• Tribology and Lubricants
• /
• v.12 no.1
• /
• pp.22-28
• /
• 1996

This study was undertaken to investigate the dry wear characteristics and mechanism of KP-4M steel for plastic molding against SKD 61 hardened by heat treatment. The wear test was carried out under different conditions such as sliding speed, contact pressure, sliding distance, with frictional tester of pin on disc type. The wear loss on variation of sliding speed was little in lower speed range below 0.5 m/sec and in higher speed range above 1.5 m/sec,'but wear loss was high in intermediate speed range. The critical sliding speed, which showed the maximum value of specific wear rate, became lower with increased contact pressure. Increasing the contact pressure, the critical sliding distance Lcr which the wear mechanism changes from severe wear to mild wear was increased due to the decrease of oxidation reaction velocity. Through this study we suggested a model of generation and elimination process of wear debris of KP-4M steel for plastic molding.

• Journal of Mechanical Science and Technology
• /
• v.15 no.9
• /
• pp.1274-1280
• /
• 2001

The fretting wear behavior of the contact between Zircaloy-4 tube and Inconel 600, which are used as the fuel rod cladding and grid, respectively, in PWR nuclear power plants was investigated in air. In the study, number of cycles, slip amplitude and normal load were selected as the main factors of fretting wear. The results indicated that wear increased with load, slip amplitude and number of cycles but was affected mainly by the slip amplitude. SEM micrographs revealed the characteristics of fretting wear features on the surface of the specimens such as stick, partial slip and gross slip which depended on the slip amplitude. It was found that fretting wear was caused by the crack generation along the stick-slip boundaries due to the accumulation of plastic flow at small slip amplitudes and by abrasive wear in the entire contact area at high slip amplitudes.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.14 no.1
• /
• pp.37-42
• /
• 1990

Carbon fiber epoxy composite materials are widely used in the structures of aircrafts, robots and other machines because of their high specific stiffness, high specific strength and damping. In order for the composite materials to be used in the robot structure or machine element, bearing mounting and joining surfaces must be provided, which require accurate machining. In this paper, the machinability and tool wear characteristics of the milling operation of the carbon fiber epoxy composite materials were experimentally measured. The tool wear mechanism and the Taylor tool wear constants were determined. Also, the surface roughness of milling operation was measured w.r.t. cutting speed and feed.

• Tribology and Lubricants
• /
• v.5 no.2
• /
• pp.94-100
• /
• 1989

Friction and Wear behavior of continuous graphite fiber composites was studied for different fiber orientations against the sliding direction. The effect of fiber orientation on friction and wear of the composite and on the deformation of the counterface was investigated experimentally. Pin on disk type testing machine was built and employed to generate the friction and wear data. A graphite fiber composite plate was produced by the bleeder ply molding in an autoclave and machined into rectangular pin specimens with specific fiber orientations, i.e., normal, transverse, and longitudinal directions. Three different wear conditions were employed for two different periods of time, 24 and 48 hours. The wear track of the worn specimens and the metal counterface was examined with a scanning electron microscope (SEM) to observe the damaged fibers on the surface and wear film generation on the counterface. Wear mechanism of the composite during sliding wear is proposed based on the experimental results.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 2001.06a
• /
• pp.319-326
• /
• 2001

The sliding wear characteristics of carbon steel castings were Investigated using a ball on disk type tester. The experiment was conducted using high carbon steel wire rods as ball material and carbon steel castings as disk material and different operating conditions, at room temperature under a lubrication and dry conditions. The results showed that the carbon steel castings appeared average wear volume Is lowed after annealing under a lubrication conditions and wear curve linear Increased. The specific wear rate of carbon steel castings Increased with wire diameter lubrication and dry also Increased 125 times In Ory. The sliding wear mechanism were Investigated due to fatigue wear lubrications and abrasive wear dries also wire Included fatigue and abrasive wear by plastic flow.

