• Journal of Welding and Joining
• /
• v.17 no.2
• /
• pp.61-65
• /
• 1999

Because of the need for packages which accommodate high pin count, high density and high speed device, PBGA(plastic ball grid array) package gets more spotlight. But the substrate material which is used for PBGA package is in nature susceptible to moisture penetration. The objective of the study is to find out the path of delamination in the stacked structure of substrate. To increase the adhesion between the cooper laminate and PSR(photo solder resist) which is the weakest part, experiments were performed by changing parameters of printing pre-treatment and post-treatment process. As a result of experiments, the factor effects on the adhesion between the cooper laminate and PSR is caused by all of the pre-treatment and post-treatment condition. A considerable change was observed depending on the amount of UV irradiation after thermal cure which is typical of printing post-treatment condition rather than pre-treatment condition.

• Journal of the Microelectronics and Packaging Society
• /
• v.22 no.1
• /
• pp.75-81
• /
• 2015

In this paper, numerical analysis by finite element method and parameter design by the Taguchi method were used to reduce warpage of a two passive components embedded double side substrate for PoP(Package on Package). The effect of thickness of circuit layers (L1, L2) and thickness of solder resist (SR_top, SR_BTM) were analyzed with 4 variations and 3 levels(minimum, average and maximum thickness) to find optimized thickness conditions. Also, paste effect of solder resist on unit area of top surface was analyzed. Finally, experiments was carried out to prove numerical analysis and the Taguchi method. Based on the numerical and experimental results, it was known that circuit layer in ball side of substrate was the most severe determining deviation for reducing warpage. Buried circuit layer in chip side, solder resist and were insignificant effects on warpage relatively. However, warpage decreased as circuit layer in ball side thickness increased but effect of solder resist and circuit layer in chip side thickness were conversely.

• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2004.09a
• /
• pp.79-92
• /
• 2004

RoHS compliant products are now being mass-produced. Eco-product(Pb-free+RoHS compliant+Halogen-free) will be possible from 2005. Pb-free flip chip will be qualified by 2004. 4Q. Lead Finish: SnBi-Under mass production Pd PPF-Under small production Matte Sn-will be internally qualified by 2004. 4Q Development of Pb-free Solder Ball: Stable Supply, Cost Down.

• Proceedings of the Korean Society of Laser Processing Conference
• /
• 2006.11a
• /
• pp.31-33
• /
• 2006

• Proceedings of the IEEK Conference
• /
• 2000.06d
• /
• pp.139-142
• /
• 2000

$\mu$BGA(Ball Grid Array) is growing in response to a great demand for smaller and lighter packages for the use in laptop, mobile phones and other evolving products. However it is not easy to find its defect by human visual due to in very small dimension. From this point of view, we are interested its development of a vision based automated inspection algorithm. For this, first a 2D view of $\mu$BGA is described under a special blue illumination. Second, a notation-invariant 2D inspection algorithm is developed. Finally a 3D inspection algorithm is proposed for the case of stereo vision system. As a simulation result, it is shown that 3D defect not easy to find by 2D algorithm can be detected by the proposed inspection algorithm.

• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2002.05a
• /
• pp.98-103
• /
• 2002

BGA(Ball Grid Array) 패키지의 솔더볼 패드 중의 하나인 Au/Ni-Co/Cu 금속층 위에 Bi가 첨가된 Sn-3.5Ag-$\chi$Bi 솔더볼을 리플로우시켰다. 리플로우한 후 130 $^{\circ}C$에서 열처리함에 따른 계면상 및 솔더 내부의 상변화를 관찰하였다. 계면에는 (Ni,Co)$_3$Sn$_4$외에 (Au,Ni,Co,Bi)Sn$_4$가 생성되었음을 관찰할 수 있었고, 솔더 내부에는 (Au,Ni,Co,Bi)SH$_4$, Ag$_3$Sn, Bi 상이 혼재되어 있었다. Nano-indentation에 의한 경도 측정 결과, Bi 함량 증가에 따라 경도는 증가하였으나, 볼전단(Ball Shear) 테스트 결과는 Bi가 증가됨에 따라 오히려 볼전단 강도값이 감소하였다. 이는 파면 검사 결과, 파괴 경로가 주로 계면의 금속간 화합물과 솔더 사이에서 진행함에 기인한 것이다. 솔더 내부의 파괴 경로를 가진 2.5Bi가 가장 우수한 볼전단 강도값을 나타내었는데, 이는 솔더내의 Bi의 고용강화에 기인한 것으로 보인다.

