• Journal of Industrial Technology
• /
• v.41 no.1
• /
• pp.25-30
• /
• 2021

Hydride-dehydride process for efficient recycling of tantalum (Ta) is used for manufacturer of Ta powder. In case of metal powder, Impurities as like nitride, oxygen, hydrogen is decreased of physical properties. For manufacture of Ta powder, control of theses impurities is important. In this study, to decreased of impurities on Ta powder using HDH process optimize dehydride condition. Dehydration behavior of Ta is depended on temperature, time, and atmosphere. Phase transition of Ta hydride is analyzed by X-ray diffraction (XRD). Concentration of hydrogen is decreased with temperature increased. At high temperature, concentration of hydrogen in Ta is similar according to time increased. Size and morphology of powder is not observed after dehydride. Ta powder, which is less than 20 um, concentration of hydrogen under 800 ppm is obtain.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2003.04a
• /
• pp.29-29
• /
• 2003

• Resources Recycling
• /
• v.12 no.4
• /
• pp.51-57
• /
• 2003

Using the wastes of Ta powder fabrication process for capacitor, TaC powder was synthesized by SHS method. In previous to synthesis, the waste Ta was needed of milling and deoxidization treatments for active reaction and prevention of oxidation. In SHS reaction, it was found that the TaC single phase was obtained in composition of 5～6wt.％C. The reaction temperature was affected by the compaction pressure of the specimens, exhibiting the maximum values at 1600psi, respectively.

• Korean Journal of Metals and Materials
• /
• v.47 no.6
• /
• pp.338-343
• /
• 2009

The purpose of this study is to make the tantalum powder for solid electrolyte capacitor with SHS (self-propagating high-temperature synthesis) process. Raw materials for manufacturing Ta powder were used $Ta_{2}O_{5}$, Mg and NaCl. While progressing SHS process, $Ta_{2}O_{5}$ powder was reduced by Mg powder. The combustion temperature and velocity were easily controled by the varying mole ratio of NaCl, Mg and initial reaction pressure. In the case of only using NaCl as an inorganic agent, the shape is unagglomerated and has high surface area. whereas we were given the powder which has good net structure by the addition of excessive Mg as a diluent.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2005.04a
• /
• pp.70-71
• /
• 2005

• Korean Journal of Materials Research
• /
• v.11 no.12
• /
• pp.1047-1051
• /
• 2001

Purity tantalum powder has been produced by sodium reduction of potassium tantalum fluoride($K_2TaF_7$)in a stainless steel bomb. The influence of experimental variable, such as excess of reductant and temperature of reduction on the yield and quality of the Ta powder has been studied. The excesses of reductant were varied from -20%, -10%, 0%, 5%, 10%, 20%. When -20% excess of sodium was used, the un-reacted sodium remained in the reacted product. The yield of 81% of Ta powder has been achieved by reducing 50g of$K_TaF_7$with 5% sodium in excess of stoichiometric amount in presence of 16.8g of sodium chloride in the charge at a reduction temperature of$905{\circ}C$. The proportion of fine fraction(~325mesh) decreased appreciably with the increase of sodium excess, and the yield of tantalum powder improved from 65% to 94%. The average particle size of Ta Powder is improved from 3 microns to 4 microns in the 5% excess sodium.

• Korean Journal of Materials Research
• /
• v.14 no.10
• /
• pp.719-724
• /
• 2004

Production of fine tantalum powder by calciothermic reduction of tantalum oxides ($Ta_{2}O_5$) pellet through an electronically mediated reaction (EMR) has been investigated. $Ta_{2}O_5$ pellet feed and reductant calcium-nickel (Ca-Ni) alloy were charged into electronically isolated locations in a molten $CaCl_2$ bath. The current flow through an external path between the feed (cathode) and reductant (anode) locations was monitored. The current approximately 4.7A was measured during the reaction in the external circuit connecting cathode and anode location. Tantalum powder with approximately 99 $mass\%$ purity was readily obtained after each experiment. Tantalum powder by EMR using $Ta_{2}O_5$ pellet feed was fine compared with that of metal powder by metallothermic reduction and EMR using $Ta_{2}O_5$ powder feed.

