• Tribology and Lubricants
• /
• v.8 no.2
• /
• pp.20-25
• /
• 1992

Friction and wear behavior of hot isostatic pressed $Al_2O_3-TiC$ was experimentally examined. Pin-on-disk type friction and wear apparatus was designed and manufactured for the experiment. The experiments were conducted under unlubricated sliding motion in both low and high humidity for three kinds of sliding speed. $Al_2O_3-TiC$ and bearing steel were used as counterface materials. Friction coefficient, wear rate, and surface roughness were measured. Wear surface and wear debris were observed through optical microscope and SEM and analyzed by EDAX. The results showed that the counterface materials, the sliding speed, and the moisture at the sliding surface have significant influence on the friction coefficient and wear rate of $Al_2O_3-TiC$.

• Transactions of the Korean Society of Machine Tool Engineers
• /
• v.15 no.6
• /
• pp.32-37
• /
• 2006

Micron size Co-alloy(T800) powder was coated on Inconel 718 by HVOF thermal spraying for the studies of the improvement of durability of high speed spindle by using Taguchi program for the parameters of spray distance, flow rates of hydrogen and oxygen and powder feed rate. The optimal coating process was determined by the studies of coating properties such as micro-structure, porosity, surface roughness and micro hardness. Friction and wear behaviors of coatings were investigated by sliding wear test at room temperature and $1000^{\circ}F(538^{\circ}C)$. At both room temperature and $538^{\circ}C$ the sliding wear debris and friction coefficients of the coating were drastically reduced compared with the surface of non-coated parent material. This shows that Co-alloy powder coating is highly recommendable for the durability improvement surface coating of high speed air-bearing spindle. At high temperature wear traces and friction coefficients of both coating and non-coating were drastically reduced compared with those of room temperature since the brittle oxides were formed easily on the surface, and the brittle oxide phases were attrited by the reciprocating sliding wear according to the complicated mixed wear mechanisms These oxide particles, partially melts and the melts play role as lubricant and reduce the wear and friction coefficient. This also shows that Co-alloy powder coating is highly recommendable far the durability improvement surface coating on the surface vulnerable to frictional heat such as high speed spindles.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 1998.10a
• /
• pp.300-305
• /
• 1998

A method of calculating wear amount which is based on digitally measured surface profile was suggested. The original profile of worn out profile was estimated from its adjacent surface profile by using least squares curve fitting with Fourier series. The approximated curve was well fitted to original surface profile. With this approach, more accurate calculation of the wear amount will be possible.

• Tribology and Lubricants
• /
• v.5 no.1
• /
• pp.36-43
• /
• 1989

Scanning electron microscopic observations were carried out on the worn surface and the wear debris of ceramic materials to investigate the wear mechanism of those in dry rolling contact. It was found from the scanning electron microscopic observations that the wear in ceramic materials is related to brittle fracture and has two types of wear mechanisms, small scale wear and larvae scare wear. Plate-like wear debris were created from the initial surface cracks and defects. The small scale wear was related to real contact area and large scale wear was related to HertzJan contact area. A wear model was proposed on the basis of scanning electron microscopic observations.

• The Journal of Korean Academy of Prosthodontics
• /
• v.39 no.1
• /
• pp.84-95
• /
• 2001

Titanium is widely used in dentistry for its low density, high strength, fatigue resistance, corrosion resistance, and biocompatibility. But it has a tendency of surface damage under circumstance of friction and impact for its low hardness of the surface. Coating is one of methods fir increasing surface hardness. Its effect is to improve surface physical characteristics without change of titanium. Diamond-like carbon and titanium nitride are known for its high hardness of the surface. So that this study was aimed at the wear test and the cytotoxicity test of the commercially pure titanium and Ti-6Al-4V alloy which were deposited by diamond-like carbon film or titanium nitride film to acertain improvement of the surface hardness and the biocompatibility. A disk (25mm diameter, 2mm thickness) was made of commercially pure titanium and Ti-6Al-4V alloy and these substrates were deposited by diamond-like carbon film or titanium nitride film. Diamond-like carbon film was deposited by the method of radiofrequency plasma assisted chemical vapor deposition and titanium nitride film was deposited by the method of reactive arc ion plating. Then these substrates were tested about wear characteristics by the pin-on-disk type wear tester in which ruby ball was used as a wear causer under the load of 32N, The fracture cycles were measured by rotating the substrates until their films were fractured. The wear volume was measured after 150 cycles and 3,000 cycles using surface profiler. The cytotoxicity test was peformed by the method of the MTT assay. The results were as follows : 1. In the results of the wear volume test, commercially pure titanium and titanium alloy which were coated by diamond-like carbon film or titanium nitride aim had higher resistance against wear than the substrates which were not coated by any films (P<0.05). 2. In the results of the fracture cycle test and the wear volume test, diamond-like carbon film had higher resistance against wear than titanium nitride film (P<0.05). 3. In both coatings of diamond-like carbon aim and titanium nitride film, Ti-6Al-4V alloy had higher resistance against wear than commercially pure titanium (P<0.05) 4. In the results of the cytotoxicity test, diamond-like carbon film and titanium nitride film had little cytotoxicity as like commercially pure titanium or Ti-6Al-4V alloy (P>0.05).

