• 한국초전도학회:학술대회논문집
• /
• 한국초전도학회 2008년도 High Temperature Superconductivity Vol.XVIII
• /
• pp.73-73
• /
• 2008

• Progress in Superconductivity
• /
• 제8권1호
• /
• pp.65-70
• /
• 2006

We fabricated $YBa_2Cu_33O_{7-x}$(YBCO) films on(00l) $LaAlO_3$ substrates prepared by metal organic deposition(MOD) method using trifluoroacetate(TFA) solution and evaluated the effects of the humidity on the microstructure, phase purity, and critical properties. The films calcined at $430^{\circ}C$ were fired at $775^{\circ}C$ at 0%, 4.2%, 12.1%, and 20.0% humidified As gas mixed with 0.1% $O_2$. We observed that the amount of $BaF_2$ phase was effectively reduced and that a sharp and strong biaxial texture formed under a humidified atmosphere, leading to increased critical properties. For the films fired at 0% humidity, the $T_c\;and\;I_c$ were undetectably small. When the humidity was increased to 4.2%, the corresponding $T_c$(onset) and $I_c$ were increased to 90.5 K and 8 A/cm-width, respectively. For the films at the humidity range of 12.1-20.0%, the $I_c$ was found to be 35 A/cm-width. According to the results of the XRD, pole-figure, and SEM, these improved critical properties are probably attributed to the formation of a purer YBCO phase, larger grain size, and stronger c-axis orientation.

• Progress in Superconductivity
• /
• 제6권2호
• /
• pp.142-145
• /
• 2005

YBCO coated conductors have been fabricated with a newly developed oxide-precursor-based MOD process. The precursor solution was synthesized with low cost YBCO powders as starting materials and YBCO coated conductors have been deposited on IBAD substrate ($CeO_2$/IBAD-YSZ/SS). YBCO coated conductor prepared by dip coating shows transport $I_c$ of 15A/cm-w at 77 K. Microstructural and crystallographic analyses indicate that YBCO layer was grown in epitaxy with substrate and exhibited well-developed dense microstructure. Also discussed are processing and analysis of YBCO coated conductor by slot-die web coating method. It was shown that this oxide-based MOD process provides a low cost route to coated conductor with high $J_c$.

• Progress in Superconductivity
• /
• 제8권1호
• /
• pp.22-26
• /
• 2006

Total Fluorine content in the precursor solution for MOD processing of YBCO coated conductors can be significantly reduced by synthesizing precursor solution with F-free Y & Cu precursor and Barium trifluoroacetate(TFA). It was shown that crack-free and uniform precursor films were formed after calcinations in humidified oxygen atmosphere. Less than 2 hours are required to finish the calcination process, and XRD measurement shows that $BaF_2,\;CuO,\;and\;Y_2O_3$ are major constituent of calcined precursor films. Film thickness after calcination was measured to be ${\sim}2.8$ um by applying slot-die coating method. In particular, addition of Samarium shows critical current of Ic=226 A/cm-w($Jc=3.4\;MA/cm^2$). Also discussed are recent developments in the reel-to-reel processing using F-free Y & Cu precursor solutions. It is shown that uniform and fast processing route to YBCO coated conductor with high Ic can be provided by employing F-free Y & Cu precursor solutions in MOD process.

• 한국초전도ㆍ저온공학회논문지
• /
• 제8권4호
• /
• pp.12-14
• /
• 2006

YBCO coated conductors have been fabricated by the reel-to-reel processing using TFA-MOD method. In this work, the fluorine-free Y & Cu precursor solution was synthesized to shorten the calcining time by reducing the evolution of HF gas, thus the meter-long YBCO precursor films can be made within few hours by the continuous slot-die coating & calcination step using the F-free Y & Cu precursor solution. The annealing step was followed to make the YBCO films by the reel-to-reel method with the vertical gas flow system onto the moving tape. To increase the growth rate of the YBCO films by enhancing the removal of HF gas, the low total pressure was adopted in the annealing processing. And the water partial pressure and the oxygen partial pressure were varied to optimize the growth conditions of the MOD-YBCO films on the buffered metal tape. FE-SEM and XRD were used to investigate the surface morphologies and the texture of the meter-long YBCO films. The end-to-end critical current $(I_c)$ of 63A/cm-width and the critical current density $(J_c)$of $0.9MA/cm^2$ with the thickness of $0.7{\mu}m$ were obtained in the 0.42m long coated conductor.

