This study was undertaken to evaluate the allowable welding heat input range for high strength steels manufactured by various processes and to compare the weldability of TMCP steel for high heat input welding with that of conventional Ti-added normalized steel. The allowable welding heat input ranges for conventional 50kg/$mm^2$ steel to guarantee D or E grade of ship structural steel were below 150 and 80kJ/cm respectively. Such a limit in welding heat input was closely related with the formation of undesirable microstructures, such as grain boundary ferrite and ferrite side plate in the coarse grain HAZ. In case of 60 and 80kg/$mm^2$ quenched and tempered steels, for securing toughness in weldments over toughness requirements for base metal, each welding heat input had to be restricted below 60 and 40kJ/cm, that was mainly due to coarsened polygonal ferrite in weld metal and lower temperature transformation products in coarse grain HAZ. The TMCP steel could be appropriate as a grade E ship hull steel up to 200kJ/cm, but the Ti-added normalized steel could be applied only below 130kJ/cm under the same rule. This difference was partly owing to whether uniform and fine intragranular ferrite microstructure was well developed in HAZ or not.

• Proceedings of the KWS Conference
• /
• 2006.05a
• /
• pp.92-93
• /
• 2006

In recent time there are vigorous requirement for the use of thick steel plate in various industrial fields including shipbuilding industry. Application of TMCP steel plates, especially, is increase progressively. As a welding process for thick steel plate assembly high heat input welding method is used. However, HAZ softening of TMCP steel plates has a possibility to reduce the strength of welded joint. In this study, therefore, tensile strength of TMCP welds had softened HAZ was examined using numerical calculation and experiment.

• Proceedings of the KWS Conference
• /
• 2005.11a
• /
• pp.79-81
• /
• 2005

Bridges constructed recently are preferred to have long spans and simple structure details considering not only the function as bridge but scenic beauty, maintenance, construction term and life cycle cost, etc. Therefore, they require high performance steels like extra-thick plate steels and TMCP steels. A TMCP steel produced by themo-mechanical control process is now spot lighted due to the weldability for less carbon equivalent. It improved at strength and toughness in microstructure. Recently, the SM570-TMC steel which is a high strength TMCP steel whose tensile strength is 600MPa has been developed and applied to steel structures. But, for the application of this steel to steel structures, it is necessary to elucidate not only the material characteristics but also the mechanical characteristic of welded joints. In this study, the characteristics of residual stresses in welded joints of SM570-TMC steel were studied through the three-dimensional thermal elastic-plastic analyses on the basis of mechanical properties at high temperatures obtained from the elevated temperature tensile test.

• Proceedings of the KWS Conference
• /
• 2006.10a
• /
• pp.57-59
• /
• 2006

• Proceedings of the KWS Conference
• /
• 2001.05a
• /
• pp.136-138
• /
• 2001

• Proceedings of the KWS Conference
• /
• 1993.10a
• /
• pp.119-121
• /
• 1993

• Journal of Advanced Marine Engineering and Technology
• /
• v.40 no.9
• /
• pp.774-779
• /
• 2016

This study was performed to study the possibility of TMCP's application for side shell plating curved structures through mechanical property testing to understand if the rules and regulations of DNV and the quality standard of IACS after line heating for TMCP steel and normalizing DH32 material steel could be satisfied. Experimental results showed that TMCP's strength was measured to YS = 385 MPa, 18% higher than the required 315 MPa and TS = 525 MPa, complying with the required range of between 440 and 570 MPa. The minus 20 degree impact test for the Charpy V-Notch complied with the required standard and in addition the hardness test satisfied the requirement of 'Hv10 = 130 ~ 320' by reaching an average of T : 216 and L : 275 respectively.

• Journal of Ocean Engineering and Technology
• /
• v.11 no.3
• /
• pp.39-47
• /
• 1997

Recently developed TMCP steels, which were manufactured by controlled rolling followed by accelerated cooling process, were examined to study their characteristics and weldability. Accelerated cooling type TMCP steel's hardness test result exhibited high value on weld zone. On the contrary, base metal and HAZ exhibited comparatively the similar value. On this experiment result Softening of HAZ is not occurred. in the-heat affected zone, grain size repression be caused by chemical composition properties which a small quantity Al-Ti-B-N. Changing stress ratio near-threshold fatigue crack propagation experiments were carried out. According to this result, crack propagation velocity of the HAZ exhibited slower than the base metal and near-threshold value had increased at the HAZ. Finally accelerated cooling type TMCP steels were exhibited excellent mechanical properties in both strength and toughness.

• Journal of Welding and Joining
• /
• v.26 no.3
• /
• pp.61-66
• /
• 2008

As ships become to be larger than ever, the thicker plate and the higher tensile steel plate are used in naval shipyard. Though special chemical composition is needed for high-tensile steels, recent high-tensile steels are made by the TMCP(Thermo-Mechanical control process) skill. The increase of yield stress and tensile stress of TMCP steels is induced from bainite phase which is transformed from austenite, but that increased yield stress can be vanished by another additional thermal cycle like welding and heating. As thermal deformations are deeply related by yield stress of material, the study for prediction of plate deformation by heating should reflect principle of TMCP steels. This study developed an algorithm which can calculate inherent strain. In this algorithm, not only the mechanical principles of thermal deformations, but also the predicting of the portion of initial bainite is considered when calculating inherent strain. The simulations of plate deformation by these values showed good agreements with experimental results of normalizing steels and TMCP steels in welding and heating. Finally we made an inherent strain database of steels used in Class rule.

• Journal of Welding and Joining
• /
• v.4 no.2
• /
• pp.1-11
• /
• 1986

최근 개발된 구조용강을 대표하는 TMCP강재는 가속냉각법의 도입으로 그 적용범위가 과거 2-3 년 동안에 거의 모든 구조용 강재에 확산되었다. 이와 같은 확대 적용에는 생산비를 절감하려는 Steel Marker의 노력과 가속 냉각처리된 강재에 대한 fabricator 측의 긍정적인 반응이 크게 작 용했는데, 이는 이 강재가 같은 우수한 기계적 성질 및 용접성에 기인하고 있다. 그러나 fabricator 측은 가속냉각된 강재에 대해 익숙치 않으므로 가속냉각된 강재와 기존의 강재에 대 한 차이점을 충분히 인식하고, 사용할 때 예상되는 문제점에 대해서는 강재 주문시 Steel Maker 측과 충분한 토의를 거친후 구매하는게 바람직하다고 하겠다. 이로 인하여서만이 fabricator측은 가속냉각된 강재의 우수성을 백분 활용할 수 있을 뿐만 아니라 제작시 야기될 문제를 미연에 방 지할 수 있을 것이다.