• E2M - 전기 전자와 첨단 소재
• /
• 제8권2호
• /
• pp.158-164
• /
• 1995

Solid solutions Sr$_{2}$(Ta$_{1-x}$ Nb$_{x}$)$_{2}$O$_{7}$, (x=0.0-1.0), composed of strontium tantalate(Tc=-107.deg. C) and strontium-niobate(Tc=1342.deg. C) were prepared by the conventional mixed oxide method and the flux method(molten salt synthesis method). Phase relation, sintering temperature, grain-orientation and dielectric properties for sintered ceramic samples were investigated with different compositions. Both Curie temperature and dielectric constant at Curie temperature were increased, and sintering behavior and the degree of grain-orientation were improved with the increase of Nb content. The single phase Sr$_{2}$(Ta/sib 1-x/Nb$_{x}$)$_{2}$O$_{7}$ powder was synthesized by using the flux method at lower temperatures, and sintering temperature was also reduced by using the flux method-derived powder than using the mixed oxide-derived powder. Sintering characteristics and dielectric properties of the specimens prepared by the flux method were better than those derived through the conventional mixed oxide method.thod.hod.

• 한국세라믹학회지
• /
• 제31권12호
• /
• pp.1561-1569
• /
• 1994

Effect of calcining temperature on the sintering behaviors and microwave dielectric properties of BMT[Ba(Mg1/3Ta2/3)O3] ceramics was studied. The calcining temperatures were varied from 80$0^{\circ}C$ to 130$0^{\circ}C$, respectively. It was found that, as calcining temperature lowered below 125$0^{\circ}C$, second phase such as Ba5Ta4O15 phases started to appear in calcined powder with unreacted powders. After sintering, exaggerately grown Ba5TaO3 phase could be found amang the uniform BMT grains in sintered body. Basis on the infiltration experiment, Ba0.05TaO3 phase should be formed by reaction of BMT grain and BaO-MgO eutectic liquid. But increase of calcining temperature above 125$0^{\circ}C$, there was not any second phase or unreated component in calcined powder and sintered body. As result, low calcining temperature led to precipitation of second phase in specimen and resulted decrease of Q value of BMT ceramics.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part2
• /
• pp.926-927
• /
• 2006

[ $Sr_2Ta_2O_7$ ], a layered perovskite compound, has been reported to possess most excellent photocatalytic properties among the layered perovskite materials. Recently, we have demonstrated that $Ba_5Ta_4O_{15}$ that was prepared under a mol ratio of Ba: Ta=1:1 has high photocatalytic performance as well as $Sr_2Ta_2O_7$. In this study, the photocatalyst samples with a mol ratio of Sr: Ba: Ta = (1-x): x: 1 were prepared. The maximum photocatalytic performance was obtained for x= 0.2, which is three times as high as that of undoped $Sr_2Ta_2O_7$.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2006년도 제37회 하계학술대회 논문집 C
• /
• pp.1420-1421
• /
• 2006

In this study, structural and micowave dielectric properties of the $Mg_{5}B_{4}O_{15}$ (B=Ta, Nb) cation-deficient perovskite ceeramics. The specimens are prepared through the solid-state route. According to the XRD pattern, $Mg_{4}Ta_{2}O_9$ and $MgTa_{2}O_6$ phase exist in calcined and sintered $Mg_{5}Ta_{4}O_{15}$ powder. Also $Mg_{5}Ta_{4}O_{15}$ phase added with increasing sintering temperature. In the case of calcined and sintered $Mg_{5}Nb_{4}O_{15}$ powder, single phase of $Mg_{5}Nb_{4}O_{15}$ were appeared. The bulk density and quality factor of the $Mg_{5}B_{4}O_{15}$ (B=Ta, Nb) ceramics were increased with sinteming temperature in $1400^{\circ}C{\sim}1450^{\circ}C$, but these were decreased in another sintering temperature. Dielectric constant of the $Mg_{5}Ta_{4}O_{15}$ ceramics was increased continuously with increasing of sintering temperature. And the dielectric constant of the $Mg_{5}Nb_{4}O_{15}$ ceramics was increased in $1400^{\circ}C{\sim}1450^{\circ}C$ but decreased in $1475^{\circ}C$. In the case of the $Mg_{5}Ta_{4}O_{15}$ and $Mg_{5}Nb_{4}O_{15}$ ceramics sintered at $1450^{\circ}C$ for 5h, the dielectric constant, quality factor, and temperature coefficient of the resonant frequency (TCRF) were 8.2, 259,473 GHz, -10.91 $ppm/^{\circ}C$ and 14, 37,350 GHz, -52.3 $ppm/^{\circ}C$, respectively.

