• Journal of Welding and Joining
• /
• v.14 no.2
• /
• pp.90-95
• /
• 1996

In order to investigate characteristics of surface fatigue crack propagation from a pit shaped surface defect which frequently exists around welded joints, SS400 steel with thickness of 12mm, which has been generally used for structure members, was welded with submerged-arc butt type and machined for both surface. An initial surface defect of pit shape with the aspect ratio of 2 was made on the specimen. The initial defect was located at 5 different zones over the weldment : weld metal zone, boundary between weld metal and HAZ, HAZ, boundary between HAZ and base metal. Characteristics of surface fatigue crack propagation from the defect on each region under the same loading condition were investigated and compared.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.6 no.3
• /
• pp.232-238
• /
• 1982

The behavior of corner crack propagation by unidirectional plane bending fatigue was investigated in the butt welded joints of SS41 and SM50 steel plates including an edge through-thickness notch. The properties of fatigue crack propagation were inspected in the weld metal, heat-affected zone, and base metal of the welded joints. Main results obtained are as follows; (1) When a plate with an edge through-thickness notch is loaded by plane bending fatigue in indirection, the 2 variant corner cracks on the upper and lower edge of the plate are initiated and propagated respectively from the notch. (2) In case of a specimen containing a corner crack, it is more reasonable to estimate the crack propagation rate by area of fracture surface than by crack surface length. (3) The rate of fatigue crack propagation becomes faster in the following order; weld metal, heat-affected zone, and base metal. (4) The specimen including reinforcement shape is rapidly failed throughout bond due to effect of its shape when the repeated load exceeds a certain cycle.

• Transactions of Materials Processing
• /
• v.29 no.1
• /
• pp.20-26
• /
• 2020

In the design of the metal forming processes, various types of ductile fracture criteria are used to predict crack initiation and to fabricate metallic products without any defects. However, the quantitative measurement method for determination of crack initiation is insufficient. It is very difficult to detect crack initiation in ductile metals with excellent deformability because no significant load drop is observed due to crack generation. In this study, the applicability of acoustic emission sensors, which are commonly used in facility diagnostics, to measure crack initiation during the metal forming process was analyzed. Cylindrical notch specimens were designed using the finite element method to induce a premature crack on the surface of pre heat-treated steel (ESW90) material. In addition, specimens with various notch angles and heights were prepared and compression tests were carried out. During the compression tests, acoustic emission signal on the dies and images of the surface of the notch specimen were recorded using an optical camera in real time. The experimental results revealed that the acoustic emission sensor can be used to detect crack initiation in ductile metals due to severe plastic deformation.

• Journal of Advanced Marine Engineering and Technology
• /
• v.10 no.1
• /
• pp.65-73
• /
• 1986

Surface fatigue crack propagation tests by plane bending fatigue were conducted on the welding specimens of an aluminium alloy, A5083-0, having an edge through thickness notch to study the fatigue crack growth characteristics. Moreover, the experiments were performed in order to clarify the fatigue crack initiation and growth. The properties of fatigue crack growth were quantitatively inspected in welded metal, heat-affected zone and base metal of the welding specimens. The main results obtained are summarized as follows: 1. It is found that the hardness distributions of A5083-0 aluminium alloy weldments are quite different with those of steel material weldments, so that the hardness distribution becomes lower in the following order: base metal, heat-affected zone and weld metal. 2. It is observed that the grain size of this specimen weldment appears to be almost equal to the base metal, when TIC welding method is adopted. 3. In a surface fatigue crack initiation and growth, the fatigue crack does not begin by opening-closing mechanism until hardening is saturated at the crack tip. 4. The fatigue crack growth characteristics of A5083-0 alluminium alloy weldments can be concluded.$${\frac{da}{dn}}=C({\Delta}K)^n=3.8{\times}10^{-9}{({\frac}{1}{2}{\Delta}S_t{\sqrt{{\pi}a}})}^{2.4}$$

• Journal of the Korean Society of Fisheries and Ocean Technology
• /
• v.25 no.2
• /
• pp.87-104
• /
• 1989

