• Journal of Welding and Joining
• /
• 제32권6호
• /
• pp.75-81
• /
• 2014

Usage of heavy metal element (Pb, Hg and Cd etc.) in electronic devices have been restricted due to the environmental banning of the European Union, such as WEEE and RoHS. Therefore, it is needed to develop the Pb-free solder plated ribbon in photovoltaic (PV) module. This study described that degradation characteristics of PV module under damp heat (DH, $85^{\circ}C$ and 85% R.H.) condition test for 1,000 h. Solar cell ribbons were utilized to hot dipping plate with Pb-free solder alloys. Two types of Pb-free solder plated ribbons, Sn-3.0Ag-0.5Cu (SAC305) and Sn-48Bi-2Ag, and an electroless Sn-40Pb solder hot dipping plated ribbon as a reference sample were prepared to evaluate degradation characteristics. To detect the degradation of PV module with the eutectic and Pb-free solder plated ribbons, I-V curve, electro-luminescence (EL) and cross-sectional SEM analysis were carried out. DH test results show that the reason of maximum power (Pm) drop was mainly due to the decrease fill factor (FF). It was attributed to the crack or oxidation of interface between the cell and the ribbon. Among PV modules with the eutectic and Pb-free solder plated ribbon, the PV module with SAC305 ribbon relatively showed higher stability after DH test than the case of PV module with Sn-40Pb and Sn-48Bi-2Ag solder plated ribbons.

• 보존과학연구
• /
• 통권6호
• /
• pp.121-196
• /
• 1985

Atomic absorption spectrophotometer was used for analyzing each 10elements(Cu, Pb, Sn, Zn, Sb, Fe, Ni, Ag, Co and Mn)on 64 Chinese coinsre covered from Shinan seabed sunken ship. The results show that Cu, Pb and Sn were found to be a major elements consisting of coins and its composition ratio was 6 to 2 to 1.The composition of trace elements on coins was classified 3 levels : Sb, Fe and Zn(0.02%-2.2%), Ag, Ni, and Co(50 ppm-5500 ppm) and Mn(Trace). Theam ount of major elements, Cu and Sn were decreased while increased in Pbby the passage of ages (10th - 13th century) in China. There seems to be no systematic compositional change in major elements but content in trace elements was confirmed to increase with age.

• 한국마이크로전자및패키징학회:학술대회논문집
• /
• 한국마이크로전자및패키징학회 2002년도 추계기술심포지움논문집
• /
• pp.105-108
• /
• 2002

환경에 관한 관심이 증대되면서 Sn37Pb 솔더를 대체하기 위한 새로운 무연솔더의 개발이 진행되고 있다1). 또한 연구의 초점이 되고 있는 것이 플럭스의 사용에 관한 것이다. 플럭스는 솔더의 산화막을 제거하는데 필수적이지만, 플럭스 세정제의 독성 문제로 무플럭스 솔더링에 대한 관심이 크게 증대되고 있다2),3). 무플럭스 솔더링의 방법에는 여러 가지가 있으며, 그 중 한가지가 플라즈마를 이용한 방법이다4). 본 연구에서는 솔더표면의 이물질과 산화막을 제거하기 위한 플라즈마 처리가 접합 후, 접합부에 미치는 영향에 대해서 알아보았다. 기판은 Evaporator를 이용하여 Au/Cu/Ni/Al UBM을 증착한 Si-wafer를 사용하였다. 사용된 솔더는 Sn37Pb, Sn3.5Ag와 Sn3.5Ag0.7Cu 솔더볼이며, 열중 및 적외선 겸용 리플로 머신과 Ar＋H$_2$를 이용한 플라즈마 에쳐를 사용하여 범프를 형성하였다. 플라즈마 처리가 계면의 미세조직과 기계적 강도에 끼치는 영향을 알아보기 위하여 플라즈마 처리된 시편과 리플로 한 후의 시편을 비교 분석하였다. 전단시험기로 계면의 강도를 측정하였으며, 주사전자현미경으로 범프의 표면과 계면 및 전단파면을 관찰하고 이에 대하여 고찰하였다. 산화막제거를 위한 플라즈마 처리가 저음점인 솔더의 미세조직을 기존의 솔더링 접합부와는 다르게 변화시킴으로써 솔더부의 전체적인 특성에 영향을 끼치는 것을 알 수 있었다.

