• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.9 no.6
• /
• pp.1555-1559
• /
• 2008

The characteristics of 304 (Fe-18%Cr-12%Ni) and 316L (Fe-18%Cr-13%Ni-2.4%Mo) austenite stainless-steel compacts sintered with $5{\sim}15{\mu}m$ powder were investigated and the results led to the following conclusions: (1) When the sintering time was 3.6ks, the relative density of sintered compacts was $95{\sim}98%$, regardless of any other sintering condition. (2) When a vacuum sintering was done with $5{\mu}m$ stainless steel powders, almost fully-dense sintered compacts were obtained at is = 57.6ks. (3) The amount of residual oxygen in 304 and 316L sintered compacts was $0.5{\sim}0.6%$, regardless of sintering atmosphere. (4) The amount of residual oxygen in the vacuum sintered compact decreased more than 0.3 % due to addition of carbon powder, thereby reducing the formation of oxides. Furthermore, the addition of carbon improved the density of sintered compact, which enables us to make a fully-dense high performance sintered compact.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.16 no.2
• /
• pp.71-75
• /
• 2006

The aggregates made of clay, carbon and $Fe_2O_3$ were prepared to investigate the mechanism of black core formation and the property differences at various sintering atmospheres. The aggregates were sintered at oxidized, neutralized and reduced atmospheres. The specific gravity, absorption rate, percent of black core area were measured at various compositions and sintering atmospheres. The aggregates sintered at oxidized atmosphere showed clear border between shell and black core area. Hence, the aggregates sintered at reduced and neutralized atmospheres showed only black core area in the cross-section of the aggregates. The specific gravity of the aggregates sintered at reduced atmosphere increased with increasing carbon contents and that was the lowest of all aggregates sintered at various atmospheres. Adsorption rate increased with increasing carbon contents at all atmospheres.

• Journal of Powder Materials
• /
• v.7 no.1
• /
• pp.42-49
• /
• 2000

Densificationbehavior of conventional austenitic stainless steel powder compacts was studied by comparing the relative density of sintered compact(Ds)with that of green compacts(Dg)prepared with various catbon contents and P/M process. Dg of 304and 316 powders by warm compaction under pressure of 686 MPa at heating temperature of powder(553K) and dies (573K) were 80% and 81%, repectively, whichwere 2 and 3% higher than those of conventional green compacts at the same pressure. Ds of 304 compacts sintered at 1373K in H2 gas has the same value of 84% max. regardless of compacting temperature, and Ds of 316 compacts at the same sintering conditions were 80% by conventional compaction and 83% by warm compaction. Oxygen contents of 304 and 316 sintered compacts were increased 1.43∼2.94% and 0.010∼0.921% higher than those of raw powders and warm green compacts, respectively. In other case, Ds of 316 compacts sintered at 1573K in vacuum had the same value of 86%max. And Ds of 316 compacts at the same sintering conditions were 83% and 86% by conventional and warm compaction, respectively. Oxygen contents of 304 sintered compacts were 0.321% and 0.360%, and in case of 316, they were 0.419% and 0.182% by the respective compating condition. With carbon additions in the range 0.1∼0.6% Ds increased to the extent of 86∼89% in 304 sintered compacts, and to 82∼84% and 85∼87% in 316 according to different two compacting peocesses compared to those of sintered compacts without carbon addition.

• Journal of Powder Materials
• /
• v.1 no.2
• /
• pp.135-144
• /
• 1994

Silicon carbide powder was prepared from mixtures of Sangdong silica sand and carbon black by SHS (Self propagating High temperature Synthesis) method which utilizes magnesiothermic reduction of silica. In the powder preparation process, the reacted powder was leached by chloric acid to remove the magnesium oxide and was subsequently roasted to remove free carbon. The impurities were mostly eliminated by hot acid treatment. The resultant SiC powder showed the mean particle size of 0.22 ${\mu}{\textrm}{m}$ and the specific surface area of $66.55 m^2/g$. The SiC powder was mixed with 1 wt% of boron and of carbon to increase densification rate. The mixed powder was pressed and sintered pressurelessly at $2100^{\circ}C$ for 30 min in argon gas. The sintered body showed the hardness of $2550 kg{\cdot}f/mm^2$ and the fracture toughness, KIC of $3.47 MN/m^{3/2}$.

• Proceedings of the KSME Conference
• /
• 2001.11a
• /
• pp.27-31
• /
• 2001

Hi-Nicalon SiC fiber reinforced SiC composites (SiC/SiC) have been fabricated by the reaction sintering process. Braided Hi-Nicalon SiC fiber with double interphases of BN and SiC was used in this composite system. The microstructures and the mechanical properties of reaction sintered SiC/SiC composites were investigated through means of electron microscopies (SEM, TEM, EDS) and bending tests. The matrix morphology of reaction sintered SiC/SiC composites was composed of the SiC phases that the composition of the silicon and the carbon is different. The TEM analysis showed that the residual silicon and the unreacted carbon were finely distributed in the matrix region of reaction sintered SiC/SiC composites. Reaction sintered SiC/SiC composites also represented proper flexural strength and fracture energy, accompanying the noncatastrophic failure behavior.