Recently, with the tendency of more lightening, high-strength and high-speed in the marine industries such as marine structures, ships and chemical plants, the use of the aluminium Alloy is rapidly enlarge and there occurs much interest in the study of corrosion fatigue crack characteristics. In this paper, the initiation of surface crack and the propagation characteristics on the base metal and weld zone of 5086-H116 Aluminium Alloy Plate which is one of the Al-Mg serious alloy(A5000serious) used most when building the special vessels, were investigated by the plane bending corrosion fatigue under the environments of marine, air and applying cathodic protection. The effects of various specific resistances on the initiation, propagation behavior of corrosion fatigue crack and corrosion fatigue life in the base metal and heat affected zone were examined and its corrosion sensitivity was quantitatively obtained. The effects of corrosion on the crack depth in relation to the uniform surface crack length were also investigated. Also, the structural, mechanical and electro-chemical characteristics of the metal at the weld zone were inspected to verify the reasons of crack propagation behavior in the corrosion fatigue fracture. In addition, the effect of cathodic protection in the fracture surface of weld zone was examined fractographically by Scanning Electron Microscope(S.E.M.). The main results obtained are as follows; (1) The initial corrosion fatigue crack sensitibity under specific resistance of 25Ω.cm% show 2.22 in the base metal and 19.6 in the HEZ, and the sensitivity decreases as specific resistance increases (2) By removing reinforcement of weldment, the initiation and propagation of corrosion crack in the HAZ are delayed, and corrosion fatigue life increases. (3) As specific resistance decreases, the sensitivity difference of corrosion fatigue life in the base metal and HAZ is more susceptible than that of intial corrosion fatigue crack. (4) Experimental constant, m(Paris' rule) in the marine environment is in the range of about 3.69 to 4.26, and as specific resistance increases, thje magnitude of experimental constant, also increases and the effect by corrosion decreases. (5) Comparing surface crack length with crack depth, the crack depth toward the thickness of specimen in air is more deeply propagated than that in corrosion environment. (6) The propagation particulars of corrosion fatigue crack for HAZ under initial stress intensity factor range of $\Delta$k sub(li) =27.2kgf.mm super(-3/2) and stress ratio of R=0 shows the retardative phenomenon of crack propagation by the plastic deformation at crack tip. (7) Number of stress cycles to corrosion fatigue crack initiation of the base metal and the welding heat affected zone are delayed by the cathodic protection under the natural sea water. The cathodic protection effect for corrosion fatigue crack initiation is eminent when the protection potential is -1100 mV(SCE). (8) When the protection potential E=-1100 mV(SCE), the corrosion fatigue crack propagation of welding heat affected zone is more rapid than that of the case without protection, because of the microfissure caused by welding heat cycle.

• Journal of Ocean Engineering and Technology
• /
• v.1 no.1
• /
• pp.111-119
• /
• 1987

The corrosion fatigue crack propagation characteristics of SS41 steel in 3.5% NaCl solution have been evaluated for loading frequencies of 1Hz and 0.2Hz. A sine wave loading profile was used for fatigue testing. Each test was carried out at a constant stress ratio, R(0.1). The main results are summarized as follows; 1. Fatigue crack propagation rate was higher in 3.5% NaCl solution than in air, higher in the base metal than in the weld metal, and higher at f =0.2Hz than at f =1Hz. 2. The crack closure level of the base metal was not influenced by cyclic frequencies, but that of the weld metal was much influenced. 3. When the crack closure effect was eliminated in the evaluation of crack propagation characteristics by using $\Delta K_{eff}$, the envirommental influence was distinctly observed. At the base metal, crack propagation rate was enhanced by the hydrogen embrittlement, and the weld metal was reduced by the crac closure. 4. There was clearly observed hydrogen embrittlement and severely corroded aspect at fracture surface of lower frequency than that of higher frequency, and at that of base metal than that of the weld metal.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.19 no.5
• /
• pp.1202-1210
• /
• 1995

