• The Journal of Korean Academy of Prosthodontics
• /
• v.49 no.1
• /
• pp.73-79
• /
• 2011

Purpose: The aim of this study was to evaluate the effect of repeated firings on the color of zirconia restoration with different shading method. Materials and methods: Three different types of zirconia frameworks (adding metallic pigments to the initial zirconia powder before sintering (Group NM), dipping the milled frameworks in dissolved coloring agents (Group KI), or application of liner material to the sintered white frameworks (Group KW) were used to support A3 shade dentin porcelain. Repeated firings (3, 5, or 7) were performed, color differences among ceramic specimens were measured using a colorimeter. Repeated measurements analysis of variance (ANOVA) was used to analyze the data for significant difference. The Tukey Honestly Significant Different (HSD) test was used to perform multiple comparisons (${\alpha}$ = .05). Results: 1. $L^*a^*b^*$ values of the ceramic systems were affected by the number of firings (1, 3, 5 or 7 firings) (P < .001) and shading methods (P < .001). 2. As the number of firings increased, the $L^*$ (for all groups) and $a^*$ value (for KW and NM groups) decreased and the $b^*$ value(for all groups) increased. 3. The mean color differences caused by repeated firings were perceptible (${\Delta}E$ > 1) for group KW and KI fired after 3 times, except for group NM fired after 7 times. 4. In order of decreasing ${\Delta}E$ value fired after 7 times, the values were group KI(${\Delta}E$ = 2.26) > group KW (${\Delta}E$ = 1.47) > group NM (${\Delta}E$ = 1.08) (P < .001). Conclusion: Repeated firings influenced the color of the zirconium-oxide all-ceramic specimens with different shading methods.

• The Journal of Korean Academy of Prosthodontics
• /
• v.49 no.2
• /
• pp.120-127
• /
• 2011

Purpose: The purpose of this study was to examine the effects of chromium chloride addition on coloration, mechanical property and microstructure of 3Y-TZP. Materials and methods: Chromium chloride was weighed as 0.06, 0.12, and 0.25 wt% and each measured amount was dissolved in alcohol. $ZrO_2$ powder was mixed with each of the individual slurry to prepare chromium doped zirconia specimen. The color, physical properties and microstructure were observed after the zirconia specimen were sintered at $1450^{\circ}C$. In order to evaluate the color, spectrophotometer was used to analyze the value of $L^*$, $C^*$, $a^*$ and $b^*$, after placing the specimen on a white plate, and measured according to the International Commission on Illumination (CIE) standard, Illuminant D65 and SCE system. The density was measured in the Archimedes method, while microstructures were evaluated by using the scanning electron microscopy (SEM) and XRD. Fracture toughness was calculated Vickers indentation method and indentation size was measured by using the optical microscope. The data were analyzed with 1-way ANOVA test (${\alpha}$ = 0.05). The Tukey multiple comparison test was used for post hocanalysis. Results: 1. Chromium chloride rendered zirconia a brownish color. While chromium chloride content was increased, the color of zirconia was changed from brownish to brownish-red. 2. Chromium chloride content was increased; density of the specimen was decreased. 3. More chromium chloride in the ratio showed increase size of grains. 4. But the addition of chromium chloride did not affect the crystal phase of zirconia, and all specimens showed tetragonal phase. 5. The chromium chloride in zirconia did not showed statistically significant difference in fracture toughness, but addition of 0.25 wt% showed a statistically significant difference (P<.05). Conclusion: Based on the above results, this study suggests that chromium chlorides can make colored zirconia while adding in a liquid form. The new colored zirconia showed a slight difference in color to that of the natural tooth, nevertheless this material can be used as an all ceramic core material.