• Korean Chemical Engineering Research
• /
• v.47 no.1
• /
• pp.84-88
• /
• 2009

Al doped $LiMn_2O_4$ cathode powders with fine size were synthesized by an ultrasonic spray pyrolysis method from the spray solution with citric acid and ethylene glycol. The as-prepared powders with spherical shape, porous structure and micron size turned into $LiMn_{11/6}Al_{1/6}O_4$ powders with micron size and regular morphology after post-treatment above $800^{\circ}C$. The $LiMn_{11/6}Al_{1/6}O_4$ powders had low initial discharge capacity of 94 mAh/g at a post-treatment temperature of $700^{\circ}C$. As the post-temperature increased from $750^{\circ}C$ to $1,000^{\circ}C$, the initial discharge capacities of the $LiMn_{11/6}Al_{1/6}O_4$ powders changed from 103 to 117 mAh/g. The $LiMn_{11/6}Al_{1/6}O_4$ powders had the maximum discharge capacity at a post-treatment temperature of $750^{\circ}C$. However, the $LiMn_{11/6}Al_{1/6}O_4$ powders post-treated at a temperature of $900^{\circ}C$ had the good cycle properties. The discharge capacities of the $LiMn_{11/6}Al_{1/6}O_4$ powders dropped from 107 to 100 mAh/g (93% capacity retention) by the 70th cycle at a current density of 0.1 C.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.9 no.5
• /
• pp.527-533
• /
• 1999

Hertzian indentation tests with spherical indenters in water were conducted to examine the contact fatigue in three dental ceramics, such as feldspathic porcelain, micaceous glass-ceramic (MGC) and glass-infiltrated alumina, which was used as dental restorations, and evaluated the effect of contact damage on strength. Initial damage was dependent of microstructure, showing cone cracks of brittle behavior in the feldspathic porcelain and deformation of quasi-plastic behavior in the MGC, with an intermediate case in the glass-infiltrated alumina. However, as increasing the number of cyclic loading (n=1~n =$10^6$)all materials showed an abrupt strength degradation, at which fracture was originated from damage in the contact fatigue. There were two strength degradation with increasing the number of cyclic loading in specific loads (200N, 500N, 1000N):first was from the cone cracks, and second was from the radial cracks created by cyclic loading. The radial cracks, once formed, led to rapid degradation in strength properties, Finally the material was failed at the high number of cyclic loading. Strength degradation with indentation load at fixed number of cyclic loading indicated that the feldspathic porcelain should be highly damage tolerant to the contact fatigue.

• Resources Recycling
• /
• v.27 no.2
• /
• pp.24-31
• /
• 2018

In this study, waste ITO target is dissolved into hydrochloric acid to generate a complex indium-tin chloride solution. Nano sized ITO powder with an average particle size below 30 nm are generated from these raw material solutions by spray pyrolysis process. Also, in this study, thermodynamic equations for the formation of indium-tin oxide (ITO) are established. As the reaction temperature increased from $800^{\circ}C$ to $900^{\circ}C$, the proportion and size of the spherical droplet shape in which nano sized particles aggregated gradually decreased, and the surface structure gradually became densified. When the reaction temperature was $800^{\circ}C$, the average particle size of the generated powder was about 20 nm, and no significant sintering was observed. At a reaction temperature of $900^{\circ}C$, the split of the droplet was more severe than at $800^{\circ}C$, and the rate of maintenance of the initial atomized droplet shape decreased sharply. The average particle size of the powder formed was about 25 nm. The ITO particles were composed of single solid crystals, regardless of reaction temperature. XRD analysis showed that only the ITO phase was formed. Remarkably, the specific surface area decreased by about 30% as the reaction temperature increased from $800^{\circ}C$ to $900^{\circ}C$.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.25 no.1
• /
• pp.209-224
• /
• 1998