Aiming at nondestructive evaluation of defect with high accuracy and resolution, ICFPD(Induced Current Focusing Potential Drop) technique was newly developed. This technique can be applied for locating and sizing of defects in components with not only simple shape such as plain surface but also more complex shape and geometry such as curved surface and dissimilar joing. This paper describes the principle of ICFPD technique and also the results of 2-dimensional surface crack in ferromagnetic metal(A508 Cl. III steel) and paramagnetic metal (pure aluminum and stainless 304 steel) measured by this technique. Results are that surface defects in each specimen are detected with the difference of potential drop, and potential drops are distributed a similar shape for each metal and each depth. The normalized potential drop ( $V_{\delta}$2/$^{t}$ / $V_{{\delta} 2}$$^{-1}$) max. in the vicinity of defect is varied with the depth of defect. Therefore, ICFPD technique can be used for the evaluation of defect not only in ferromagnetic metal but also in paramagnetic steel..

• Proceedings of the KWS Conference
• /
• 1995.10a
• /
• pp.214-217
• /
• 1995

In order to investigate characteristics of surface fatigue crack propagation from a pit shaped surface defect which frequently exists near weld joints, SS400 steel with thickness of 12mm, which generally used for structure members, was submerged-arc welded with butt type and machined for both surface. The weld joints were devided into 5 regions, weld metal, boundary between heat affected zone (HAZ), HAZ, boundary between HAZ and base metal, and base metal. Specimens from each region were machined for a pit shaped initial surface defect with aspect ratio of 2. characteristics of surface fatigue crack por pagation from the defect under the same loading condition were compared and discussed.

• Journal of Power System Engineering
• /
• v.7 no.2
• /
• pp.66-72
• /
• 2003

Recently, the steel parts used at the aerospace and automobile industries are required to be used light weight parts. Therefore, used material, steel have to be a high stress, which is an indispensable condition in this field. At the consideration of parts design, high hardness of the lightweight parts have an benefit of saving fuel and material. A high stress of metal has a point of difference according to the shape of design, external cyclic load and condition of vibration. A crack generates on the surface of metal or under yield stress by defect of inner metal defect or surface defect and slowly, this crack grow stable growth. Finally, rapidity failure phenomena is happen. Fatigue failure_phenomena, which happen in metal, bring on danger in human life and property therefor, anti-fatigue failure technology take an important part of current industries Currently, the shot peening is used for removing the defect from the surface of steel and improving the fatigue strength on surface. Therefore, this paper investigated the effect on frcature toughness using shot peening which is improve the resistance of crack growth and crack expansion rate by fatigue that make a compressive residual stress on surface.

• Journal of the Korean Society of Fisheries and Ocean Technology
• /
• v.24 no.4
• /
• pp.164-171
• /
• 1988

Recently with the rapid development in marine and shipbuilding industries such as marine structures, ships and chemical plants, it takes much interest in the study of corrosion fatigue characteristics that was close up an important role in mechanical design. In this study, characteristics of corner crack propagation on the base metal and heat affected zone of 5086 Al-Alloy was tested by using of a rotary bending fatigue tester and was investigated under the environments of specific resistance, $\rho$=25$\Omega$ cm and air. The corrosion fatigue crack initiation and corrosion fatigue life sensitivity were quantitatively inspected for 5086 Al-Alloy in the specific resistance, $\rho$=25$\Omega$ cm. Main results obtained are as follows: (1) The corrosion sensitivity of heat affected zone under specific resistance, $\rho$=25$\Omega$cm shows approximately 1.69~2.22 and corrosion sensitivity of base metal is more susceptible than that of heat affected zone. (2) The corrosion fatigue life sensitivity on heat affected zone decreases eminently than that of initial corrosion fatigue crack. (3) The characteristics of quarter elliptical corner crack propagation shows that depth crack is more grown than surface crack at crack initiation, but the surface crack is more propagated than depth crack as the crack propagation is increased. (4) The surface crack and depth crack growth on heat affected zone by softness show delayed phenomenon than that of base metal.