• 한국식품영양과학회지
• /
• 제20권2호
• /
• pp.156-161
• /
• 1991

고추가루의 돌연변이유발, 보돌연변이 및 항돌연변이 효과를 검토하기 위해 매운맛의 재래종과 덜 매운맛의 교배종을 극성이 다른 용매로 3분획한 것과 고추의 주요한 매운 성분으로 알려진 capsaicin을 Ames mutagenicity test를 이용하여 연구하였다. 고추가루 추출획분들을 모두 direct한 돌연변이유발성이 없는 것으로 나타났고 MNNG가 존재할 때의 보돌연변이 효과도 나타나지 않았다. 또한 이들은 rat S9이 존재할 때의 indirect한 mutagenicity도 일으키지 않는 결과를 보였다. 고추가루의 주요 매운 성분인 capsaicin도 Aroclor 1254, phenobarbital로 induce시킨 rat S9과 Aroclor 1254로 induce시킨 hamster S9 등의 activation system을 이용하여도 돌연변이유발의 효과는 나타나지 않았다. 그러나 고추가루 추출획분들은 TA100 strain에서 모두 aflatoxin $B_1$의 mutagencity를 오히려 억제시키는 결과를 나타내었는데 이 효과는 고추가루의 첫번째 획분(1st fraction)이 가장 컸었다.

• 대한금속재료학회지
• /
• 제50권11호
• /
• pp.823-828
• /
• 2012

Direct reduction of $Ta_2O_5$ using liquid calcium was investigated. The experiment was conducted in a closed stainless steel chamber in an Ar atmosphere for 5-120 minutes. Most of $Ta_2O_5$ was reduced to ${\alpha}-Ta$ in 30 minutes above 1173 K and at a molar ratio of Ca and $Ta_2O_5$ above 10. The particles size increased with the reaction temperature, but it did not change much above 1223 K. The oxygen content of metal Ta was about 1 wt%.

• 한국분말재료학회지
• /
• 제10권5호
• /
• pp.349-352
• /
• 2003

This study examined the correlation of various operational factors including reaction temperature and the quantity of reductant and diluent with the characteristics of powder using $K_2$ TaF$_{7}$ as feed materials, Na as a reductant and KCl/KF as a diluent. Also to control the particle size and shape, external supply system developed, it can provide a feed material and a reductant at a fixed quantity and evaluated the characteristics of tantalum powder. When the external supply system was applied instead of the batch type process that charges feed material, reductant and diluent at the same time, it was possible to induce regular reduction reaction between feed material and reductant, which increased the recovery rate and reduced the mixture of impurities. In particular, the application of the external supply system enabled the control of reaction temperature and reaction speed according to the feeding rate of feed material during reduced reaction, and resultantly it enabled the manufacturing of granular-shaped powder with a regular granularity of 2∼3 ${\mu}{\textrm}{m}$ and purity of 99.5%.

• 한국분말재료학회지
• /
• 제14권3호
• /
• pp.173-179
• /
• 2007

In the metallothermic reduction (MR) process used to obtain tantalum powder in one batch, it is difficult to control the morphology and location of the tantalum deposits. On the other hand, an electronically mediated reaction (EMR) process is capable of overcoming this difficulty. The effect of using $K_2TaF_7$ as the raw material and sodium as the reducting agent on the characteristics of tantalum powder are investigated. As the temperature of the reduction varied from 1023K to 1223K, the powder particles obtained with MR were relatively large $({\sim}34{\mu}m)$, while those prepared via EMR were of uniform $(13{\mu}m)$. In the MR process, the Ta powder recovery rate increased from 37% to 83% at 1123K in constrat with EMR process.

• 한국분말재료학회지
• /
• 제10권5호
• /
• pp.344-347
• /
• 2003

Pure tantalum powder has been produced by combining Na as a reducing agent, $K_2$TaF$_{7}$ as feed material, KCl and KF as a diluent in a stainless steel (SUS) bomb, using the method of metallothermic reduction. And we examined various types of after-treatment that affect the high purification of powder. A significant amount of impurities contained in recovered powder was removed in various conditions of acid washing. In particular, 20% (HCl + HNO$_3$) was effective in removing heavy metal impurities such as Fe, Cr and Ni, 8% H$_2$SO$_4$ + 8% $Al_2$(SO$_4$)$_3$ in removing fluorides such as K and F from non-reactive feed material, and 2% $H_2O$$_2$ + 1 % HF in removing oxides that formed during reaction. Significant amounts of oxygen and part of light metal impurities could be removed through deoxidation and heat treatment process. On the other hand, because it is difficult to remove completely heavy metal impurities such as Fe, Cr, and Ni through acid washing or heat treatment process if their contents are too high, it is considered desirable to inhibit these impurities from being mixed during the reduction process as much as possible.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2003년도 international symposium on advanced powder metallurgy
• /
• pp.57-58
• /
• 2003