• 한국재료학회지
• /
• 제18권1호
• /
• pp.12-17
• /
• 2008

Carbon nanotube (CNT) cathodes were fabricated using nano-sized silver (Ag) powders as a bonding material between the CNTs and cathode electrodes. The effects of the powder size on the sintering behavior, the current density and emission image for CNT cathodes were investigated. As the diameter of the Ag powders decreases to 10 nm, the sintering temperature of the CNT cathode was lowered primarily due to the higher specific surface area of the Ag powders. In this study, it was demonstrated that nano-sized Ag powders can be feasibly used as a bonding material for a screen-printed CNT cathode, yielding a high current density and a uniform emission image.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2014년도 제46회 동계 정기학술대회 초록집
• /
• pp.155.2-155.2
• /
• 2014

Plasma Enhanced Atomic Layer Deposition(PEALD)와 Atomic Layer Deposition(ALD) Techniques는 '정확한 두께 조절' 및 '우수한 균일도'를 가지는 신뢰할 수 있는 진공 기술이다. 본 연구에서는 다공성 구조를 가지는 기판을 대상으로 PEALD와 ALD Techniques을 이용한 $Al_2O_3$ 형성 공정의 증착 특성을 비교하였다. 각 공정은 공통적으로 Tris-Methyl-Aluminium(TMA)을 첫번째 전구체로 사용하였고 purge gas로는 Nitrogen를 사용하였다. 그리고 두번째 전구체로 PEALD 공정에서는 Oxygen Plasma를 사용하였고 ALD 공정에서는 Water를 사용하였다. 복잡한 다공성 구조를 가지는 기판은 $TiO_2$ Nano-Particle paste과 colloidal Silver paste를 소결시켜 제작하여 사용하였다. 각 공정의 차이점을 비교하기 위해서 배기단에 Capacitor Diaphram Gauge(CDG)와 Residual Gas Analyzer(RGA)를 통해서 압력과 잔류 가스를 모니터하였다. 그리고 각 공정을 통해서 porous한 Nano-Particles Network에 형성된 $Al_2O_3$막의 특성을 비교하기 위해서 FE-SEM과 EDX를 통해서 관찰하였다. 또한 좀 더 자세한 비교 분석을 위해서 $Al_2O_3$ 막이 형성된 porous한 Nano-Particles Networks의 각 각의 particles들을 분산시켜 TEM과 AFM를 통해서 관찰하였다. 나아가 전기적 물성의 차이점을 비교하기 위해서 IV 및 CV를 측정하였다. 위의 일련의 비교 실험을 통해서 'PEALD과 ALD을 이용한 다공성 기판의 증착 특성'에 대하여 고찰하였다.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2012년도 제42회 동계 정기 학술대회 초록집
• /
• pp.546-546
• /
• 2012

Traditional screen printing is still a dominant method to print electrodes on c-Si solar cells. In order to achieve higher efficiency for c-Si solar cells, improvement of the electrode material is one of the key approaches. Shadowing loss can be reduced by using high aspect ratio finger electrode with width of finger electrode less than 80um. The rheological properties of Ag paste for applying c-Si solar cells are improved by using Ag nanowires. The printing properties including the aspect ratio of printed electrode can be improved with higher Thixotropic index (T.I.) values.

• 한국인쇄학회지
• /
• 제30권2호
• /
• pp.1-12
• /
• 2012

In this experiment, we have manufactured thermal-curable silver pastes for direct printing. And to enhance conductivity, printability, adhesion and hardness during polymer direct-gravure prints, we have manufactured Ag pastes by adding variety of filter contents. Then we have investigated characteristics of rheology in paste according to the gravure printability and the properties of printed conductive patterns. Depending on a variety of Ag powder, there was a big difference in sharpness of printed pattern. And also by the use of carbon, there was a big difference in amount of solvent used, conductivity and in hardness. We could improve doctoring and the sharpness of a pattern by adding Ag paste in carbon particle, but as we have used nano-sized particle, there was an increase in the amount of solvent used and also we have found out that it gives a bad effect as adhesive and hardness becomes weaker. Even though Ag particle has the same spherical shape, the surface treatments could differ from one another. And by the appropriate choice and with the suitable combination of Ag powder, excellent printability and conductivity could be obtained.

