• 대한금속재료학회지
• /
• 제50권5호
• /
• pp.395-400
• /
• 2012

In this study, we have investigated the surface morphology of hydroxyapatite (HA) coated Ti alloy surface using pulsed laser plating. The HA (tooth ash) films were grown by pulsed KrF excimer laser, film surfaces were analyzed for topology, chemical composition, crystal structure and electrochemical behavior. The Ti-6Al-4V alloy showed ${\alpha}$ and ${\beta}$ phase, Cp-Ti showed ${\alpha}$ phase and the HA coated surface showed HA and Ti alloy peaks. The HA coating layer was formed with $1-2{\mu}m$ droplets and grain-like particles, particles which were smaller than the HA target particle, and the composition of the HA coatings were composed of Ca and P. From the electrochemical test, the pitting potential (1580 mV) of HA coated Ti-6Al-4V alloy was higher than those of Cp-Ti (1060 mV) and HA coated Cp-Ti (1350 mV). The HA coated samples showed a lower current density than non-HA coated samples, whereas, the polarization resistance of HA coated samples showed a high value compared to non-HA coated samples.

• Corrosion Science and Technology
• /
• 제23권2호
• /
• pp.139-144
• /
• 2024

Recently, due to the rapid spread and continuation of COVID-19, customer demand for health and hygiene has increased, requiring the development of new products that express antiviral and antibacterial properties. In particular, viruses are much smaller in size than bacteria and have a fast propagation speed, making it difficult to kill. POSCO has developed eco-friendly PCM color coated steel sheets with excellent antiviral properties by introducing inorganic composite materials to the color coating layer on the surface of Zn-Al-Mg alloy plated steels. The virus is not only destroyed by adsorption of metal ions released from the surface of the coating film, but is also further promoted by the generation of reactive oxygen species by the reaction of metal ions and moisture. As a result of evaluating the developed products under the International Standard Evaluation Act, the microbicidal activity was 99.9% for viruses, and 99.99% for bacteria and 0% fungi. In particular, excellent results were also shown in the durability evaluation for life cycle of the product. The developed product was applied as a wall of school classrooms and toilets and ducts for building air conditioning, resulting in excellent results. Developed products are being applied for construction and home appliances to practice POSCO's corporate citizenship.

• 대한치과보철학회지
• /
• 제36권1호
• /
• pp.26-49
• /
• 1998

The purpose of this study was to confirm the formation of hybrid layer and resin tags in dentin tissue and the possibility of bonding between luting cements used for the prosthesis and the resinous surface coated with resin bonding agents to prevent the dentin hypersensitivity after abutment preparation. Some resin bonding agents, which may have the possibility of bonding with polyacrylic acid as a liquid ingredient of polycarboxylate and glass ionomer cements, were selected. All-Blond desensitizer containing NTG-GMA and BPDM, Scotch-Bond Multipurpose plus containing HEMA, and XR-bond containing organophosphate were selected as a coating agent. Dental cements were zinc phosphate, polycarboxylate, and glass ionomer cement. After the exposed dentin surface of premolars was ethced with 10% phosphoric acid and coated with resin bonding agents, the morphology of treated surfaces and the resin tags and hybrid layers on sectioned surfaces were observed by SEM. Shear bond strength between the resin bonding agents and 3 kinds of cements was measured 24 hours after bonding. On the debonded surfaces of the shear bond strength tested specimens, the cement tags and the bonding sites between the resin materials and cements were examined by SEM. Following conclusions were drawn : 1. Coating of dentin with resin bonding agents had no effect on the shear bond strength of zinc phosphate cement. 2. Both of polycarboxylate and glass ionomer cements showed the increased shear bond strength by the dentinal coating with Scotch-Bond Multipurpose plus containing HEMA. However, in the case of dentinal coating with some agents containing NTG-GMA and BPDM or organophosphate, polycarboxylate cement exhibited the lowered shear bond strength, and glass ionomer cement showed the unchanged shear bond strength. 3. Complete obstructions of dentinal tubules were observed on the dentin coated with All-Bond desensitizer or XR-bond, but distinct shape of the orifices of dentinal tubules was observed consistently on the dentin coated with Scotch-Bond Multipurpose plus. 4. The hybrid layer was thickest on the dentin coated with All-Bond desensitizer, and the length of resin tags was longest on the dentin coated with Scotch-Bond Multipurpose plus. 3. On the debonded specimens which had been bonded with polycarboxylate cement or glass ionomer cement after coating with Scotch-Bond Multipurpose plus, the cement tags and the bonding sites between the resinous surface and the cements could be examined.