The purpose of this study was to compare the amount of calcium fluoride deposited on the enamel and dentin surface and to obtain information on the morphological change and crystallographic details of mineral deposition after 12,000ppm APF application in vitro. The bovine enamel and dentin blocks were randomly assigned to eight groups according to artificial caries lesion formation and difference of fluoride application time. The fluoride concentration and morphological characteristics on the treated enamel and dentin surface were investigated by using fluoride quantitative analysis and SEM. The powdered enamel and dentin of the intact bovine incisors were prepared for the X-ray diffraction analysis. The following results were obtained. 1. The amounts of KOH-soluble fluoride on the carious enamel and dentin surface after 24h APF application were higher than after only 5min APF application(p<0.05), but in the case of the sound enamel and dentin surface were similar after 5min and 24h application (P>0.05). The fluoride content was highly increased in the carious dentin as compared with sound dentin after APF application(P<0.05). 2. The carious enamel surface after APF application, the demineralized enamel surface were recovered a more dense enamel surface and precipitation of crystal was observed a distintive surface layer of spherical globules of about 1 m diameter. In the case of the fluorided carious dentin surface, precipitation of calcium fluoride-like material was deposited both inside the dentinal tubules as well as in the intertubular regions. 3. The crystallographic structure of powdered enamel and dentin after 24h APF application had large crystallities of apatite and CaF2 diffraction peaks in the enamel as compared with dentin. The diffraction data collected from the 27.50-29.50(2) angular range of the powdered enamel, the (105) apatite, (225) apatite and (111) CaF2 peaks of the enamel crystallities were detected after 24h APF application.

• Journal of the Korean Magnetics Society
• /
• v.14 no.4
• /
• pp.131-137
• /
• 2004

For the aim of thin electromagnetic wave absorbers used in mobile telecommunication frequency band (0.8-2.0㎓), we investigate high-frequency magnetic, dielectric and microwave absorbing properties of iron particles dispersed in rubber matrix in this study. The major experimental variables are particle shape (sphere and flake) and initial particle size (in the range 5-70 $\mu\textrm{m}$) of iron powders. High value of magnetic permeability and dielectric permittivity can be obtained in the composites containing thin plate-shape (flake) iron particles (of which thickness is less than skin depth in ㎓frequency), which can be produced by mechanical forging of spherical iron powders using an attrition mill. This result is attributed to the reduction of eddy current loss (increase of permeability) and the increase of space charge polarization (increase of permeability). The optimum initial particle size is found to be about 10 $\mu\textrm{m}$ for the attainment of the material parameters (particularly, real part of complex permeability) satisfying the wave impedance matching. With the iron powders controlled in size and shape as absorbent fillers in rubber matrix, the thickness can be reduced to about 0.7mm with respect to -5㏈ reflection loss (70% power absorption) in mobile telecommunication frequency band.

• Korean Chemical Engineering Research
• /
• v.44 no.6
• /
• pp.609-613
• /
• 2006

Ba2-xSrxSiO4:Eu2+ phosphor particles with the high photoluminescence (PL) intensity under long wavelength ultraviolet (UV) were prepared by spray pyrolysis. The photoluminescence, morphological and crystalline characteristics of $Ba_{2-x.}Sr_{x.}SiO_4:Eu^{2+}$ phosphor particles prepared by spray pyrolysis were investigated. $Ba_{2-x.}Sr_{x.}SiO_4:Eu^{2+}$ phosphor particles prepared by spray pyrolysis had various colors from bluish green to yellow by changing the ratio of barium and strontium of the host material. In case of x=0, the main emission peak of $Ba_2SiO_4:Eu^{2+}$ phosphor was 500 nm. In case of x=2, the main emission peak of $Sr_2SiO_4:Eu^{2+}$ phosphor was 554nm. $Ba_{2-x.}Sr_{x.}SiO_4:Eu^{2+}$ phosphor particles obtained by spray pyrolysis had spherical shape and hollow structure. On the other hand, the post-treated $Ba_{2-x.}Sr_{x.}SiO_4:Eu^{2+}$ phosphor particles had large size and irregular shape. The $Ba_{1.488}Sr_{0.5}SiO_4:Eu_{0.012}{^{2+}}$ phosphor particles had the maximum PL intensity after post-treatment at temperature of $1300^{\circ}C$ for 3h under reduction atmosphere.