• Korean Journal of Materials Research
• /
• v.24 no.3
• /
• pp.166-173
• /
• 2014

The effects of printed circuit board electroless nickel immersion gold (ENIG) and organic solderability preservative (OSP) surface finishes on the electromigration reliability and shear strength of Sn-3.5Ag Pb-free solder bump were systematically investigated. In-situ annealing tests were performed in a scanning electron microscope chamber at 130, 150, and $170^{\circ}C$ in order to investigate the growth kinetics of intermetallic compound (IMC). Electromigration lifetime and failure modes were investigated at $150^{\circ}C$ and $1.5{\times}10^5A/cm^2$, while ball shear tests and failure mode analysis were conducted under the high-speed conditions from 10 mm/s to 3000 mm/s. The activation energy of ENIG and OSP surface finishes during annealing were evaluated as 0.84 eV and 0.94 eV, respectively. The solder bumps with ENIG surface finish showed longer electromigration lifetime than OSP surface finish. Shear strengths between ENIG and OSP were similar, and the shear energies decreased with increasing shear speed. Failure analysis showed that electrical and mechanical reliabilities were very closely related to the interfacial IMC stabilities.

• Journal of the Microelectronics and Packaging Society
• /
• v.15 no.4
• /
• pp.77-86
• /
• 2008

The reliability of leaded and lead-free solders of BGA type packages on a printed circuit board was investigated by employing the standard drop test and 4-point bending test. Tested solder joints were examined by optical microscopy to identify associated failure mode. Three-dimensional finite element analysis(FEM) with ANSYS Workbench v.11 was carried out to understand the mechanical behavior of solder joints under the influence of bending or drop impact. The results of numerical analysis are in good agreement with those obtained by experiments. Packages in the center of the PCB experienced higher stress than those in the perimeter of the PCB. The solder joints located in the outermost comer of the package suffered from higher stress than those located in center region. In both drop and bending impact tests, the lead-free solder showed better performances than the leaded solders. The numerical analysis results indicated that stress and strain behavior of solder joint were dependent on various effective parameters.

• Journal of the Microelectronics and Packaging Society
• /
• v.8 no.3
• /
• pp.37-42
• /
• 2001

The concerns of the toxicity and health hazard of lead in solders have demanded the research to find suitable lead-free solder alloys. It was discussed that effect of the intermetallic formation and structure on the reliability of solder joints. In this study, lead-free solder alloys with compositions of Sn/3.5Ag/0.75Cu, Sn/2.0Ag/0.5Cu/2.0Bi were applied to the 48 $\mu$BGA packages. Also, the lead-free solder alloys compared with eutectic Sn/37Pb solder using shear test under various aging temperature. Common $\mu$BGA with solder components was aged at $130^{\circ}C$, $150^{\circ}C$ and $170^{\circ}C$. And the each temperature applied to 300, 600 and 900 hours. The thickness of the intermetallics was measured for each condition and the activation energy for their growth was computed. The fracture surfaces were analyzed using SEM (Scanning Electron Microscope) with EDS (Energy Dispersive Spectroscopy). These results for reliability of lead-free interconnections are discussed.

• Korean Journal of Metals and Materials
• /
• v.49 no.8
• /
• pp.635-641
• /
• 2011

The effect of high shear speed on shear force, shear energy and fracture surface was investigated for the solder joint of a $Sn-_{3.0}Ag-_{0.5}Cu$ ball. For both ENIG and OSP pads, the shear force increased with an increase in shearing speed to 0.3 m/s. However, for an ENEPIG pad, the shear force increased with an increase in shear speed to 0.6 m/s and kept almost constant afterward. The shear energy decreased with an increase in shearing speed for ENIG and OSP pads. For the ENEPIG pad, however, the shear energy almost remained constant in a shearing speed range 0.3-3.0 m/s. The fracture mode analysis revealed that the amount of brittle fracture for the ENIG and the OSP pads increased with shearing speed, and a complete brittle fracture appeared at 1.0 m/s for ENIG and 2.0 m/s for OSP. However, the ENEPIG pad showed only a ductile fracture until 0.25 m/s, and a full brittle fracture didn't occur up to 3.0 m/s. The fracture mode matched well with the shear energy. The results from the high speed shear test of SAC305 were similar to those of SAC105.