• 한국재료학회지
• /
• 제10권4호
• /
• pp.295-300
• /
• 2000

반응성 이온 식각과 산화막을 이용한 첨예화 공정을 통하여 균일한 실리콘 팁 어레이를 제작한 후, 그 위에 Pd을 증착하여, Pd 코팅이 전계 방출특성에 미치는 영향에 대해 조사하였다. 어레이에 존재하는 표면 산화막을 제거한 후의 전계 방출 특성의 향상은 매우 작았으나, $100{\AA}$의 Pd을 코팅한 후에는 30V의 구동전압이 감소하는 등 전계 방출특성이 크게 향상되었다. 이는 Pd 코팅에 의해 팁의 표면 거칠기가 증가하고, 전자가 방출되는 팁 끝부분의 반경이 감소하였기 때문이다. 한편 Pd을 코팅한 에미터는 높은 방출 전류 영역에서 우수한 동작 안전성을 보였다. 이를 통하여 Pd이 코팅된 실리콘 에미터가 고온에서의 동작과 표면안정성에서 우수한 특성을 보임을 알 수 있었다.

• 대한기계학회논문집A
• /
• 제22권3호
• /
• pp.529-539
• /
• 1998

A quantitative study of impact damage of ${Al_2}}O_3}-TiO_2$ plasma coated soda-lime glasses was carried out and compared with that of the uncoated smooth glass specimen. The shape of cracks by the impact of steel ball was observed by stereo-microscope and the decrease of the bending strength due to the impact of steel ball was measured through the 4-point bending test. At the low velocity, cone cracks were occurred. As the impact velocity increases, initial lateral cracks were propagated on the slanting surface of a cone crack, and radial cracks were generated at the crushed site. When the impact velocity of steel ball exceeds the critical velocity, the contact site of specimen was crushed due to plastic deformation and then radial and lateral cracks were largely grown. Crack length of coated specimens was smaller than that of uncoated smooth specimen due to the effect of coating layer on the substrate surface. According to impact velocity, the bending strength of coated specimens had no significant difference, compared with that of the uncoated smooth specimen. But this represents that the bending strength of coated specimens was increased, considering the effect of sand blasting damage which was performed to increase the adhesion force of coating layer.

• 전기학회논문지
• /
• 제67권10호
• /
• pp.1375-1381
• /
• 2018

In this paper, we studied coatings of the DLC thin film for improving loosening torque of dental implant screw. We used a filtered arc ion plating process which can realize the most dense DLC layer by coating the DLC thin film on the surface of the dental abutment screw. It showed both hardness comparable to diamond and low friction coefficient similar to graphite, and to improve the loosening phenomenon by increasing the screw tightening force Cr/CrN, Ti/TiN or Ti/TiN/Cr/CrN buffer layers were deposited for 5 to 10 minutes to improve the adhesion of the DLC thin film to the surface of the Ti (Gr.5), and then the DLC thin film was coated for about 15 minutes. As a result, the Cr/CrN buffer layer exhibited the highest hardness of 29.7 GPa, the adhesion of 18.62N on average, and a very low coefficient of friction of less than 0.2 as a whole. And we measured loosening torque after one million times with masticatory movement simulator. As a result, the values of the coated screw loosening torque were clearly higher than those of the uncoated screw. From this, it was found that the DLC coating was effective methods improving the loosening torque. In addition, it was confirmed that the cytotoxicity test and cell adhesion test showed high biocompatibility.