• Korean Journal of Materials Research
• /
• v.22 no.12
• /
• pp.701-705
• /
• 2012

The effects of clay, aluminum hydroxide, and carbon powder on the sintering of a Si/SiC mixture from photovoltaic silicon-wafer production were investigated. Sintering temperature was fixed at $1,350^{\circ}C$ and the sintered bodies were characterized by SEM and XRD to analyze the microstructure and to measure the apparent porosity, absorptivity, and apparent density. The XRD peak intensity of SiC in the sintered body was increased by adding 5% carbon to the Si/SiC mixture. From this result, it is confirmed that Si in the Si/SiC mixture had reacted with the added carbon. Addition of aluminum hydroxide decreased the cristobalite phase and increased the stable mullite phase. The measurement of the physical properties indicates that adding carbon to the Si/SiC mixture enables us to obtain a dense sintered body that has high apparent density and low absorptivity. The sintered body produced from the Si/SiC mixture with aluminum hydroxide and carbon powder as sintering additives can be applied to diesel particulate filters or to heat storage materials, etc., since it possesses high thermal conductivity, and anticorrosion and antioxidation properties.

• Journal of the Korean Magnetics Society
• /
• v.10 no.6
• /
• pp.291-296
• /
• 2000

The manufacturing method of permalloy soft magnet with the Ni contents of 46.6 and 47.2 wt% was investigated by powder injection molding technology. The magnetic properties of permalloy were greatly affected on the residual carbon and oxygen content of the sintered magnet. Solvent extraction and thermal debinding process to minimize the residual carbon content in sintered magnet were developed by controlling the debinding atmosphere. The residual carbon content depends on the debinding condition of the binder system for powder injection molding and the residual oxygen content on the sintering atmosphere. The sintered magnet produced by powder injection molding process had a 50 ppm. residual carbon, 150 ppm. residual oxygen. The coercivity and maximum relative permeability of permalloy soft magnet were 0.46 Oe and 14,600 respectively.

• Journal of Powder Materials
• /
• v.22 no.3
• /
• pp.157-162
• /
• 2015

SKD11(ASTM D2) tool steel is a versatile high-carbon, high-chromium, air-hardening tool steel that is characterized by a relatively high attainable hardness and numerous, large, chromium rich alloy carbide in the microstructure. SKD11 tool steel provides an effective combination of wear resistance and toughness, tool performance, price, and a wide variety of product forms. Adding of CNTs increased the performance of mechanical properties more. 1, 3 vol.% CNTs was dispersed in SKD11 matrix by mechanical alloying. SKD11 carbon nanocomposite powder was sintered by spark plasma sintering process. FE-SEM, HR-TEM and Raman analysis were carried out SKD11 carbon nanocomposites.

• Journal of Power System Engineering
• /
• v.21 no.4
• /
• pp.94-99
• /
• 2017

Single walled carbon nanotubes were mixed with various metal powders by mechanical ball milling and sintered by spark plasma sintering processes. Two compositional (0.1 and 1 vol%) of the single walled carbon nanotubes were dispersed onto the pure aluminum, 5052 aluminum alloy, pure titanium, Ti6Al4Vanadium alloy, pure copper, and stainless steel 316L. Each composite powders were spark plasma sintered at $600^{\circ}C$ and well synthesized regardless of the matrices. Vickers hardness of the composite materials was measured and they exhibited higher values regardless of the carbon nanotubes composition than those of the pure materials. Moreover, single walled carbon nanotubes reinforced copper matrix composites showed highest enhancement between the other metal matrices system. We believe that low energy mechanical ball milling and spark plasma sintering processes are useful tool for fabricating of the carbon nanotubes-reinforced various metal matrices composite materials. The single walled carbon nanotubes-reinforced various metal matrices composite materials could be used as an engineering parts in many kind of industrial fields such as aviation, transportation and electro technologies etc. However, detail strengthening mechanism should be carefully investigated.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.37 no.3
• /
• pp.373-378
• /
• 2013

The speed change performance of transmissions has become a serious issue because of the increase in the inertia moment that has accompanied increases in engine output and transmission size. Therefore, it is necessary to develop better wear resistant friction materials. In this study, an appropriate sintered friction component for the synchronizer ring of a diesel manual transmission was developed, and its bonding characteristics were analyzed. That is, a process for bonding an Fe-based base material and Cu-based sintered friction material was developed. BSE and EDX analyses of this bonding layer were conducted, along with a shear strength test, to determine the bonding characteristics.