• Korean Journal of Materials Research
• /
• v.8 no.9
• /
• pp.807-812
• /
• 1998

Interfacial reaction and mechanical properties between Sn-Bi-X ternary alloys(X : 2Cu. 2Sb 5In) and Cu-substrate were studied. Cu/solder joints were subjected to aging treatments for up to 60days to see interfacial reaction at $100^{\circ}C$ and then were examined changes of microstructure and interfacial compound by optical microscopy, SEM and EDS. Cu/solder joints were aged to 30days and then loaded to failure at cross head speed of 0.3mm $\textrm{min}^{-1}$ to measure strength and elongation. According to the result of EDS, it is supposed that the soldered interfacial zone was composed of $\textrm{Cu}_{3}\textrm{Sn}$ and $\textrm{Cu}_{6}\textrm{Sn}_{5}$. According to the tensile test of Cu/solder joint, joint strength was decreased by aging treatment. Fractographs of Cu/Sn-Bi solder detailed the effect of aging on fracture behavior. When intermetallic was thin, the fracture occurred through the solder. But as the interfacial intermetallic is thickened, the fracture propagated along the intermetallic/solder interface.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.21 no.9
• /
• pp.414-423
• /
• 2020

Fiber-reinforced polymer (FRP) laminate sheets, which are lightweight with high strength, are commonly used to reinforce concrete structures. The bonding strength is vital in structural design. Therefore, experiments and analytical studies with differing variables (concrete compressive strength and tensile strength, the elastic modulus of concrete and FRP, thickness of concrete and FRP, width of concrete and FRP, bond length, effective bond length, fracture energy, maximum bond stress, maximum slip) have been conducted to obtain an accurate numerical model of the bond strength between an FRP sheet and concrete. Although many models have been proposed, no validated model has emerged that could be used easily in practice. Therefore, this study analyzed the parameters that influence the bond strength that were used in 23 of the proposed models (Khalifa model, Iso model, Maeda model, Chen model, etc.) and compared them to the test results of 188 specimens via the numerical results of each model. As a result, an easy-to-use practical model with a simple and high degree of expression was proposed based on the Iso model combined with the effective bond length model that was proposed by Holzenkӓmpfer.

• Journal of Conservation Science
• /
• v.25 no.2
• /
• pp.197-206
• /
• 2009

Natural preservative agents are generally made of antibiotic substances that are extracted from plants. They are used mainly to keep in an original good state food, natural cosmetic goods and medicines which are likely to get rotten. The purpose of this study is to investigate whether natural preservative agents can be applied to fabrics for the preservation of textile cultural properties. For the purpose, this researcher experimented with a certain natural preservative agent which was developed to preserve natural cosmetic goods. The study found that when treated with the foresaid natural preservative agent whose ratio to water was 1%, fabrics showed little changes in color and tensile strength, almost neutral pH, high antibiosis and anti-fungus and high resistance to Bacillus cereus that is much detrimental to silk fabrics. As a part of the study, a preliminary test on the possibility of using natural preservative agents to preserve textile cultural properties, found that when kept covered up with the 1% natural preservative agent-treated fabrics for 72 hours, excavated textile relics showed a dramatic decrease in microbial growth.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.34 no.3
• /
• pp.763-771
• /
• 2014

Recently, a huge amount of sulfur has been produced as a byproduct of petroleum refining processes in Korea. Sulfur concrete is made of modified sulfur binder instead of cement paste, which has advantages of reducing $CO_2$ emission from cement industry as well as utilizing surplus sulfur. Also, sulfur concrete is a sustainable material that can be repetitively recycled. In this study, the physical properties of sulfur concrete are experimentally investigated. From the test results, sulfur concrete showed compressive strengths higher than at least 50MPa. Also, the unit weight, modulus of elasticity and splitting tensile strength of sulfur concrete was similar to that of Portland cement concrete (PCC). The coefficient of thermal expansion of sulfur concrete was a little larger than that of Portland cement concrete and sulfur concrete with mineral filler is helpful to lower the coefficient of thermal expansion. recycled aggregate sulfur concrete resulted in a slight reduction in the compressive strength, but sulfur concrete with recycled aggregate can achieve the high strength characteristics.

