• Journal of the Korean Ceramic Society
• /
• v.34 no.2
• /
• pp.188-194
• /
• 1997

Wet gel with surface modification by TMCS was redispersed in EtOH and redispersed silica sol for coat-ing was prepared. After spin coating of redispersed sol was conducted on silicon substrate, processes of drying(8$0^{\circ}C$) and heat treatment(>25$0^{\circ}C$) were, followed at ambient pressure. The influence of heat treat-ment of properties of film was observed, changing temperature at heat treatment. The optimum redisp-ersion condition for stable silica sol was wet gel:EtOH=1g:110$m\ell$ and the concentration and viscosity of redispersed silica sol with average particle size of 30nm were 0.11 M, 2.0-2.2 cP respectively. Crack-free thin film with the refractive index of 1.14 and thickness of 400 nm was obtained through drying at 8$0^{\circ}C$ and subsequent heat treatment at 45$0^{\circ}C$ for 2 hrs respectively after spin coating of 1500rpm, 10 times.

• Journal of the Korean Applied Science and Technology
• /
• v.31 no.1
• /
• pp.83-91
• /
• 2014

In this study, we synthesized two different silica monoliths by using sol-gel, solvent exchange, surface modification, ambient pressure drying processes, and surfactant-based templating technique followed by calcination process. All of the prepared two silica monoliths showed crack-free appearance with fairly good transparency, and furthermore were confirmed to have extremely high porosity, specific surface area, and mean pore size below 30 nm. The silica aerogel sample exhibited finer and more homogeneous nano-sized pore structure due to spring back effect caused by surface modification, which resulted in better thermal insulation performance. Based on measured thermal conductivities and theoretical relationship, multi-layered glass window system in which silica monolith prepared in this study was inserted as a middle layer was revealed to have superior thermal insulation performance compared to conventional air-inserted glass window system.

• Journal of the Korean Ceramic Society
• /
• v.36 no.3
• /
• pp.307-318
• /
• 1999

동결건조법에 의한 저유전성 실리카 박막의 제조공정 개발 및 층간 절연물질로의 응용성이 연구되었다. 코팅용 폴리머 실리카 졸은 TEOS와 이소프로판올(iso-propanol:IPA)또는 터트부탄올(tert-butanol:TBA)을 용매로한 2단계 공정에 의하여 제조되었으며, 이들 졸을 p-Si(111)웨이퍼 상에 스핀코팅한 습윤겔 박막을 동결건조 하여 다공성 실리카 박막을 제조하였다. 균일한 박막 코팅층을 얻을 수 있는 실리카 졸의 최적 점도범위는 IPA와 TBA를 용매로 한 실리카 졸의 경우 각각 10~14 cP와 20~30cP 정도였으며 스핀속도는 2000 rpm 이상이었다. 결함이 없는 다공성 실리카 박막은 TBA(빙점 $25^{\circ}C$)를 동결용매로 하여-196$^{\circ}C$까지 급랭시킨 후 $0^{\circ}C$와 0.1 torr 까지 가열 감압한 상태에서 고상의 TBAFMF 모두 제거한 다음 20$0^{\circ}C$까지 열처리하여 제조되었다. 다공성 실리카 박막의 두께는 졸의 타입과 스핀코팅 속도에 의해 2500~15000$\AA$범위 내에서 제어가 가능하였으며 이들 막의 밀도와 유전상 수 값은 각각 0.9$\pm$0.3g/㎤(기공율 60$\pm$10%)과 2.4 정도였다.