• 한국초전도ㆍ저온공학회논문지
• /
• 제9권1호
• /
• pp.1-4
• /
• 2007

The total Fluorine content in the precursor solution for MOD processing of YBCO coated conductors can be significantly reduced by synthesizing precursor solution with F-free Y & Cu precursor and Barium trifluoroacetate(TFA). It was shown that crack-free and uniform precursor films were formed after calcinations in humidified oxygen atmosphere. Less than 2 hours are required to finish the calcinations process and XRD measurement shows that $BaF_2,\;CuO,\;Y_2O_3$ are major constituent of calcined precursor films. Film thickness after calcinations was improved to be 2.8um by applying slot-die coating method. In particular, addition of Samarium shows critical current of $I_c=273A/cm-w(J_c=3.8MA/cm^2)$. It is shown that uniform and fast processing route to YBCO coated conductor with high Ic can be provided by employing F-free Y & Cu precursor solution in MOD process.

• 한국초전도ㆍ저온공학회논문지
• /
• 제20권1호
• /
• pp.1-10
• /
• 2018

The improvement of critical current properties of $REBa_2Cu_3O_{7-x}$ (REBCO) coated conductors by introducing artificial pinning centers (APCs) is examined with respect to the field-angle anisotropy, high-field performance and relaxation property with time. Nano-rods along the c-axis introduced by PLD method and isotropic nano-particles introduced by TFA-MOD method are treated. The theoretical analysis is also shown to understand the effect of APCs quantitatively. The effects of superconducting layer thickness that influences the high-field performance and relaxation property are also discussed. It is shown that the upper critical field, which is another important factor to determine the high-field property, can be improved by introduction of APCs through electron scattering at interfaces with the superconducting matrix. The optimum critical current property can be obtained by properly designing the morphology and number density of APCs and the superconducting layer thickness.

• 한국세라믹학회지
• /
• 제43권2호
• /
• pp.98-105
• /
• 2006

YBCO film was synthesized by using a new approach to the TFA-MOD method. In the fabrication process, $Y_2Ba_1Cu_1O_x\;and\;Ba_3Cu_5O_8$ powders were used as precursors (the so called '211 process'), instead of Y-, Ba-, and Cu-based acetates, and dissolved in trifluoroacetic acid followed by calcining and firing heat treatment. Consequently, we successfully fabricated YBCO film and evaluated the phase formation, texture evolution, and critical properties as a function of the calcining and firing temperature and humidity, in order to explore its possible application in coated conductor fabrication. The films were calcined at $430-460^{\circ}C$ and then fired at $750-800^{\circ}C\;in\;a\;0-20\%$ humidified $Ar-O_2$ atmosphere. We observed that $BaF_2$ phase was effectively reduced and that a sharp and strong biaxial texture formed under humidified atmosphere leading to increased critical properties. In addition, we found that the microstructure varied significantly with the firing temperature: the grain grew further, the film became denser, and the degree of texture and phase purity varied as the firing temperature increased. For the film fired at $775^{\circ}C$ after calcining at $460^{\circ}C$, the critical current was obtained to be 39 A/cm-width (corresponding critical current density is $2.0\;MA/cm^2$ which was probably attributed to such factors as the enhanced phase purity and out-of-plane texture, the moderate film density and grain size, and crack-free surface.

• 한국초전도학회:학술대회논문집
• /
• 한국초전도학회 2007년도 High Temperature Superconductivity Vol.XVII
• /
• pp.94-94
• /
• 2007

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2005년도 제36회 하계학술대회 논문집 C
• /
• pp.1998-2000
• /
• 2005

The effects of the addition of nanocrystalline Y2O3 powder on the microstructure and superconducting properties have been investigated in YBCO films prepared by TFA-MOD process. Precursor solution doped with extra $Y_2O_3$ Powder was prepared by adding $Y_2O_3$ powder into a stoichiometic precursor solution with a cation ratio of Y:Ba:Cu=1:2:3. Coating solutions with and without $Y_2O_3$ doping were coated on $LaAlO_3(100)$ single crystal by a dip coating method, cacination and conversion heat treatments were performed at the controlled atmosphere containing water vapor Current carry capacity(Jc) of YBCO film was enhanced about 50% by $Y_2O_3$ doping. It is thought that the enhancement of Jc is due to the better connectivity of YBCO grains and/or the flux pinning by the presence of nanocrystalline $Y_2O_3$ Particles embedded in YBCO grains.