• 한국분말재료학회지
• /
• 제20권3호
• /
• pp.215-220
• /
• 2013

In the present work, 6061 Al-$B_4C$ sintered composites containing different $B_4C$ contents were fabricated and their characteristic were investigated as a function of sintering temperature. For this, composite powders and their compacts with $B_4C$ various contents from 0 to 40 wt.% were fabricated using a planetary ball milling equipment and cold isostatic pressing, respectively, and then they were sintered in the temperature ranges of 580 to $660^{\circ}C$. Above sintering temperature of $640^{\circ}C$, real density was decreased due to the occurrence of sweat phenomena. In addition, it was realized that sinterability of 6061Al-$B_4C$ composite material was lowered with increasing $B_4C$ content, resulting in the decrease in its real density and at the same time in the increment of porosity.

• Journal of Electrochemical Science and Technology
• /
• 제2권1호
• /
• pp.39-44
• /
• 2011

Sub-micrometer $La_{0.8}Ca_{0.2}CrO_3$ powders for ceramic interconnects of solid oxide fuel cells were synthesized by the aqueous combustion process. The materials were prepared from the precursor solutions with different glycine (fuel)-to-nitrate (oxidant) ratios (${\phi}$). Single-phase $La_{0.8}Ca_{0.2}CrO_3$ powders with a perovskite structure were obtained after combustion when ${\phi}$ was equal to or larger than 0.480. Especially, the stoichiometric precursor with ${\phi}$ = 0.555 yielded the spherical $La_{0.8}Ca_{0.2}CrO_3$ particles with 150-250 nm diameters after calcination at $1000^{\circ}C$. When compared with the powders synthesized by the solid-state reaction, the combustion-derived, fine powders exhibited improved sinterability, leading to near-full densification at $1400^{\circ}C$ in oxidizing atmospheres. Moreover, a small quantity of glass additives was used to reduce the sintering temperature, and considerable densification was indeed achieved at temperatures as low as $1100^{\circ}C$.

• 한국세라믹학회지
• /
• 제43권12호
• /
• pp.781-787
• /
• 2006

NiO-coated YSZ powder was prepared using heterogeneous precipitation of Ni hydroxides on YSZ particle surface and high energy milling. The powders were characterized by TG/DTA, XRD, XPS, and SEM. Amorphous Ni precipitate completely decomposed into NiO at $500^{\circ}C$ and the growth of NiO crystallites was constrained by the core particles. Nanocrystalline NiO-coated YSZ core-shell structure powder could be obtained after calcination at $800^{\circ}C$ for 2 h. A core-shell powder compact, due to high sinterability, showed a near theoretical density at $1350^{\circ}C$. After reduction at $900^{\circ}C$, interpenetrating Ni-YSZ microstructure with very uniformly distributed fine Ni and YSZ grains and pores was observed. In contrast, the mechanically mixed oxide sample showed less uniform distribution of pores and larger discontinuous We particles as compared with the core-shell samples.

• 대한전기학회논문지:전기물성ㆍ응용부문C
• /
• 제53권7호
• /
• pp.347-351
• /
• 2004

The $ZnNb_2O_{6}$ ceramics with CuO(1, 3, 5wt%) were prepared by the conventional mixed oxide method. The ceramics were sintered at the temperature of $950^{\circ}C$∼$1075^{\circ}C$ for 3hr in air The structural properties and the microwave dielectric properties of $ZnNb_2O_{6}$ ceramics were investigated with sintering temperature and the addition of CuO. Increasing the addition of CuO, the peak of second phase($Cu_3Nb_2O_{8}$) was increased. The grain size of the $ZnNb_2O_{6}$ ceramics with CuO was increased with CuO addition at same temperature. The dielectric constant of $ZnNb_2O_{6}$ ceramics with CuO was increased with sintering temperature and CuO addition. While the quality factor of the $ZnNb_2O_{6}$ ceramics with lwt% CuO depended on sinterability, the quality factor of $ZnNb_2O_{6}$ with 3wt% and 5wt% CuO depended on second Phase due to the CuO addition. The optimum dielectric Properties of $\varepsilon$$_{r}$ = 21.73 Q${\times}$f = 19,276 were obtained from the condition of 3wt% CuO addition and sintering temperature of $1025^{\circ}C$(3hr).

• 한국전기전자재료학회논문지
• /
• 제19권6호
• /
• pp.524-530
• /
• 2006

$xCa(Li_{1/4}Nb_{3/4})O_{3}-(1-x)CaTiO_{3}$ ceramics were sintered under the presence of zinc-borosilicate(ZBS) glass and resultant microwave dielectric properties were investigated with a view to applying the composition to low-temperature co-fired ceramic(LTCC) technology. The addition of $5{\sim}15wt%$ ZBS glass ensured successful sintering below $900\;^{\circ}C$. In general, increased addition of ZBS glass increased sinterability but it decreased the quality factor($Q{\times}f_{0}$) significantly due to the formation of an excessive liquid and second phases. As for the addition of $CaTiO_3$, the dielectric constant(${\epsilon}_r$) and temperature coefficient of resonant frequency(${\tau}_f$) increased, while the quality factor($Q{\times}f_{0}$) did not show an apparent change. The sintered $0.9Ca(Li_{1/4}Nb_{3/4})O_{3}-0.1CaTiO_{3}$ specimen at $900\;^{\circ}C$ with 10 wt% ZBS glass demonstrated 39.6 in dielectric constant(${\epsilon}_r$), 4,400 in quality factor$(Q{\times}f_{0}),\;and\;-11ppm/^{\circ}C$ in temperature coefficient of resonant frequency(${\tau}_f$).