• Journal of the Korean Applied Science and Technology
• /
• v.29 no.4
• /
• pp.618-625
• /
• 2012

In this study, prepared synthesis waterborne acrylic resin and water soluble milk casein resin. And than extent of casein contents in acrylic resin. We measured property of these samples by Lamb leather which is coated by acrylic-casein resins. According to measure data for solvent resistance, WAR resin and Hybrid resins had good property. Among this result knew that increase of casein constant did not influence to big change of hybrid resin property. As test of tensile strength, WAR had lowest strength($1.399kg_f/mm^2$) and WAC-3 had highest strength($1.426kg_f/mm^2$). Also we knew that best property of abrasion was WAC-3(69.774 mg.loss). In elongation case, WAR had best property(820%) in this experiment.

• The Journal of Korean Academy of Prosthodontics
• /
• v.36 no.5
• /
• pp.701-720
• /
• 1998

Research advances in dental implantology have led to the development of several different types of materials and it is anticipated that continued research will lead to advanced dental implant materials. Currently used pure titanium has relatively low hardness and strength which may limit its ability to resist functional loads as a dental implant. Ti-6Al-4V also has potential problems such as corrosion resistance. osseointegration properties and neurologic disorder due to aluminium and vanadium, known as highly toxic elements, contained in Ti-6Al-4V. Newly developed titanium based alloys(Ti-20Zr-3Nb-3Ta-0.2Pd-1In, Ti-20Zr-3Nb-3Ta-0.2Pd) which do not contain toxic metallic components were designed by the Korea Institute of Science and Technology (KIST) with alloy design techniques using Zr, Nb, Ta, Pd, and In which are known as non-toxic elements. Biocompatibility and osseointegration properties of these newly designed alloys were evaluated after implantation in rabbit femur for 3 months. The conclusions were as follows : 1. Mechanical properties of the new designed Ti based alloys(Ti-20Zr-3Nb-3Ta-0.2Pd-1In, Ti-20Zr-3Nb-3Ta-0.2Pd) demonstrated close hardness and tensile strength values to Ti-6Al-4V. 2. New desinged experimental alloys showed stable corrosion resistance similar to the pure Ti but better than Ti-6Al-4V. However, the corrosion rate was higher for the new alloys. 3. Cell culture test showed that the new alloys have similar cell response compared with pure Ti and Ti-6Al-4V with no cell adverse reaction. 4. New designed alloys showed similar bone-metal contact ratio and osseointegration properties compared to pure Ti and Ti-6Al-4V after 3 months implantation in rabbit femur. 5. Four different surface treatments of the metals did not show any statistical difference of the cell growth and bone-metal contact ratio.

• Journal of Power System Engineering
• /
• v.9 no.4
• /
• pp.96-101
• /
• 2005

Magnesium alloys have been widely used for many structural components of automobiles and aircraft because of high specific strength and good cast ability in spite of hexagonal closed-packed crystal structure of pure magnesium. In this study, uniaxial tension tests at high temperature and creep tests are done in order to investigate the characteristics of high temperature and mechanisms for creep deformation of AZ31 Mg alloy. Yield stress and ultimate tensile stress decreased with increasing temperature, but elongation increased from results of uniaxial tension test at high temperature. The apparent activation energy Qc, the applied stress exponent n and rupture life have been determined during creep of AZ31 Mg alloy over the temperature range of 473K to 573K and stress range of 23.42 MPa to 93.59 MPa, respectively, in order to investigate the creep behavior. Constant load creep tests were carried out in the equipment including automatic temperature controller, whose data are sent to computer. At around the temperature of $473K{\sim}493K$ and under the stress level of $62.43{\sim}93.59%MPa$, and again at around the temperature of $553K{\sim}573K$ and under the stress level of $23.42{\sim}39.00MPa$, the creep behavior obeyed a simple power-law relating steady state creep rate to applied stress and the activation energy for the creep deformation was nearly equal, respectively, and a little low to that of the self diffusion of Mg alloy including aluminum. Also rupture surfaces at high temperature have had bigger dimples than those at lower temperature by SEM.