• The Korean Journal of Malacology
• /
• v.26 no.3
• /
• pp.235-244
• /
• 2010

Ultrastructural characteristics of the testis and spermatogenesis of Crassostrea gigas were investigated by Transmission and Scanning Electron microscope observations. The testis is a diffuse organ consisting of branching acini containing differentiating germ cells in a variety of stages. The acinus is surrounded by an intermitent layer of myoepithelial cells andis divided into subcompartments that are partially separated by pleomorphic accessory cells which remain in close contact with germ cells until late stages of development. these accessory cells contain a large quantity of glycogen particles and lipid droplets in the cytoplasm. Therefore, it is assumed that they are involved in the supplying of the nutrients for germ cell development, while any phenomena associated with phagocytosis of undischarged, residual sperms by lysosomes could be find in the cytoplasm of the accessory cells. The morphology of the spermatozoon has a primitive type and is similar to those of other bivalves. Mature spermatozoa consist of broad, cap-shaped acrosomal vesicle, subacrosomal material (containing axial rod embedded in a granular matrix), a oval nucleus showing deeply invaginated anteriorly, two triplet substructure centrioles surrounded by four spherical mitochondria, and satelite fibres appear to the distal centriole and plasma membrane. Spermatozoa of C. gigas resemble to those of other investigated ostreids. In particular, the anterior region of the acrosomal vesicle is transversely banded. It is assumed that differences in this acrosomal substructure are associated with the inability of fertilization between the genus Crassostrea and other genus species in Ostreidae. Therefore, we can use sperm morphology in the resolution of taxonomic relationships within the Ostreidea. The spermatozoon is approximately $42-47{\mu}m$ in length including an oval sperm nucleus (about $0.91{\mu}m$ in length), an acrosome (about $0.42{\mu}m$ in length) and tail flagellum ($40-45{\mu}m$). The axoneme of the sperm tail flagellum consists of nine pairs of microtubules at the periphery and a pair at the center. The axoneme of the sperm tail shows a 9 + 2 structure. These morphological charateristics of acrosomal vesicle belong to the family Ostreidae in the subclass Pteriomorphia.

• Korean Chemical Engineering Research
• /
• v.60 no.3
• /
• pp.327-333
• /
• 2022

In this study, silicon/carbon nanotube/carbon (Si/CNT/C) composites for anode were prepared to improve the volume expansion of silicon used as a high-capacity anode material. Si/CNT were prepared by electrostatic attraction of the positively charged Si and negatively charged CNT and then hydrothermal synthesis was performed to obtain the spherical Si/CNT/C composites. Poly(vinylidene fluoride) (PVDF), polyacrylic acid (PAA), and styrene butadiene rubber (SBR) were used as binders for electrode preparation, and coin cell was assembled using 1.0 M LiPF₆ (EC:DMC:EMC = 1:1:1 vol%) electrolyte and fluoroethylene carbonate (FEC) additive. The physical properties of Si/CNT/C anode materials were analyzed using SEM, EDS, XRD and TGA, and the electrochemical performances of lithium-ion batteries were investigated by charge-discharge cycle, rate performance, dQ/dV and electrochemical impedance spectroscopy tests. Also, it was confirmed that both capacity and rate performance were significantly improved using the PAA/SBR binder and 10 wt% FEC-added electrolyte. It is found that Si/CNT/C have the reversible capacity of 914 mAh/g, the capacity retention ratio of 83% during 50 cycles and the rate performance of 70% in 2 C/0.1 C.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.33 no.5
• /
• pp.167-173
• /
• 2023

Li₃V₂(PO₄)₃ and Li₃V₂(PO₄)₃/C composite with single phase monoclinic structure for the cathode materials are successfully synthesized by direct co-precipitation method using N₂H₄·H₂O as the reducing agent and alginic acid as the carbon source, and their electrochemical properties were compared. The particles with approximately 1~2 ㎛ size and the uniform spherical-like morphology of the narrow particle size distribution were obtained. In addition, the residual carbon can also improve the electrical conductivity. The Li₃V₂(PO₄)₃/C composite has improved initial specific discharge capacity and excellent cycle characteristics to maintain capacity stably than Li₃V₂(PO₄)₃. The results indicate that the reducing agent and carbon composite can affect the good crystallinity and electrochemical performance of the cathode materials.

• Clean Technology
• /
• v.30 no.1
• /
• pp.1-12
• /
• 2024

Nanoplastics (NP) exhibit distinct material properties compared to microplastics (MP), necessitating their separate recognition. Review of research outcomes and policy documents on NP reveals that most policy frameworks predominantly define MPs as solid synthetic polymer materials measuring 5 mm or less, but do not distinguish them from NP. However, recent revisions in regulations by the EU classify NPs as particles that range in size from 1 to 1,000 nm, as confirmed by some academic studies. Research on NPs often relies on experimental investigations centered around water systems, with a focus on high-concentration experimental conditions using spherical polystyrene-based NPs in behavior and impact studies. Notably, the environmental behavior characteristics of NP show differences in influence depending on the NP type, emphasizing the need for field simulation research. These challenges are mirrored in Korean society, so it is necessary to redefine NP to be distinct from MP in both research and policy. This study aimed to assess the current state of NP management globally and domestically and highlight policy considerations and issues in the existing response to NP. Upon comprehensive review, it becomes apparent that reaching an international agreement on MP faces methodological limitations, which could potentially burden efforts to precisely define NP size. Therefore, referencing the EU's recent regulatory revisions is crucial in domestic policy. Specific adjustments should commence from the MP concept through insights from the domestic industry, guidance from the academic community, and thorough discussions to ensure social acceptance.