• 한국세라믹학회지
• /
• 제40권11호
• /
• pp.1096-1101
• /
• 2003

생체친화성이 증진된 생체재료를 얻기 위하여 실리콘 원료로 tetraethyl orthosilicate를 사용하여 실리콘이 치환된 hydroxyapatite를 합성하였으며 FT-IR, XRD, 그리고 ICP 분석결과로부터 실리콘이 hydroxyapatite 구조내에 치환되어 있음을 확인하였다. 성분분석 결과 2 wt%까지의 실리콘을 함유하는 hydroxyapatite인 경우는 120$0^{\circ}C$에서 소결 후에도 원래의 hydroxyapatite 구조를 잘 유지하고 있는 것이 XRD와 HRTEM으로 확인되었으나 그 이상의 실리콘을 함유하는 hydroxyapatite인 경우는 110$0^{\circ}C$에서 부터 상분리가 일어나 XRD에서 tricalcium phosphate와 calcium phosphate silicate상이 검출되기 시작하였다.

• 한국세라믹학회지
• /
• 제48권5호
• /
• pp.368-372
• /
• 2011

Aluminum nitride (AlN) has excellent thermal conductivity, whereas it has some disadvantage such as low sinterability. In this study, the effects of sintering additive content and sintering condition on thermal conductivity of pressureless sintered AlN ceramics were examined on the variables of 1~3 wt% sintering additive ($Y_2O_3$) content at $1900^{\circ}C$ in $N_2$ atmosphere with holding time of 2~10 h. All AlN specimens showed higher thermal conductivity as the $Y_2O_3$ content and holding time increase. The formation of secondary phases (yttrium aluminates) by reaction of $Y_2O_3$ and $Al_2O_3$ from AlN surface promoted the thermal conductivity of AlN specimens, because the secondary phases could reduce the oxygen contents in AlN lattice. Also, thermal conductivity was increased by long sintering time because of the uniform distribution and the elimination of the secondary phases at the grain boundary by the evaporation effect during long holding time. A carbothermal reduction reaction was also affected on the thermal conductivity. The thermal conductivity of AlN specimens sintered at $1900^{\circ}C$ for 10 h showed 130~200W/mK according to the content of sintering additive.

• 한국전기전자재료학회논문지
• /
• 제24권9호
• /
• pp.728-732
• /
• 2011

In this study, piezoelectric and dielectric properties of Lead-free $0.97[(K_{0.5}Na_{0.5})(Nb_{0.97}Sb_{0.03})O_3]+0.03[(Bi_{0.5}K_{0.5})TiO_3]$ (abbreviated as 0.97NKNS-0.03BKT)ceramics synthesized by conventional solid-state reaction process were investigated as a function of $K_{5.4}Cu_{1.3}Ta_{10}O_{29}$ addition. The results indicated that the $K_{5.4}Cu_{1.3}Ta_{10}O_{29}$ addition significantly improved the sinterability, grain growth and piezoelctric properties of 0.97NKNS-0.03BKT ceramics. The optimum values as planar piezoelectric coupling coefficient ($k_p$= 0.355), piezoelectric constant ($d_{33}$= 207 pC/N) and mechanical quality factor ($Q_m$= 128) were obtained when 0.009KCT was added. The electromechanical coupling factor($k_p$) was slightly decreased according to the increasing temperature.

• 한국분말재료학회지
• /
• 제19권1호
• /
• pp.25-31
• /
• 2012

In this study, a high energy ball milling process was employed in order to improve the densification of direct nitrided AlN powder. The densification behavior and the sintered microstructure of the milled AlN powder were investigated. Mixture of AlN powder doped with 5 wt.% $Y_2O_3$ as a sintering additive was pulverized and dispersed up to 50 min in a bead mill with very small $ZrO_2$ beads. Ultrafine AlN powder with a particle size of 600 nm and a specific surface area of 9.54 $m^2/g$ was prepared after milling for 50 min. The milled powders were pressureless-sintered at $1700^{\circ}C-1800^{\circ}C$ for 4 h under $N_2$ atmosphere. This powder showed excellent sinterability leading to full densification after sintering at $1700^{\circ}C$ for 4 h. However, the sintered microstructure revealed that the fraction of yitttium aluminate increased with milling time and sintering temperature and the newly-secondary phase of ZrN was observed due to the reaction of AlN with the $ZrO_2$ impurity.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2007년도 하계학술대회 논문집 Vol.8
• /
• pp.260-260
• /
• 2007

Low-temperature sintering and dielectric properties of the $1-xBiNbO_4-xZnNb_2O_6$ ceramics (x=0.3, 0.5, and 0.7) with 10 wt% zinc borosilicate (ZBS) glass was investigated as a function of the substitution of $ZnNb_2O_6$ with a view to applying this system to LTCC technology. The all composition addition of 10 wt% ZBS glass ensured a successful sintering below $900^{\circ}C$. The the amount of $ZnNb_2O_6$ on $ZnNb_2O_6$ ceramics increased the $Q{\times}f$ values, but it decreased the sinterability and dielectric constant due to the higher $Q{\times}f$ value and sintering temperature of $ZnNb_2O_6$ than that of $ZnNb_2O_6$ ceramics. The increase of $ZnNb_2O_6$ content from 0.3 to 0.7 in the $1-xBiNbO_4-xZnNb_2O_6$ ceramics with 10 wt% ZBS glass sintered at $900^{\circ}C$ demonstrated 30~20 in the dielectric constant (${\varepsilon}_r$), 3,500~4,500 GHz in the $Q{\times}f$ value.