• 열처리공학회지
• /
• 제21권1호
• /
• pp.10-19
• /
• 2008

To investigate the effect of ultrasonic nano-crystalline surface modification (UNSM) treatment on rolling contact fatigue and residual stress properties of bearing steels, this paper carried out a rolling contact fatigue test, measured residual stress and retained austenite, performed a wear test, observed microstructure, measured micro hardness, and analyzed surface topology. After the UNSM treatment, it was found that the surface became minute by over $100{\mu}m$. The micro surface hardness was changed from Hv730~740 of base material to Hv850~880 with about 20% improvement, and hardening depth was about 1.3 mm. The compressive residual stress was measured as high as -700~-900 MPa, and the quantity of retained austenite was reduced to 27% from 34%. The polymet RCF-6 ball type rolling contact fatigue test showed over 4 times longer fatigue lifetime after the UNSM treatment under 551 kgf load and 8,000 rpm. In addition, this paper observed the samples, which went through the rolling contact fatigue test, with OM and SEM, and it was found that the samples had a spalling phenomenon (the race way is decentralized) after the UNSM treatment. However, before the treatment, the samples had excessive spalling and complete exploration. Comparison of the test samples before and after the UNSM treatment showed a big difference in the fatigue lifetime, which seems to result from the complicated effects of micro particles, compressive residual stress, retained austenite, and surface topology.

• Journal of Welding and Joining
• /
• 제33권1호
• /
• pp.24-29
• /
• 2015

Residual stresses arising from the materials processing such as welding and joining affect significantly the structural integrity depending on the external loading condition. The quantitative measurement of the residual stresses is of great importance in order to characterize the effects of the residual stresses on the structural safety. In this paper, we introduce a newly devised destructive technique, the contour method (CM), which is applied for the measurements of the residual stress distributions through the thickness of a 80 mm thick steel weld. Residual stresses are evaluated from the contour, which is the normal displacement on a cut surface produced by the relaxation of residual stresses, using a finite element model. The CM provides a two-dimensional map of the residual stresses normal to the cut surface. The CM developed in the present study was validated in comparison with the residual stress distribution determined by a well-established neutron-diffraction residual stress instrument (RSI) instrumented in HANARO neutron research reactor.

• 대한기계학회논문집A
• /
• 제29권2호
• /
• pp.341-349
• /
• 2005

Damage often occurs on the surface of railway wheel by wheel-rail contact fatigue. It should be removed before reaching wheel failure, because wheel failure can cause derailment with loss of life and property. The increase or decrease of the contact fatigue life by the metal removal of the contact surface were shown by many researchers, but it has not explained precisely why fatigue life increases or decreases. In this study, the effect of metal removal depth on the contact fatigue life for railway wheel has been evaluated by applying finite element analysis. It has been revealed that the residual stress and the plastic flow are the main factors determining the fatigue life. The railway wheel has the initial residual stress formed during the manufacturing process, and the residual stress is changed by thermal stress induced by braking. It has been found that the initial residual stress determines the amount of metal removal depth. Also, the effects of the initial residual stress and metal removal on the contact fatigue lift has been estimated, and an equation is proposed to decide the optimal metal removal depth for maximizing the contact fatigue life.

• 대한기계학회논문집A
• /
• 제29권10호
• /
• pp.1384-1391
• /
• 2005

Damage often occurs on the surface of railway wheels due to wheel-rail contact fatigue. It should be removed before reaching wheel failure, because wheel failure can cause derailment with loss of life and property. The increase or decrease of the contact fatigue lift by the metal removal of the contact surface were investigated by many researchers, but they have not considered initial residual stress and traction force. The railway wheel has the initial residual stress formed during the manufacturing process, and the residual stress is changed by thermal stress induced by braking. The traction force and residual stress are operated on wheels of locomotive and electric motor vehicle. In this study, the effect of metal removal depth on the contact fatigue life for a railway wheel has been evaluated by applying lolling contact fatigue test. The effect of the traction force and metal removal on the contact fatigue life has been estimated by finite element analysis. It has been found that the initial residual stress determines the amount of metal removal depth if the traction coefficient is less than 0.15. If the traction coefficient is greater than 0.2, however, the amount of metal removal depth is independent on the intial residual stress.

• 대한기계학회논문집A
• /
• 제28권6호
• /
• pp.732-738
• /
• 2004

One of the main degradation mechanisms in steam generator tubes is stress corrosion cracking induced by residual stress. The resulting damages can cause tube bursting or leakage of the primary water which contains radioactivity. Shot peening technique has been used to prevent stress corrosion crack growth in steam generator tubes. In order to investigate the shot peening effect on stress corrosion cracking stress intensity factors are calculated for the semi-elliptical surface crack which is located in residual stress region. The residual stress distribution in steam generator tubes is obtained from the simple model proposed by Frederick et al.

