• Advances in concrete construction
• /
• 제12권6호
• /
• pp.479-490
• /
• 2021

Present research is mainly focused on, microstructural and durability analysis of Graphene Oxide (GO) in Wollastonite (WO) induced cement mortar with silica fume. The study was conducted by evaluating the mechanical properties (compressive and flexural strength), durability properties (water absorption, sorptivity and sulphate resistance) and microstructural analysis by SEM. Cement mortar mix prepared by replacing 10% ordinary portland cement with SF was considered as the control mix. Wollastonite replacement level varied from 0 to 20% by weight of cement. The optimum replacement of wollastonite was found to be 15% and this was followed by four sets of mortar specimens with varying substitution levels of cementitious material with GO at dosage rates of 0.1%, 0.2%, 0.3% and 0.4% by weight. The results indicated that the addition of up to 15%WO and 0.3% GO improves the hydration process and increase the compressive strength and flexural strength of the mortar due to the pore volume reduction, thereby strengthening the mortar mix. The resistance to water penetration and sulphate attack of mortar mixes were generally improved with the dosage of GO in presence of 15% Wollastonite and 10% silica fume content in the mortar mix. Furthermore, FE-SEM test results showed that the WO influences the lattice framework of the cement hydration products increasing the bonding between silica fume particles and cement. The optimum mix containing 0.3% GO with 15% WO replacement exhibited extensive C-S-H formation along with a uniform densified structure indicating that calcium meta-silicate has filled the pores.

• 한국건설순환자원학회논문집
• /
• 제8권1호
• /
• pp.88-96
• /
• 2020

이 연구에서는 고흡수율 폴리머(SAPs)를 포함하는 시멘트계 재료의 자기치유에 대한 습윤/건조 반복 작용의 영향을 실험적으로 평가하였다. 매 주기마다 SAP 함량을 변수로 하는 시멘트 페이스트 시편을 균열 이후 1시간 동안 습윤 조건에 노출시키고(흡수율시험 및 투수시험 진행), 47시간 동안 건조 조건에 노출시켰다. 흡수율시험 결과 SAP 미혼입 시편, SAP 0.5%, SAP 1.0%, SAP 1.5% 혼입 시편의 균열을 통한 흡수율이 각각 1주기 대비 8주기 이후 22.9%, 36.8%, 42.8%, 46.3% 감소한 것으로 나타났다. 또한, 투수시험 결과 모든 시편의 균열을 통한 물 유출량은 습윤/건조 주기에 따라 점차 감소하였으며, 특히 SAP 함량이 증가할수록 유량 감소율은 증가하였다. 또한, X-ray CT 분석을 통해 균열 내 SAPs의 유입수에 의한 팽윤 거동이 확인되었다. 실험 결과는 SAPs가 유입수를 흡수하여 팽윤함에 따라 유효 균열폭이 감소될 수 있고, SAPs는 흡수한 물을 건조 조건에서 주변 균열부에 공급함에 따라 치유 생성물의 형성을 촉진시킬 수 있음을 나타낸다. 이 연구의 결과는 SAPs의 혼입이 균열의 수밀성을 증가시킴에 따라 시멘트계 재료의 자기치유 성능을 향상시킬 수 있음을 나타낸다.