• 한국염색가공학회지
• /
• 제32권4호
• /
• pp.226-231
• /
• 2020

This study investigated effect of particle sizes of polymer binders for digital textile printing(DTP) pigment inks on touch of fabrics. The polymer binders were synthesized via miniemulsion polymerization of methyl methacrylate(MMA), butyl acrylate(BA), N-ethylolacrylamide(NEA) and methacrylic acid(MAA). The prepared binders were applied to black pigment inks and those black pigment inks were used to dye cotton fabrics. Then, color strength, rubbing fastness, stiffness, surface and bending properties of the dyed fabrics were investigated. Depending on the particle size of the polymer binder used, color strength, friction fastness, stiffness, surface and bending properties change. Generally, the larger the particle size of the polymer binder, the softer properties.

• 한국염색가공학회지
• /
• 제33권4호
• /
• pp.182-190
• /
• 2021

The purpose of this study is to provide the dyeing and physical characteristics of napped knit fabrics composed of latent crimped yarn. The K/S values, dyeing fastness, thickness, bulkiness, and shrinkage characteristics of three knit fabrics were investigated. The original knit fabric (SK) was composed of 1ply latent crimped yarn (75/36) in the ground and PET DTY (70/100) in the pile loop, in order of napped process the napped knit fabric (SN) was napped SK fabric. In order to compare of latent crimped yarn content, the last knit fabric (DN) was napped 2ply latent crimped yarn were included in the same structure of SK. Dyeability of three knit fabrics was similar but the shrinkage properties of DN fabric were significant different. The bulkiness shows a tendency to increase the bulkiness as increasing the dyeing temperature, and the bulkiness of the SN was higher because of the napping process and optimal content of latent crimped yarn.

• 한국염색가공학회지
• /
• 제33권4호
• /
• pp.169-181
• /
• 2021

Five dyes based on phthalocyanine, a dye on azo, and a dye on anhraquinone were prepared from corresponding starting material to investigate the effects of substituent on thermal-stability of dyes which is essentially required to apply to the color filters. Synthesized dyes were confirmed their chemical structure using by 1H-NMR, MASS and Elemental analysis. The thermal-stability was evaluated by the weight reductions measured by TGA analysis comparing to that of conventional C.I. Pigment Blue 15:6. The absorption maxima were measured by UV-VIS spectrophotometer then the effects of substituent on absorption maximum was also investigated.

• 한국염색가공학회지
• /
• 제33권4호
• /
• pp.327-337
• /
• 2021

The uniformly dispersed Aramid and Poly (phenylene benzobisoxazole) (PBO) in a variety of rubber was investigated. The mechanical properties of rubber were characterized by hardness, tensile strength, elongation at break, heat resistance, oil resistance, cold resistance, ozone resistance measurements. The 3mm Aramid chopped fiber better tensile strength than the other Chopped fiber. The Aramid of 3mm chopped fiber showed excellent reinforcing in rubber composite because of homogeneous dispersion. Consequently, the best 3mm Aramid chopped fiber and rubber improved the tensile strength and elongation at break of the composite. Also, 3mm Aramid chopped fiber improved the oil-resistant, ozone resistant and cold resistant.

• 한국염색가공학회지
• /
• 제33권4호
• /
• pp.338-347
• /
• 2021

In the case of occlusive dressings currently used in dressings for burn treatment, it is impossible to confirm the replacement time, so replacement is delayed, resulting in additional infection. To solve this problem, liposomes capable of bacterial sensing were prepared using 5(6)-Carboxyfluorescein, Phosphatidylcholine, 1,2-Dipalmitoyl-sn-glycero-3-phosphocholine, Cholesterol, and 10,12-Tricosadiynoic acid. In this study, evaluation of changes in drug encapsulation rate in liposomes according to changes in three types of phosphatidylcholine phospholipids during liposome production, high-performance phosphatidylcholine phospholipids selected through vesicle size analysis, low and high temperature stability evaluation, bacterial sensitization ability evaluation, animals cell responses were assessed.

