• 한국안전학회지
• /
• 제19권2호
• /
• pp.125-129
• /
• 2004

수화열에 의한 균열은 대규모 콘크리트 타설시 흔하게 접하는 문제이며 이에 대한 해결은 시공이음을 만드는 것이다. 일반적인 방법으로 접합면을 할석으로 처리 하나 이 작업은 번거롭고 품질의 일관성을 유지하기 쉽지 않다. 본 연구에서는 접합면을 3가지 방법으로 처리하여 접합면의 전단강도를 비교하기 위한 18개의 시험체에 대한 push-out실험을 수행하였다. 할석으로 접합면을 만든 시험체에 비해 리브라스를 이용한 시험체가 전단저항에 월등한 성능을 보여 주었으며 그리고 리브라스를 절곡하여 만든 전단키가 전단저항을 향상시키는데 큰 역할을 하였다.

• 콘크리트학회논문집
• /
• 제17권3호
• /
• pp.481-485
• /
• 2005

The present study examines the distribution of calcium hydroxide, unhydrated cement grain and porosity at the steel-concrete interface. The formation of calcium hydroxide has been confirmed by microscopic analysis using BSE images containing the ITZ between the steel and concrete. It was found that calcium hydroxide does not form a layer on the steel surface, different from the hypothesis that has been available in investigating the corrosion of steel in concrete, ranging from 5 to $10\%$ within the steel surface. Moreover, the high level of porosity at the ITZ was observed, accounting for $30\%$, which may reduce the buffering capacity of cement hydration products against a local fall in the pH. These findings may imply that the mole of ($Cl^-$) :($OH^-$) in pore solution as chloride threshold level lead to wrong judgement or to a wide range of values.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2005년도 추계 학술논문 발표대회
• /
• pp.25-28
• /
• 2005

This study investigates the field application of surface insulation curing method, which combined double layer bubble sheet(DBS) and thick-curing-material(TCM) for cold weather concreting. According to the test, deck slab, curing only upper section with DBS and TCM, does not make big different temperature history with that, curing both upper and bottom section during daily average temperature 6.5t. It is concluded that combination of DBS and TCM in only upper section can be safely cured in early period of time during cold water concreting. The field test was carried out with this favourable data. The upper deck slab was insulated by combination of DBS and TCM, and the construction was surrounded by tent. in order to protect from outside wind. The test result shows that the lowest temperature of deck slab indicated 6$ ^{circ}C $. It demonstrated that this curing method can resist early frost and save construction cost in the side of management and saving labor cost, compared with previous method. In addition, the column specimen, combined both form and bubble board, exhibited favorable temperature history, due to internal hydration heat insulation effect.

• Bulletin of the Korean Chemical Society
• /
• 제13권3호
• /
• pp.230-235
• /
• 1992

The conformational analysis has been done for catecholamines (dopamine, norepinephrine, and epinephrine) in the cationic and di-anionic states. The species responsible for adsorption on silver metal surface is anionic deprotonated at hydroxyl groups of catechol moiety, i.e., di-anionic states of catecholamines. This was deduced from Fourier-transform Raman spectra of sodium salts of catecholamines. High resolution proton NMR (400 MHz) spectra of catecholamines in basic and neutral $D_2O$ solution show that the conformations of norepinephrine and epinephrine in the di-anionic states are preferred in gauche, but not for dopamine in the di-anionic state. However the energy difference between trans and gauche of catecholamines in the protonated cationic states is small enough to rotate freely through C-C bond in ethylamine moiety. The conformational calculations using an empirical potential function and the hydration shell model (a program CONBIO) show consistent with above experimental results. The calculations suggest that the species of catecholamines adsorbed on silver metal surface would be in favor of the gauche conformations.

• Journal of Korean Biological Nursing Science
• /
• 제2권2호
• /
• pp.20-37
• /
• 2000

