High Resistivity Characteristics of the Sinter Dust Generated from the Steel Plant

  • Lee, Jae-Keun;Hyun, Ok-Chun;Lee, Jung-Eun;Park, Sang-Deok
    • Journal of Mechanical Science and Technology
    • /
    • 제15권5호
    • /
    • pp.630-638
    • /
    • 2001
  • The electrical resistivity of sinter dusts generated from the steel industry and coal fly ash from the coal power plant has been investigated using the high voltage conductivity cell based on JIS B 9915 as a function of temperature and water content. Dust characterization such as the chemical composition, size distribution, atomic concentration, and surface structure has been conducted. Major constituents of sinter dusts were Fe$_2$O$_3$(40∼74.5%), CaO (6.4∼8.2%), SiO$_2$(4.1∼6.0%), and unburned carbon (7.0∼14.7%), while the coal fly ash consisted of mainly SiO$_2$(51.4%), Al$_2$O$_3$(24.1%), and Fe$_2$O$_3$(10.5%). Size distributions of the sinter dusts were bi-modal in shape and the mass median diameters (MMD) were in the range of 24.7∼137㎛, whereas the coal fly ash also displayed bi-modal distribution and the MMD of the coal fly ash was 35.71㎛. Factors affecting resistivity of dusts were chemical composition, moisture content, particle size, gas temperature, and surface structure of dust. The resistivity of sinter dusts was so high as 10(sup)15 ohm$.$cm at 150$\^{C}$ that sinter dust would not precipitate well. The resistivity of the coal fly ash was measured 1012 ohm$.$cm at about 150$\^{C}$. Increased water contents of the ambient air lowered the dust resistivity because current conduction was more activated for absorption of water vapor on the surface layer of the dust.

  • PDF

황산암모늄 주입에 따른 전기집진기(ESP)에서의 미세분진 제거 (A Study on Fine Particle Removal of ESP according to $(NH_4)_2SO_4$ Injection Rate)

  • 서정민
    • 한국환경과학회지
    • /
    • 제7권4호
    • /
    • pp.505-510
    • /
    • 1998
  • This study has been carried out to investigate Electrostatic Precipitator's(ESP) performance enhancement and removal efficiency of fine particle according to (NH4)2SO4injection rate. The following conclusions are derived from the these test results : 1) For plant condition cases, according to the variation of concentration agent [(NH4)2SO4]-10ppm, when inlet dust loading was 2g/m2. And when Inlet dust loading was 3g/m", that was increased to 98 19% 99.16% 99.23%, 99.58%, 2) It Is seen from thins experiments that the increasing 30ppm concentration of (NH4)2SO4 increase the collection efficiency and fine particle omission control.

  • PDF

Fabrication Methods of Porous Ceramics and Their Applications in Advanced Engineering - Large Flat Precision Plate for Flat Display Industries

  • Matsumaru, Koji;Ishizaki, Kozo
    • 한국재료학회:학술대회논문집
    • /
    • 한국재료학회 2009년도 춘계학술발표대회
    • /
    • pp.3.1-3.1
    • /
    • 2009
  • Normal sintering process of producing porous ceramics is not to sinter perfectly, i.e., stop sintering in middle-process. Our porous ceramic materials are a product of complete sintering. For example if one want to make a porous carborundum, raw carborundum powder is sintered at either lower temperatures than normal sintering temperature or shorter sintering periods than normal sintering time to obtain incompletely sintered materials, i.e., porous carborundum. This implies normally sintered porous ceramic materials can mot be used in high vacuum conditions due to dust coming out from uncompleted sintering. We could produce completely sintered porous ceramic materials. For example, we can produce porous carborundum material by using carborundum particles bonded by glassy material. The properties of this material are similar to carborundum. We could make quasi-zero thermal expansion porous material by using carborundum and particles of negative thermal expansion materials bonded by the glassy material. We apply to sinter them also by microwave to sinter quickly. We also use HIP process to introduce closed pores. We could sinter them in large size to produce $2.5m{\times}2.5m$ ceramic plate to use as a precision plate for flat display industries. This flat ceramic plate is the world largest artificial ceramic plate. Precision plates are basic importance to any advanced electronic industries. The produced precision plate has lower density, lower thermal expansivity, higher or similar damping properties added extra properties such as vacuum vise, air sliding capacity. These plates are highly recommended to use in flat display industries. We could produce also cylindrical porous ceramics materials, which can applied to precision roller for polymer film precision motion for also electronic industries.

  • PDF

함철 더스트를 원료로 한 고로용 비소성 펠릿의 강도 및 환원거동 (Strength and Reduction Behaviour of Cold-bonded Pellet for Blast Furnace Burden using Iron-bearing Dust)

  • 김태동;백찬영;조종민
    • 자원리싸이클링
    • /
    • 제4권1호
    • /
    • pp.60-68
    • /
    • 1995
  • 철강공정에서 발생하는 함철더스트에 시멘트를 첨가한 비소성 더스트 펠릿을 제조하여 고로용으로서의 특성을 평가하였다. 시멘트를 10wt.% 첨가한 펠릿은 적절한 양생조건하에서 150kg/p 이상의 압축강도에 도달하였다. 더스트 펠릿은 특히 $900^{\circ}C$에서의 환원성이 우수하였는데, 이는 비소성 펠릿 중에 함유된 탄소의 직접환원 반응과 고온에서 증가된 기공 때문이다. 이외에 비소성 펠릿의 회전강도, 환원분화성 및 환원 팽창성도 철광석 소결광 및 소성 펠릿에 비교하여 우수하거나 대등한 성상을 나타내는 것을 확인하였다.

  • PDF

산화철계 형석대체제의 전로 정련특성 (BOF Refining of Fluorspar Substitute Using Iron Oxide Based By-product)

  • 금창훈;허보영
    • 한국재료학회지
    • /
    • 제16권5호
    • /
    • pp.336-340
    • /
    • 2006
  • Fluorspar has been essential flux in steelmaking process. The main effects of fluorspar addition are lowering of the viscosity and melting temperature of slag. In recent years, due to the increasing price and environmental problem of fluorspar, various types of fluorspar substitute have been investigated. In this study, iron oxide by-products such as sinter dust, basic oxygen furnace (BOF) sludge and mill scale were developed as a substitute in terms of waste recycling. Several plant trials were carried out by addition of briquetted substitutes of $4{\sim}6$ kg/ton to compare with the fluorspar of $0.7{\sim}1$ kg/ton. The substitutes showed a similar behavior of slag formation, phosphorus removal and MgO saturation content.