• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 1996년도 가을 학술발표회 논문집
• /
• pp.84-92
• /
• 1996

The flexural and compressive strengths of polymer-modified mortars containing FRP wastes were investigated. The specimens of polymer-modified mortars containing FRP mortat were perpared by using styrene-butadiene rubber(SBR) latex, ethylene-vinyl acetate(EVA) emulsion and polyacrylic ester(PAE) emulsion with various FRP-sand ratios(10, 20, 30, 40, 50wt%). The compressive and flexural strengths of polymer-mokified mortars containing FRP wastes were decreased with an increase of FRP-sand ratio. But the compressive and flexural strengths of PAE polymer-modified mortar were more improved than OPC, whereas those of SBR and EVA polymer-modified mortars containing FRP wastes were decreased than OPC.

• 한국정밀공학회지
• /
• 제16권4호통권97호
• /
• pp.110-115
• /
• 1999

The surface gloss of an injection molded part is one of the most significant point for evaluating the quality of products appearance. The effects of process condition on the gloss of ABS(Acrylonitrile-Butadiene-Styrene) molded part were investigated in this work. The measurements of gloss and morphology on the surface of molded part were carried out with different melt temperature, mold temperature, mold surface roughness, injection pressure and holding pressure. Gloss had a maximum value with melt temperature in the range of 210 to 220 ${^\circ}C$ and with mold temperature 40 to 50${^\circ}C$ and with injection pressure 80~90 MPa, respectively. Melt temperature was shown to have the largest effect on gloss in our work. Gloss was not improved in the region of melt temperature 240${^\circ}C$ above and of mold temperature 60${^\circ}C$ above. It was concluded that the variation of gloss was mainly caused by rubber particles migration under shear stress not by their aggregation or necklace.

• 한국소음진동공학회:학술대회논문집
• /
• 한국소음진동공학회 2006년도 추계학술대회논문집
• /
• pp.875-879
• /
• 2006

Noise reduction has become a major issue of the duct air-conditioners. This paper describes the reduction of noise and vibration of rotational slim duct system. The design of slim duct system is the most important point of noise reduction in terms of the motor of 2f line noise, resonance noise between forced frequency and natural frequency of Sirocco fan, unbalance noise of motor axis and the noise induced refrigerant. The noise of duct system is mainly measured from diffuser and bottom of duct. The optimal design was implemented after measuring the effect of noise and vibration in each part which is composed of duct system. In this paper, experimental results show that the main elements in air-conditioner duct design. These elements are anti-vibration rubber of motor, axis length of motor, rubber coupler, materials of sirocco fan and control method of motor which are the most vital factors in reducing noise.

• 한국환경과학회지
• /
• 제10권1호
• /
• pp.73-77
• /
• 2001

This study examined blends of styrene butadiene rubber(SBR) and chloroprene rubber(CR) prepared from an open 2-roll mill following the conventional polymer blend method for a wide range of the blend composition. Rubber vulcanizates were manufactured by hot press and then mechanical properties, heat and ozone resistance of the specimens were examined. Due to the post cure during the aging test, hardness of vulcanizates was increased. It was found that the undesirable characteristics of heat and ozone resistance of pure SBR was significantly improved through the blending of SBR with CR.

• Korean Membrane Journal
• /
• 제10권1호
• /
• pp.1-7
• /
• 2008

Polystyrene-co-divinylbenzene (PS-co-DVB) asymmetric membranes were prepared. In order to control their structure and mechanical properties the degree of cross-linking and the composition of casting solution were varied. The rubber added PS-DVB membranes was also prepared to overcome the mechanical limitation of cross-linked membrane, and their mechanical properties were investigated. It was revealed that the concentration of polymer in the casting solution affected the determination of skin formation. When the PS-co-DVB membrane consists of styrene-butadiene (SB) rubber or liquid polybutadiene (PBD), the structures formed showed that the PS content in the PS/DVB system played an important role in determining the porous sublayer structure.

• Elastomers and Composites
• /
• 제7권2호
• /
• pp.183-192
• /
• 1972

As a series of tile studies of EPDM-Polymer blends, tile experiment are concentrated to the investigation of the physical properties of tile EPDM-NR-SBR blends. The results are shown as follows: 1. In blending, tensile strength decreased with increase in EPDM contents, especially the ratio of EPDM/NR-SBR is 75/25. 2. Elongation and tear strength were much influenced by blending, especially the ratio of EPDM/NR-SBR is 50/50. 3. Ozone resistance is much improved after blending. It was effective more than tile ratio of EPDM/NR-SBR is 25/75. 4. Aging resistance is much improved after blending. It was effective more than the ratio of EPDM/NR-SBR is 50/50. 5. Hardness increased with increase in EPDM contents and on the other hand, abrasion resistance decreased.