The purpose of this study was to investigate the relationships between the differentials in life styles and their effect on the epidermal facial tissue in order to provide a basis for health professionals so that they might better be able to maintain and promote healthy skin care and further delay the premature ageing of the epidermal facial tissue. The subjects consisted of 145 females of various ages who visited skin care room in cerming health promoting behaviors(Park In sook's Profile) and questions on their behavioral practices pertaining to personal skin care were used. The investigation also ess of the four parts of the epidermal facial tissue studied. All data collected wee entered into the SAS program and analyzed for frequency, percentages, the utilized Pusan. The study dates ranged from May 1, 1998 to May 30, 1998. The methods used for this investigation were a questionnaire survey consisting of general objective questions. The questions con a "skin analyzer" to measured levels of moisturizing hydrated, facial oils, and roughnmean, t-test, ANOVA, and Pearson Correlation Coefficients. The results of this study were as follows ; 1. Epidermal facial oil was at its highest levels in the chin area with additional decreasing levels in the forehead and nose regions. The least regions were those of the cheeks. The highest levels of hydration on the other hand started with the forehead followed by the area of the chin, the cheeks and the lowest level of epidermal facial hydration was in the region of the nose. 2. The average score of the performance in the health promoting behaviors variable was 139.51. The variables with the highest degree of the performance were rest and sleeping(35.71). The lowest degree was hiegenic life(23.44). 3. The relationship health promoting behaviors and epidermal condition was not correlated with oil, hydration and roughness of the skin surface. 4. Skin care behavioral characteristics related to epidermal condition were washing style and temperature of washing water. 5. General characteristics related to epidermal condition were occupation, education level, acne and melasma. In conclusion, this study showed that several factors were significant in the behavior of skin care. Clear knowledge of both internal and external factors which affect the epidermal condition will help women to pursue active and appropriate practices in their health behaviors and skin care.

• 한국건설순환자원학회논문집
• /
• 제4권3호
• /
• pp.292-298
• /
• 2016

본 연구에서는 매스 매트 콘크리트에 있어, 상 하부를 구분하여 타설하는 실무조건을 고려하여, 상부 및 하부배합의 혼화재 종류와 치환율을 동일 및 달리하는 배합 조건 변화로부터 최적치를 도출한 다음, 실구조체에 적용하여 해석치와 실측치간을 비교하므로서, 혼화재를 활용한 매스콘크리트의 효율적인 수화열균열 저감방안을 제안하고자 하였다. 연구결과 먼저, 현장적용 전 사전검토를 위해 Midas gen을 이용하여 수화열 해석을 실시한 결과 상부는 OPC : FA = 85 : 15 배합, 하부는 OPC : FA : BS = 50 : 20 : 30 배합을 본 대상 구조물 매스 매트콘크리트의 최적배합으로결정하였다. 이를 적용한 실제 현장의 시험결과 슬럼프, 공기량 및 압축강도는 모두 목표범위를 만족하였다. 또한, 봄철 실제 현장의 매스 매트콘크리트의 온도특성으로 최적배합의 경우는 중심부의 최고 온도 약 $59^{\circ}C$, 표층부 온도 약 $49^{\circ}C$로 나타나, 약 $10^{\circ}C$의 온도차가 나타났으며, 수화열 해석결과 약 1.4의 균열지수를 나타내었다. 따라서, 실무를 고려한 매스 매트콘크리트의 경우 상 하부 타설 콘크리트간의 저발열 배합정도를 달리 고려하는 수화발열량차 공법적용은 침하균열 방지 및 수화열 균열제어에 효과적인 방법이 될 것으로 사료된다.

• 한국구조물진단유지관리공학회 논문집
• /
• 제14권5호
• /
• pp.153-160
• /
• 2010

고로슬래그 미분말을 순환골재 모르타르 및 콘크리트의 제조에 활용할 경우, 순환골재에서 용출된 $Ca(OH)_2$가 고로슬래그에 대한 자극제 역할을 수행하여 수화반응을 개선할 수 있을 것으로 판단되고 고로슬래그를 통해 알칼리 저감 효과를 얻을 것으로 예상되어 본 연구를 진행하게 되었다. 그 결과 고로슬래그 미분말을 혼입 사용한 순환 잔골재 모르타르는 재령 3일에서는 고로슬래그 혼입율에 따라 강도가 감소하는 결과를 나타냈다. 이는 고로슬래그의 수화반응이 일어나지 않았기 때문으로 판단되며 또한, 순환 잔골재 혼입률에 관계없이 고로슬래그 미분말의 혼입률이 증가함에 따라 재령 3일 측정한 수화활성도도 저하되는 것으로 나타났다. 재령 7일에서는 순환 잔골재에서 용출된 수산화칼슘($Ca(OH)_2$)이 자극제 역할을 수행하여 고로슬래그 미분말을 혼입한 배합의 압축강도 발현이 천연 잔골재를 사용한 모르타르보다 서서히 증가하는 결과를 보이기 시작하였으며 이로 인해 재령 7일 측정한 고로슬래그 미분말을 단계별로 혼입한 배합의 수화활성도가 고로슬래그를 혼입하지 않은 배합보다 높아지는 것으로 나타났다. 재령 28일에서는 고로슬래그 미분말 혼입률 30% 배합에서는 고로슬래그의 수화반응으로 인해 천연 잔골재를 사용한 배합보다 높은 압축강도를 보이기 시작하였으며 이때 측정한 수화활성도는 천연 잔골재를 사용한 배합과 특별한 차이를 보이지 않았으며, 이는 지속적으로 수산화칼슘($Ca(OH)_2$)이 공급되지 못하였기 때문으로 판단된다.