• 한국표면공학회지
• /
• 제55권6호
• /
• pp.368-375
• /
• 2022

YSZ (Yttria Stabilized Zirconia) is used as a thermal barrier coating material for gas turbines due to its low thermal conductivity and high fracture toughness. However, the operating temperature of the gas turbine is rising according to the market demand, and the problem that the coating layer of YSZ is peeled off due to the volume change due to the phase transformation at a high temperature of 1400℃ or higher is emerging. To solve this problem, various studies have been carried out to have phase stability, low thermal conductivity, and high fracture toughness in a high temperature environment of 1400℃ or higher by doping trivalent and tetravalent oxides to YSZ. In this study, the monoclinic phase formation behavior and crystallinity were comparatively analyzed according to the total doping amount of oxides by controlling the doping amounts of Sc₂O₃ and Gd₂O₃, which are trivalent oxides, and TiO₂, which are tetravalent oxides, in YSZ. Through comparative analysis of monoclinic phase formation and crystallinity, the thermal conductivity of the thermal barrier coating layer according to the amount of doping was predicted.

• 공업화학
• /
• 제29권2호
• /
• pp.196-200
• /
• 2018

본 연구에서는 복합 수소분리막 중간층의 pin hole, crack 및 defect를 최소화하기 위하여 powder type과 sol type의 금속산화물을 이용하여 복합화하였다. 중간층의 표면 형상과 투과 특성은 주사전자현미경(SEM) 분석과 $N_2$ 투과도 테스트를 통해 평가하였으며, 제조한 수소분리막의 성능평가를 위해 $N_2$와 $H_2$를 이용하여 단일가스 투과 테스트를 수행하였다. Powder type과 sol type의 금속산화물을 각각 이용하여 중간층을 적층한 결과 sol type 금속산화물을 이용하여 적층한 중간층의 표면 조도가 매우 낮았으며, 특히 $TiO_2$ sol로 형성된 중간층의 pin-hole, crack 및 defect가 현저히 감소하였다. Powder와 sol을 복합화하여 적층한 중간층은 sol로 형성된 중간층과 거의 유사한 특성을 보였으며, 이를 기반으로 제조한 수소분리막은 1 bar의 압력구배, 672 K의 온도에서 약 $0.32mol/m^2s$의 수소 투과도를 나타내었으며, 선택도는 약 10,890 이상으로 측정되었다.

• 한국자기학회지
• /
• 제17권6호
• /
• pp.226-231
• /
• 2007

나노결정질 비정질 리본 표면에 졸-겔법에 의해 제조된 $TiO_2$ 및 $SiO_2$ 졸을 딥 코팅법을 이용하여 절연막을 형성시킴으로써 전기 비저항의 증가를 통한 고주파 손실을 제어하고자 하였다. 졸-겔법에 의한 슬러리 제조에서, 금속 알콕사이드의 혼합조건 및 절연층 형성용 슬러리의 제조조건을 확립하였고, 비정질 합금 리본 표면에 균일하고 우수한 점착력을 가지는 절연층을 형성시킬 수 있었다. 그리고 표면 절연층이 형성된 나노 결정질 합금 재료를 이용하여 제조한 자심재료는 전기 비저항의 증가로 인해 코어 손실을 약 40% 이상 감소시킬 수 있었다. 또한 표면 절연층을 형성시킨 자심재료를 이용하여 제조한 비접촉식 커플러는 코어 손실의 감소로 인해 삽입손실의 감소 효과가 나타났으며, 삽입손실의 감소효과는 주파수 증가에 따라 증가하였다.

• 한국초전도ㆍ저온공학회논문지
• /
• 제11권1호
• /
• pp.1-4
• /
• 2009

Mechanical and electrical properties of silver stabilizer layer of coated conductor, which as prepared with nano silver paste as starting materials, have been investigated, Nano silver paste was coated on a YBCO film by dip coating process at a diping speed of 20m/min. Coated film was dried in air and heat treated at $400{\sim}700^{\circ}C$ in an oxygen atmosphere. Adhesion strength between YBCO and silver layer was measured by a tape est(ASTM D 3359). Hardness and electrical conductivity of the samples were measured by pencil hardness test (ASTM D 3363) and volume resistance test by LORESTA-GP (MITSHUBISHD, respectively. The sample heat-treated at $500^{\circ}C$ showed poor adhesion 1B, but samples heat treated at higher than $600^{\circ}C$ showed enhanced adhesion of 5B. The silver layer heat-treated at $700^{\circ}C$ showed the high hardness value larger than 9 H, low volume resistance, surface resistance value as well as superior current carrying capacity compared to sputtered silver. SEM observations showed that a dense silver layer was formed with a thickness of about $2{\mu}m$. Dip coated silver layer prepared by using nano silver paste showed superior electrical and mechanical characteristics.