• Proceedings of the KWS Conference
• /
• 1996.10a
• /
• pp.77-78
• /
• 1996

• Proceedings of the KWS Conference
• /
• 1999.05a
• /
• pp.241-244
• /
• 1999

The purpose of this study is to examine the characteristics of stress corrosion cracking(SCC) and acoustic emission(AE) signals for the weld HAZ of HT-60 steel under corrosion control in synthetic seawater. Corrosive environment was controlled by potentiostat, and SCC experiment was conducted using a slow strain rate test method at strain rate of 10$^{-5}$ /sec. In order to verify the miroscopic fracture behaviour of the weldment during SCC phenomena, AE test was done simultaneously. Besides, correlationship between mechanical parameters and AE ones was investigated. In case of the parent, reduction of area(ROA) at -0.5V was samller than any other applied voltage such as -0.8V and -1.1V. In addition, reduction of area for the PWHT specimens at -0.8mV was larger than that of the weldment due to the softening effect according to PWHT. In case of the weldment, a lots of events was produced because of the singularities of the weld HAZ compared with the parent.

• Journal of Welding and Joining
• /
• v.11 no.3
• /
• pp.48-60
• /
• 1993

The cause of corrosion failure found in structures or various components operating in severe corrosive environments has been attributed to stress corrosion cracking(SCC)which is resulting from the combined effects of corrosive environments and static tensile stress. Slow strain rate test (SSRT) provides a rapid reliable method to determine SCC susceptibility of metals and alloys for a broad range of application. The chief advantage of SSRT procedures is that it is much more aggressive in producing SCC than conventional constant strain or constant load tests, so that the testing time is considerably reduced. Therefore, in this paper, the combined effects of material properties and strain rate on the tensile ductility and fracture morphology of parents and weldment for SM45C, SCM440 and SM20C steels were examined and discussed in synthetic sea water. The susceptibility of SCC was the most severe under the strain rate of $1.0{\times}10^{-6} sec^{-1}$, and R.O.A. can be used for parent and maximum load for weldment to evaluate the parameter for SCC susceptibility.

• Journal of Welding and Joining
• /
• v.12 no.2
• /
• pp.87-96
• /
• 1994

Correlation between microstructural features and segregation of elements (Si, Mn, P and S) near the mid of thickness in the base metal and the synthetic HAZ was investigated. Furthermore, the relationship between the degree of center segregation and weld cold cracking susceptibility in the thickness direction was also conducted by evaluating the effect of P concentration on the critical applied stress. The results obtained are as follows: 1) Pearlite band, containing the MnS type inclusion and a locally transformed structure with a higher hardness, was observed in the center segregation region. 2) By the weld thermal cycle, center segregation region was transformed to the white band which had a higher hardness than that of base metal due to a greater hardenability of concentrated Mn, P etc.. 3) Weld cold cracking susceptibility in the thickness direction was mainly dependent on the concentration of impurity elements rather than on the number of the segregated particles near the mid of thickness. 4) During welding, the higher concentrated region was easily changed into white band. Therefore, it could be predicted that the initiation and propagation of a cold crack would be promoted by increasing the restraint stress and hydrogen content.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.14 no.2
• /
• pp.492-501
• /
• 1990

It was known that the fracture incidences of offshore structure were mostly originated from the surface defects. Especially, in the case of the welded structures, since the welded region has some defects and incomplete beads which are apt to behave like the surface cracks, it has been necessary to evaluate the environmental effects on crack growth at HAZ for the design crack growth behaviour at multi-pall HAZ for SWS41 steel under free corrosion and cathodic protection(-0.9V vs Ag/Agcl) conditions. The results are summarized as follows ; (1) Crack growth rate of the as weld in air was faster than that of the parent and PWHT specimens over all .DELTA.K rang. (2) In free corrosion test, surface crack growth rate of the as welded was decreased in comparison with that of the parents. (3) In fatigue test under cathodic protection, cathodic electric potential(-0.9V vs Ag/Agcl) for the SWS41 steel parent was effective, while for the as welded ineffective. (4) There was a tendency that the exponent(m) of the Paris' equation was decreased in order of microhardness magnititude in air and under cathodic protection conditions and vise versa in free corrosion. (5) Fracture surface has dimples and ductile striations in air test, but transgranular cracks and brittle striations under cathodic protection test.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.21 no.1
• /
• pp.62-68
• /
• 2001

In order to characterize the microscopic fracture behaviour of the weldment din stress corrosion cracking(SCC) phenomena, SCC and acoustic emission(AE) tests were carried out simultaneously and the correlation between mechanical paramenters obtained from SCC and AE tests was investigated. In the case of base metal, much more AE events were produced at -0.5V than at -0.8V because of the dissolution mechanism before the maximum load. Regardless of the applied voltages to the specimens, however, AE events decreased after the maximum load. In the case of weldment, lots of AE events with larger amplitude $range(40{\sim}100dB)$ were produced because of the singularities of weld HAZ in comparision to the base metal and post-weld heat-treated(PWHT) specimens. Numerous and larger cracks for the weldment were observed on the fractured surfaces by SEM examination. From these results, it was concluded that SCC for the weldment appeared most severely in synthetic seawater. Weld HAZ was softened by PWHT which also contributed to the reduced susceptibility to corrosive environment in comparison to the weldment.