• Korean Journal of Materials Research
• /
• v.32 no.5
• /
• pp.249-257
• /
• 2022

Transparent thin films of pure and nickel-doped ZrO₂ are grown successfully by sol-gel dip-coating technique. The structural and optical properties according to the different annealing temperatures (300 ℃, 400 ℃ and 500 ℃) are investigated. Analysis of crystallographic properties through X-ray diffraction pattern reveals an increase in crystallite size due to increase in crystallinity with temperature. All fabricated thin films are highly-oriented along (101) planes, which enhances the increase in nickel doping. Scanning electron microscopy and energy dispersive spectroscopy are employed to confirm the homogeneity in surface morphology as well as the doping configuration of films. The extinction coefficient is found to be on the order of 10^-2, showing the surface smoothness of deposited thin films. UV-visible spectroscopy reveals a decrease in the optical band gap with the increase in annealing temperature due to the increase in crystallite size. The variation in Urbach energy and defect density with doping and the change in annealing temperature are also studied.

• Journal of the Korean Applied Science and Technology
• /
• v.40 no.4
• /
• pp.913-923
• /
• 2023

In this study, a triboelectric nanogenerator was fabricated using the composite of teflon-based polymer and graphene flower, which are stable in air and have relatively high electronegativity. The composite was used to fabricate an electronegative layer of a nanogenerator using a spin-coating method. For the electropositive layer, a zinc oxide film was prepared using a sol-gel method. The fabricated triboelectric nanogenerator produced a maximum power of about 44 ㎼. In conclusion, since all the active layers of the triboelectric nanogenerator was made by the solution process, it is scalable to a large area.

• Journal of Powder Materials
• /
• v.21 no.5
• /
• pp.377-381
• /
• 2014

This work describes the coloration, chemical stability of $SiO_2$ and $SnO_2$-coated blue $CoAl_2O_4$ pigment. The $CoAl_2O_4$, raw materials, were synthesized by a co-precipitation method and coated with silica ($SiO_2$) and tin oxide ($SnO_2$) using sol-gel method, respectively. To study phase and coloration of $CoAl_2O_4$, we prepared nano sized $CoAl_2O_4$ pigments which were coated $SiO_2$ and $SnO_2$ using tetraethylorthosilicate, $Na_2SiO_3$ and $Na_2SiO_3$ as a coating material. To determine the stability of the coated samples and their colloidal solutions under acidic and basic conditions, colloidal nanoparticle solutions with various pH values were prepared and monitored over time. Blue $CoAl_2O_4$ solutions were tuned yellow color under all acidic/basic conditions. On the other hand, the chemical stability of $SiO_2$ and $SnO_2$-coated $CoAl_2O_4$ solution were improved when all samples pH values, respectively. Phase stability under acidic/basic condition of the core-shell type $CoAl_2O_4$ powders were characterized by transmission electron microscope, X-ray diffraction, CIE $L^*a^*b^*$ color parameter measurements.

• Journal of Electrochemical Science and Technology
• /
• v.11 no.1
• /
• pp.92-98
• /
• 2020

SnO₂-based high-capacity anode materials are attractive candidate for the next-generation high-performance lithium-ion batteries since the theoretical capacity of SnO₂ can be ideally extended from 781 to 1494 mAh g^-1. Here 3D etched Cu foam is applied as a current collector for electron path and simultaneously a substrate for the SnO₂ coating, for developing an integrated electrode structure. We fabricate the 3D etched Cu foam through an auto-catalytic electroless plating method, and then coat the SnO₂ onto the self-supporting substrate through a simple sol-gel method. The catalytic dissolution of Cu metal makes secondary pores of both several micrometers and several tens of micrometers at the surface of Cu foam strut, besides main channel-like interconnected pores. Especially, the additional surface pores on etched Cu foam are intended for penetrating the individual strut of Cu foam, and thereby increasing the surface area for SnO₂ coating by using even the internal of Cu foam. The increased areal capacity with high structural integrity upon cycling is demonstrated in the SnO₂-coated 3D etched Cu foam. This study not only prepares the etched Cu foam using the spontaneous chemical reactions but also demonstrates the potential for electroless plating method about surface modification on various metal substrates.

• Korean Journal of Materials Research
• /
• v.29 no.6
• /
• pp.385-391
• /
• 2019

In the present study, vanadium oxide($V_2O_5$) films for electrochromic(EC) application are fabricated using sol-gel spin coating method. In order to optimize the EC performance of the $V_2O_5$ films, we adjust the amounts of polyvinylpyrrolidone(PVP) added to the solution at 0, 5, 10, and 15 wt%. Due to the effect of added PVP on the $V_2O_5$ films, the obtained films show increases of film thickness and crystallinity. Compared to other samples, optimum weight percent(10 wt%) of PVP led to superior EC performance with transmittance modulation(45.43 %), responding speeds(6.0 s at colored state and 6.2 s at bleached state), and coloration efficiency($29.8cm^2/C$). This performance improvement can be mainly attributed to the enhanced electrical conductivity and electrochemical activity due to the increased crystallinity and thickness of the $V_2O_5$ films. Therefore, $V_2O_5$ films fabricated with optimized amount of PVP can be a promising EC material for high-performance EC devices.