• 자원리싸이클링
• /
• 제10권5호
• /
• pp.29-35
• /
• 2001

본 연구는 폐컴퓨터 인쇄회로기판으로부터 Au와 Ag 및 유가금속을 회수하기 위해 수행하였다. 시료는 슈레더를 사용하여 1 mm이하 입자로 분쇄한 후 정전선별하여 약 70%의 부도체를 분리제거하고, 회수된 30%의 도체는 자력선별에 사용하였다. 자력선별에 의해 42%의 자성체는 제거되고 58%의 비자성체를 유가물 침출 원료로 사용하였으며, 비자성체의 Au및 Ag의 함량은 각각 0.227mg/g, 0.697 mg/g 이였다. 회수된 물질로부터 Cu, Fe, Zn, Ni, Al를 침출분리하기 위해 황산과 과산화수소수를 혼합한 침출용매를 사용하였다. 2.0M 황산, 0.2M과산화수소수, 반응온도 $85^{\circ}C$에서 95%이상의 Cu, 로n, Fe, Ni, Al를 침출 할 수 있었으며, Au와 Ag는 침출되지 않았다. 반면에 황산침출 후 잔사로부터 Au, Ag의 선택적인 침출을 위해 혼합용매(0.2M(NH$_4$)$_2$S$_2$O$_3$, 0.02M $CusO_4$,0.4M NH$_4$OH)를 사용하였을 때 Ag는 100%, Au는 95%이상 침출하였다 또한 최종 잔사로부터 Pb침출은 NaCl용액을, Sn침출은 황산용액을 사용하였으며 침출율은 각각 95%, 98%를 나타냈다.

• Journal of Welding and Joining
• /
• 제23권4호
• /
• pp.34-40
• /
• 2005

There have been numerous approaches to examine the bonding strengths of solder joints. However, despite the technical and practical limitations, the precedent test methods such as the ball shear and ball pull tests are being used in industrial applications. In this study, the optimum jaw pressure with the modified protrusion jaw was introduced in order to obtain higher successful rate f3r ball pull testing. Furthermore, the pull strengths and fracture modes of Sn-8Zn-3Bi, Sn-4Ag-0.7Cu, and Sn-37Pb eutectic solder after isothermal aging tests ($100^{\circ}C,\;150^{\circ}C$), were evaluated with the protrusion jaw. The pull strength-displacement hysteresis curves and fracture surfaces were carefully investigated to evaluate the correlation between the pull strengths and the fracture modes of each solder. In conclusion, it is verified that Au-Zn IMCs (Intermetallic Compounds) have a detrimental effect on the pull strengths and changed fracture modes of Sn-8Zn-3Bi solder. Meanwhile, the microstructure transformation influences the degradation of pull strengths of Sn-4Ag-0.7Cu and Sn-37Pb solders.

• 대한금속재료학회지
• /
• 제48권11호
• /
• pp.1041-1046
• /
• 2010

The reactions between a Sn-3.0Ag-0.5Cu solder alloy and electroless Ni/electroless Pd/immersion Au (ENEPIG) surface finishes with various Pd layer thicknesses (0, 0.05, 0.1, 0.2, $0.4{\mu}m$) were examined for the effect of the Pd layer on the massive spalling of the $(Cu,Ni)_6Sn_5$ layer during reflow at $235^{\circ}C$. The thin layer deposition of an electroless Pd (EP) between the electroless Ni ($7{\mu}m$) and immersion Au ($0.06{\mu}m$) plating on the Cu substrate significantly retarded the massive spalling of the $(Cu,Ni)_6Sn_5$ layer during reflow. Its retarding effect increased with an increasing EP layer thickness. When the EP layer was thin (${\leq}0.1{\mu}m$), the retardation of the massive spalling was attributed to a reduced growth rate of the $(Cu,Ni)_6Sn_5$ layer and thus to a lowered consumption rate of Cu in the bulk solder during reflow. However, when the EP layer was thick (${\geq}0.2{\mu}m$), the initially dissolved Pd atoms in the molten solder resettled as $(Pd,Ni)Sn_4$ precipitates near the solder/$(Cu,Ni)_6Sn_5$ interface with an increasing reflow time. Since the Pd resettlement requires a continuous Ni supply across the $(Cu,Ni)_6Sn_5$ layer from the Ni(P) substrate, it suppressed the formation of $(Ni,Cu)_3Sn_4$ at the $(Cu,Ni)_6Sn_5/Ni(P)$ interface and retarded the massive spalling of the $(Cu,Ni)_6Sn_5$ layer.