• 전자공학회논문지
• /
• 제53권8호
• /
• pp.119-126
• /
• 2016

본 논문에서는 의복용 무선전력전송 시스템을 구축을 위한 평면형 직물공진기를 제안하고, 공진기에 사용된 의복용 직물기판의 재질별 특성을 분석하였다. 평면형 직물공진기는 공진주파수가 1-10 MHz가 되도록 직물기판 위에 전도성 물질로 루프 및 코일을 평면 설계하였다. 의복용으로 많이 사용되고 있는 폴리에스테르 섬유와 면을 직물기판으로 사용하였으며, 평면 루프와 코일은 동테이프(copper tape)와 실버페이스트(silver paste)로 설계하였다. 자기공진형 무선전력전송 시스템에 적용된 직물의 재질별 특성을 분석하기 위해 송신부와 수신부를 대칭으로 설계하였다. 실험 결과, 낮은 유전상수 및 비교적 두꺼운 두께를 가진 직물기판과 표면저항이 작은 도체성 재질의 패턴(루프 및 코일)으로 제작되었을 때, 의복용 무선전력전송 시스템이 높은 전송효율을 보였다. 본 연구를 통해 제안된 평면형 직물 공진기는 무선전력전송 기술의 영역을 의복용으로 넓힐 수 있는 가능성을 보여주었다.

• 한국전기전자재료학회논문지
• /
• 제34권4호
• /
• pp.242-245
• /
• 2021

In this work, we fabricated oxide on an n-type silicon substrate through local anodic oxidation (LAO) using atomic force microscopy (AFM). The resulting oxide thickness was measured and its correlation with load force, scan speed and applied voltage was analyzed. The surface oxide layer was stripped using a buffered oxide etch. Ohmic contacts were created by applying silver paste on the silicon substrate back face. LAO was performed at approximately 70% humidity. The oxide thickness increased with increasing the load force, the voltage, and reducing the scan speed. We confirmed that LAO/AFM can be used to create both lateral and, to some extent, vertical shapes and patterns, as previously shown in the literature.

• 센서학회지
• /
• 제10권5호
• /
• pp.292-303
• /
• 2001

본 연구에서는 수평형 전계 방출 소자를 제작하고 그 특성을 측정하였다. 이를 진공자장 센서에 이용하기 위하여 Lorentz 원리를 응용하여 센서를 설계하고 제작하였다. $POCl_3(10^{20}cm^{-3})$ 도핑된 다결정 실리콘을 전계 방출 소자의 음극 및 양극 재료로 이용하였으며 그 두께는 각각 $2\;{\mu}m$였다. PSG(두께 $2\;{\mu}m$)를 희생층으로 사용하여 최종 단계에서 불산을 이용하여 제거하고 승화건조법을 이용하여 소자의 기판 점착 현상을 방지하였다. 제작된 소자를 유리기판 #1 위에 silver paste로 고정시키고 Cr 전극 패드와 와이어본딩 한 뒤 진공내에서 양극접합공정을 이용하여 소자를 $1.0{\times}10^{-6}\;Torr$에서 진공 실장하였다. 실장 후 게터를 활성화하여 내부진공도를 향상시켰다. 이렇게 패키징된 소자는 두달여 기간 동안 특별한 특성저하 없이 잘 동작되었으며 그 이상의 기간에 대해서는 확인하지 못하였다. 패키징된 자장 센서는 패키징하기 전 진공챔버 내에서 보인 특성치와 별다른 차이 없이 잘 동작되었으며 단지 약간의 전류 감소 현상만이 관찰되었다. 측정된 센서의 감도는 약 3%/T로서 작은 값이었으나 그 가능성을 확인할 수는 있었다.