• Journal of the Korean Ceramic Society
• /
• v.40 no.8
• /
• pp.777-783
• /
• 2003

The mechanical properties of B$_4$C/Al composites normally depend on the species and quantity of reaction products between B$_4$C and Al and then the control of reaction products is necessary to make desirable composites for lightweight advanced or armor materials. TiB$_2$ is chemically inert with aluminum and has a lower contact angle (85$^{\circ}$ at 100$0^{\circ}C$) to liquid aluminum than B$_4$C. Thus, TiB$_2$ coating on B$_4$C may lower infiltration temperature of aluminum when the B$_4$C/Al composites is fabricated by infiltration process. In this study, the effects of TiB$_2$ on the microstructure and mechanical properties of the B$_4$C/Al composites have been investigated. TiB$_2$ coated B$_4$C powder was prepared using the sol-gel technique. It was found that the B$_4$C surface is homogeneously covered with TiB$_2$ having a particles size of 20-50 nm. While the B$_4$C/Al composites prepared by infiltration after TiB$_2$ coating had 17 wt% of unreacted Al, on the other hand, the B$_4$C/Al composites without coating included 14 wt% of Al. As a result, the composites infiltrated after the coating showed higher fracture toughness and lower hardness. This strongly suggests that TiB$_2$ not only lowers the infiltration temperature, but also inhibits the reaction between B$_4$C and Al.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.29 no.2
• /
• pp.71-76
• /
• 2019

Recently, the demand of labels for product management is increasing, as the automation system becomes more common. the development of functional labels which can be used in various environments has been rapidly proceeded. In the case of a printed circuit board, barcode labels with thermal and chemical stability are generally used due to a high temperature process around $300^{\circ}C$ and chemical cleaning in the manufacturing process. However, the yellowing phenomenon of labels that can lower the resolution of printed barcode image still needs to be prevented. In this study, we prepared a composite coating layer using a silica inorganic binder and a titanium dioxide white pigment, and developed a functional labels with thermal and chemical stability. The silica inorganic binder prepared by sol-gel process was confirmed to show excellent adhesion and abrasion resistance with the polyimide film. The white coating layer could be formed on the polyimide film with mixing the silica inorganic binder and titanium dioxide white pigment. The prepared coating layer showed excellent whiteness and glossiness above $400^{\circ}C$. The excellent chemical stability of the coating layer was also confirmed by the chemical treatment with acidic (pH 1.6) and basic (pH 13.6) cleaners.

• Membrane Journal
• /
• v.21 no.2
• /
• pp.193-200
• /
• 2011

An amphiphilic graft copolymer comprising a poly(vinyl chloride) (PVC) backbone and poly (styrene sulfonic acid) (PSSA) side chains (PVC-g-PSSA) was synthesized via atom transfer radical polymerization (ATRP). Mesoporous titanium dioxide $(TiO_2)$ films with crystalline anatase phase were synthesized via a sol-gel process by templating PVC-g-PSSA graft copolymer. Titanium isopropoxide (TTIP), a $TiO_2$ precursor was selectively incorporated into the hydrophilic PSSA domains of the graft copolymer and grew to form mesoporous $TiO_2$ films, as confirmed by scanning electron microscopy (SEM) and X-ray diffraction (XRD) analysis. The performances of dye-sensitized solar cell (DSSC) were systematically investigated by varying spin coating times and the amounts of P25 nanoparticies. The energy conversion efficiency reached up to 2.7% at 100 mW/$cm^2$ upon using quasi-solid-state polymer electrolyte.

• Korean Chemical Engineering Research
• /
• v.53 no.1
• /
• pp.78-82
• /
• 2015

Hollow silica particles were prepared using sodium silicate and organic templates. Polystyrene latex (PSL) particles produced by dispersion polymerization were used as organic templates. PSL particles ranged from $1{\mu}m$ to $3{\mu}m$ in diameter were synthesized by adjusting the amount of 2,2'-azobisisobutyronitrile (AIBN). The PSL/$SiO_2$ core-shell particles were prepared by coating of silica nanoparticles originated from sodium silicate using sol-gel method. The organic templates were removed by the organic solvent, tetrahydrofuran (THF). Morphology of hollow silica particles was investigated with respect to types of the reaction medium and pH during the process. By changing the solvent from ethanol to water, hollow silica particles were successfully formed. Hollow silica particles with the uniform shell thickness were produced at low pH as well. The reflectivity of the as-prepared silica particles was measured in the range of the wavelength of UV and visible light. Hollow silica particles showed much better reflective properties than the commercial light reflector, Insuladd.

• Journal of the Korean Magnetics Society
• /
• v.12 no.2
• /
• pp.41-45
• /
• 2002

The low-field tunnel-type magnetoresistance (MR) properties of sol-gel derived $La_{0.7}Pb_{0.3}MnO_3(LPMO)$ thin film deposited on different substrate have been investigated. Polycrystalline thin films were fabricated by spin-coating on $SiO_2/Si(100)$ substrate and that with yttria-stabilized zirconia (YSZ) buffer layer, while c-axis-oriented thim film was grown on $LaAlO_3(001)$ (LAO) single crystal substrate. The full width half maximum (FWHM) of the rocking curve scan of LPMO/LAO film is $0.32^{\circ}$. Tunnel-type MR ratio is 0.52 % in $LPMO/SiO_2/Si$(100) film and that of $LPMO/YSZ/SiO_2/Si$(100) film is as high as 0.68 %, whereas that of LPMO/LAO(001) film is less than 0.4 % under the applied field of 500 Oe at 300 K. Well-pronounced MR hysteresis was registered with an MR peak in the vicinity of the coercive field. The low-field tunnel-type MR characteristics of thin films deposited on different substrates originates from the behavior of grain boundary properties.