• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2003.11a
• /
• pp.265-269
• /
• 2003

Sn(또는 SnAg)/Ni(P)와 Sn/Cu 계의 열사이클동안 형성되는 금속간화합물에 의해 유기되는 응력의 변화를 in-situ로 관찰하였다. Sn(또는 SnAg)/Ni(11.7P) 박막은 계면반응으로 인해 $Ni_3P$와 $Ni_3Sn_4$ 상이 형성되고 이때 인장응력이 발생하였으며, 한편, Sn(또는 SnAg)/Ni(3P) 박막의 계면반응에 의해서는 동일한 $Ni_3P$와 $Ni_3Sn_4$ 상이 형성됨에도 불구하고 압축응력이 발생하였다. SmAg를 사용할 때 형성되는 $Ag_3Sn$이 응력에 미치는 영향은 거의 없었다. Sn/Cu 박막의 경우는 계면반응 초기에는 인장응력이 발생하였고 어느 정도 이상 반응이 진전됨에 따라 압축응력이 발생하였고 최종적으로 $Cu_3Sn$ 상이 형성되었다. 초기의 인장응력은 계면에서 원자들의 intermixing 베 의한 것이고 압축응력은 Sn 방향으로 일방향 성장하는 금속간화합물 형성에 기인한다.

• Journal of the Microelectronics and Packaging Society
• /
• v.7 no.1
• /
• pp.19-24
• /
• 2000

To make stacked chip packages far high-density packaging of memory chips used in workstations or PC severs, several lead-frames are to be connected vertically. Fer this purpose. Sn or Sn/Ag were electrochemically deposited on Cu lead-frames and their microstructures were examined by XRD and SEM. Then, two specimens were annealed at $250^{\circ}C$ for 10 min. and pressed to be joined. The shear stresses of joined lead-frames were measured fur comparison. In the case of Sn only, $Cu_3Sn$ was formed by the reaction of Sn and Cu lead-frames. In the case of Sn/Ag, besides $Cu_3Sn$. $Ag_3Sn$ was formed by the reaction of Sn and Ag. Compared to joined specimens made from Sn only, those made from Sn/Ag showed 1.2 times higher shear stress. This was attributed to the $Ag_3Sn$ phase formed at the joined interface.

• Korean Chemical Engineering Research
• /
• v.45 no.5
• /
• pp.433-441
• /
• 2007

This work investigated the stability of a Sn-modified Pt electrode, which was used for reduction of nitrate, fabricated by an adsorption or electro-deposition of Sn on Pt. In order to find the causes for instability of the electrode, the effects of the solutions in which the electrode was used and the potential applied to the electrode on the electrochemical and metallurgical behaviors of Sn on Pt were studied. The Sn of freshly- prepared modified-Sn Pt electrode existed as Sn hydroxide form, which brought about an easy loss of the electro-activity of the electrode even staying in water, especially in acid solution. When the Sn-modified Pt electrode was used for the reduction of nitrate, the electro-activity of the electrode was affected depending on the potential applied to the electrode. When a more negative potential than the redox equilibrium potential between $Sn(OH)_2$ and Sn was applied to the electrode, the Sn hydroxide was converted to Sn that could diffused into Pt, which leaded to the loss of electro-activity of the electrode as well. The solid diffusion of Sn increased linearly with the applied potential. The Sn-electrodeposited Pt electrode which had more Sn on the electrode was more favorable to maintaining the integrity of the electrode during the reduction of nitrate than the Sn-adsorbed Pt electrode prepared in the under-potential deposition way.

• Journal of the Microelectronics and Packaging Society
• /
• v.12 no.1 s.34
• /
• pp.35-40
• /
• 2005

The oxidation of pure Sn and Sn-0.7Cu, Sn-3.5Ag, Sn-lZn, and Sn-9Zn alloys at $150^{\circ}C$ was investigated. Both the chemical nature and the amount of oxides were characterized using electrochemical reduction analysis by measuring the electrolytic reduction potential and total transferred electrical charges. X-ray photoelectron spectroscopy (XPS) was also conducted to support the results of reduction analysis. The effect of Cu, Ag and Zn addition on surface oxidation of Sn alloys is reported. For Sn, Sn-0.7Cu and Sn-3.5Ag, SnO grew first and then the mixture of SnO and $SnO_2$ was found. $SnO_2$ grew predominantly for a long-time aging. For Zn containing Sn alloys, both ZnO and $SnO_2$ were formed. Zn promotes the formation of $SnO_2$. Sn oxide growth rate of Pb-free solder alloys was also discussed in terms of alloying elements.

• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2003.11a
• /
• pp.114-117
• /
• 2003

본 연구에서는 계산을 통해 나온 Sn-Ag-Cu 삼원계 공정점(Sn-3.7Ag-0.9Cu)을 바탕으로 그 근처의 응고경로가 다른 6가지 조성(Sn-4.6Ag-0.4Cu, Sn-4.9Ag-1.0Cu, Sn-3.9Ag-1.3Cu, Sn-2.2Ag-1.2Cu, Sn-2Ag-0.7Cu, Sn-2.7Ag-0.3Cu)에 대한 솔더합금의 미세조직을 관찰하였다. 응고경로는 $L\;\rightarrow\;L+Primary\;\rightarrow\;L+Primary+Secondary\;\rightarrow\;Ternary\;Eutectic+Primary+Secondary$로 되며 6가지 경우를 예상할 수 있다 솔더합금의 미세조직은 느린 냉각으로 인하여 빠른 냉각, 보통 냉각에 비해 상대적으로 커다란 $\beta-Sn$ dendrite를 보였고 $Ag_3Sn,\;Cu_6Sn_5$과는 다르게 $\beta-Sn$는 약 $30^{\circ}C$의 과냉(DSC분석)이 존재하게 되어 Sn-4.6Ag-0.4Cu의 경우에는 $Ag_3Sn$상이, Sn-2.2Ag-1.2Cu의 경우에는 $Cu_6Sn_5$가 과대성장을 하였다. 솔더의 기계적 특성을 살펴보고자 Cu 기판위에서 각 조성의 솔더볼을 솔더링한 후 다양한 냉각 속도를 적용하여 reflow 솔더링을 하고 솔더/기판 접합에 대한 전단 강도 시험을 실시했다. 냉각 속도가 빠를수록 $\beta-Sn$의 dendrite가 미세해져서 높은 전단 강도를 보였고 6가지 조성의 솔더볼중 공정조직 분율이 낮은 Sn-2Ag-0.7Cu 조성의 경우에서 낮은 전단 강도가 나타났다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.07a
• /
• pp.658-662
• /
• 2000

The microstructure, adhesion strength and conductivity of electroplated Sn-Cu Films on Alloy42 lead Frame were measured for comparison. In the case of electroplated 90Sn10Cu, 99Sn1Cu, Cu$\sub$10/Sn$_3$Phase was formed and Ni$_3$Sn$_2$Phase was formed after 200$^{\circ}C$, 30min annealing. In the case of electroplated 99Sn1Cu, Cu$\sub$10/Sn, Ni$_3$Sn phases were formed and Ni$_3$Sn$_4$, Ni$_3$Sn$_4$phases were formed after 200$^{\circ}C$, 30min annealing. 90Sn10Cu film was measured better uniformity, adhesion strength and conductivity than 99Sn1Cu.

• Korean Journal of Materials Research
• /
• v.23 no.2
• /
• pp.143-148
• /
• 2013

Well-distributed $SnO_2$-Sn-$Ag_3Sn$ nanoparticles embedded in carbon nanofibers were fabricated using a co-electrospinning method, which is set up with two coaxial capillaries. Their formation mechanisms were successfully demonstrated. The structural, morphological, and chemical compositional properties were investigated by field-emission scanning electron spectroscopy (FESEM), bright-field transmission electron microscopy (TEM), X-ray diffraction (XRD), and X-ray photoelectron spectroscopy (XPS). In particular, to obtain well-distributed $SnO_2$ and Sn and $Ag_3Sn$ nanoparticles in carbon nanofibers, the relative molar ratios of the Ag precursor to the Sn precursor including 7 wt% polyacrylonitrile (PAN) were controlled at 0.1, 0.2, and 0.3. The FESEM, bright-field TEM, XRD, and XPS results show that the nanoparticles consisting of $SnO_2$-Sn-$Ag_3Sn$ phases were in the range of ~4 nm-6 nm for sample A, ~5 nm-15 nm for sample B, ~9 nm-22 nm for sample C. In particular, for sample A, the nanoparticles were uniformly grown in the carbon nanofibers. Furthermore, when the amount of the Ag precursor and the Sn precursor was increased, the inorganic nanofibers consisting of the $SnO_2$-Sn-$Ag_3Sn$ nanoparticles were formed due to the decreased amount of the carbon nanofibers. Thus, well-distributed nanoparticles embedded in the carbon nanofibers were successfully synthesized at the optimum molar ratio (0.1) of the Ag precursor to the Sn precursor after calcination of $800^{\circ}C$.