• 한국표면공학회지
• /
• 제42권5호
• /
• pp.191-196
• /
• 2009

Nanocrystalline Cu thin films were electrodeposited from sulfate baths and investigated systematically the influences of $Cu^{2+}$ concentration and additives on current efficiency, residual stress, surface morphology, and XRD patterns of electrodeposited Cu film. Current efficiency was nearly 100% at from 0.2M to 1.0 M $Cu^{2+}$ concentration. but it was linearly increased with $Cu^{2+}$ concentration at less than 0.2M. The residual stress was observed in range of 7.9 to 18.4 MPa and tensile stress mode. Dendritic and powdered form was obtained at below 0.1 M. As increased with $Cu^{2+}$ concentration in solution, the main peak in the XRD pattern shifted (111) and (220) from (200). In the other hand, all about 100% current efficiency observed in all additive concentration systems, and residual stress observed in range of 20.4 to 26.3 MPa tensile stress. The condition 5(Ultra make-up - 10 ml/l, Ulta A - 0.5ml/l, Ultr B - 0.5 ml/l) was good surface morphology, and fcc(111) peak in XRD patterns increased with increasing additive concentration.

• 열처리공학회지
• /
• 제2권2호
• /
• pp.27-32
• /
• 1989

The effect of quenchant temperature on the surface residual stress was studied for AISI 8620 steel. Specimens were carburized at $900^{\circ}C$ in all case type furnace using a gas-base atmosphere of methanol cracked and liquefied petroleum gas, and then subjected to single reheat quenchant in oil or salt bath in the temperature range of $60^{\circ}C$ to $300^{\circ}C$. After carburizing and reheat Quenching, residual stress was measured by the hole drilling method. Experimental results showed that the surface residual stress was increased as the quenchant temperature was raised. This is in contrast to the fact that the formation of phase of low transformation strain such as bainite results in lower surface compressive stress. The greater compressive stress observed in specimens Quenched at higher temperature may be attributed to the shifting of the transformation start point farther from the surface, as was reported in other carburizing steels.

• 한국정밀공학회:학술대회논문집
• /
• 한국정밀공학회 2002년도 춘계학술대회 논문집
• /
• pp.820-823
• /
• 2002

MEMS structures Generally have been fabricated using surface-machining, but the interface failure between silicon substrate and evaporated thin film frequently takes place due to difference of linear coefficient of thermal expansion. Therefore this paper studied the effect of the residual stress caused by variable external loads. This study did not analyzed accurate quantity of the residual stress but trend for the effect of residual stress. Several specimens were fabricated using other material(Al, Au and Cu) and thermal load was applied. The residual stress was measured by nano-indentation using AFM. The results showed the existence of the residual stress due to thermal load. The indentation area of the thermal loaded thin film reduced about 3.5% comparing with the virgin thin film caused by residual stress. The finite element analysis results are similar to indentation test.

• 한국표면공학회지
• /
• 제36권6호
• /
• pp.475-479
• /
• 2003

In this study, to investigate the effects of 2-step shot peening at the surface of spring steel, tests are conducted on spring steel and shot peened specimens. Various tests are accomplished to evaluate mechanical properties influenced by shot peening process, and fatigue tests are also performed to evaluate the improvement of fatigue strength. And then the residual stresses are examined. The mechanical properties of material did not change so much by shot peening. However, the fatigue strength of notched specimen remarkably increased. In the case of 1-step shot peening, fatigue strength increased by about 20％ than unpeened specimen. Especially, in the case of 2-step shot peening, fatigue strength increased by about 40％, because the residual compressive stress at surface was higher than that of 1-step shot peened specimen. The fatigue strength and life are closely related to the value and position of maximum compressive residual stress by shot peening.

• Journal of Welding and Joining
• /
• 제30권6호
• /
• pp.74-79
• /
• 2012

It depends on the joint configuration, dimensions and constraints of the joint whether the residual stress at the root of single-sided butt weld is tensile or not. Therefore, recommendation is generally made that high R ratio should be used in the fatigue test of welded joint in order to prevent excessively long life caused by compressive residual stress. In this research, the residual stress profile in butt weld joint was obtained through compliance method, using successive extension of a slot and measurement of the variation of strain during the slot extension. The residual stress profile was firstly assumed to be the linear summation of Legendre polynomials up to 9th order excluding 0th and 1st order. Strain variation on the surface was measured while the slot was being extended by cutting to find out the 8 unknown coefficients of each polynomial term. The cut was made by the electric discharge machine. It was concluded that the residual stress near the surface is positive valued, however, it turned into the negative value as soon as it passed through 2 or 3 mm of the depth.