decomposition of HA and the diffusion of CaO, as follows. CaO, which was derived from the decomposition of HA at high temperature ($1400^{\circ}C$), diffused into the surface of 3Y-TZP and acted as a stabilizer. As a result, the Vickers hardness value of the treated specimens was higher than that of the non-treated specimen due to the formation of the cubic phase on the surface of 3Y-TZP.

• Journal of the Korean Ceramic Society
• /
• v.33 no.6
• /
• pp.637-644
• /
• 1996

Phase stability and isothermal phase transformation during gaging at 25$0^{\circ}C$ were investigated in yttria stabilized zirconia powders prepared from hydrolysis of zirconium isopropoxide. The stability of tetragonal phase at room temperature in zirconia powder was decreased with calcination temperature but increased with the addition of yttria content. During aging at 25$0^{\circ}C$ in humid atmosphere isothermal phase transformation occurred in tetragonal zirconia powder stabilized by constraint effect not by alloying effect and grain size effect. Many twins and microcrackings were found in transformed monomlinic zirconia particles.

• The Journal of Advanced Prosthodontics
• /
• v.10 no.2
• /
• pp.147-154
• /
• 2018

PURPOSE. This study was performed to evaluate the osteogenic potential of 3mol% yttria-stabilized tetragonal zirconia polycrystals (3Y-TZP) and niobium oxide containing Y-TZPs with specific ratios, new (Y,Nb)-TZPs, namely YN4533 and YN4533/Al20 discs. MATERIALS AND METHODS. 3Y-TZP, YN4533 and YN4533/Al20 discs (15 mm diameter and 1 mm thickness) were prepared and their average surface roughness ($R_a$) and surface topography were analyzed using 3-D confocal laser microscope (CLSM) and scanning electron microscope (SEM). Mouse pre-osteoblast MC3T3-E1 cells were seeded onto all zirconia discs and evaluated with regard to cell attachment and morphology by (CLSM), cell proliferation by PicoGreen assay, and cell differentiation by Reverse-Transcription PCR and Quantitative Real-Time PCR, and alkaline phosphatase (Alp) staining. RESULTS. The cellular morphology of MC3T3-E1 pre-osteoblasts was more stretched on a smooth surface than on a rough surface, regardless of the material. Cellular proliferation was higher on smooth surfaces, but there were no significant differences between 3Y-TZP, YN4533, and YN4533/Al20. Osteoblast differentiation patterns on YN4533 and YN4533/Al20 were similar to or slightly higher than seen in 3Y-TZP. Although there were no significant differences in bone marker gene expression (alkaline phosphatase and osteocalcin), Alp staining indicated better osteoblast differentiation on YN4533 and YN4533/Al20 compared to 3Y-TZP. CONCLUSION. Based on these results, niobium oxide containing Y-TZPs have comparable osteogenic potential to 3Y-TZP and are expected to be suitable alternative ceramics dental implant materials to titanium for aesthetically important areas.

• Korean Journal of Materials Research
• /
• v.23 no.10
• /
• pp.543-549
• /
• 2013

The purpose of this paper was to investigate the effect of a high-energy milling (HEM) process on the particle morphology and the correlation between a thermal treatment and tetragonal/monoclinic nanostructured zirconia powders obtained by a precipitation process. To eliminate chloride residue ions from hydrous zirconia, a modified washing method was used. It was found that the used washing method was effective in removing the chloride from the precipitated gel. In order to investigate the effect of a pre-milling process on the particle morphology of the precipitate, dried $Zr(OH)_4$ was milled using a HEM machine with distilled water. The particle size of the $Zr(OH)_4$ powder exposed to HEM reduced to 100~150 nm, whereas that of fresh $Zr(OH)_4$ powder without a pre-milling process had a large and irregular size of 100 nm~1.5 ${\mu}m$. Additionally, modified heat treatment process was proposed to achieve nano-sized zirconia having a pure monoclinic phase. It was evident that two-step calcining process was effective in perfectly eliminating the tetragonal phase, having a small average particle of ~100 nm with good uniformity compared to the sample calcined by a single-step process, showing a large average particle size of ~300 nm with an irregular particle shape and a broad particle size distribution. The modified method is considered to be a promising process for nano-sized zirconia having a fully monoclinic phase.