• Journal of the Society of Naval Architects of Korea
• /
• v.45 no.1
• /
• pp.73-80
• /
• 2008

An improved method to measure the dynamic viscoelastic properties of elastomers is proposed. The method is based on the analysis of forced oscillation of a cylindrical sample loaded with inertial mass. No special equipment or instrumentation other than the ordinary vibration measurement apparatus is required. Typical measurement of the viscoelastic properties of a silicone rubber $Silastic^{(R)}$ S2 were measured over the wide frequency range from 10 Hz to 3 kHz under the action of wide region of deformation from $10^{-4}%$ to 5%. It was shown that modulus of elasticity and loss tangent fall on the single curves when the ratio of load mass to sample mass changed from 1 to 20.

• Elastomers and Composites
• /
• v.36 no.2
• /
• pp.102-110
• /
• 2001

The three types of surfactants such as nonylphenoxy poly(ethylene) ethanol homologues, caster oil poly(ethylene) ethanol homologues, and sodium perfluoroalkyl carboxylates are used to improve the wettability of rubber impression material. Among the surfactants, the usage of sodium perfluoroalkyl carboxylates containing fluoro group resulted in the lowest surface energy of impression material and the result gave the positive effect on the wettability of rubber impression material to teeth. Also, the anti-foaming agents were used to reduce or remove the hydrogen gas generating on the impression material by reaction. In the case of rubber impression material containing sodium perfluoroalkyl carboxylate as a surfactant, it was found that the tear strength of rubber impression material increased over 3 N/mm with the addition of anti-forming agent. Therefore, the anti-foaming agent could contribute to the mechanical property of rubber impression material without the change of surface property.

• Journal of Biomedical Engineering Research
• /
• v.22 no.5
• /
• pp.403-412
• /
• 2001

The Present study analyzed the pressure-flow characteristics of a Korean shunt valve. Changes in the characteristic currie depending on the design parameters were also investigated. The Korean shunt valve used in the present study was constant pressure type and our analyses were validated through experiments. We applied fluid-structure interaction to solve the flow dynamic Problem because the small diaphragm in the valve was made from flexible silicone elastomers. Considering the material nonlinearity of the hyper-elastic material. the Mooney-Rivlin approximation was employed. The results of the numerical analyses were close to the experimental results The major Pressure drop was observed to happen in the small diaphragm. The slope of the pressure-flow characteristic curve was computed to be 0.37mm$H_2O$.hr/cc, which was similar to the average value of commercial shunt valves. 0.40mm$H_2O$.hr/cc. Therefore. our valves analyzed in the Present study showed a Proper Pressure control characteristics of the constant pressure type shunt valves. The opening pressure could be controlled by adjusting the amount of predeflection of the valve diaphragm. In order to obtain opening pressures of 25mm$H_2O$ and 80mm$H_2O$, respectively, and the required predeflection was found to be 10.2$\mu$m and 35.3$\mu$m. The flow orifice size was found to be within 10$\mu$m during valve operation Therefore, Precision design and manufacturing techniques are necessary for successful operations of the shunt valve. The study indicated the amount of predeflection as well as the magnitude of corner rounding of the diaphragm edge are important design parameters to influence the slope of the pressure-flow characteristic curve.

• Elastomers and Composites
• /
• v.44 no.2
• /
• pp.150-155
• /
• 2009

This study examined the effects of the concentration variation of the silyl hydride (Si-H) functional group in polymethylhydrogen siloxane cross-linker and the vinyl-functional group in silicone prepolymer on the physical properties of the dental polyvinylsiloxane impression materials (PVS). When the SiH/Vinyl ratio was 1.6 (Group $\underline{C6}$ containing ${\underline{C}}ross$-linker $\underline{6}$ parts), the setting rate was too slow even though their tensile strength was the highest within the tested groups. When the SiH/Vinyl ratio was 3.2 (Group C12), the setting rate was too fast to allow appropriate working time even though their mechanical properties were good. The C14 group showed rather lower tensile strength compared to the groups having lower cross-linker contents. Notably, too much incorporation of cross-linker, like C16 group, induced delay of the setting, by which the mechanical and manipulation properties were detrimentally affected.