• Journal of the Korean Wood Science and Technology
• /
• v.43 no.3
• /
• pp.364-373
• /
• 2015

This study was carried out to estimate the effects of density and mixing ratio of mandarin peels on the bending performances of the sawdust-mandarin peels particle boards. The board density influenced significantly to the bending performance of boards. Dynamic modulus of elasticity (dMOE) and static modulus of elasticity (sMOE) and modulus of rupture (MOR) of particle boards decreased with an increase in the mixing ratio of mandarin peels at the board densities of $0.4g/cm^3$ and $0.5g/cm^3$. High correlations were found between the dMOE and sMOE, and dMOE and MOR of particle boards prepared. Therefore, it was concluded that the dMOE obtained by free vibration test using resonance frequency could be used for predicting the sMOE and MOR of sawdust-mandarin peels particle boards.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.6 no.4
• /
• pp.319-323
• /
• 2018

Ferronickel slag is a by-product from the ferronickel smelting process and it is divided into air-cooled ferronickel slag and water granulated ferronickel slag according to cooling system. The purpose of this experimental resesrch is to investigate the mechanical properties and resistance to freezing and thawing of concrete using air-cooled ferronickel slag(ACFNS) fine aggregate. For this purpose, the concrete specimens with water-cement ratio of 50% were made with ACFNS's replacement ratios of 0%, 20%, 30%, 40%, 50%, 70%, and 100% by volume of fine aggregate. It was observed from the test results that the compressive strength and static modulus of elasticity of ACFNS fine aggregate concrete were increased with increasing replacement ratio of ACFNS and the resistance to freezing and thawing of this was similar to reference concrete which had the relative dynamic modulus of elasticity of more than 90% during the freezing and thawing of 300 cycles.

• Journal of the Korean Wood Science and Technology
• /
• v.24 no.3
• /
• pp.12-17
• /
• 1996

This study was carried out to investigate some mechanical properties for wood rational utilization of heartwood and sapwood in radiata pine according to basic density, ring width and proportion of latewood which were grown in New Zealand. This result were summarized as follow: Heartwood showed 35.78(MPa) of the compression strength parallel to the grain while sapwood showed 42.08(MPa). The modulus of rupture in static bending was higher in sapwood showing 86.12(MPa) than in heartwood 72.99(MPa) Heartwood had 7.38(GPa) for the modulus of elasticity in static bending and sapwood 8.17(GPa). As the basic density and proportion of latewood increased: compression strength parallel to the grain, MOR and MOE in static bending had a tendency to increase. As ring width increased, the mechanical properties decreased.

• Journal of agriculture & life science
• /
• v.46 no.1
• /
• pp.35-41
• /
• 2012

Nondestructive evaluation (NDE) technique method using a resonance frequency mode was carried out for woodceramics made by different carbonizing temperature (600, 800, 1000, $1200^{\circ}C$) for Broussonetia kazinoki Sieb. Dynamic modulus of elasticity increased with increasing carbonizing temperature. There was a close relationship of dynamic modulus of elasticity and static bending modulus of elasticity to MOR. Therefore, the dynamic modulus of elasticity using resonance frequency mode is useful as a nondestructive evaluation method for predicting the MOR of woodceramics made by different carbonizing temperature for B. kazinoki Sieb.

• Journal of The Korean Society of Agricultural Engineers
• /
• v.56 no.5
• /
• pp.45-54
• /
• 2014

This study was performed to evaluate compressive strength, flexural strength, static modulus of elasticity, stress-strain ratio and durability of abrasion on EVA concrete reinforced steel fiber (SF) in order to use hydraulic structures, underground utilities, offshore structures and structures being applied soil contaminated area. It is used ordinary portland cement, crushed coarse aggregate, nature fine aggregate, EVA redispersible polymer powder, superplasticizer and deforming agent to find optimum mix design of EVA concrete reinforced steel fiber. EVA concrete reinforced SF was effected on the improvement of mechanical properties and durability of abrasion.

• Korean Journal of Agricultural Science
• /
• v.23 no.1
• /
• pp.61-69
• /
• 1996

This study was performed to evaluate the engineering properties of permeable polymer concrete with fillers and unsaturated polyester resin. The following conclusions were drawn. 1. The highest strength was achieved by stone dust filled permeable polymer concrete, it was increased 17% by compressive, 148% by tensile and 188% by bending strength than that of the normal cement concrete, respectively. 2. The static modulus of elasticity was in the range of $1.17{\times}10^5{\sim}1.32{\times}10^5kg/cm^2$, which was approximately 53~56% of that of the normal cement concrete. Stone dust filled permeable polymer concrete was showed relatively higher elastic modulus. The poisson's number of permeable polymer concrete was less than that of the normal cement concrete. 3. The dynamic modulus of elasticity was in the range of $1.3{\times}10^5{\sim}1.5{\times}10^5kg/cm^2$, which was approximately less compared to that of the normal cement concrete. Stone dust filled permeable polymer concrete was showed higher dynamic modulus. The dynamic modulus of elasticity were increased approximately 10~13% than that of the static modulus. 4. The water permeability was in the range of $3.076{\sim}4.390{\ell}/cm^2/h$, and it was largely dependent upon the mix design. These concrete can be used to the structures which need water permeability. 5. The compressive strength, tensile strength, bending strength and elastic modulus were largely showed with the decrease of water permeability.