• Proceedings of the KWS Conference
• /
• 2002.10a
• /
• pp.481-486
• /
• 2002

We have investigated the effects of plating materials for Cu lead (Sn-lOPb, AwPdJNi, Sn-3.5Ag, Sn-3Bi and Sn-0.7Cu) on properties of QFP joints using a Sn-8Zn-3Bi solder. The results were compared with the joints using Sn-3. 5Ag-0. 7Cu and Sn-37Pb solders. As a result, the joints with the Sn-3.5Ag, Sn-3Bi and Sn-0.7Cu plated Cu lead had the reliability comparable to those of the Sn-3.5Ag-0.7Cu and Sn-37Pb soldered joints with respect to the joint strength after the high temperature holding tests at 348K to 423k. In particular, the joint with the Sn-3.5Ag plated Cu lead had the best reliability. This is caused by the low growth rate of a Cu-Sn interfacial reaction layer that degrades the joint strength of the soldered joints. Consequently, the Sn-3.5Ag plating was found to be most feasible plating for the Sn-8Zn-3Bi soldered joint.

• Journal of Welding and Joining
• /
• v.16 no.3
• /
• pp.157-166
• /
• 1998

Recently as environmental pollution caused by Pb has posed a serious threat to the global environment, the trend to regulate the usage of Pb in electronic industry is one the rise. Currently, the solder alloy with high Pb content, Sn-37%Pb, is utilized in the electronic assembly therefore, the objective of this study is to develop an alternative solder alloy for the existing Sn-37%Pb solder alloy. First thing, this work choosed Sn-5%Pb-1.5%Ag, Sn-5%Pb-1.5%Ag-x%Bi(x=1~5%) for candidate solder alloys, and examined their properties such as melting range, wettability, microhardness, tensile property, oxidation behavior and microstructure. Wettability was on the same level of Sn-37%Pb. Dissolution of Pb ion in Sn-5%Pb solder was 0.46ppm. This solder alloy revealed cellular dendrite microstructure $\beta$-Sn matrix, Pb-rich phase, Ag/Sn, and Cu/Sn Intermetallic compounds. The range of solidification temperature was within 3$0^{\circ}C$. Also these alloy displayed higher tensile strength and lower elongation than Sn-37%Pb. The resistance of oxidation in Sn-5%Pb-1.5%Ag solder alloy was superior to that of Sn-37%Pb solder alloy. But that of Sn-5%Pb-1.5%Ag-5%Bi solder alloy was equal to that of Sn-37%Pb solder alloy.

• Journal of the Microelectronics and Packaging Society
• /
• v.15 no.4
• /
• pp.9-15
• /
• 2008

Microstructure and contact resistance of the Au-Sn solder joints were characterized after flip-chip bonding of the Au/Sn bumps processed by successive electrodeposition of Au and Sn. Microstructure of the Au-Sn solder joints, formed by flip-chip bonding at $285^{\circ}C$ for 30 sec, was composed of the $Au_5Sn$+AuSn lamellar structure. The interlamellar spacing of the $Au_5Sn$+AuSn structure increased by reflowing at $310^{\circ}C$ for 3 min after flip-chip bonding. While the Au-Sn solder joints formed by flip-chip bonding at $285^{\circ}C$ for 30 sec exhibited an average contact resistance of 15.6 $m{\Omega}$/bump, the Au-Sn solder joints reflowed at $310^{\circ}C$ for 3 min after flip-chip bonding possessed an average contact resistance of 15.0 $m{\Omega}$/bump.