• 한국염색가공학회지
• /
• 제33권4호
• /
• pp.309-316
• /
• 2021

Due to the rigid nature of the silicon carbide fiber(SiC), fiber damage occurs from the friction during the carding process. This damage not only lowers the spun yarn yield, but also lowers the heat resistance of the spun yarn, so that ultra-high heat resistant yarn cannot be manufactured. Therefore, in the carding process where the most friction between fiber and machine(wire, etc.) occurs, some factors were modified and tested, and as a result of measuring the change in physical properties, fiber damage decreased due to the wire angle or wire density, resulting in improved yield. The test method used to measure the yield of SiC fiber was the carbonization method, and the content of SiC fibers was calculated using the remaining amount after carbonization. Carbonization test was performed at air condition, 700℃, and for 2 hours. Analysis by SEM-EDX showed that the carbide was consistent with the composition of the SiC fiber.

• 한국염색가공학회지
• /
• 제33권4호
• /
• pp.258-268
• /
• 2021

This study conducted on the introduction of recycled cellulose fibers, which are widely used in the textile industry as eco-friendly biomass materials, into polypropylene resins, which are mainly used for interior and exterior materials such as door trims and console parts of automobiles. In general, cellulose fibers can affect mechanical properties and have a lightening effect when used as a reinforcing agent. However, since cellulose fibers have hydrophilic properties and have relatively low compatibility with industrial polymer resins, they are used in combination through fiber hydrophobic surface treatment. Therefore, through this study, the reforming reaction conditions optimized in terms of hydrophobicity and workability for cellulose fibers are studied. Furthermore, polypropylene containing surface-modified cellulose fibers was prepared to compare physical properties by fiber content and study optimized content.

• 한국염색가공학회지
• /
• 제35권4호
• /
• pp.206-213
• /
• 2023

This study attempted to investigate what color would fade more during hair bleaching and examine what should be done to make hair color last longer. For this, hair was colored differently in ash gray with permanent hair dyes and semi-permanent hair dyes each. Hair in multiple levels was created through such bleaching. Color retention was improved in consideration of the degree of color fading in sample hair. In terms of post-bleaching hair coloring, it was more efficient to color hair by eliminating redness without hair damage after shampooing with a permanent hair dye. Therefore, it is anticipated that the study results would be highly useful for beauty salons to find a base level in consideration of bleaching effects and make improve- ments according to hair retention and moisturizing effects.

• 한국염색가공학회지
• /
• 제35권4호
• /
• pp.221-230
• /
• 2023

Meta-aramid and polyamic acid were separated and the manufactured films were analyzed for their integration and logarithmic properties. The miscibility of meta-aramid and polyamic acid was analyzed by Fourier transform infrared spectroscopy and scanning electron microscopy. Using calorimetric analysis and differential scanning calorimetry, the storage of meta-aramid and polyamic acid, indicated on the right side of the column, was analyzed. It was confirmed that the initial thermal resistance occurs because the polyamic acid is accounted for in the meta-aramid, and the glass transition temperature and persistence phenomenon are explained.

• 한국염색가공학회지
• /
• 제35권4호
• /
• pp.274-283
• /
• 2023

Conductive polymers are polymers that conduct electricity like metal conductors. Unlike typical organic polymers, they are polymers that have the electrical, magnetic, and optical properties of metals or semiconductors. For Example, these conductive polymers include Polypyrrole (PPy), Polyaniline (PANI), and Polythiophene (PT). On the other hand, Insulating polymers do not conduct electricity well while providing insulation, which is the opposite of conductivity. With the exception of conductive polymers, most polymers are non-conductors. Insulating polymers include polyimide (PI), polystyrene (PS), and poly(vinyl alcohol) (PVOH, PVA, or PVAl). Although many different polymers exist, we have simply illustrated the properties and recent developments of conductive and insulating polymers, which have opposite properties.