• Elastomers and Composites
• /
• 제39권4호
• /
• pp.263-273
• /
• 2004

The effects of zinc surfactant (ZB) on the bis(triethoxysilylpropyl)disulfide (TESPD)-silica mixture in natural rubber (NR) and solution butadiene-co-styrene rubber(S-SBR) were compared with respect to their rheological property, processability, physical properties, and silica dispersion. In the NR compound, addition of the ZB increased the reversion resistance time (T-2), the tensile modulus, and the BO time; however, lowered the viscosity, the HBU, and tans values. In the S-SBR copound, addition of the ZB increased the $tan{\delta}$ values while lowered the T-2, the tensile modulus the BO time, the viscosity, and the HBU of the compound. In the NR compounds, addition of the ZB significantly increased the processability and mechanical property. However, in the S-SBR compounds, it improved the processability the mechanical property was not improved.

• Carbon letters
• /
• 제9권2호
• /
• pp.115-120
• /
• 2008

Rubber reinforcing carbon black N330 was treated by physical activation under $CO_2$ to different degrees of burn-off. The mechanical properties indicating the reinforcement of SBR (Styrene-Butadiene Rubber) vulcanizates filled by activated carbon blacks, such as tensile strength, modulus at 300% strain and elongation at break were determined. During $CO_2$ activation of fresh carbon blacks, the development of microporous structure caused an increase of extremely large specific surface area and the porosity turned out to be an increasing function of the degree of burn-off. The tensile strength and modulus at 300% of activated carbon blacks filled rubber composites were improved at lower loading ratios of 20 and 30 phr, but decreased drastically after 30 phr, which is considered that it might be difficult to get a fully dispersed rubber mixture at higher loading ratios for fillers having very large specific surface areas. However, the Electromagnetic Interference (EMI) shielding effectiveness of SBR rubber composites having activated carbon black at 74% yield were improved at a large extent when compared to those having raw carbon black and increased significantly as a function of increasing loading ratio.

• 폴리머
• /
• 제34권2호
• /
• pp.108-115
• /
• 2010

본 연구는 MWCNT로 보강된 SBR 나노복합재료를 컴파운딩법(compounding)으로 제조하여 산 처리된 MWCNT와 커플링제 상호간의 물리적 화학적 특성을 조사하였다. 황산과 질산으로 산화된 MWCNT는 FT-IR 분석 결과 -COOH로 기능화됨을 확인하였고, Raman 분석 결과 표면의 defect 존재와 disorder됨을 확인하였다. 또한, 제조된 SBR 복합재료의 가황 특성, 전기적 열적 특성 및 기계적 특성을 비교 평가하였다. 그 결과 산 처리된 MWCNT와 커플링제와의 상호 결합력으로 인해 기계적 물성은 상대적으로 증가하였으나, 전기적 열적 특성은 MWCNT의 defects나 disorder의 형성과 chopping으로 인해 감소됨을 확인할 수 있었다.

• Elastomers and Composites
• /
• 제44권4호
• /
• pp.401-407
• /
• 2009

용액중합 스티렌-부타디엔 고무 컴파운드 가교체의 균열저항성 및 마모특성에 미치는 공정오일의 영향을 조사하기 위해 방향족 고리화합물(PCA) 성분을 다량 함유하고 있는 방향족 오일과 저 PCA 오일을 선택하였다. 인장강도 및 인열강도 결과에 의하면 방향족 오일함유 컴파운드가 저 PCA 오일함유 컴파운드에 비해 우수한 물성을 나타내었다. 또한 방향족 오일함유 컴파운드가 균열저항성이 월등히 우수하였고, 특히 인열에너지가 낮은 범위에서 더 우수한 결과를 나타내었다. 마모저항특성은 마찰에너지가 낮은 범위에서는 방향족 오일함유 컴파운드가 우수한 결과를 나타낸 반면, 높은 마찰에너지 범위에서는 저 PCA 오일 함유 컴파운드가 오히려 높은 저항성을 나타내었다.