• Journal of Powder Materials
• /
• v.9 no.5
• /
• pp.315-321
• /
• 2002

Pure tantalum powder has been produced by combining Na as a reducing agent, $K_2TaF_{7}$ as feed material, KCl and KF as a diluent in a stainless steel(SUS) bomb, using the method of metallothermic reduction. The present study investigated the effect of the amount of the diluent and reaction temperature on the characteristics of tantalum powder in the production process. The temperature applied in this study $850^{\circ}C$ and the amount of the additional reductant from +5% of the theoretical amount used for the reduction of the entire $K_2TaF_{7}$. The results showed that as the amount of the diluent increased, the reaction temperature became lower because the diluent prevented a temperature rise. Also, according to the mixture ratio of the feed materials and the diluent changed from 1 : 0.25 to 1 : 2, the particle size decreased from $5\mutextrm{m}$ to $1\mutextrm{m}$ and a particle size distribution which is below 325 mesh in fined powder increases from 71% to 83%. The average size of Tantalum powder, $2-4\mutextrm{m}$, was close to that of the commercial powders($2-5\mutextrm{m}$). Also under this condition, impurities contained in the powder were within the range allowed for the commercial Ta powders.

• Journal of Powder Materials
• /
• v.10 no.4
• /
• pp.255-261
• /
• 2003

Ultrafine TaC-5%Co composite powders were synthesized by spray conversion process using tantalum oxalate solution and cobalt nitrate hexahydrate(Co($(NO_3)_2$ . 6$H_2O$). The phase of Ta-Co oxide powders had amorphous structures after calcination below 50$0^{\circ}C$ and changed $Ta_2O_5$, $TaO_2$ and $CoTa_2O_6$ phase by heating above $600^{\circ}C$. The calcined Ta-Co oxide powders were spherical agglomerates consisted of ultrafine primary particles <50 nm in size. By carbothermal reaction, the TaC phase began to form from 90$0^{\circ}C$. The complete formation of TaC could be achieved at 105$0^{\circ}C$ for 6 hours. The observed size of TaC-Co composite powders by TEM was smaller than 200 nm.

• Journal of the East Asian Society of Dietary Life
• /
• v.12 no.1
• /
• pp.15-22
• /
• 2002

This study was carried out to investigate antimutagenic and cytotoxic effects of Korean traditional Mackjang added with sea tangle powder. The content percentage of most of minerals among general composition increased by adding sea tangle powder. By the Ames test, the antimutagenic effect of ethanol extract of Korean traditional Mackjang added with 5% sea tangle powder was strongest exceeding the control, 10%, and 15% sea tangle additions. The ethanol extract (400$\mu$g/plate) of Mackjang added with 5% sea tang1e powder in the S. typhimurium TA 100 strain showed inhibition rate of 95.0% against the mutagenesis induced by MNNG. The inhibition rate of ethanol extract (400$\mu$g/plate) of Mackjang added with 5% sea tang1e powder in the S. typhimurium TA98 and TA100 strains was 81.4% and 88.8%, respectively, against the mutagenesis induced by 4NQO. Under the same conditions, the suppression against B($\alpha$)P and Trp-P-1 in the TA98 and TA100 strains were 85.3% and 91.0%, and 96.5% and 96.5%, respectively. For the anticancer effects, an investigation was done on the cytotoxicity of Mackjang added with 5% sea tangle powder on the cell lines with human lung carcinoma (A549), human hepatocellular carcinoma (HepG2), and human gastric carcinoma (KATOIII). The cytotoxicities were inhibited with increasing the extract concentration. The treatment of 1.0 mg/mL Mackjang added with 5% sea tang1e powder showed relatively strong cytotoxicity of 61.2%, 61.8% and 66.8% against A549, KATOIII, and HepG2, respectively.