• Journal of the KSME
• /
• v.16 no.2
• /
• pp.122-127
• /
• 1976

It was reported in the Journal of KSME Vol. 15, No. 3 and No. 4, 1975 that could be finished the best smooth surface by applying frictional work to the metal surface. Even if we can finish the best smooth surface of methal, it is not available when it has not anti-wear. Present study tried to investigate the anti-wear and the characteristics of frictional worked surface by using the sliding contact between plain bearing of brass and frictional worked jornal of mild steel. The results were compared with the case of ground journal.

• Tribology and Lubricants
• /
• v.28 no.1
• /
• pp.1-6
• /
• 2012

In this paper, a three elastic body sliding contact problem is modeled to investigate more precise wear mechanisms related with the sealing surface. A 3-D finite element contact model, a small spherical elastic particle, PTFE seal and steel surface, is solved using a nonlinear finite element code MARC. The deformed seal and steel surface shapes, von-Mises and principal stress distributions are obtained for different seal sliding distances. The entrapped small particle within PTFE seal results in very high stresses on the steel surface which exceeded its yield strength and produce plastic deformation such as groove and torus. The sealing surface could also be worn down by sub-surface fatigue due to intervening small particles together with the well-known abrasive wear. Therefore the proposed contact model adopted in this paper can be applied in design of various sealing systems, and further studies are required.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.20 no.5
• /
• pp.1468-1476
• /
• 1996

Surface integrity is dictated by the fabrication process of the metal part. In this work, steel specimens were prepared under various mechine conditions to achieve different degrees of deformation state. The tribological characteristics of the speciments were tested using a pin-on-disk type apparatus and other surface characterization tools. It is shown that though frictional characteristics are similar, the wear rate is significantrly affected by the properties of the surface. In the case of steel, surface cracks resulted in high wear despite the relatively high hardness of the specimen. Also, the sliding action were found to reduce the residual stress on the surface. These results indicate that there is a strong relationship between surface integrity and the tribological properties of steel, and therefore the machining condition should be optimized woth respect to tribological performance of a steel part.

• Tribology and Lubricants
• /
• v.40 no.3
• /
• pp.84-90
• /
• 2024

This study investigates the effect of the surface microstructure on the tribological characteristics of glass substrates. Chemical etching using hydrofluoric acid and ammonium hydrogen fluoride was employed to create controlled asperity structures on glass surfaces. By varying the etching time from 10 to 50 min, different surface morphologies were obtained and characterized using optical microscopy, surface roughness measurements, and water contact angle analysis. Friction tests were performed using a stainless steel ball as the counter surface to evaluate the tribological behavior of the etched specimens. The results showed that the specimen etched for 20 min exhibited the lowest and most stable friction coefficient, which was attributed to the formation of a uniform and dense asperity structure that effectively reduced the stress concentration and wear at the contact interface. In contrast, specimens etched for shorter (10 min) or longer (30-50 min) durations displayed higher friction coefficients and accelerated wear owing to nonuniform asperity structures that led to local stress concentration. Optical microscopy of the wear tracks further confirmed the superior wear resistance of the 20-minute etched specimen. These findings highlight the importance of optimizing the etching process parameters to achieve the desired surface morphology for enhanced tribological performance, suggesting the potential of chemical etching as a surface modification technique for various materials in tribological applications.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.12 no.3
• /
• pp.489-496
• /
• 1988

This paper is studied to know wear mechanism in variation of austempering temperature and holding time of austempered ductile cast iron against mating material SM45C hardened by heat treatment. The wear tests were carried out by rubbing the annular surface of two test pieces in dry sliding friction. The wear mechanism was investigated by scanning electron microscopy and the retained austenite volume fraction was investigated by X-ray diffractometer. The experimental results show that the wear characteristics depend largely on the oxidation of the testing materials which is influenced by the sliding velocity and distance. The retained austenite has a negative effect during frictional contact because it has increased severe wear by softened surface layer. It is shown experimentally that hard metals have lower frictional resistance and hence the resistance to adhesion is increased due to stronger interatomic linking bonds and increase in the surface energy.