• Polymer(Korea)
• /
• v.29 no.4
• /
• pp.375-379
• /
• 2005

The morphology and therma]/viscoelastic characteristics were investigated for PLLA/MMT nanocomposite manufactured by incorporating inorganic nanosized silicate nanoplatelets into biodeuadable poly(l-lactic acid) (PLLA). The XRD difiactogram and TEM image may be regarded as a formation of homogeneously dispersed nanocomposites. The melting energy(${\Delta}H_m$) was increased during hydrolysis process because of increase of crystallinity. As MMT played a role of reinforcing agent, the storage modulus was increase in case of PLLA/MMT nanocomposite, it was well coincided with our previous results. From SEM image, many tiny pinholes formed by spinodal decomposition were observed on the surface, and the shape of nanocomposite was maintained during hydrolysis process. In this study, it was shown that the control of biodegradation rate, thermal/mechnical property was possibile by incorporating MMT.

• Journal of the Korean Ceramic Society
• /
• v.25 no.5
• /
• pp.561-569
• /
• 1988

Mixtures of very small amounts of additive, carbon and silica(about 0.46${\mu}{\textrm}{m}$) which synthesized by the hydrolysis of ethyl silicate, the molar ratio of SiO2/C was fixed to 1/10, was nitrided at 145$0^{\circ}C$. It was considered that the optimum amount of additive to promote the nitridation reaction was below 2.0wt%. By the addition of additive, the nitridation reaction was promoted and formation of $\beta$-Si3N4 was promoted at 145$0^{\circ}C$ for 1hour, but, the nitridation reaction was decreased and the ratio of $\alpha$/$\beta$ of Si3N4, was increased at 145$0^{\circ}C$ for 5 hours. The crystal phase was $\alpha$ phase and the nitridation reaction was promoted and the particle size of silicon nitride was become smaller by the addition of $\alpha$-Si3N4, but silicon nitride of whisker-like form was produced by the addition of transition elements. There was a difference in the lattice constants of $\alpha$-Si3N4, but no difference in its of $\beta$-Si3N4 according to kinds of added substance and reaction time.

• Journal of the Korean Ceramic Society
• /
• v.26 no.2
• /
• pp.195-200
• /
• 1989

The Silica-Carbon mixture was made with addition of carbon black in the composition which monodispersed spherical fine silica was formed by the hydrolysis of ethylsilicate, mole ratio of Carbon/Alkoxide was 3.1 and $\beta$-SiC powder was synthesized by reacting this mixture at 1,350~1,50$0^{\circ}C$ in Ar atmosphere. The results of this study are as follow : (1) The purity of synthesized $\beta$-SiC powder was above 99.98% and it was in cubic modification with lattice constant of 4.3476$\AA$. (2) The rate-controlling steps varied with the reaction temperature for the syntehsis of $\beta$-SiC in this study ; nucleation and growth of $\beta$-SiC at 1,350~1,40$0^{\circ}C$, interfacial reaction at 1,45$0^{\circ}C$ and diffusion described by Jander Equation at 1,50$0^{\circ}C$. (3) When the rate-determining step was nucleation and growth, the activation energy was about 87.8kcal/mol.

• Journal of the Korean Ceramic Society
• /
• v.26 no.3
• /
• pp.416-422
• /
• 1989

The particle size of synthesized SiC powders was decreased with increasing carbon content when the mixture of carbon and silica was carbonized at 1, 45$0^{\circ}C$ after hydrolysis of the mixture with the ranges of 3.1 to 3.5 in the mole ratio of Carbon/Alkoxide. The reacted fraction of $\beta$-SiC nearly had nothing to do with the mole ratio of Carbon/Alkoxide. When the reaction was made by adding 0.5wt% additives in the composition of 3.1 in the mole ratio of carbon/alkoxide, the additives decreased the yield of $\beta$-SiC and its sequence was Ba2O3>B>Fe>Al>Al2O3>Si. The effect of additives promoted the transformation of $\beta$-SiC to $\alpha$-SiC form and shwoed the increasing tendency of lattice constant. The two colors of $\beta$-SiC powder came out : one was the black grey with addition of Al, Al2O3 and B the other the light grey with addition of Fe, B2O3 and Si.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.02a
• /
• pp.37-37
• /
• 2010

Silicate-silsesquioxane or siloxane-silsesquioxane hybrid thin films are strong candidates as matrix materials for ultra low dielectric constant (low-k) thin films. We synthesized the silicate-silsesquioxane hybrid resins from tetraethoxyorthosilicate (TEOS) and methyltrimethoxysilane (MTMS) through hydrolysis and condensation polymerization by changing their molar ratios ([TEOS]:[MTMS] = 7:3, 5:5, and 3:7), spin-coating on Si(100) wafers. In the case of [TEOS]:[MTMS] 7:3, the dielectric permittivity value of the resultant thin film was measured at 4.30, exceeding that of the thermal oxide (3.9). This high value was thought to be due to Si-OH groups inside the film and more extensive studies were performed in terms of electronic, ionic, and orientational polarizations using Debye equation. The relationship between the mechanical properties and the synthetic conditions of the silicate-silsesquioxane precursors was also investigated. The synthetic conditions of the low-k films have to be chosen to meet both the low orientational polarization and high mechanical properties requirements. In addition, we have investigated a new solution-based approach to the synthesis of semiconducting chalcogenide films for use in thin-film transistor (TFT) devices, in an attempt to develop a simple and robust solution process for the synthesis of inorganic semiconductors. Our material design strategy is to use a sol-gel reaction to carry out the deposition of a spin-coated CdS film, which can then be converted to a xerogel material. These devices were found to exhibit n-channel TFT characteristics with an excellent field-effect mobility (a saturation mobility of ${\sim}\;48\;cm^2V^{-1}s^{-1}$) and low voltage operation (< 5 V). These results show that these semiconducting thin film materials can be used in low-cost and high-performance printable electronics.