• 마이크로전자및패키징학회지
• /
• 제21권3호
• /
• pp.43-50
• /
• 2014

전자 제품의 경박 단소화 및 고집적화가 이루어 지면서 실리콘 집과 인쇄회로기판의 인터커넥션의 고신뢰도가 요구되고 있다. 본 연구는 Sn-4.0wt%Ag-0.5wt%Cu (SAC405) 솔더와 다양한 무전해 Ni-P 도금 두께에서의 high speed shear 에너지 및 파괴 모드를 연구하였다. 파괴 모드 분석을 위하여 집속이온빔(FIB) 분석이 이용되었다. 질산 기상 처리하지 않은 $1{\mu}m$ Ni-P 시편에서 낮은 shear 에너지가 나왔으며, 이는 솔더레지스트 선단에서 파단의 원인을 제공하는 것이 확인되었다. 질산 기상 처리한 시편에서 무전해 Ni-P 도금 두께가 커질수록 취성 파괴 모드는 감소한다. 또 Ni-P 도금 두께와 표면 거칠기(Ra)는 반비례 관계를 가진다. 이는 Ni-P 도금의 표면 거칠기를 낮추면 SAC405 솔더 조인트의 신뢰도를 향상시킨다는 사실을 나타낸다.

• 대한화학회지
• /
• 제15권2호
• /
• pp.49-54
• /
• 1971

It is shown that the impurities of Cu(II), Pb(II), Zn(II) and Ag(I) in Bismuth metal and the components of Pb(II), Zn(II) and Sn(IV) in Bismuth alloy are separated into their components from each other by elutions through $3.14cm^2{\times}10cm$ cation exchange resin, $Dowex\;50w\;{\times}\;8$ (100~200 mesh), column with the mixed solutions of HAc and NaAc as the eluents. The elution curve of Fe(III) has a long tailing and is not separated quantitatively from Bi(III). The eluents used for this separation are as follows; 1M HAc + 0.1M NaAc (pH 3.36) for Fe(III) and Bi (III). 0.3M HAc + 0.3M NaAc (pH 4.70) for Cu(II), Pb(II) and Zn(II). 0.5M HAc + 0.5M NaAc (pH4.70) for Ag(I) and Sn(IV). The analysis of cations eluted are carried out by spectrophotometry and EDTA titrimetry. Their recoveries are more than 99%.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2006년도 춘계 학술대회 개요집
• /
• pp.21-23
• /
• 2006

The microstructural investigation and thermo-mechanical reliability evaluation of the Sn-3.0Ag-0.5Cu solder bumped flip chip package were carried out during the thermal shock test of the package. In the initial reaction, the reaction product between the solder and Cu mini bump of chip side was Cu6Sn5 layer, while the two phases which were (Cu,Ni)6Sn5 and (Ni,Cu)3Sn4 were formed between the solder and Ni-P layer of the package side. The cracks were occurred at the corner solder joints after the thermal shocks of 400 cycles. The primary failure mechanism of the solder joints in this type of package was confirmed to be thermally activated solder fatigue failure.

• 한국자동차공학회논문집
• /
• 제22권3호
• /
• pp.90-96
• /
• 2014

The conventional SnPb solders were widely used for several decades in the electronic packing system due to the superior mechanical properties such as low melting point, better wettavility and good mechanical fatigue. However, in recent years, owing to adverse effect on the human health and environment, conventional SnPb solders have been replaced by Lead-free solders. In this research, the shear punch(SP) test of Sn-4Ag-(Cu)/Ni pad was performed. Pb-free solder alloys which are the environmentally friendly of the electronic components were performed at $150^{\circ}C$ for 100hr~1000hr to artificial aging processing. In order to evaluate the mechanical properties of solder joints, the SP test was conducted at $30^{\circ}C$ and $50^{\circ}C$. As a result, the maximum shear strength of almost the whole specimens was decreased with the increase in aging time and temperature of SP test. The mechanical properties of Sn-4Ag-0.5Cu solder were most excellent in all Pb-free solder which were produced by the SP test at $30^{\circ}C$.