• Journal of Mechanical Science and Technology
• /
• 제16권11호
• /
• pp.1428-1434
• /
• 2002

The ball-on-disk type sliding tests with boundary lubricated steels were carried out to verify the effect of initial spacing in surface profiles on wear and scuffing. Three kinds of surface spacing, which are closely related with initial surface micro-cracks on sliding surfaces, were produced on AISI 1045 steel surfaces using different grinding and polishing processes. Frictional forces and time to scuffing were measured, and the shape and amount of wear particles were analyzed to compare the with original surface profiles. From the tests, it was confirmed that the size of wear particles are related closely to the original spacing of the surface profile. The time to failure and amount of wear were sensitive to the surface spacing. The wider surface spacing shows much longer sliding life and smaller amount of wear than the others. Time to scuffing was increased with increasing surface pro(lie spacing. The size of wear particles increased while the wear and wear rate K were decreased with an increase in surface spacing. After the sliding tests, surface cracks of inner parts of the wear track formed due to scuffing were observed and compared among the specimens having the different surface spacing.

• Tribology and Lubricants
• /
• 제17권5호
• /
• pp.399-405
• /
• 2001

In this paper the ball-on-disk type sliding tests with boundary lubricated steels were carried out to verify the relation between surface profiles and wear as well as scuffing. Three kinds of surface roughness and asperity radius were produced on AISI 1045 steels using the different processes of grinding and polishing. Frictional forces and time to scuffing were measured. Also, the shape and amount of wear particles were analyzed to compare with original profiles. From the tests, it was confirmed that the size of wear particles are very related to original surface profile. The time to failures and wear amounts were sensitive to the surface spacing. The large surface spacing shows much longer sliding life and smaller wear amount than the others. Time to scuffing was increased with increasing surface profile spacing. The sire of wear particles was increased and the amount was decreased with increasing surface profile spacing. Wear volume and wear rate K were decreased with increasing surface profile spacing. And after sliding tests, surface cracks of inner parts of the wear track occurred scuffing were observed and compared the differences about each specimen having the different surface profile spacing.

• 한국윤활학회:학술대회논문집
• /
• 한국윤활학회 2001년도 제33회 춘계학술대회 개최
• /
• pp.64-71
• /
• 2001

In this paper the ball-on-disk type sliding tests with boundary lubricated steels were carried out to verify the relation between surface profiles and wear as well as scuffing. Three kinds of surface roughness and asperity radius were produced on AISI 1045 steels using the different processes of grinding and polishing. Frictional forces and time to scuffing were measured. Also, the shape and amount of wear particles were analyzed to compare with original profiles. From the tests, it was confirmed that the size of wear particles are very related to original surface profile. The time to failures and wear amounts were sensitive to the surface spacing. The large surface spacing shows much longer sliding life and smaller wear amount than the others. Time to scuffing was increased with increasing surface profile spacing. The size of wear particles was increased and the amount was decreased with increasing surface profile spacing. Wear volume and wear rate K were decreased with increasing surface profile spacing. And after sliding tests, surface cracks of inner parts of the wear track occurred scuffing were observed and compared the differences about each specimen having the different surface profile spacing.

• Tribology and Lubricants
• /
• 제38권3호
• /
• pp.115-119
• /
• 2022

This paper selected three kinds of grease with the same type but different consistency for the experiment. The purpose of the experiment is tested the effect of different consistency of grease on the wear of the gear surface. Different torque test groups were selected in the test, and the lubrication effect of different greases was tested in the test groups with the same torque. After each set of tests, the wear of the gear surfaces was observed and recorded. The data recorded in the experiment included the area of the wear area on the gear surface, the type of wear and the volume of wear. After the test, the gear surface roughness was measured. By calculating the wear volume, the effects of different concentrations of grease on the gear surface wear were compared. The experimental results show that under different stress conditions, the consistency of the grease has a great influence on the lubricating effect of the gear surface and the gear wear. Under the condition with low speed and high torque, different grease consistency affect the gear surface wear, the high consistency grease can reduce the wear of the gear surface, so that the gear can get better lubrication effect during the work.

• Tribology and Lubricants
• /
• 제36권4호
• /
• pp.232-243
• /
• 2020

It is essential to predict the amount of wear and surface parameters for a surface where relative motion occurs. In the asperity-based model for wear prediction, only the average contact pressure can be obtained. Hence, the accuracy of wear analysis is poor. In this study, DC-FFT is used to obtain the pressure of each node, and wear analysis is performed by considering the effect of the pressure gradient. The numerical surface generation method is used to create Gaussian, negatively skewed, and positively skewed surfaces for wear analysis. The spatial and height distributions of each surface are analyzed to confirm the effectiveness of the generated surface. Furthermore, wear analysis is performed using DC-FFT and Archard's wear formula. After analysis, it is confirmed that all peaks are removed and only valleys remain on the surface. The RMS roughness and Sk continue to decrease and Ku increases as the cycle progresses. It is observed that the surface parameters are significantly affected by the radius of curvature of the asperity. This analysis method is more accurate than the existing average wear and truncation models because the change in asperity shape during the wear process is reflected in detail.