• Journal of the Korean Society of Safety
• /
• v.12 no.4
• /
• pp.79-85
• /
• 1997

In order to improve the surface characteristics of polymethylmethacrylate(PMMA), oxide thin film coatings were applied using the sol-gel dip-coating technique. The $Si(OC_2H_5)_4$, tetra-ethyl-ortho-silicate(TEOS) was used as a starting material for $SiO_2$ coating. The hardness of the alkoxy-derived oxide-coated PMMA was increased from 190 MPa for non-coated PMMA with increasing film thickness. By optimizing the heating conditions and the hydrolysis conditions, a maximum apparent hardness obtained In the present study was achieved 310 MPa using the withdrawal velocity of 5cm/min and heat treatment at $90^{\circ}C$ for 5 hours, which is about 1.6 times larger than that of uncoated PMMA.

• Journal of Applied Biological Chemistry
• /
• v.42 no.2
• /
• pp.81-84
• /
• 1999

Blood glue was prepared to reutilize porcine blood. Plasma proteins after lyophilization were treated by addition of wood flour, sodium hydroxide, sodium silicate, and hydrated lime to make blood glue with a suitable adhesivity. Characteristics of the prepared blood glue was monitored by measuring the viscosity with time, and the relationship between degree of hydrolysis of plasma proteins by addition of various amounts of sodium hydroxide and adhesivity was studied. To prevent the emission of formaldehyde during manufacturing of plywood by blood glue, the cross-linking reaction of plasma protein with formaldehyde was also examined. Fourier transform infrared, circular dichroism, and fluorescence spectroscopy study showed that blood plasma proteins react with formaldehyde, resulting in removal of formaldehyde by cross-linking reaction.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1996.10a
• /
• pp.154-165
• /
• 1996

As II-anhydrite reacts with C3A(aluminate), C4AF(ferrite) at initial hydration of cement and assists the hydrolysis of C3S(calcium silicate), the production rate of ettringite(3C3A.3CaSO4.32H2O) and C-S-H gel was acclerated. It was known that compressive strength of cement concrete improved due to the effect of II-anhydrite. For the checking these effects of II-anhydrite, the fluidity and compressive strength of cementmortar admixed with II-anhydrite and pozollanic fine powders were investigated. By means of SEM analysis, the surface structure of mortar with the condition of steam curing at curing days=28 was investigated. As a result of this experiment, it was examined that II-anhydrite had an increase on the fluidity of cementpaste and compressive strength of mortar.

• Bulletin of the Korean Chemical Society
• /
• v.21 no.8
• /
• pp.817-822
• /
• 2000

Crack-free hard coating siIica films were prepared by sol-gel processfrom twokinds of silicon alkoxide (tetra-ethoxysilane and methyltrimethoxysilane) and two kinds of alcohol (methanol and isopropyl alcohol) with an acid catalyst,acetic acid. A silicate framework of the precursor solution was investigated by infrared spectros-copy (IR) in the process of hydrolysis and condensation. Theextent of the condensation in the intermediates was elucidated by gel permeation chromatography (GPC) and 29Si-NMR spectroscopy. The hard coating films werecharacterized by IR,scanning electron microscope (SEM), thermo gravimetric analyzer (TGA) and dif-ferential scanning calroimeter (DSC). The synthetic condition for the crack-free and transparent silica film for-mation was optimized interms of starting materials for the precursor solution as well as preparation method of the silica film.

• Journal of the Korea Concrete Institute
• /
• v.19 no.5
• /
• pp.639-646
• /
• 2007

This study performed several tests for the durability of the concrete coated with nano synthesis ceramics which do not contain volatile organic compounds harmful to environment. The tests were adhesion test on dry and humid concrete, SEM test, MIP analysis, carbonation, chloride diffusion by electronic facilitation, freezing-thawing resistance, alkaline resistance, and brine resistance test. In the adhesion test on dry and humid concrete, nano synthesis ceramics coating produced the highest results among all the coatings tested. Nano synthesis ceramics adhered solidly on the concrete surface. The adhesive strength seemed to result from the hydrogen bond between nano synthesis ceramics which are inorganic and generated by hydrolysis and re-condensation reaction and the concrete's hydrates such as calcium silicate aluminate or calcium silicate hydrate. SEM test and MIP analysis results show surface structure with finest crevices pore in the nano synthesis ceramics coating applied concretes. In the carbonation, chloride diffusion, and freezing-thawing resistance tests, the concretes with nano synthesis ceramics coating indicated the best results. Based on these test results, further progress in application of nano synthesis ceramics coatings to various concrete structures including costal structures and sewerage arrangements can be expected.