• Journal of the Korean Ceramic Society
• /
• v.37 no.7
• /
• pp.645-650
• /
• 2000

Effects of the chemical composition and sintering atmosphere on the formation of reaction phases and physical properties of reactive hot-pressed TiB2-AlN-BN composites were investigated. At N2 atmosphere, TiN was formed by the reaction between Ti and N2, which inhibited the densification and results in inferior mechanical-and electrical properties of the composites. However, at Ar atmosphere, enhanced densification and physical properties of composites were obtained due to that the TiN formation reaction was excluded. Densification of the composites was also hindered by BN, therefore, inferior mechanical-and electrical properties of composites were obtained with amount of BN in the starting materials. At Ar atmosphere, TiB2-AlN-BN composites having 318 MPa of flexural strength, 3.5 MPa.m1/2 of fracture toughness and 276$\mu$Ω.cm of electrical resistivity were fabricated from mole ratio 1:2:1.6 of Ti-Al-BN mixtures.

• Journal of Powder Materials
• /
• v.5 no.4
• /
• pp.241-249
• /
• 1998

Sintering kinetics of ball-milled $MoSi_2$ was studied with the addition of Ni. $MoSi_2$ powder with the average particle size of 1 $\mu\textrm{m}$ was obtained from ball-milling of 10 $\mu\textrm{m}$ powder. Small amount of Ni was added to the ball-milled $MoSi_2$ powder by salt solution and reduction method. The powder was compacted into cylindrical shape at 200 MPa and isothermally sintered in a $H_2$ atmosphere at the temperature range of 1100~$1400^{\circ}C$ for 3~600 minutes. The changes of linear shrinkage and sintered density were monitored as a function of sintering time. The microstructure was observed by using optical microscopy and scanning electron microscopy. Phases were identified by X-ray diffratometer and electro-probe micro analysis. Sintering kinetics of Ni-added powder was compared to as-milled powder and the apparent activation energy was calculated from Arrhenius plot.

• Journal of the Korean Ceramic Society
• /
• v.33 no.8
• /
• pp.863-870
• /
• 1996

Fabricated modified PZT system for pyroelectric IR sensor were analyzed and characterized for dielectric piezoelectric and pyroelectric properties. Particle size and distribution of source powders were controlled by attrition milling process. 0.05PSS+yPT+(0.95-y)PZ+0.4 wt%MnO2 system was fabricated and investigated sintering density crystal structure and micro-structure through sintering conditions sintering temperature and sintering atmosphere. The poled sintered system of y=0.11 showed the lowest dielectric constant. The dielectric constants were increased with increasing y-mole ratio. The pyroelectric properties of modified PZT systems which were assembled to TO-5 package were measured by IR measurement system average out-voltage of 0.05PSS+0.1PT+0.84PZ+ wt%MnO2 was 3V.

• The Transactions of the Korean Institute of Electrical Engineers
• /
• v.39 no.2
• /
• pp.183-191
• /
• 1990

Polycrystalline CdS film have been prepared by coating a slurry constiting of CdS, CdCl2, various amount of InCl3 and propylene glycol on glass substrate and by sintering in a nitrogen atmosphere, and their sintering behaviors, electrical properties and optical properties have been investigated. As the amount of InCl3 increases, the enhancing effect of CdCl2 on sistering decreses resulting in a sharp decrease in optical transmittance and an increase in electrical resistivity. The carrier concentration is almost independent of InCl3 added due to the occurrence of chlorine doping and to the compensating effect of indium dopant. Microstructure an optical properties of CdS film, which contain CdCl2 and InCl3 before sintering, can be improved by sintering in a sealed boat.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1988.05a
• /
• pp.88-91
• /
• 1988

In this paper, PLZT Ceramics were fabricated by two stage sintering method whose first stage vacuum hot pressing and second stage PbO atmosphere sintering. Using Graphite Mould instead of Alumina Mould in first stage prevented the adhision between PLZT substrate and the mould. The grain sizes of PLZT Ceramics were controlled by varying the hot pressing time and second sintering time.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.1126-1127
• /
• 2006

The kinetics of sintering of Co-Fe materials was studied. The main objective was to establish the effects of iron content and sintering parameters on the microstructure and phase composition of the as-sintered material. Specimens containing from 3 to 25 wt.% iron were sintered in a dilatometer for one hour at 900, 1000 and $1150^{\circ}C$ in either hydrogen or nitrogen atmosphere. The length of specimens during the heating, hold at temperature and cooling steps were monitored to establish the sample's shrinkage. Microstructural observations were carried out on polished and etched transverse sections which were also subjected to the X-ray phase analysis.

• Journal of the Korean Ceramic Society
• /
• v.17 no.2
• /
• pp.89-95
• /
• 1980

The effect of non-stoichimetry and sintering temperature on the magnetic properties of materials in the system $Ni_{0.39}Zn_{0.61}Fe_{2.0+x}O_4$ have been investigated. The value of x used in initial weighing of oxides were varied from -0.04 to -0.12. The value of x, however, appears to be from +0.04 to -0.04 after ferrite powder preparation due to iron pick up during ball mill mixing and grinding. The densities of specimens which were deficientinrion were higher than those with excess ion. Specimens with near stoichiometric composition showed maximum initial permeability an dminimum coercivity whereas high values of quality factor (Q) were observed in iron deficient specimens. The quality factor decreased monotonically with increasing sintering temperature, but the permeability showed maxima with increasing sintering temperature. Thus highest value of figure of merit $\mu$Q was obtained in composition $Ni_{0.39}Zn_{0.61}Fe_{1.98O4}$ sintered at 100$0^{\circ}C$ for 3 hrs. in an air atmosphere.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.209-210
• /
• 2006

Organic binders are usually pre-mixed with ceramic powders to enhance the formability during the shape forming process. These binders, however, must be eliminated before sintering in order to avoid pore formation and unusual grain growth during sintering. The present work was performed to investigate the effects of residual binder on grain growth behavior during sintering of $Pb(Mg_{1/3}Nb_{2/3})O_3-PbTiO_3$ piezoelectric ceramics. The microstructures of sintered samples were examined for various thermal processes and atmosphere at debinding. Addition of binder seems to promote abnormal grain growth especially in incompletely debinded regions and to make the grain shape change from corner-rounded to faceted.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.274-275
• /
• 2006

The sintering behavior of titanium-titanium nitride nanocomposite powders has been studied by dilatometry. Titanium. titanium nitride nanocomposite powders were produced by the reactive milling of micron sized titanium powder $(12\;{\mu}m)$ in nitrogen atmosphere. The Ti-TiN nanocomposite powders milled for various durations along with the initial micron sized Ti powders were then sintered in the temperature range of $450-1000^{\circ}C$ by a constant rate of heating $(10^{\circ}C/min)$. The linear shrinkage, shrinkage rate, activation energy for sintering and microstructure has been studied and discussed as a function of milling time.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.614-615
• /
• 2006

Investigation of influence the morphology of initial powder particles, application pore-formers for sintering of nickel powders and application of flux for sintering of aluminum was made. Using different methods was prepared material with size of porous in wide range size of pores ($1-500{\mu}m$). Using the flux for gravity sintering of aluminum in air atmosphere was manufactured porous material with porosity about 45%..