• 대한토목학회논문집
• /
• 제41권4호
• /
• pp.357-364
• /
• 2021

본 연구에서는 서로 다른 종류의 TiO₂ 혼입이 시멘트 페이스트의 수화특성 및 질소산화물 제거성능에 미치는 영향에 대해 조사하였다. 상용 제품인 P-25와 NP-400, 폐수 슬러지에서 제조된 GST, 총 세 종류의 TiO₂를 시멘트 무게대비 0, 5, 10, 20 % 첨가하여 시멘트 페이스트의 수화특성 및 질소산화물 제거성능을 분석하였다. 미소수화열 측정결과 TiO₂의 혼입은 시멘트 페이스트의 초기 수화반응에 큰 영향을 미치는 것이 확인되었으며, P-25, NP-400, GST 순으로 더 높은 누적 발열량을 나타내었다. 이로 인해 Rietveld 분석결과 TiO₂ 혼입 샘플에서 더 많은 C-S-H의 생성량이 관찰되었으며, 이는 TiO₂ 혼입 시멘트 페이스트의 28일 압축강도 증가에 영향을 미친 것으로 판단된다. SEM/EDS 분석결과 P-25, GST, NP-400 순으로 페이스트 샘플 표면에 더 많은 Ti 원소의 함량이 관찰되었지만, NO_x 제거 성능은 P-25, NP-400, GST 순으로 우수한 것으로 확인되었다.

• 한국건설순환자원학회논문집
• /
• 제10권3호
• /
• pp.204-210
• /
• 2022

시멘트는 건설산업 분야에서 주된 이산화탄소의 원인으로 지목되고 있다. 시멘트의 제조과정에서 나오는 이산화탄소를 저감하기 위해 시멘트 대체재로 산업부산물인 고로슬래그를 사용하는 연구가 진행 중이다. 고로슬래그를 시멘트 대체재로 사용할 경우 장기강도 증진과 내화학성 향상 등의 장점을 지니고있다. 하지만 고로슬래그는 초기강도 저하의 문제점을 지니고 있다. 이는 고로슬래그의 생산과정에서 만들어지는 표면의 불투성 피막이 원인이다. 생성된 피막은 알칼리 환경에서 파괴되는 것으로 알려져 있으며, 이를 바탕으로 선행연구에서는 다양한 알칼리 자극제를 사용한 해결방안을 제시해왔다. 알칼리 자극제는 강알칼리성 물질이기 때문에 위험성이 존재하며, 비용이 고가인 단점을 가지고 있다. 본 연구에서는 고로슬래그의 초기 수화반응성을 향상시켜 고로슬래그를 치환한 모르타르의 초기강도를 확보함과 동시에 탄산화 저항성 증가 여부를 확인하기 위한 실험을 진행하였다. 실험결과, 알칼리 수를 활용한 모르타르가 일반 배합수를 사용한 모르타르에 비해 높은 강도발현을 보였으며, 내부에 더 많은 수화생성물이 있음을 확인했다. 또한, 알칼리 수를 배합수로 활용한 모르타르가 탄산화 저항성이 높은 것을 확인하였다.

• 한국세라믹학회지
• /
• 제24권4호
• /
• pp.335-342
• /
• 1987

There were several numbers of studies on chemically strengthening glass. Most of them were strengthened in molten salt bath below transformation range of glass. Apart from them, this study used solution hydration technique by Autoclave. After determining proper concentration of AgNO3 salt solution, experimental condition varied from 4hrs to 16hrs at relatively low temperature (180, 200, 220$^{\circ}C$). The results showed that the Soda-Lime-Silica glass could be strengthened by diffusion mechanism without influence of water above 15% salt solution. Because of Ag+ ion penetration in glass surface, yellow color appeared and decreased transmittance at visible range. Modulus of rupture was increased with the amount of exchange and brittleness was decreased.