• International Journal of Highway Engineering
• /
• v.4 no.1 s.11
• /
• pp.135-147
• /
• 2002

Application of the foamed asphalt techniques in recycling the waste asphalt shows that large quantify of waste asphalt(60$\sim$70% of the total mix) can be used comparing with hot mix asphalt techniques and also is environmentally safe. However, the constant quality of the recycling foamed asphalt mixtures is not readily achieved and can not be applied to the heavy traffic road due to the characteristics of the conventional foamed asphalt mixtures. The semi-hot technique that the RAP and the aggregate is heated below $100^{\circ}C$ is adopted in this study and expected to solve the problems of conventional foamed asphalt mixtures. This study presents the viability of the semi-hot foamed asphalt mixtures when using the RAP. The semi-hot recycling foamed mixtures are tested and evaluated in the laboratory. The test results including coating rates, creep tests, resilient modulus tests, indirect tensile tests and the Marshall stability tests showed significant improvement.

• International Journal of Korean Welding Society
• /
• v.2 no.2
• /
• pp.14-18
• /
• 2002

Titanium and titanium alloy are excellent in corrosion resistance and specific intensity, and also in the biocompatibility. On the other hand, the brazing is bonding method of which productivity and reliability are high, when the complicated and precise structure of the thin plate is constructed. However, though conventional titanium-based brazing filler metal was excellent in bond strength and corrosion resistance, it was disadvantageous that metal structure and mechanical property of the base metal deteriorated, since the brazing temperature ( about $1000^{\circ}C$ ) is considerably high. Authors developed new brazing filler metal which added Zr to Ti-Cu (-Ni) alloy which can be brazed at $900^{\circ}C$ or less about 15 years ago. In this paper, the development of more low-melting-point brazing filler metal was tried by the addition of the fourth elements such as Ni, Co, Cr for the Ti-Zr-Cu alloy. As a method for finding the low-melting-point composition, eutectic composition exploration method was used in order to reduce the experiment point. As the result, several kinds of new brazing filler metal such as 37.5Ti-37.5-Zr-25Cu alloy (melting point: $825^{\circ}C$) and 30Ti-43Zr-25Cu-2Cr alloy (melting point: $825^{\circ}C$) was developed. Then, the brazing joint showed the characteristics which were almost equal to the base metal from the result of obtaining metallic structure and strength of joint of brazing joint. However, the brazing filler metal composition of the melting point of $820^{\circ}C$ or less could not be found. Consequentially, it was clarified that the brazing filler metal developed in this study could be practically sufficiently used from results such as metal structure of brazing joint and tensile test of the joint.

• Journal of Korean Society of Occupational and Environmental Hygiene
• /
• v.15 no.3
• /
• pp.166-175
• /
• 2005

Health effects associated with metal working fluid (MWF) exposures include dermatitis, respiratory disease, hypersensitive pneumonitis, and asthma. Frequently, occupational exposures to MWFs are controlled by ventilating an enclosure with an air cleaning unit that includes a fan preceded by various kinds of filtration. There are several kinds of air cleaning units used in machining centers. But the associated troubles have hindered from efficiently using these devices. The main problem is the relatively short period of filter replacement. The reason is that the air cleaning units usually do not have the de-oiling systems, thus leading the earlier clogging of filters and reducing the flow rate of hood. Thus, the first stage of study was conducted to overcome this problem by developing the new oil mist collector equipped with the easy de-oiling system. The principle of de-oiling is that the centrifugal force generated by spinning the drum covered by filter fabric separates oils from the filter fabric. It would be very similar to the spin-dry laundry. By adopting this de-oiling technique, the problems associated with the conventional oil mist collectors could be solved. Several tests/analyses were performed to make the lab-scale oil mist collector. The collection efficiencies and the de-oiling efficiencies of commercially available filter fabrics were tested. Subsequently, the endurance test were conducted by observing SEM photos of filter fabrics and measuring tensile strength/expansion coefficient after spinning the filter drum for 20 minutes at the different rotation speeds. By doing these experiments, the most appropriate filter fabric and rotation speed/duration were selected. Finally, the new oil mist collector was designed. In the near future, this device must be tested in the real machining center.