• Journal of the Korean Wood Science and Technology
• /
• v.12 no.2
• /
• pp.3-9
• /
• 1984

This study was carried out to examine the practicality of DAP[$(NH_4)_2HPO_4$] as fire retardant for plywood by static bending test the redried plywoods which had been soaked in 20% $(NH_4)_2HPO_4$ solution. Being hot/cold soaked in the solution for 3/3, 6/3, 9/3 and 12/3 hours and redried by cyclic press-drying method at the platen temp. of 130, 145, 100 and $175^{\circ}C$, the treated plywoods were tested to offer the mechanical data, that is, $S_{pl}$(stress at proportional limit), MOE(modulus of elasticity), MOR(modulus of rupture) and $W_{pl}$(work per unit volume to proportional limit ) in flexure. The results obtained were summarized as follows. 1. $S_{pl}$ of fire retardant treated plywoods ("FRP" would be used hereinafter) decreased as the platen temperature increased, but it was superior to that of non-treated plywoods(Control) at $160^{\circ}C$ or higher. 2. MOE of FRP decreased roughly with the increase of temperature, hut this tendency was not constant. And the value of FRP was higher than that of Control even at $175^{\circ}C$. 3. MOR of FRP showed same temperature-dependent tendency as MOE, but it was influenced more sensitively at the higher temperature. 4. $W_{pl}$ of FRP also decreased gradually with the increase of platen temperature and the value in DAP 9/3 treatment was Jess than 70% of control plywoods. 5. In view of redrying time and mechanical properties, the most reasonable platen temperature for DAP treated FRP was $160^{\circ}C$ in this study.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2003.11a
• /
• pp.437-440
• /
• 2003

This study has focused on the possibility for recycling of tailings from the Sangdong tungsten mine as powder of self-compacting concrete(SCC). The experimental tests for slump-flow, reaching time to the slump-flow of 500mm, V-funnel and U-box were carried out in accordance with the specified by the Japanese Society of Civil Engineering(JSCE). The result of this study, in case of SCC mixed with tailings, slump-flow was decreased with increasing mixing ratio. But reaching time slump-flow of 500mm, V-funnel and U-box were satisfied a prescribed range. The mechanical properties including compressive strength, splitting tensile strength and static modulus of elasticity were checked with the requirements specified by Korean Industrial Standard(KS). The compressive strength of SCC was decreased with increasing replacement, splitting tensile strength and static modulus were similar to those of normal concrete.

• Korean Journal of Agricultural Science
• /
• v.23 no.1
• /
• pp.120-130
• /
• 1996

Concrete is the most commonly used structural materials, but in concrete construction, its self-weight represents a very large proportion of the total load on the structure, and there are clearly considerable advantages in reducing the density of concrete. This study was carried out to investigate the stress-strain properties of no-fines synthetic lightweight concrete with synthetic lightweight coarse aggregates. The used synthetic lightweight coarse aggregate were two types, one was expanded clay with grading 3~8mm, the other is pumice stone with grading 4.75~10mm. The results of this study were summarized as follows ; The static modulus of elasticity of the synthetic lightweight concrete was $1.8{\times}10^5kg/cm^2$ at type CE using the expanded clay and $1.6{\times}10^5kg/cm^2$ at type CL using the pumice stone. The dynamic modulus of elasticity was $1.9{\times}10^5kg/cm^2$(CE) and $2.0{\times}10^5kg/cm^2$(CL). The dynamic modulus of elasticity was 10~30% larger than that of the static modulus of elasticity. The load-time curves of synthetic lightweight concrete were shown approximately similar to each other type except for added foaming agent. The stress-strain curves in uniaxial compressive of synthetic lightweight concrete were similar to each other.

• Journal of Biosystems Engineering
• /
• v.43 no.3
• /
• pp.173-184
• /
• 2018

Purpose: This study was conducted to investigate the mechanical and physical properties of a Korean red pepper variety for particle behavior analysis. Methods: Poisson's ratio, modulus of elasticity, shear modulus, density, coefficient of restitution, and coefficient of friction were derived for "AR Legend," which is a domestic pepper variety. The modulus of elasticity and Poisson's ratio were measured through a compression test using a texture analyzer. The shear modulus was calculated from the modulus of elasticity and Poisson's ratio. The density was measured using a water pycnometer method. The coefficient of restitution was measured using a collision test, and the static and dynamic friction coefficients were measured using a inclined plane test. Each test was repeated 3-5 times except for density measurement, and the results were analyzed using mean values. Results: Poisson's ratios for the pepper fruit and pepper stem were 0.295 and 0.291, respectively. Elastic moduli of the pepper fruit and pepper stem were $1.152{\times}10^7Pa$ and $3.295{\times}10^7Pa$, respectively, and the shear moduli of the pepper fruit and pepper stem were $4.624{\times}10^6Pa$ and $1.276{\times}10^7Pa$, respectively. The density of the pepper fruit and the pepper stem were $601.8kg/m^3$ and $980.4kg/m^3$, respectively. The restitution coefficients between pepper fruits, pepper stems, a pepper fruit and a pepper stem, a pepper fruit and plastic, and a pepper stem and plastic were 0.383, 0.218, 0.277, 0.399, and 0.148, respectively. The coefficients of static friction between pepper fruits, pepper stems, a pepper fruit and a pepper stem, a pepper fruit and plastic, and a pepper stem and plastic were 0.455, 0.332, 0.306, 0.364, and 0.404, respectively. The coefficients of dynamic friction between a pepper fruit and plastic and a pepper stem and plastic were 0.043 and 0.034, respectively.