• Elastomers and Composites
• /
• v.58 no.2
• /
• pp.87-94
• /
• 2023

Abrasion tests of an SBR compound were conducted using four different types of abrasion testers (cut and chip, Lambourn, DIN, and LAT100). The abrasion test results were analyzed in terms of size distributions and morphologies of the wear particles. Most wear particles were larger than 1000 ㎛. The wear particle size distributions tended to decrease as the particle size decreased. Except for the Lambourn abrasion test, the wear particles smaller than 212 ㎛ were rarely generated by the other three abrasion tests, implying that small wear particles were produced through friction by introducing talc powder. Shapes of the wear particles varied depending on the abrasion testers. The wear particles generated from the Lambourn abrasion tester had stick-like shapes. The cut and chip abrasion test showed a clear abrasion pattern, but the DIN abrasion test did not show any specific abrasion pattern. The Lambourn and LAT100 abrasion tests showed irregular abrasion patterns.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.38 no.9
• /
• pp.1005-1012
• /
• 2014

Gears are critical elements in automobiles, and their use as power transmitting machine elements in engineering applications is quite extensive. In the areas of contact between gear teeth, the condition of a gear is likely to deteriorate due to contact fatigue, wear, material defects, lubrication failure, etc. Thus, it is necessary to monitor its condition to ensure smooth power transmission. Gear teeth deterioration causes failures such as abrasive wear, scuffing, pitting, and spalling. These failures lead to a higher level of vibration signals in the gear system. This paper presents the results of an experiment on the surface fatigue wear of a spur gear system. The correlation between the estimated specific film thickness, statistical parameter of the vibration signals, and Stribeck curve was considered in this study.

• Journal of Power System Engineering
• /
• v.5 no.3
• /
• pp.88-94
• /
• 2001

Stellite 12 alloy-powders were overlaid on 410 stainless steel valve seat using plasma transferred arc(PTA) process. Variation of the microstructure, hardness, wear and corrosion of overlaid deposit with current change was investigated. The deposit showed hypoeutectic microstructure, which was consisted of primary cobalt dendrite and networked $M_7C_3$ type eutectic carbides. As current increased, the amount of eutectic carbide decreased and its dendritic secondary arm spacing increased. Hardness of the deposit was decreased with increase of current. Stress relief heat treatment at $600^{\circ}C$ for two hours resulted in slight increase of hardness in the deposit and showed uniform hardness distribution in base metal without any hardened layer in HAZ. Specific wear decreased with increase of sliding distance. The deposit of high hardness with a lot of eutectic carbide showed relatively low specific wear. Initial corrosion current density of the deposit in 0.1N sulfuric acid was lower than those of 410 stainless steel, and showed a little variation with PTA current.

• Journal of Power System Engineering
• /
• v.6 no.1
• /
• pp.74-81
• /
• 2002

The characteristics of corrosion resistance for the surface of ductile cast iron(GCD40) by plasma nitriding process have been studied in terms of electrochemical polarization behaviors including corrosion potential($E_{corr}$), anodic polarization trends, polarization resistance($R_p$), and also have been studied microstructures, hardness and specific wear of nitrided layer Nitrided layer showed an enhanced hardness values in all the plasma nitriding condition investigated. In the result of wear test, specific wear of nitrided specimens were much decreased than that of non-treated specimens. In the results of XRD, ${\gamma}'phase\;and\;{\varepsilon}$ phase were detected in nitrided surface. And it was found that ${\varepsilon}$ phase was decreased and ${\gamma}'phase$ was increased respectively, as the nitriding time became longer. In the test of corrosion resistance, natural potentials in all the nitrided specimens were towards noble directions than in the case of non-treated specimens. The measurement of electrode potentials revealed that corrosion resistivity of plasma nitrided specimens were higher than in the case of the non-treated specimens.

• Transactions of Materials Processing
• /
• v.19 no.6
• /
• pp.357-362
• /
• 2010

Dry sliding wear behavior of pure Fe and Cu which have BCC and FCC crystal structure, respectively, was investigated. The wear characteristics of the pure metals with different crystal structure were compared. Dry sliding wear tests were carried out using a pin-on-disk wear tester at various loads under the constant sliding speed condition of 0.15 m/s against a silica ball at room temperature. Sliding distance was fixed as 600 m for all wear tests. Wear rate of a specimen was calculated by dividing the weight loss of the specimen after the test by the specific gravity and sliding distance. Worn surfaces and wear debris were analyzed by SEM. The wear of both pure Fe and Cu proceeded with surface deformation, resulting in similar wear rates despite of their structure difference under the current test conditions. Wear rates of both metals were low if the surface deformation due to wear forms thick surface-deformation layer that is strain hardened beneath the wearing surface. The pure Cu specimens showed a lot of oxides on the worn surface when tested at low loads less than 5 N, which resulted in very low wear rate.