• 소성∙가공
• /
• 제19권6호
• /
• pp.357-362
• /
• 2010

Dry sliding wear behavior of pure Fe and Cu which have BCC and FCC crystal structure, respectively, was investigated. The wear characteristics of the pure metals with different crystal structure were compared. Dry sliding wear tests were carried out using a pin-on-disk wear tester at various loads under the constant sliding speed condition of 0.15 m/s against a silica ball at room temperature. Sliding distance was fixed as 600 m for all wear tests. Wear rate of a specimen was calculated by dividing the weight loss of the specimen after the test by the specific gravity and sliding distance. Worn surfaces and wear debris were analyzed by SEM. The wear of both pure Fe and Cu proceeded with surface deformation, resulting in similar wear rates despite of their structure difference under the current test conditions. Wear rates of both metals were low if the surface deformation due to wear forms thick surface-deformation layer that is strain hardened beneath the wearing surface. The pure Cu specimens showed a lot of oxides on the worn surface when tested at low loads less than 5 N, which resulted in very low wear rate.

• 한국윤활학회:학술대회논문집
• /
• 한국윤활학회 1997년도 제25회 춘계학술대회
• /
• pp.80-88
• /
• 1997

Repeated sliding contact wear test was performed with copper specimens to obtain the relationship between wear and surface hardening. Wear surface and wear track section were observed by optical microscopy. Wear volume and micro-vikers hardness of sublayer below wear surface were obtained. These results suggested that wear mechanism depended on contact load than sliding velocity. Therefore wear mechanism was abrasive wear within critical contact load and adhesive wear over critical contact load. Wear rate increased with contact load, sliding distance but decreased with sliding velocity. Surface hardening increased with sliding velocity and sliding distance but decreased with contact load.

• Tribology and Lubricants
• /
• 제20권3호
• /
• pp.125-131
• /
• 2004

Nano-wear behavior of amorphous carbon films was studied by Atomic Force Microscopy. The a-C films are deposited on Si(100) substrate by DC magnetron sputtering method. The influences of different surface roughness on the nano-wear are investigated. Nano-wear tests were carried out using a very sharp diamond coated tip. Its spring constant was 1.6 N/m and radius of curvature was 110 nm. Normal force used in the wear tests ranged 0 to 400 nN. It was found that surface depression occurred during scratching because of plastic deformation and abrasive wear (cutting St ploughing). Wear depth increased linearly with normal force. Changing the surface roughness variables according to the bias pulse control, the less surface roughness decreased the wear depth. The thickness did not affect the wear resistance.

• 소성∙가공
• /
• 제32권5호
• /
• pp.247-254
• /
• 2023

This study conducted the wear tests on bending punches coated with PVD CrN and examined the surface quality of the product formed by each punch in the forming of uncoated TRIP1180 sheets. The study quantitatively estimated the surface quality of the product by measuring the roughness and imaging the product surface. The correlation between the punch wear depth and the product surface roughness was quantitatively analyzed. The results showed that before failure occurs, the product roughness was comparable with that of the as-received, and the product surface was smooth without scratches and defects. However, after failure, the punch wear is caused by fretting wear mechanism, and a punch whose coating is not completely peeled plows the product surface, resulting in severe scratches with grooves and ridges on the product surface. Severe wear on the punch surface caused by fretting wear can rapidly degrade the product surface quality as it is directly affected by the punch surface condition, and the product surface quality accurately reflects the punch wear condition.

• Tribology and Lubricants
• /
• 제20권1호
• /
• pp.7-13
• /
• 2004

High strength steels are widely used as tribo-materials in the field. Previous study revealed that for mild steel, the states of strain on the worn surface measured by X-ray diffraction has a good relationship with the state of wear. The objective of this study is to identify the relationship between the state of strain on the worn surface and the state of wear in high strength steels. Sliding wear tests were carried out using several hardened steels. X-ray diffraction tests were conducted to analyze the state of strain on the worn surface during wear. The experimental results indicated that the state of strain on worn surface in the hardened steel shows the same tendency as in the mild steel. It is clear that change of half value width on the worn surface as a function of sliding speeds is broadly similar in shape to wear characteristics curve and its magnitude has a good relationship with the wear rate at two different wear modes in the hardened steel.