• 한국재료학회지
• /
• 제11권11호
• /
• pp.972-977
• /
• 2001

It was investigated the effect of ultrasonic treatment on magnetic property of ultra fine magnetic Fe powders ($\alpha$-Fe) for magnetic tape. The properties were characterized with vibrating sample magnetometer (VSM), particle size analyzer (PSA) and scanning electron microscope (SEM). At 4hours ultrasonic treatment of 70 kHz, magnetic properties such as squareness ratio (S.Q. : 0.8868), orientation ratio (O.R. : 2.45) and switching field distribution (S.F. D. : 0.394) before taping were relatively enhanced. Cumulative particle size distribution of less than 5$\mu\textrm{m}$ fine powder was above 90% below 1 hour leaving time after ultrasonic treatment and it was supposed that ultrasonic treatment prevent aggregation. The magnetic values of S.Q. and S.F.D. of tape manufactured at 70 kHz and 4hour ultrasonic treatment were improved from 0.7747, 0.3818 to 0.8037, 0.3706, respectively. Electro-magnetic property used as in-output signal characteristic was improved, which showed that ultrasonic treatment developed the magnetic properties.

• 한국세라믹학회지
• /
• 제39권8호
• /
• pp.758-763
• /
• 2002

초음파 에너지(28 kHz, 40 kHz, 70 kHz)를 사용하여 수직자기기록용 Ba-ferrite의 자기적 특성 향상에 대하여 조사하였다. 한편, 분산된 Ba-ferrite를 sheet에 수직으로 배향시키기 위해 다양한 형태의 배향기들을 사용하여 실험을 행하였다. Ba-ferrite가 도포된 sheet 중 초음파 에너지가 40 kHz이고 초음파 처리 시간이 2시간에서 자기적 특성인 S. Q. (Squareness Ratio)와 O. R. (Orientation Ratio)값이 각각 0.7831과 2.87로 비교적 좋은 값을 얻을 수 있었다. 이때 얻어진 sheet의 표면 형상을 SEM(Scanning Electron Microscopy)으로 분석한 결과 Ba-ferrite가 자화용이축인 c 축에 수직방향으로 배향되어 수직자기기록용으로서의 응용에 가능성을 보였다. 또한, VSM(Vibrating Sample Magnetometer)으로 자기장의 각도변화에 따른 S. Q.의 측정시, 자기장의 각도가 증가함에 따라 S. Q. 값이 감소하였고 이는 수직자기기록용으로써 가능성을 재확인 시켜주었다.