• 한국재료학회지
• /
• 제13권1호
• /
• pp.18-23
• /
• 2003

Properties of Ag thick films fabricated by using low temperature curable silver pastes were investigated. Ag pastes were consisted of polymer resins and silver powders. Ag pastes were used for conductive or fixing materials between board and various electrical and electronic devices. Low temperature curable Ag pastes have some advantages over high temperature curable types. In cases of chip mounting, soldering properties were required for screen printed Ag thick films. In this study, four types of Ag pastes were fabricated with different compositions. Screen printed Ag thick films on alumina substrates were fabricated at various curing temperatures and times. Thickness, resistivity, adhesive strength and solderability of fabricated Ag thick films were characterized. Finally, Ag thick films produced using Ag pastes, sample A and B, cured at $150^{\circ}C$ for longer than 6 h and $180^{\circ}C$ for longer than 2 h, and $150^{\circ}C$ for longer than 1 h and $180^{\circ}C$ for 1 h, respectively, showed low resistivities of $10^{-4}$ $∼10^{-5}$ Ωcm and good adhesive strength of 1∼5 Mpa. Soldering properties of those Ag thick films with curing temperatures at solder of 62Sn/36Pb/3Ag were also investigated.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2015년도 추계학술대회 논문집
• /
• pp.340-340
• /
• 2015

상지 절단 장애인들을 위한 미관형 의수는 95% 이상의 시장 보급률을 보인다. 하지만 외부 형상 향상에만 연구 초점이 맞추어져 있어 많은 장애인들이 의수를 착용할 때 차가운 표면으로 인해 이질감을 느낀다. 이로 인해 의수 제작 업체 및 절단 장애인들은 착용 시 이질감이 적은 의수의 보급을 희망하고 있다. 그러므로 본 연구에서는 인체와 유사한 온도를 발생시켜 이질감을 감소시키는 의수를 개발하기 위해 유연 기판인 TPU (Temperature Polyurethane)와 PET (Polyethylene terephthalate) 위에 상용 silver nano paste를 3D 프린터로 인쇄하였으며, UV 표면처리를 사용하여 단시간 내에 낮은 저항과, 높은 회로 접착강도를 갖는 회로를 개발 하였다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2009년도 하계학술대회 논문집
• /
• pp.21-21
• /
• 2009

후막 광식각 기술을 이용하여 형성된 Ag 전극과 LTCC 기판 사이의 접착력을 향상시키기 위하여 무기 바인더로서 anorthite, diopside 및 MLS-62 glass frit을 첨가하여 감광성 Ag paste를 제조하였다. 소성 후의 glass pool effect를 감소시키기 위해 attrition mill을 통하여 미세 glass 분말을 준비하였다. Glass frit은 Ag powder의 5vol%~25vol%의 함량으로 첨가하여 감광성 Ag paste를 제조하였고 패턴 형성 후 $850^{\circ}C$에서 1시간 소결하였다. 전극과 기판 사이의 접착력은 micro-ball shear test 법으로 측정하였으며, Ag 전극 부착력은 glass frit의 함량 증가에 따라 증가하다가 감소하는 경향을 보이는데, 이는 과량의 glass frit 첨가로 인한 전극 내부에 액상 풀의 형성에 기인한 것으로 보여진다. Ag 전극의 면저항은 glass frit의 함량이 증가함에 따라 $0.13m{\Omega}{/\square}$에서 $2.06m{\Omega}{/\square}$까지 증가하는 경향을 나타내었다. 소성 전후의 전극 패턴의-수축율은 $100{\mu}m$의 선폭을 기준으로 glass frit의 첨가랑이 증가할수록 43.3%에서 35.0%로 감소하였으며, 그 결과 최소 선폭 $25{\mu}m$의 미세 전극 패턴의 형성이 가능하였다.